WO2019003812A1 - Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope, article multicouche pour une utilisation de transfert, plaque de polarisation et dispositif d'affichage d'image - Google Patents

Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope, article multicouche pour une utilisation de transfert, plaque de polarisation et dispositif d'affichage d'image Download PDF

Info

Publication number
WO2019003812A1
WO2019003812A1 PCT/JP2018/021402 JP2018021402W WO2019003812A1 WO 2019003812 A1 WO2019003812 A1 WO 2019003812A1 JP 2018021402 W JP2018021402 W JP 2018021402W WO 2019003812 A1 WO2019003812 A1 WO 2019003812A1
Authority
WO
WIPO (PCT)
Prior art keywords
optically anisotropic
group
carbon atoms
layer
substituent
Prior art date
Application number
PCT/JP2018/021402
Other languages
English (en)
Japanese (ja)
Inventor
航 中野
Original Assignee
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ゼオン株式会社 filed Critical 日本ゼオン株式会社
Priority to KR1020197037285A priority Critical patent/KR102589809B1/ko
Priority to CN201880033980.1A priority patent/CN110651208B/zh
Priority to JP2019526741A priority patent/JP7276128B2/ja
Publication of WO2019003812A1 publication Critical patent/WO2019003812A1/fr

Abstract

L'invention concerne une couche optiquement anisotrope contenant un polymère de type C positif et un produit de polymérisation d'un composé mésogène, le composé mésogène étant un composé ayant un squelette mésogène et une structure d'acrylate, et la couche optiquement anisotrope satisfait l'exigence représentée par la formule : 0,073 < AC-H/AC=O (composé mésogène) < 0,125. AC-H représente une absorption infrarouge associée à la vibration de flexion hors plan d'une liaison C-H dans la structure d'acrylate dans des spectres d'absorption infrarouge de la couche optiquement anisotrope ; et AC=O (composé mésogène) représente la somme totale d'une absorption infrarouge associée à la vibration d'étirement d'une liaison C = O dans la structure d'acrylate et d'une absorption infrarouge associée à la vibration d'étirement d'une liaison C = O dérivée de la liaison C = O dans la structure d'acrylate dans des spectres d'absorption infrarouge de la couche optiquement anisotrope. La présente invention concerne également une production d'une couche optiquement anisotrope, et une utilisation de la couche optiquement anisotrope.
PCT/JP2018/021402 2017-06-30 2018-06-04 Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope, article multicouche pour une utilisation de transfert, plaque de polarisation et dispositif d'affichage d'image WO2019003812A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020197037285A KR102589809B1 (ko) 2017-06-30 2018-06-04 광학 이방성층 및 그 제조 방법, 광학 이방성 적층체, 전사용 복층물, 편광판, 그리고 화상 표시 장치
CN201880033980.1A CN110651208B (zh) 2017-06-30 2018-06-04 光学各向异性层及其制造方法、光学各向异性层叠体、转印用多层物、偏振片、以及图像显示装置
JP2019526741A JP7276128B2 (ja) 2017-06-30 2018-06-04 光学異方性層及びその製造方法、光学異方性積層体、転写用複層物、偏光板、並びに画像表示装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017129753 2017-06-30
JP2017-129753 2017-06-30

Publications (1)

Publication Number Publication Date
WO2019003812A1 true WO2019003812A1 (fr) 2019-01-03

Family

ID=64741447

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/021402 WO2019003812A1 (fr) 2017-06-30 2018-06-04 Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope, article multicouche pour une utilisation de transfert, plaque de polarisation et dispositif d'affichage d'image

Country Status (5)

Country Link
JP (1) JP7276128B2 (fr)
KR (1) KR102589809B1 (fr)
CN (1) CN110651208B (fr)
TW (1) TWI767015B (fr)
WO (1) WO2019003812A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111752034A (zh) * 2019-03-28 2020-10-09 夏普株式会社 液晶面板的制造方法以及液晶面板
JPWO2019069855A1 (ja) * 2017-10-03 2020-11-26 日本ゼオン株式会社 光学異方性層及びその製造方法、光学異方性積層体及びその製造方法、光学異方性転写体、偏光板、並びに画像表示装置

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7464058B2 (ja) * 2019-09-30 2024-04-09 日本ゼオン株式会社 光学異方性複層物及び製造方法
CN113004729A (zh) * 2021-02-25 2021-06-22 张家港莱拓新材料科技有限公司 新型可聚合介晶混合物涂料及其在近红外波段的应用

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004163452A (ja) * 2002-11-08 2004-06-10 Nippon Kayaku Co Ltd 液晶性配合組成物およびこれを用いた位相差フィルム
JP2008158310A (ja) * 2006-12-25 2008-07-10 Nitto Denko Corp 積層体、液晶パネル、および液晶表示装置
JP2008545856A (ja) * 2005-06-10 2008-12-18 メルク パテント ゲゼルシャフト ミット ベシュレンクテル ハフトング ホメオトロピック配向の材料
JP2010020269A (ja) * 2007-09-28 2010-01-28 Fujifilm Corp 液晶表示装置
WO2017170455A1 (fr) * 2016-03-30 2017-10-05 日本ゼオン株式会社 Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope et son procédé de production, corps de transfert optiquement anisotrope, plaque polarisante, et dispositif d'affichage d'images

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1192256C (zh) * 1999-07-29 2005-03-09 帝人株式会社 相位差薄膜、层压相位差薄膜和使用该材料的液晶显示装置
JP3832301B2 (ja) * 2001-10-03 2006-10-11 チッソ株式会社 液晶性フマル酸ジエステルおよびその高分子体
JP2007241071A (ja) * 2006-03-10 2007-09-20 Fujifilm Corp 反射透過型液晶表示装置
WO2008105538A1 (fr) * 2007-03-01 2008-09-04 Zeon Corporation Composé polymérisable de cristaux liquides, composition polymérisable de cristaux liquides, substance polymère et anisotrope sur le plan optique de cristaux liquides
KR101115075B1 (ko) * 2007-12-26 2012-02-28 주식회사 엘지화학 위상차 필름, 이를 포함하는 편광판 및 액정 표시 장치
JP2012224734A (ja) * 2011-04-19 2012-11-15 Asahi Glass Co Ltd 高分子化合物、配向膜用組成物、配向膜、光学素子および光ヘッド装置
CN102304365B (zh) * 2011-05-23 2014-06-11 西安彩晶光电科技股份有限公司 极低光学各向异性混合液晶材料
EP2910986B1 (fr) * 2012-10-22 2019-03-13 Zeon Corporation Retardateur, plaque de polarisation circulaire et dispositif d'affichage d'images
TWI582218B (zh) * 2012-10-30 2017-05-11 Zeon Corp Liquid crystal composition, retardation plate, image display device, and optical anisotropic layer
JP2015014712A (ja) 2013-07-05 2015-01-22 大日本印刷株式会社 光学フィルム及び光学フィルムの作製方法
CN104339796B (zh) 2013-08-09 2018-03-02 住友化学株式会社 层叠体
KR102550872B1 (ko) * 2015-07-24 2023-07-03 스미또모 가가꾸 가부시끼가이샤 액정 경화막, 액정 경화막을 포함하는 광학 필름, 및 표시 장치
WO2017038266A1 (fr) * 2015-09-03 2017-03-09 Dic株式会社 Composition comprenant un composé ayant un groupe mésogène, polymère et corps optiquement anisotrope obtenus par polymérisation d'une composition polymérisable, et film à différence de phase

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004163452A (ja) * 2002-11-08 2004-06-10 Nippon Kayaku Co Ltd 液晶性配合組成物およびこれを用いた位相差フィルム
JP2008545856A (ja) * 2005-06-10 2008-12-18 メルク パテント ゲゼルシャフト ミット ベシュレンクテル ハフトング ホメオトロピック配向の材料
JP2008158310A (ja) * 2006-12-25 2008-07-10 Nitto Denko Corp 積層体、液晶パネル、および液晶表示装置
JP2010020269A (ja) * 2007-09-28 2010-01-28 Fujifilm Corp 液晶表示装置
WO2017170455A1 (fr) * 2016-03-30 2017-10-05 日本ゼオン株式会社 Couche optiquement anisotrope et son procédé de production, stratifié optiquement anisotrope et son procédé de production, corps de transfert optiquement anisotrope, plaque polarisante, et dispositif d'affichage d'images

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2019069855A1 (ja) * 2017-10-03 2020-11-26 日本ゼオン株式会社 光学異方性層及びその製造方法、光学異方性積層体及びその製造方法、光学異方性転写体、偏光板、並びに画像表示装置
JP7156294B2 (ja) 2017-10-03 2022-10-19 日本ゼオン株式会社 光学異方性層及びその製造方法、光学異方性積層体及びその製造方法、光学異方性転写体、偏光板、並びに画像表示装置
CN111752034A (zh) * 2019-03-28 2020-10-09 夏普株式会社 液晶面板的制造方法以及液晶面板

Also Published As

Publication number Publication date
CN110651208A (zh) 2020-01-03
CN110651208B (zh) 2021-10-01
KR20200019143A (ko) 2020-02-21
JPWO2019003812A1 (ja) 2020-04-30
JP7276128B2 (ja) 2023-05-18
TW201905119A (zh) 2019-02-01
TWI767015B (zh) 2022-06-11
KR102589809B1 (ko) 2023-10-13

Similar Documents

Publication Publication Date Title
US10705274B2 (en) Optically anisotropic layer and production method therefor, optically anisotropic laminate and production method therefor, optically anisotropic transfer body, polarization plate, and image display device
JP6860012B2 (ja) 光学異方性積層体、偏光板及び、画像表示装置
WO2018164126A1 (fr) Dispositif d&#39;affichage à diodes électroluminescentes organiques, film à différence de phase et plaque de polarisation circulaire
JP2024051161A (ja) 液晶硬化膜、液晶硬化膜を含む光学フィルム、及び表示装置
KR20200003879A (ko) 액정 필름, 광학 적층체, 원편광판, 유기 일렉트로 루미네선스 표시 장치
JP7276128B2 (ja) 光学異方性層及びその製造方法、光学異方性積層体、転写用複層物、偏光板、並びに画像表示装置
WO2016136901A1 (fr) Corps de transfert pour film optique, film optique, dispositif d&#39;affichage à électroluminescence organique, et procédé de fabrication de film optique
WO2018123725A1 (fr) Plaque de polarisation circulaire, et dispositif d&#39;affichage électroluminescent organique
CN108780186A (zh) 光学各向异性层叠体、圆偏振片以及图像显示装置
JP6724297B2 (ja) 光学積層体の製造方法、円偏光板の製造方法及び有機エレクトロルミネッセンス表示装置の製造方法
WO2017110631A1 (fr) Couche anisotrope optique et son procédé de fabrication, stratifié anisotrope optique, et plaque à polarisation circulaire
JP2017072786A (ja) 積層光学フィルム、照明装置及び表示装置
JP2018146637A (ja) 光学異方性層の製造方法
JP6287371B2 (ja) 光学フィルム、光学フィルム用転写体、及び画像表示装置
JP7156294B2 (ja) 光学異方性層及びその製造方法、光学異方性積層体及びその製造方法、光学異方性転写体、偏光板、並びに画像表示装置
JP7355955B1 (ja) 光学積層体
JP2019066777A (ja) 光学異方性層及びその製造方法、光学異方性積層体及びその製造方法、光学異方性転写体、偏光板、並びに画像表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18824695

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019526741

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20197037285

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18824695

Country of ref document: EP

Kind code of ref document: A1