WO2018123911A1 - Procédé de production de propène contenant du chlore - Google Patents
Procédé de production de propène contenant du chlore Download PDFInfo
- Publication number
- WO2018123911A1 WO2018123911A1 PCT/JP2017/046251 JP2017046251W WO2018123911A1 WO 2018123911 A1 WO2018123911 A1 WO 2018123911A1 JP 2017046251 W JP2017046251 W JP 2017046251W WO 2018123911 A1 WO2018123911 A1 WO 2018123911A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formula
- catalyst
- reaction
- compound represented
- chlorine
- Prior art date
Abstract
L'invention concerne un procédé de production capable de produire de manière efficace un propène contenant du chlore, tel que le HCFO-1224yd. Le procédé de production d'un propène contenant du chlore selon la présente invention consiste à faire réagir un composé représenté par la formule (1) avec de l'hydrogène en présence d'un catalyseur pour produire un composé représenté par la formule (2). Le catalyseur est supporté par un porteur, et contient au moins un premier élément choisi parmi Pd et Pt, et au moins un second élément choisi parmi Ru, Cu, Au, Zn, Cd, Hg, Al, Ga, In, Si, Ge, Sn, Pb, P, As, Sb, Bi, S, Se, Te et Po. Formule (1) : CX3CY=CCl2 (dans laquelle chaque X représente indépendamment F, Cl ou H et Y représente F ou H). Formule (2) : CX3CY=CHCl (dans laquelle X et Y sont identiques à X et Y dans la formule (1)).
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016-255659 | 2016-12-28 | ||
JP2016255659 | 2016-12-28 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2018123911A1 true WO2018123911A1 (fr) | 2018-07-05 |
Family
ID=62707490
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2017/046251 WO2018123911A1 (fr) | 2016-12-28 | 2017-12-22 | Procédé de production de propène contenant du chlore |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2018123911A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019123759A1 (fr) * | 2017-12-22 | 2019-06-27 | Agc株式会社 | Composition de solvant, procédé de nettoyage, composition de formation de revêtement, procédé de fabrication de substrat revêtu, composition d'aérosol, composition de rinçage, procédé pour élément de nettoyage, et dispositif pour élément de nettoyage |
WO2020213600A1 (fr) * | 2019-04-16 | 2020-10-22 | Agc株式会社 | Procédé de production de 1-chloro-2,3,3,3-tétrafluoropropène |
WO2021044983A1 (fr) * | 2019-09-06 | 2021-03-11 | Agc株式会社 | Procédé de production d'hydrofluorooléfine |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011162336A1 (fr) * | 2010-06-23 | 2011-12-29 | 旭硝子株式会社 | Procédé de fabrication de 1,1-dichloro-2,3,3,3-tétra-fluoropropène et de 2,3,3,3-tétrafluoropropène |
WO2015160532A1 (fr) * | 2014-04-16 | 2015-10-22 | The Chemours Company Fc, Llc | Conversion de chlorofluororopanes et de chlorofluropropènes en fluoropropanes et fluororopènes plus recherchés |
WO2016031777A1 (fr) * | 2014-08-25 | 2016-03-03 | 旭硝子株式会社 | Procédé de production d'une hydrofluorooléfine |
-
2017
- 2017-12-22 WO PCT/JP2017/046251 patent/WO2018123911A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011162336A1 (fr) * | 2010-06-23 | 2011-12-29 | 旭硝子株式会社 | Procédé de fabrication de 1,1-dichloro-2,3,3,3-tétra-fluoropropène et de 2,3,3,3-tétrafluoropropène |
WO2015160532A1 (fr) * | 2014-04-16 | 2015-10-22 | The Chemours Company Fc, Llc | Conversion de chlorofluororopanes et de chlorofluropropènes en fluoropropanes et fluororopènes plus recherchés |
WO2016031777A1 (fr) * | 2014-08-25 | 2016-03-03 | 旭硝子株式会社 | Procédé de production d'une hydrofluorooléfine |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019123759A1 (fr) * | 2017-12-22 | 2019-06-27 | Agc株式会社 | Composition de solvant, procédé de nettoyage, composition de formation de revêtement, procédé de fabrication de substrat revêtu, composition d'aérosol, composition de rinçage, procédé pour élément de nettoyage, et dispositif pour élément de nettoyage |
WO2020213600A1 (fr) * | 2019-04-16 | 2020-10-22 | Agc株式会社 | Procédé de production de 1-chloro-2,3,3,3-tétrafluoropropène |
JP7484900B2 (ja) | 2019-04-16 | 2024-05-16 | Agc株式会社 | 1-クロロ-2,3,3,3-テトラフルオロプロペンの製造方法 |
WO2021044983A1 (fr) * | 2019-09-06 | 2021-03-11 | Agc株式会社 | Procédé de production d'hydrofluorooléfine |
JP7511113B2 (ja) | 2019-09-06 | 2024-07-05 | Agc株式会社 | ハイドロフルオロオレフィンの製造方法 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10781151B2 (en) | Process for producing hydrofluoroolefin | |
JP6673413B2 (ja) | フルオロオレフィンの製造方法 | |
JP5947337B2 (ja) | 2,2,3,3−テトラフルオロ−1−プロペンの製造方法 | |
JP6477712B2 (ja) | ハイドロフルオロオレフィンの製造方法 | |
US10189758B2 (en) | Method for producing hydrofluoroolefin | |
US9850189B2 (en) | Method for producing trifluoroethylene | |
JP6780696B2 (ja) | 1−クロロ−2,3,3,3−テトラフルオロプロペンの製造方法 | |
WO2018123911A1 (fr) | Procédé de production de propène contenant du chlore | |
JP5533002B2 (ja) | 3,3,3−トリフルオロプロペンの製造方法 | |
JP5817591B2 (ja) | 2,3,3,3−テトラフルオロプロペンの製造方法 | |
JP5713018B2 (ja) | 2,3,3,3−テトラフルオロプロペンの製造方法 | |
JP7511113B2 (ja) | ハイドロフルオロオレフィンの製造方法 | |
JP7553758B2 (ja) | ビニル化合物の製造方法 | |
CN107262092A (zh) | 一种合成顺式1,1,1,4,4,4‑六氟‑2‑丁烯的催化剂及其制备方法和用途 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 17889025 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 17889025 Country of ref document: EP Kind code of ref document: A1 |
|