WO2018123077A1 - Élément optique - Google Patents

Élément optique Download PDF

Info

Publication number
WO2018123077A1
WO2018123077A1 PCT/JP2017/006188 JP2017006188W WO2018123077A1 WO 2018123077 A1 WO2018123077 A1 WO 2018123077A1 JP 2017006188 W JP2017006188 W JP 2017006188W WO 2018123077 A1 WO2018123077 A1 WO 2018123077A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin layer
compound
optical element
functional resin
functional
Prior art date
Application number
PCT/JP2017/006188
Other languages
English (en)
Japanese (ja)
Inventor
忠史 鳥居
敬介 荻野
Original Assignee
伊藤光学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 伊藤光学工業株式会社 filed Critical 伊藤光学工業株式会社
Priority to JP2018537546A priority Critical patent/JP6585850B2/ja
Priority to PCT/JP2017/046616 priority patent/WO2018124063A1/fr
Publication of WO2018123077A1 publication Critical patent/WO2018123077A1/fr

Abstract

La présente invention concerne la fourniture d'un élément optique qui présente une excellente adhérence d'une couche de résine fonctionnelle dans laquelle une fracture est peu susceptible de se produire même lorsque l'élément optique est soumis à une force excessive. Cet élément optique est doté d'une couche de résine fonctionnelle (15) intégrée dans une ou les deux surfaces d'un substrat de verre organique (11) qui est un moulage de résine, la couche de résine fonctionnelle (15) contient un agent chimique fonctionnel, un composé isocyanate et un composé polyol, et le composé polyol contient un composé polymère d'alcool polyhydrique ayant un poids moléculaire moyen de 180 ou plus. Comme le composé polymère d'alcool polyhydrique ayant un poids moléculaire moyen de 180 ou plus est hautement hydrophile, et qu'un polymère qui est formé à partir du composé polymère d'alcool polyhydrique et du composé isocyanate qui est lipophile est utilisé en tant que liant, la couche de résine fonctionnelle (15) a une combinaison bien équilibrée entre l'hydrophilie et la lipophilie et présente une excellente adhérence au substrat en verre organique (11).
PCT/JP2017/006188 2016-12-28 2017-02-20 Élément optique WO2018123077A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2018537546A JP6585850B2 (ja) 2016-12-28 2017-12-26 光学要素およびその製造方法
PCT/JP2017/046616 WO2018124063A1 (fr) 2016-12-28 2017-12-26 Élément optique et son procédé de production

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016255420 2016-12-28
JP2016-255420 2016-12-28

Publications (1)

Publication Number Publication Date
WO2018123077A1 true WO2018123077A1 (fr) 2018-07-05

Family

ID=62710008

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/006188 WO2018123077A1 (fr) 2016-12-28 2017-02-20 Élément optique

Country Status (2)

Country Link
JP (1) JP6585850B2 (fr)
WO (1) WO2018123077A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110330784A (zh) * 2019-07-24 2019-10-15 上海康耐特光学有限公司 一种聚氨酯混合物及其制备方法和应用、包含其的改性镜片
CN112812667A (zh) * 2019-10-31 2021-05-18 天元清水光学(上海)有限公司 一种功能性树脂层及其应用于防蓝光镜片的制备工艺
CN113348223A (zh) * 2019-01-30 2021-09-03 三井化学株式会社 光学材料用聚合性组合物的制造方法
CN115768746A (zh) * 2020-05-28 2023-03-07 株式会社德山 光学材料用化合物、固化性组合物、固化物和光学物品

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001518960A (ja) * 1997-04-04 2001-10-16 コーニング ソシエテ アノニム 自己光安定化フォトクロミック・ポリマー、その製法、およびそれを含む物品
JP2009507264A (ja) * 2005-09-07 2009-02-19 トランジションズ オプティカル， インコーポレイテッド フォトクロミック多重焦点光学製品
JP2010031294A (ja) * 2002-12-05 2010-02-12 Tokuyama Corp コーティング組成物および光学物品

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3600625B2 (ja) * 1993-09-02 2004-12-15 三井化学株式会社 二成分系ポリウレタン発泡型シーリング材組成物、シーリング方法及び灯具
JP3288151B2 (ja) * 1993-09-02 2002-06-04 三井化学株式会社 二成分系ポリウレタン発泡型シーリング材組成物、シーリング方法及び灯具
JP2006039394A (ja) * 2004-07-29 2006-02-09 Canon Chemicals Inc 導電性ローラ
US9475903B2 (en) * 2013-09-26 2016-10-25 Mitsui Chemicals, Inc. 1,4-bis(isocyanatomethyl)cyclohexane, polyisocyanate composition, polyurethane resin, molded article, eyewear material, eyewear frame, and lens
CN105658694A (zh) * 2013-10-21 2016-06-08 三井化学株式会社 光学材料用聚合性组合物和光学材料
CN105658693B (zh) * 2013-10-21 2018-10-09 三井化学株式会社 光学材料用聚合性组合物和光学材料
EP3103822B1 (fr) * 2014-02-03 2019-11-06 Mitsui Chemicals, Inc. Composition polymérisable pour matériau optique et matériau optique et lentille en plastique obtenue à partir de ladite composition

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001518960A (ja) * 1997-04-04 2001-10-16 コーニング ソシエテ アノニム 自己光安定化フォトクロミック・ポリマー、その製法、およびそれを含む物品
JP2010031294A (ja) * 2002-12-05 2010-02-12 Tokuyama Corp コーティング組成物および光学物品
JP2009507264A (ja) * 2005-09-07 2009-02-19 トランジションズ オプティカル， インコーポレイテッド フォトクロミック多重焦点光学製品

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113348223A (zh) * 2019-01-30 2021-09-03 三井化学株式会社 光学材料用聚合性组合物的制造方法
CN110330784A (zh) * 2019-07-24 2019-10-15 上海康耐特光学有限公司 一种聚氨酯混合物及其制备方法和应用、包含其的改性镜片
CN112812667A (zh) * 2019-10-31 2021-05-18 天元清水光学(上海)有限公司 一种功能性树脂层及其应用于防蓝光镜片的制备工艺
CN115768746A (zh) * 2020-05-28 2023-03-07 株式会社德山 光学材料用化合物、固化性组合物、固化物和光学物品

Also Published As

Publication number Publication date
JPWO2018124063A1 (ja) 2019-01-10
JP6585850B2 (ja) 2019-10-02

Similar Documents

Publication Publication Date Title
AU2008245205B9 (en) Infrared ray-absorbable eyeglass lens, and method for production thereof
KR101761828B1 (ko) 광학수지 조성물 및 이를 이용한 광학용 렌즈
US7035010B2 (en) Polarized lenses with variable transmission
WO2018123077A1 (fr) Élément optique
EP1243621B1 (fr) Matiere a base de plastique
US11774636B2 (en) Blue light cutting optical material having a bluish appearance
JP2012173704A (ja) 防眩光学要素
JP2010085911A (ja) 赤外線吸収性眼鏡用レンズ基材
KR20180040651A (ko) 광학 재료용 중합성 조성물, 광학 재료, 광학 재료용 중합성 조성물의 제조 방법 및 광학 재료의 제조 방법
WO2017047684A1 (fr) Procédé de préparation d'une composition polymérisable pour matériau optique, et procédé de production dudit matériau optique
KR20170008679A (ko) 전자기파 차단용 광학 조성물 및 이로부터 광학 렌즈의 제조 방법
AU2018227845B2 (en) Optical articles comprising photochromic poly(urea-urethane)
JP2020530524A (ja) 光学接着剤ならびにそれにより形成された光学積層体および光学レンズ
US20120229759A1 (en) Infrared absorbing eyeglass lens substrate
KR20210134700A (ko) 광학 재료의 제조 방법, 광학 재료용 중합성 조성물
JP2019015922A (ja) 眼鏡レンズ素材
JP7228206B2 (ja) 光学材料
WO2018124063A1 (fr) Élément optique et son procédé de production
WO2018008179A1 (fr) Matériau de lunettes
WO2018037621A1 (fr) Élément optique de modulation de lumière
JP6692249B2 (ja) 眼鏡素材
JP7160649B2 (ja) 光学材料用重合性組成物および該組成物から得られた光学材料
JP7540625B2 (ja) 光学材料、光学材料用重合性組成物、プラスチックレンズ、アイウェア及び光学センサー
CN112812667A (zh) 一种功能性树脂层及其应用于防蓝光镜片的制备工艺
JP2019086550A (ja) 光学要素

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17887266

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17887266

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载