WO2018008179A1 - Matériau de lunettes - Google Patents

Matériau de lunettes Download PDF

Info

Publication number
WO2018008179A1
WO2018008179A1 PCT/JP2017/006187 JP2017006187W WO2018008179A1 WO 2018008179 A1 WO2018008179 A1 WO 2018008179A1 JP 2017006187 W JP2017006187 W JP 2017006187W WO 2018008179 A1 WO2018008179 A1 WO 2018008179A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin layer
organic glass
functional resin
glass substrate
absorption peak
Prior art date
Application number
PCT/JP2017/006187
Other languages
English (en)
Japanese (ja)
Inventor
忠史 鳥居
Original Assignee
伊藤光学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 伊藤光学工業株式会社 filed Critical 伊藤光学工業株式会社
Priority to JP2018525926A priority Critical patent/JPWO2018008179A1/ja
Publication of WO2018008179A1 publication Critical patent/WO2018008179A1/fr

Abstract

La présente invention vise à proposer une matière de lunettes qui peut supprimer le jaunissement de celle-ci et des différences de niveau de gris dans la gradation de couleur provoquée par la différence d'épaisseurs des périphéries interne et externe de celle-ci même lorsqu'une matière de lunettes contient un absorbant d'ultraviolets ayant un taux de coupure élevé contre la lumière bleue. Dans ce matériau de lunettes, une couche de résine fonctionnelle est intégrée à une surface ou aux deux surfaces d'un substrat en verre organique qui est un corps moulé en résine, la couche de résine fonctionnelle 15 contient un absorbant d'ultraviolets ayant une longueur d'onde de pic d'absorption de 320 nm ou plus et une épaisseur plus petite que le substrat de verre organique 11. Par conséquent, la matière de lunettes peut avoir un jaunissement (Y1) inférieur à 10.
PCT/JP2017/006187 2016-07-06 2017-02-20 Matériau de lunettes WO2018008179A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018525926A JPWO2018008179A1 (ja) 2016-07-06 2017-02-20 眼鏡素材

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016134505 2016-07-06
JP2016-134505 2016-07-06

Publications (1)

Publication Number Publication Date
WO2018008179A1 true WO2018008179A1 (fr) 2018-01-11

Family

ID=60901680

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/006187 WO2018008179A1 (fr) 2016-07-06 2017-02-20 Matériau de lunettes

Country Status (2)

Country Link
JP (1) JPWO2018008179A1 (fr)
WO (1) WO2018008179A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112812667A (zh) * 2019-10-31 2021-05-18 天元清水光学(上海)有限公司 一种功能性树脂层及其应用于防蓝光镜片的制备工艺
CN113573900A (zh) * 2019-03-20 2021-10-29 积水化学工业株式会社 热塑性膜及夹层玻璃

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11295502A (ja) * 1998-02-10 1999-10-29 Asahi Optical Co Ltd プラスチックレンズ
JP2001091906A (ja) * 1999-09-20 2001-04-06 Hoya Corp 紫外線吸収性に優れたプラスチック眼鏡レンズ及びその製造方法
JP2008132783A (ja) * 2001-07-16 2008-06-12 Asahi Lite Optical Co Ltd 樹脂レンズの製造方法とその樹脂レンズ
JP2012173704A (ja) * 2011-02-24 2012-09-10 Ito Kogaku Kogyo Kk 防眩光学要素
JP2013011840A (ja) * 2011-06-02 2013-01-17 Ito Kogaku Kogyo Kk 防眩光学要素
JP2014156067A (ja) * 2013-02-15 2014-08-28 Ito Kogaku Kogyo Kk 樹脂レンズの製造方法
WO2015046540A1 (fr) * 2013-09-30 2015-04-02 ホヤ レンズ タイランド リミテッド Substrat en plastique transparent ainsi que lentille en plastique
WO2015088015A1 (fr) * 2013-12-13 2015-06-18 三井化学株式会社 Composition polymérisable pour matériaux optiques

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101582783B1 (ko) * 2013-02-27 2016-01-05 미쓰이 가가쿠 가부시키가이샤 광학 재료, 광학 재료용 조성물 및 그 용도

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11295502A (ja) * 1998-02-10 1999-10-29 Asahi Optical Co Ltd プラスチックレンズ
JP2001091906A (ja) * 1999-09-20 2001-04-06 Hoya Corp 紫外線吸収性に優れたプラスチック眼鏡レンズ及びその製造方法
JP2008132783A (ja) * 2001-07-16 2008-06-12 Asahi Lite Optical Co Ltd 樹脂レンズの製造方法とその樹脂レンズ
JP2012173704A (ja) * 2011-02-24 2012-09-10 Ito Kogaku Kogyo Kk 防眩光学要素
JP2013011840A (ja) * 2011-06-02 2013-01-17 Ito Kogaku Kogyo Kk 防眩光学要素
JP2014156067A (ja) * 2013-02-15 2014-08-28 Ito Kogaku Kogyo Kk 樹脂レンズの製造方法
WO2015046540A1 (fr) * 2013-09-30 2015-04-02 ホヤ レンズ タイランド リミテッド Substrat en plastique transparent ainsi que lentille en plastique
WO2015088015A1 (fr) * 2013-12-13 2015-06-18 三井化学株式会社 Composition polymérisable pour matériaux optiques

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113573900A (zh) * 2019-03-20 2021-10-29 积水化学工业株式会社 热塑性膜及夹层玻璃
CN113573900B (zh) * 2019-03-20 2023-09-15 积水化学工业株式会社 热塑性膜及夹层玻璃
US11833784B2 (en) 2019-03-20 2023-12-05 Sekisui Chemical Co., Ltd. Thermoplastic film and laminated glass
CN112812667A (zh) * 2019-10-31 2021-05-18 天元清水光学(上海)有限公司 一种功能性树脂层及其应用于防蓝光镜片的制备工艺

Also Published As

Publication number Publication date
JPWO2018008179A1 (ja) 2019-04-18

Similar Documents

Publication Publication Date Title
AU2008245205B9 (en) Infrared ray-absorbable eyeglass lens, and method for production thereof
EP1243621B1 (fr) Matiere a base de plastique
KR101761828B1 (ko) 광학수지 조성물 및 이를 이용한 광학용 렌즈
US11067834B2 (en) High refractive index polarized spectacle lens
US7035010B2 (en) Polarized lenses with variable transmission
JP5075080B2 (ja) 赤外線吸収性眼鏡用レンズ基材
JP7033605B2 (ja) フォトクロミックアイウェアレンズの製造方法およびフォトクロミックアイウェア製品
JP7123082B2 (ja) レンズおよびレンズの製造方法
US20120229759A1 (en) Infrared absorbing eyeglass lens substrate
JP6585850B2 (ja) 光学要素およびその製造方法
WO2018008179A1 (fr) Matériau de lunettes
CN112219157A (zh) 颜色增强镜片
US20120188503A1 (en) Eyeglass lens made of allyl diglycol carbonate resin
CN113692552B (zh) 光学材料
WO2018124063A1 (fr) Élément optique et son procédé de production
JP6692249B2 (ja) 眼鏡素材
WO2018037621A1 (fr) Élément optique de modulation de lumière
CN112812667A (zh) 一种功能性树脂层及其应用于防蓝光镜片的制备工艺

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2018525926

Country of ref document: JP

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17823788

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17823788

Country of ref document: EP

Kind code of ref document: A1