WO2018196033A1 - 一种白乳胶黏合剂及其制备方法 - Google Patents
一种白乳胶黏合剂及其制备方法 Download PDFInfo
- Publication number
- WO2018196033A1 WO2018196033A1 PCT/CN2017/083430 CN2017083430W WO2018196033A1 WO 2018196033 A1 WO2018196033 A1 WO 2018196033A1 CN 2017083430 W CN2017083430 W CN 2017083430W WO 2018196033 A1 WO2018196033 A1 WO 2018196033A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- white latex
- latex adhesive
- filler
- adhesive
- Prior art date
Abstract
一种白乳胶黏合剂及其制备方法,按重量份包括聚乙烯醇300-400份、盐酸5-8份、三聚磷酸钠30-50份、液碱7-9份、乳化剂12-16份、邻苯二甲酸二丁酯10-20份、聚醋酸乙烯450-500份、填料200-300份、油酸三乙醇胺2-4份。由此,黏合剂冷结温度低、防冻性好、抗拉及抗剪切强度高;具有防水性能、不脱胶;耐热性好,可抗100℃以上的高温;成本较低,在有反应釜或没有反应釜的条件下均可进行生产。
Description
本发明涉及黏合剂,尤其涉及一种白乳胶黏合剂及其制备方法。
白乳胶是目前用途最广、用量最大的粘合剂品种之一。它是以水为分散介质进行乳液聚合而得,是一种水性环保胶。主要被用在木材加工、家具组装、卷烟接嘴、建筑装潢、织物粘结、制品加工、印刷装订、工艺品制造以及皮革加工、标签固定、瓷砖黏贴等,是一种环保型的胶黏剂。
一般所称的白乳胶即聚醋酸乙烯乳液,由于制备操作工艺较复杂,设备投资大,而且醋酸乙烯单体价格也较高,所以白乳胶的生产成本较高。它的较为明显的缺点是耐水性和耐湿性差,易在潮湿空气中吸湿,在高温下使用会产生蠕变现象,使胶接强度下降,在-5℃以下储存易冻结,使乳液受到破坏。
发明内容
本发明的目的提供一种白乳胶黏合剂及其制备方法,解决上述现有技术问题中的一个或者多个。
根据本发明的一个方面,提供一种白乳胶黏合剂,按重量份包括聚乙烯醇300-400份、盐酸5-8份、三聚磷酸钠30-50份、液碱7-9份、乳化剂12-16份、邻苯二甲酸二丁酯10-20份、聚醋酸乙烯450-500份、填料200-300份、油酸三乙醇胺2-4份。
在一些实施方式中:乳化剂为OP-10或TX-10。
在一些实施方式中:填料为滑石粉、钛白粉或锌钡白。
本发明还提供了上述的一种白乳胶黏合剂的制备方法,包括以下步骤:
步骤一:在90-95℃下,将聚乙烯醇溶解于水中,用盐酸调节pH值至2-3,保持温度在85-95℃,在搅拌下加入三聚磷酸钠,反应0.5-1h,降温至50℃以下,加入液碱调节pH值至6-8;
步骤二:在搅拌下,保持温度为50℃,加入乳化剂、领苯二甲酸二丁酯,在40-50℃下保温1h并搅拌,然后冷却至常温,搅拌,加入聚醋酸乙烯,继续搅拌0.5h以上;
步骤三:向步骤二所得物料中加入填料及油酸三乙醇胺,并搅拌1.5h,即可得成品。
本发明的黏合剂冷结温度低、防冻性好、抗拉及抗剪切强度高;具有防水性能、不脱胶;耐热性好,可抗100℃以上的高温;成本较低,在有反应釜或没有反应釜的条件下均可进行生产。
下面通过实施例对本发明作进一步详细说明。
实施例1:
白乳胶黏合剂,按重量份包括聚乙烯醇400份、盐酸8份、三聚磷酸钠50份、液碱9份、乳化剂13份、邻苯二甲酸二丁酯15份、聚醋酸乙烯460份、填料250份、油酸三乙醇胺3.5份。
其中,乳化剂为OP-10或TX-10;填料为滑石粉、钛白粉或锌钡白。
本发明白乳胶黏合剂的制备方法:包括以下步骤:
步骤一:在90℃下,将聚乙烯醇溶解于水中,用盐酸调节pH值至2.5,保持温度在90℃,在搅拌下加入三聚磷酸钠,反应1h,降温至50℃以下,加入液碱调节pH值至7;
步骤二:在搅拌下,保持温度为50℃,加入乳化剂、领苯二甲酸二丁酯,在45℃下保温1h并搅拌,然后冷却至常温,搅拌,加入聚醋酸乙烯,继续搅拌0.5h以上;
步骤三:向步骤二所得物料中加入填料及油酸三乙醇胺,并搅拌1.5h,即可得成品。
用锯齿形镘刀在基面上梳理出饱满无间断的锯齿状条纹,能有效保证胶粘剂均匀的涂抹在基面上,当将木材、地板等按压到胶粘剂上时,胶粘剂条纹凸出部分被压入凹槽内,并在外界压力的作用下与木材、地板等充分接触,有效避免了木材、地板等因无法与胶粘剂很好接触而出现空鼓的现象。
实施例2:
白乳胶黏合剂,按重量份包括聚乙烯醇330份、盐酸7份、三聚磷酸钠45份、液碱7.5份、乳化剂13份、邻苯二甲酸二丁酯14份、聚醋酸乙烯500份、填料300份、油酸三乙醇胺2份。
其中,乳化剂为OP-10或TX-10;填料为滑石粉、钛白粉或锌钡白。
本发明白乳胶黏合剂的制备方法:包括以下步骤:
步骤一:在95℃下,将聚乙烯醇溶解于水中,用盐酸调节pH值至2,保持温度在95℃,在搅拌下加入三聚磷酸钠,反应1h,降温至50℃以下,加入液碱调节pH值至7.2;
步骤二:在搅拌下,保持温度为40℃,加入乳化剂、领苯二甲酸二丁
酯,在40℃下保温1h并搅拌,然后冷却至常温,搅拌,加入聚醋酸乙烯,继续搅拌1h以上;
步骤三:向步骤二所得物料中加入填料及油酸三乙醇胺,并搅拌1.5h,即可得成品。
用锯齿形镘刀在基面上梳理出饱满无间断的锯齿状条纹,能有效保证胶粘剂均匀的涂抹在基面上,当将木材、地板等按压到胶粘剂上时,胶粘剂条纹凸出部分被压入凹槽内,并在外界压力的作用下与木材、地板等充分接触,有效避免了木材、地板等因无法与胶粘剂很好接触而出现空鼓的现象。
实施例3:
白乳胶黏合剂,按重量份包括聚乙烯醇380份、盐酸7份、三聚磷酸钠35份、液碱8.5份、乳化剂14份、邻苯二甲酸二丁酯17份、聚醋酸乙烯490份、填料280份、油酸三乙醇胺3份。
其中,乳化剂为OP-10或TX-10;填料为滑石粉、钛白粉或锌钡白。
本发明白乳胶黏合剂的制备方法:包括以下步骤:
步骤一:在92℃下,将聚乙烯醇溶解于水中,用盐酸调节pH值至2-3,保持温度在92℃,在搅拌下加入三聚磷酸钠,反应1h,降温至50℃以下,加入液碱调节pH值至6.5;
步骤二:在搅拌下,保持温度为45℃,加入乳化剂、领苯二甲酸二丁酯,在45℃下保温1h并搅拌,然后冷却至常温,搅拌,加入聚醋酸乙烯,继续搅拌0.5h以上;
步骤三:向步骤二所得物料中加入填料及油酸三乙醇胺,并搅拌2h,即可得成品。
用锯齿形镘刀在基面上梳理出饱满无间断的锯齿状条纹,能有效保证胶粘剂均匀的涂抹在基面上,当将木材、地板等按压到胶粘剂上时,胶粘剂条纹凸出部分被压入凹槽内,并在外界压力的作用下与木材、地板等充分接触,有效避免了木材、地板等因无法与胶粘剂很好接触而出现空鼓的现象。
上述实施例的产品与常规黏合剂对于使用后各项效果试验如下:
其中,发明人通过大量的实验得出,本品对如木材、纸张、棉布、皮革、陶瓷等有很强的粘结力,能够室温固化,且固化速度快,同时固化后的胶膜有一定的韧性,耐稀碱,稀酸,且耐油性、防水性也很好。
综上所述,本发明的黏合剂冷结温度低、防冻性好、抗拉及抗剪切强度高;具有防水性能、不脱胶;耐热性好,可抗100℃以上的高温;成本较低,在有反应釜或没有反应釜的条件下均可进行生产。
以上所述仅是本发明的一种实施方式,应当指出,对于本领域普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干相似的变形和改进,这些也应视为本发明的保护范围之内。
Claims (4)
- 一种白乳胶黏合剂,其特征在于:按重量份包括聚乙烯醇300-400份、盐酸5-8份、三聚磷酸钠30-50份、液碱7-9份、乳化剂12-16份、邻苯二甲酸二丁酯10-20份、聚醋酸乙烯450-500份、填料200-300份、油酸三乙醇胺2-4份。
- 根据权利要求1所述的一种白乳胶黏合剂,其特征在于:所述乳化剂为OP-10或TX-10。
- 根据权利要求1所述的一种白乳胶黏合剂,其特征在于:所述填料为滑石粉、钛白粉或锌钡白。
- 一种制备权利要求1-3任一项所述白乳胶黏合剂的方法,其特征在于,包括以下步骤:步骤一:在90-95℃下,将聚乙烯醇溶解于水中,用盐酸调节pH值至2-3,保持温度在85-95℃,在搅拌下加入三聚磷酸钠,反应0.5-1h,降温至50℃以下,加入液碱调节pH值至6-8;步骤二:在搅拌下,保持温度为50℃,加入乳化剂、领苯二甲酸二丁酯,在40-50℃下保温1h并搅拌,然后冷却至常温,搅拌,加入聚醋酸乙烯,继续搅拌0.5h以上;步骤三:向步骤二所得物料中加入填料及油酸三乙醇胺,并搅拌1.5h,即可得成品。