WO2018182006A1 - Diaphragme, bain électrolytique, et procédé de fabrication d'hydrogène - Google Patents

Diaphragme, bain électrolytique, et procédé de fabrication d'hydrogène Download PDF

Info

Publication number
WO2018182006A1
WO2018182006A1 PCT/JP2018/013957 JP2018013957W WO2018182006A1 WO 2018182006 A1 WO2018182006 A1 WO 2018182006A1 JP 2018013957 W JP2018013957 W JP 2018013957W WO 2018182006 A1 WO2018182006 A1 WO 2018182006A1
Authority
WO
WIPO (PCT)
Prior art keywords
diaphragm
less
ptfe
electrolysis
mass
Prior art date
Application number
PCT/JP2018/013957
Other languages
English (en)
Japanese (ja)
Inventor
稔幸 平野
悠介 鈴木
一洋 大海
則和 藤本
Original Assignee
旭化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭化成株式会社 filed Critical 旭化成株式会社
Priority to JP2019509422A priority Critical patent/JPWO2018182006A1/ja
Publication of WO2018182006A1 publication Critical patent/WO2018182006A1/fr

Abstract

L'objet de l'invention est caractéristique en ce qu'il contient au moins un polytétrafluoroéthylène (PTFE) et un composé inorganique, le diamètre moyen d'orifice de perméation est supérieur ou égal à 0,02μｍ et inférieur ou égal à 1,0μｍ, le diamètre maximal d'orifice est supérieur ou égal à 0,2μｍ et inférieur ou égal à 2,0μｍ, sa porosité est supérieure ou égale à 30% et inférieure ou égale à 90%, son épaisseur est supérieure ou égale à 100μｍ et inférieure ou égale à 600μｍ, sa teneur en composé inorganique est supérieure ou égale à 70% en masse et inférieure ou égale à 95% en masse, lorsque la masse totale de PTFE et de composé inorganique vaut 100% en masse.
PCT/JP2018/013957 2017-03-31 2018-03-30 Diaphragme, bain électrolytique, et procédé de fabrication d'hydrogène WO2018182006A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2019509422A JPWO2018182006A1 (ja) 2017-03-31 2018-03-30 隔膜、電解槽及び水素製造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2017072978 2017-03-31
JP2017-072978 2017-03-31
JP2017199785 2017-10-13
JP2017-199785 2017-10-13

Publications (1)

Publication Number Publication Date
WO2018182006A1 true WO2018182006A1 (fr) 2018-10-04

Family

ID=63676385

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/013957 WO2018182006A1 (fr) 2017-03-31 2018-03-30 Diaphragme, bain électrolytique, et procédé de fabrication d'hydrogène

Country Status (2)

Country Link
JP (1) JPWO2018182006A1 (fr)
WO (1) WO2018182006A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020105557A (ja) * 2018-12-26 2020-07-09 株式会社日本触媒 アルカリ水電解用隔膜
JP2020169349A (ja) * 2019-04-01 2020-10-15 株式会社日本触媒 アルカリ水電解用隔膜ならびに該隔膜の製造方法
WO2021019985A1 (fr) * 2019-07-30 2021-02-04 旭化成株式会社 Cuve d'électrolyse d'eau alcaline
WO2021085334A1 (fr) * 2019-10-31 2021-05-06 株式会社トクヤマ Tapis élastique pour cellules d'électrolyse d'eau alcaline
CN114086213A (zh) * 2021-10-27 2022-02-25 四川华能氢能科技有限公司 一种降低碱性电解水制氢能耗的复合隔膜
CN115074775A (zh) * 2022-07-22 2022-09-20 北京化工大学 一种一体化复合膜及其制备方法和在碱性水解制氢中的应用
CN119239017A (zh) * 2024-12-04 2025-01-03 苏州希倍优氢能源科技有限公司 一种三明治夹芯结构电解水复合隔膜、制备方法及应用
CN119529453A (zh) * 2025-01-23 2025-02-28 山东东岳未来氢能材料股份有限公司 一种Al2O3/PTFE复合微孔膜及其制备方法与应用
CN119529453B (zh) * 2025-01-23 2025-05-27 山东东岳未来氢能材料股份有限公司 一种Al2O3/PTFE复合微孔膜及其制备方法与应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5177674A (ja) * 1974-12-27 1976-07-06 Sumitomo Electric Industries Shifutsukaechirenjushitakoseikozobutsu
JPS56169782A (en) * 1980-06-03 1981-12-26 Asahi Glass Co Ltd Production of caustic alkali
JPS57131236A (en) * 1980-11-06 1982-08-14 Gore & Ass Multi-component porous high strength ptfe products and manufacture
JPS591690A (ja) * 1982-06-09 1984-01-07 インペリアル・ケミカル・インダストリ−ズ・ピ−エルシ− 電解槽用の多孔質隔膜及びその製造法
JPS59166541A (ja) * 1983-03-10 1984-09-19 Japan Goatetsukusu Kk 耐薬品性多孔質膜の製造方法
JPS6217193A (ja) * 1985-07-13 1987-01-26 Shirakawa Seisakusho:Kk 電極・隔膜組立体
WO2016148302A1 (fr) * 2015-03-18 2016-09-22 旭化成株式会社 Membrane pour électrolyse d'eau alcaline, appareil d'électrolyse d'eau alcaline, procédé pour produire de l'hydrogène, et procédé pour produire une membrane pour électrolyse d'eau alcaline

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5177674A (ja) * 1974-12-27 1976-07-06 Sumitomo Electric Industries Shifutsukaechirenjushitakoseikozobutsu
JPS56169782A (en) * 1980-06-03 1981-12-26 Asahi Glass Co Ltd Production of caustic alkali
JPS57131236A (en) * 1980-11-06 1982-08-14 Gore & Ass Multi-component porous high strength ptfe products and manufacture
JPS591690A (ja) * 1982-06-09 1984-01-07 インペリアル・ケミカル・インダストリ−ズ・ピ−エルシ− 電解槽用の多孔質隔膜及びその製造法
JPS59166541A (ja) * 1983-03-10 1984-09-19 Japan Goatetsukusu Kk 耐薬品性多孔質膜の製造方法
JPS6217193A (ja) * 1985-07-13 1987-01-26 Shirakawa Seisakusho:Kk 電極・隔膜組立体
WO2016148302A1 (fr) * 2015-03-18 2016-09-22 旭化成株式会社 Membrane pour électrolyse d'eau alcaline, appareil d'électrolyse d'eau alcaline, procédé pour produire de l'hydrogène, et procédé pour produire une membrane pour électrolyse d'eau alcaline

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7260298B2 (ja) 2018-12-26 2023-04-18 株式会社日本触媒 アルカリ水電解用隔膜
JP2020105557A (ja) * 2018-12-26 2020-07-09 株式会社日本触媒 アルカリ水電解用隔膜
JP7232110B2 (ja) 2019-04-01 2023-03-02 株式会社日本触媒 アルカリ水電解用隔膜ならびに該隔膜の製造方法
JP2020169349A (ja) * 2019-04-01 2020-10-15 株式会社日本触媒 アルカリ水電解用隔膜ならびに該隔膜の製造方法
JPWO2021019985A1 (fr) * 2019-07-30 2021-02-04
JP7170144B2 (ja) 2019-07-30 2022-11-11 旭化成株式会社 アルカリ水電解槽
WO2021019985A1 (fr) * 2019-07-30 2021-02-04 旭化成株式会社 Cuve d'électrolyse d'eau alcaline
CN114555866A (zh) * 2019-10-31 2022-05-27 株式会社德山 碱性水电解槽用弹性垫
WO2021085334A1 (fr) * 2019-10-31 2021-05-06 株式会社トクヤマ Tapis élastique pour cellules d'électrolyse d'eau alcaline
CN114086213A (zh) * 2021-10-27 2022-02-25 四川华能氢能科技有限公司 一种降低碱性电解水制氢能耗的复合隔膜
CN115074775A (zh) * 2022-07-22 2022-09-20 北京化工大学 一种一体化复合膜及其制备方法和在碱性水解制氢中的应用
CN115074775B (zh) * 2022-07-22 2024-06-07 北京化工大学 一种一体化复合膜及其制备方法和在碱性水解制氢中的应用
CN119239017A (zh) * 2024-12-04 2025-01-03 苏州希倍优氢能源科技有限公司 一种三明治夹芯结构电解水复合隔膜、制备方法及应用
CN119529453A (zh) * 2025-01-23 2025-02-28 山东东岳未来氢能材料股份有限公司 一种Al2O3/PTFE复合微孔膜及其制备方法与应用
CN119529453B (zh) * 2025-01-23 2025-05-27 山东东岳未来氢能材料股份有限公司 一种Al2O3/PTFE复合微孔膜及其制备方法与应用

Also Published As

Publication number Publication date
JPWO2018182006A1 (ja) 2019-11-07

Similar Documents

Publication Publication Date Title
WO2018182006A1 (fr) Diaphragme, bain électrolytique, et procédé de fabrication d'hydrogène
JP6746721B2 (ja) 複極式電解槽、アルカリ水電解用複極式電解槽、及び水素製造方法
JP6637556B2 (ja) アルカリ水電解用隔膜、アルカリ水電解装置、水素の製造方法及びアルカリ水電解用隔膜の製造方法
JP7009146B2 (ja) アルカリ水電解用隔膜及びその製造方法、複極式電解槽
WO2018139616A1 (fr) Bain électrolytique, dispositif d'électrolyse, procédé d'électrolyse et procédé de production d'hydrogène
CA2932016C (fr) Membrane a electrolyte polymere
JP6596289B2 (ja) ポリフェニレン共重合体を含む微多孔膜、及びその製造方法
JP6030952B2 (ja) アルカリ水電解用隔膜及びその製造方法
US11035046B2 (en) Woven or nonwoven web
JP2015117417A (ja) アルカリ水電解用隔膜及びこれを用いたアルカリ水電解槽
KR102436919B1 (ko) Koh 전해액 환경에서 이온 전도도가 향상된 알칼라인 수전해 셀룰로오스 격막
JP7136580B2 (ja) 隔膜、隔膜の製造方法、電解槽及び水素製造方法
WO2018139609A1 (fr) Cellule électrolytique bipolaire, récipient électrolytique bipolaire et procédé de fabrication d'hydrogène
Guo et al. Effect of porous irregular ZrO2 nanoparticles on the performance of alkaline water electrolysis composite separator membranes under complex conditions
JP2023129128A (ja) 非水電解液二次電池用セパレータ、非水電解液二次電池用部材、非水電解液二次電池
JP2022063055A (ja) アルカリ水電解用隔膜、及び、その製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18777322

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019509422

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18777322

Country of ref document: EP

Kind code of ref document: A1