WO2018181580A1 - Aimant permanent et machine tournante - Google Patents

Aimant permanent et machine tournante Download PDF

Info

Publication number
WO2018181580A1
WO2018181580A1 PCT/JP2018/012975 JP2018012975W WO2018181580A1 WO 2018181580 A1 WO2018181580 A1 WO 2018181580A1 JP 2018012975 W JP2018012975 W JP 2018012975W WO 2018181580 A1 WO2018181580 A1 WO 2018181580A1
Authority
WO
WIPO (PCT)
Prior art keywords
phase
permanent magnet
atomic
content
coercive force
Prior art date
Application number
PCT/JP2018/012975
Other languages
English (en)
Japanese (ja)
Inventor
信宏 神宮
敦 古田
Original Assignee
Tdk株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tdk株式会社 filed Critical Tdk株式会社
Publication of WO2018181580A1 publication Critical patent/WO2018181580A1/fr

Abstract

La présente invention concerne : un aimant permanent qui a une force coercitive magnétique élevée parmi les aimants permanents qui contiennent Ce en tant qu'élément de substitution pour Nd ; et une machine rotative équipée dudit aimant permanent. Cet aimant permanent 10 est pourvu de : une pluralité de particules de phase principale comprenant chacune un élément terre rare R, un élément de métal de transition T et du bore ; et une phase de joint de grain 9 qui est située entre les particules de phase principale 11, l'élément de terre rare R comprenant au moins du néodyme et du cérium, et l'élément de métal de transition T comprend au moins du fer, la quantité contenue de cuivre dans l'aimant permanent 10 étant de 0,1 à 2 % at., la phase de joint de grain 9 comprend une phase R-T 3 comprenant un composé intermétallique de l'élément terre rare R et l'élément métal de transition T, et, lorsque la quantité totale de l'élément terre rare R contenue dans la phase R-T 3 est [R]L % at. et la quantité de cérium contenue dans la phase R-T 3 est [Ce]L % at., 100×[Ce]L/[R]L est égale à 75 à 100.
PCT/JP2018/012975 2017-03-30 2018-03-28 Aimant permanent et machine tournante WO2018181580A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017068787A JP2020095991A (ja) 2017-03-30 2017-03-30 焼結磁石及び回転機
JP2017-068787 2017-03-30

Publications (1)

Publication Number Publication Date
WO2018181580A1 true WO2018181580A1 (fr) 2018-10-04

Family

ID=63677019

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/012975 WO2018181580A1 (fr) 2017-03-30 2018-03-28 Aimant permanent et machine tournante

Country Status (2)

Country Link
JP (1) JP2020095991A (fr)
WO (1) WO2018181580A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7535837B2 (ja) 2022-08-30 2024-08-19 煙台東星磁性材料株式有限公司 Ｃｅ添加型ＲＥ－Ｔ－Ｂ－Ｍ系焼結磁性体

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022123992A1 (fr) * 2020-12-09 2022-06-16 Tdk株式会社 Aimant permanent à base de r-t-b

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012171490A1 (fr) * 2011-06-17 2012-12-20 Ningbo Institute Of Materials Technology And Engineering, Chinese Academy Of Sciences Aimant permanent à base de néodyme/fer/bore
JP2015204390A (ja) * 2014-04-15 2015-11-16 Tdk株式会社 永久磁石およびモータ

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012171490A1 (fr) * 2011-06-17 2012-12-20 Ningbo Institute Of Materials Technology And Engineering, Chinese Academy Of Sciences Aimant permanent à base de néodyme/fer/bore
JP2015204390A (ja) * 2014-04-15 2015-11-16 Tdk株式会社 永久磁石およびモータ

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7535837B2 (ja) 2022-08-30 2024-08-19 煙台東星磁性材料株式有限公司 Ｃｅ添加型ＲＥ－Ｔ－Ｂ－Ｍ系焼結磁性体

Also Published As

Publication number Publication date
JP2020095991A (ja) 2020-06-18

Similar Documents

Publication Publication Date Title
JP5754232B2 (ja) 高保磁力ＮｄＦｅＢ磁石の製法
JP6733576B2 (ja) Ｒ−ｔ−ｂ系永久磁石
JP6274216B2 (ja) Ｒ−ｔ−ｂ系焼結磁石、および、モータ
JP6269279B2 (ja) 永久磁石およびモータ
JP6330813B2 (ja) Ｒ−ｔ−ｂ系焼結磁石、および、モータ
KR101378089B1 (ko) Ｒ－ｔ－ｂ계 소결 자석
JP6729446B2 (ja) Ｒ−ｔ−ｂ系永久磁石
JP5120710B2 (ja) ＲＬ−ＲＨ−Ｔ−Ｍｎ−Ｂ系焼結磁石
JP6572550B2 (ja) Ｒ−ｔ−ｂ系焼結磁石
JP7180096B2 (ja) 永久磁石及び回転機
WO2012002059A1 (fr) Aimant permanent de terres rares de type r-t-b, moteur, véhicule automobile, générateur d'énergie électrique et système de production d'énergie éolienne
JP6536816B2 (ja) Ｒ−ｔ−ｂ系焼結磁石およびモータ
JP6733577B2 (ja) Ｒ−ｔ−ｂ系永久磁石
WO2018181592A1 (fr) Aimant permanent et machine rotative
CN110537232B (zh) 永久磁铁和旋转电机
JP2011021269A (ja) Ｒ−ｔ−ｂ系希土類永久磁石用合金材料、ｒ−ｔ−ｂ系希土類永久磁石の製造方法およびモーター
JP6037093B1 (ja) Ｒ−ｔ−ｂ系焼結磁石の製造方法
WO2018181581A1 (fr) Aimant permanent et machine tournante
JP4951703B2 (ja) Ｒ−ｔ−ｂ系希土類永久磁石用合金材料、ｒ−ｔ−ｂ系希土類永久磁石の製造方法およびモーター
JP6624455B2 (ja) Ｒ−ｔ−ｂ系焼結磁石の製造方法
WO2018181580A1 (fr) Aimant permanent et machine tournante
JP5743458B2 (ja) Ｒ−ｔ−ｂ系希土類永久磁石用合金材料、ｒ−ｔ−ｂ系希土類永久磁石の製造方法およびモーター
JP7228096B2 (ja) Ｒ－ｔ－ｂ系焼結磁石の製造方法
JP2000082610A (ja) 高電気抵抗率希土類永久磁石とその製造方法
JP2005197299A (ja) 希土類焼結磁石及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18776830

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18776830

Country of ref document: EP

Kind code of ref document: A1