WO2019246265A1 - Nanostructural designs for electrode materials of fluoride ion batteries - Google Patents

Abstract

The present disclosure relates to a fluoride shuttle battery and nanostructures of copper based cathode materials in the fluoride shuttle battery. The F-shuttle batteries of present disclosure comprise a liquid electrolyte, which allows the F-shuttle batteries to operate under room temperature. The minimum thickness of copper layer within the copper nanostructures is no more than 20 nm. The thickness of copper layer within the copper nanostructures is controlled and reduced to ensure the energy densities of F-shuttle batteries.

Description

NANOSTRUCTURAL DESIGNS FOR ELECTRODE MATERIALS OF

FLUORIDE ION BATTERIES

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This application claims priority to U.S. Provisional Application No. 62/687,653, entitled“Barium-Doped Composite Electrode Materials For Fluoride-Ion Electrochemical Cells,” filed June 20^th, 2018 and to U.S. Patent Application No. 16/445,022, entitled“Nanostructural Designs for Electrode Materials of Fluoride Ion Batteries,” filed June Id¹¹¹, 2019.

INCORPORATION BY REFERENCE

[0002] Each of the following applications is hereby incorporated herein by reference in its entirety: U.S. Patent Application No. 62/687,653, entitled “Barium-Doped Composite Electrode Materials For Fluoride-Ion Electrochemical Cells,” filed June 20, 2018; U.S. Patent Application No. 16/013,739, entitled“Barium-Doped Composite Electrode Materials For Fluoride-Ion Electrochemical Cells,” filed June 20, 2018, which claims priority to U.S. Patent Application No. 62/676,693, entitled“Composite Electrode Materials for Fluoride-Ion Electrochemical Cells,” filed May 25, 2018; U.S. Patent Application No. 15/844,079, entitled“Composite Electrode Materials for Fluoride-Ion Electrochemical Cells,” filed December 15, 2017, which claims priority to U.S. Patent Application No. 62/434,611, entitled“Composite Electrode Materials for Fluoride-Ion Electrochemical Cells,” filed December 15, 2016; U.S. Patent Application No. 62/453,295, entitled“Core Shell,” filed February 1, 2017; U.S. Provisional Application No. 62/775,748 filed December 5, 2018; U.S. Patent Application No. 16/444,854, entitled “Electroactive Materials Modified with Molecular Thin Film Shell,” filed June 18^th, 2019; and U.S. Patent Application No. 16/445,022, entitled “Nanostructural Designs for Electrode Materials of Fluoride Ion Batteries,” filed June 18^ώ, 2019.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0003] This invention was made with government support under Grant No. 80NM0018D004 awarded by NASA Jet Propulsion Laboratory (JPL). The government has certain rights in the invention. TECHNICAL FIELD

[0004] The present disclosure relates to electrochemically active materials, and more particularly to fluoride ion battery systems that include electrode materials with tailored structures and compositions to improve battery performance. More specifically, this disclosure relates to a fluoride shuttle battery and nanostructures of copper based cathode materials in the fluoride shuttle battery.

BACKGROUND

[0005] Metal nanoparticles are highly desirable for use in a number of applications including as catalysts, and as electrode materials for batteries. However, the use of metal nanoparticles may be limited by the system operating conditions or other factors.

[0006] F (fluoride) shuttle batteries are a novel and underexplored alternative next generation energy storage. Its energy density is much larger than lithium ion batteries, around four times in volumetric and two times at gravimetric densities. F-shuttle batteries offer lower cost and/or improved safety characteristics compared to lithium and lithium- ion batteries. Fluoride-ion batteries are electrochemical cells that operate via fluoride- mediated electrode reactions. For example, F anions are shuttled between the cathode and the anode electrodes. During discharge, MeF_x is reduced to Me (metal) or low valence MeF_x and releases F ions at the cathode side. Meanwhile, F ions combine with metal to form MeFx and release electrons at the anode side. F-shuttle batteries can be manufactured as primary or secondary batteries.

[0007] Transition metal fluorides are usually used as cathode materials, and alkaline earth or rare-earth metals are used as anode materials.

[0008] There are two types of F-shuttle batteries, i.e., all-solid-state type and liquid type. Currently most of the research being conducted is focused on all-solid-state F- shuttle batteries, which may be rechargeable at elevated temperatures to some extent. However, slow reaction kinetics impose significant challenges to all-solid-state F-shuttle batteries. Fluoride-ion systems have been demonstrated in the solid state, for example, in US 7,722,993 to Potanin, which describes an embodiment of a secondary electrochemical cell where fluoride ions are reversibly exchanged between anode and cathode electrodes during charge-discharge cycles, with these electrodes in contact with a solid-state fluoride-conducting electrolyte. Potanin describes solid state electrolytes containing fluorides of La, Ce or the compound fluorides based on them, together with alloying additives, such as fluoride/fluorides of alkaline-earth metals (CaF₂, SrF₂, BaF₂) and/or fluorides of alkaline metals (LiF, KF, NaF) and/or alkaline metal chlorides (LiCl, KC1, NaCl), as well as a wide range of other compound fluorides. However, such electrochemical cells only operate usefully above room temperature (e.g. 150 °C) due to the limited conductivity of the solid-state electrolyte.

[0009] Reaction kinetics are good in the liquid type F-shuttle batteries. However, this type of F-shuttle battery still faces many challenges, such as the lack of good electrolytes and reversible cathode/anode materials at room temperature.

[0010] Recently, a F-shuttle battery assembled with heavy metals was reported to be reversible in an ionic liquid-based electrolyte at room temperature, where Bi was used as a cathode and Pb was used as an anode (K Okazaki, et ah, Charge-Discharge Behavior Of Bismuth In A Liquid Electrolyte For Rechargeable Batteries Based On A Fluoride Shuttle, Acs Energy Letters, 2017, 2 1460-1464). However, the battery had a low voltage (-0.2Y) and a low capacity (maximum 0.15 mAh). Furthermore, Pb, which is known to be toxic and not environmental friendly, is used as anode in such a battery. Other attempts have also been made to provide fluoride ion-based electrochemical systems capable of using liquid electrolytes. For example, US 2011/0143219 Al by Weiss et al. and US 9,166,249 by Darolles et al. disclose fluoride-ion battery configurations that include a solvent-borne fluoride salt that is at least partially present in a dissolved state in the electrolyte. However, for many applications the chemical reactivity of the electrode materials with the liquid electrolyte is significant, and these liquid electrolyte systems do not provide sufficiently reliable high discharge and/or high capacity operation.

SUMMARY

[0011] The following presents a simplified summary of one or more aspects of the present disclosure in order to provide a basic understanding of such aspects. This summary is not an extensive overview of all contemplated aspects and is intended to neither identify key or critical elements of all aspects nor delineate the scope of any or all aspects. Its purpose is to present some concepts of one or more aspects in a simplified form as a prelude to the more detailed description that is presented later.

[0012] In some embodiments, the present disclosure is directed to a fluoride shuttle battery which comprises a cathode, an anode, and an electrolyte between the cathode and the anode, wherein the cathode includes a cathode material, which comprises a metal nanostructure core and a shell layer surrounding the core. [0013] These and other aspects of the invention will become more fully understood upon a review of the detailed description, which follows.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee.

[0015] FIG. 1A shows a cross section of a core-shell nanoparticle including a core comprising a metal nanoparticle, and a shell comprising a metal halide or a metal oxyhalide in an aspect of the present disclosure.

[0016] FIG. 1B depicts energy densities of various types of batteries.

[0017] FIG. 1C depicts examples of suitable anode and cathode metals.

[0018] FIG. 2 is a schematic illustration of a fluoride ion electrochemical cell in an aspect of the present disclosure.

[0019] FIG. 3A depicts TEM images of Cu@LaF₃ core-shell nanoparticles and Cu@La0.97Ba0.03F2.97 core-shell nanoparticles, respectively. The inset in the TEM image of Cu@LaF₃ nanoparticle is the zoom-in image of Cu (core) and LaF₃ (shell) areas.

[0020] FIG. 3B shows schematic representations of Cu@LaF₃ and Cu@La0.97Ba0.03F2.97 nanoparticles, respectively, according to some aspects of the present disclosure.

[0021] FIG. 4A shows the voltage profile of the first charge-discharge cycle of a Cu@LaF₃ electrode or a Cu@La_0.97Ba_0.03F_2.97 electrode, compared to the Ag/Ag⁺ reference electrode, according to some aspects of the present disclosure.

[0022] FIG. 4B shows a comparison of the capacity achieved for Cu@LaF₃ (9.5% of theoretical capacity), for Cu@La_0.97Ba_0.03F_2.97 (18% of theoretical capacity), and for CuF₂ (theoretical capacity of 528 mAh/g) according to some aspects of the present disclosure.

[0023] FIG. 5 shows the percentage of energy densities achieved by copper based F- shuttle batteries, which is normalized by theoretical capacity of CuF₂ (528 mAh/g).

[0024] FIG. 6 illustrates the structure of Cu and fluorinated Cu (CUF₂) nanoparticles.

[0025] FIG. 7 shows XRD spectra of 6 nm Cu nanoparticles.

[0026] FIG. 8 shows XRD spectra of 6 nm Cu@LaF₃ after initial synthesis.

[0027] FIG. 9A illustrates a TEM image of 6 nm Cu core nanoparticles after initial synthesis. [0028] FIG. 9B shows a TEM image of 6 nm Cu core with a LaF₃ shell after initial synthesis.

[0029] FIG. 10 shows XRD spectra of 6 nm Cu core NP with a LaF₃ shell after reduction of Cu₂0.

[0030] FIG. 11 illustrates the structure of Cu nanowires with a Lai-_xBa_xF_3-x or LaF₃ coating and a cross-sectional view of the Cu nanowires.

[0031] FIG. 12 shows XRD spectra of Cu nanowires (without a Lai-_xBa_xF_3-x or LaF₃ coating) having a cross-sectional diameter of about or less than 20 nm, according to some aspects of the present disclosure.

[0032] FIG. 13A and FIG. 13B show TEM images of Cu nanowires (without a Lai- _xBa_xF_3-x or LaF₃ coating) having a cross-sectional diameter of about 20 nm.

[0033] FIG. 14 shows the XRD spectra of Cu nanowires (with a diameter about or less than 20 nm), small amount of Cu₂0 after shell formation, and LaF₃ shell of Cu nanowires, according to some aspects of the present disclosure.

[0034] FIG. 15A shows a SEM image of Cu nanowires after initial synthesis and before the two phase shell formation, according to some aspects of the present disclosure.

[0035] FIG. 15B shows a SEM image of two phase LaF₃ shell formation on Cu nanowires, according to some aspects of the present disclosure.

[0036] FIG. 16A, 16B, and 16C show TEM images of LaF₃ formation on/around Cu nanowires under different magnifications/resolutions, according to some aspects of the present disclosure.

[0037] FIG. 17 shows the voltage profile of the charge-discharge cycle of an electrode made of Cu nano wires encapsulated in LaF₃ shells (CuNW@LaF₃), according to some aspects of the present disclosure.

[0038] FIG. 18 shows the XRD spectra of CuNW@LaF₃ in initial condition, after a charge (fluorination,‘F’), and a subsequent discharge (defluorination,‘deF’), according to some aspects of the present disclosure.

[0039] FIG. 19 shows the voltage profile of the charge-discharge cycle of an electrode made of Cu nanowires (with an average diameter about or less than 20 nm) encapsulated in soft shells (surfactant shells), according to some aspects of the present disclosure.

[0040] FIG. 20 shows the XRD spectra of CuNW@soft shell (surfactant shell) after a charge (fluorination) and after a subsequent discharge (defluorination), according to some aspects of the present disclosure. The Cu nanowires in the Fig have an average diameter about or less than 20 nm. [0041] FIG. 21 illustrates the structure of Cu nanotubes with a Lai_-xBa_xF3-_x or LaF₃ coating and a cross-sectional view of the Cu nanotubes.

[0042] FIG. 22 illustrates the structure of Cu nanoflakes and Cu nanosheets with a Lai_-xBa_xF3-_x or LaF₃ coating. The minimum thickness of these structures is no more than 20 nm.

[0043] FIG. 23 illustrates the structure of Cu nanoframes with a Lai_-xBa_xF3-_x or LaF₃ coating. An inner copper wall within the Cu nano frame has a thickness no more than 20 nm.

[0044] FIG. 24 depicts the voltage profiles of the charge-discharge cycles of a variety electrodes. The electrodes in the figure are made of about 50 nm CuNP@LaF3, about 50 nm CuNP@La0.97Ba0.03F2.97, about 20 nm CuNW@LaF3, and about 20 nm CuNW@soft shell, respectively.

[0045] FIG. 25 shows a comparison of the capacity achieved for about 50 nm CuNP@LaF3, about 50 nm CuNP@La0.97Ba0.03F2.97, about 20 nm CuNW@LaF₃, about 20 nm CuNW@soft shell, and the theoretical capacity of CuF₂, according to some aspects of the present disclosure.

[0046] FIG. 26 demonstrates percentage capacity achieved for about 50 nm CuNP@LaF₃, about 50 nm CuNP@La0.97Ba0.03F2.97, and about 20 nm CuNW@LaF₃, about 20 nm CuNW@soft shell, which are normalized by the theoretical capacity of CuF2 (528 mAh/g).

[0047] FIG. 27A shows an example electrochemically active structure according to aspects of the present disclosure.

[0048] FIG. 27B shows an example electrochemically active structure according to aspects of the present disclosure

[0049] FIG. 27C shows an example electrochemically active structure according to aspects of the present disclosure.

[0050] FIG. 28 shows an example schematic of charging and discharging an electrochemically active structure according to aspects of the present disclosure.

DETAILED DESCRIPTION

[0051] The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details. In some instances, well known components are shown in block diagram form in order to avoid obscuring such concepts.

[0052] In general, the present disclosure is related to electrochemically active materials, and fluoride-ion battery systems that include electrode materials with tailored structures and compositions to improve battery performance. In some aspects, the present disclosure is related to core-shell nanoparticles, devices incorporating the core-shell nanoparticles, as well as methods of making and using the core-shell nanoparticles and devices including the core-shell nanoparticles.

[0053] As used herein, the core is not limited to particles, e.g., spherical particles, and also encompasses structures including, but not limited to, nanoparticles, nanotubes, nanowires, frames, flakes, nanoporous, sheets, thin films, and foams. In an embodiment, the size of the core material is determined either by electron conductivity or F ion mobility. In an illustrative example, 20 nm may be the distance limit of F ion penetration in the core material. If the path of either electron or F is greater than 20 nm, resistance to this will prevent it. Accordingly, a spherical core particle having a diameter of less than or equal to 20 nm may be applied as the spherical particle has less than or equal to 20 nm pathway in all directions. Therefore, all or nearly all of the core material can be utilized, thereby reducing the weight and volume of the cathode. However, the core is not limited to spherical particles. Other core structures may be used that have a dimension that is greater than 20 nm, if it has, for example, a pathway of 20 nm or less in one direction. So while the spherical particle has less than or equal to 20 nm pathway in all directions, a flake (like a piece of paper, for example) may have very large distances in the x and y direction, but if diffusion/electron transport only occurs in the Z direction of 20 nm or less, since that is path of least resistance, it will dominate.

[0054] Primary and secondary electrochemical cells, such as batteries, utilizing fluoride ion charge carriers, active electrode materials, and suitable liquid electrolytes can provide an alternative to conventional state of the art lithium batteries and lithium ion batteries. Such fluoride-ion battery (FIB) systems can operate usefully at room temperature while utilizing fluoride anions carried in a liquid electrolyte as at least some of the charge carriers in an electrochemical cell. The FIB system has an anode and cathode physically separated from each other, but in common contact with a fluoride ion conducting electrolyte. The anode is typically a low potential element or compound, and can be a metal, metal fluoride, or intercalating composition. Similarly, the cathode can be element or composition, and can be a metal, metal fluoride, or intercalating composition that has a higher potential than the anode. Fluoride ions (F ) in the fluoride conducting electrolyte go from the cathode to the anode during discharge and from the anode to the cathode during the charge of the battery (Fig. 2):

Discharge:

Anode: M’F_X + nF ® M’F_x+n + ne- (Fluoride ion accommodation, oxidation)

Cathode: MF_y+ n e— > MF_y-n + nF (Fluoride ion release, reduction)

Transition metal fluorides are preferably used as cathode materials and alkaline earth or rare-earth metals are preferably used as anode materials. Examples of suitable anode and cathode metals are depicted in Fig. 1C.

[0055] During charge, the reverse reactions occur. For example, a FIB cell reaction based on fluoride anion transfer between Ca and Cu, both metals capable of forming metal fluorides, might be:

Discharge:

Ca + CUF₂— CaF₂ + Cu

Charge:

CaF₂+ C u— Ca+ C uF₂

[0056] Two major challenges exist to enable stable, reliable long-term cycling of FIB electrodes. Firstly, reversibility of the electrochemical reactions above is observed when the metal or metal fluoride active materials are nano-sized (i.e. at least one of the particle size dimensions is less than 1 pm). However, particles with such small dimensions have high surface energies and are often reactive with the electrolyte components (e.g. F ) to give undesirable side-reactions including "self-discharge" (i.e. a chemical reaction such as M + nF ® MF_n that does not general electrical current). What is needed is formation of a coating, shell, layer or the like to encapsulate the active material particles while still permitting passage of F ions when desired (i.e. during electrochemical charge or discharge) The encapsulating material can also protect the active materials from such side-reactions, enabling long-term cycling stability of these electrode materials.

[0057] Secondly, such electrochemical reactions are conversion processes, with the structure of the metal or metal fluoride being broken down during the electrochemical process and reformed as the metal fluoride or metal, respectively, during the process. This conversion process results in a significant volume change between charged and discharged states of the active material, as indicated by the examples given in Table 1 below:

Table 1: Volume Change In Metal To Metal Fluoride Conversion

[0058] Such significant volume changes limit usefulness of conformal protective coatings encapsulating an FIB electrode material particle, since one particular state of charge will not necessarily be conformal with the particle in a different state of charge, due to the volume changes. What is needed are compositions and processes that protect the electrode active material from side reactions with the electrolyte, allow ion conduction through an encapsulant, and have sufficient void space within the encapsulant and/or encapsulant expansion/contraction properties to accommodate the volume changes of the active material during charge and discharge without permitting direct contact between the active material and the electrolyte. In some embodiments, sufficient void space may be no void space. Such compositions and their preparation are outlined below.

[0059] As used herein, the term“about” is defined to being close to as understood by one of ordinary skill in the art. In one non-limiting embodiment, the term“about” is defined to be within 10%, preferably within 5%, more preferably within 1%, and most preferably within 0.5%.

[0060] In some embodiments as shown in FIG. 1A, the core-shell nanoparticles include a core that comprises a metal or metal alloy (“Me”), and a shell that comprises a metal halide or a metal oxyhalide. The metal of the core may be the same as the metal of the metal halide shell. In some embodiments, the metal of the core and the metal of the metal halide or metal oxyhalide shell are different metals. In some embodiments, the metal halide shell may itself comprise two metals. The core-shell nanoparticles of the present disclosure may be incorporated into a variety of methods and applications including, but not limited to, electrodes for use in electrochemical cells, including fluoride shuttle batteries as shown in FIG. 2. Compared to lithium ion batteries, F-shuttle batteries have much higher energy density, which is around four times in volumetric and two times at gravimetric densities. The energy densities of various types of batteries are illustrated in Fig. 1B and in Table 2 below:

Table 2. Energy Densities of F-Shuttle Batteries and Lithium Ion Batteries

[0061] The metals or metal alloys used to form the core include, but are not limited to, iron nanoparticles, cobalt nanoparticles, nickel nanoparticles, copper nanoparticles, lead nanoparticles, and alkaline earth metal nanoparticles. In a preferred embodiment, the metal nanoparticles are selected from the group consisting of cobalt nanoparticles and copper nanoparticles. In another preferred embodiment, the metal nanoparticles are copper nanoparticles. The metals used to form the core may be synthesized by mixing a metal precursor solution with a reducing agent to form metal nanoparticles. [0062] In some embodiments, the metal nanoparticles used to form the core may be synthesized in the presence of a stabilizer that prevents or otherwise inhibits oxidation of the metal nanoparticles during synthesis, and is readily removable from the metal nanoparticles prior to formation of the metal halide or metal oxyhalide shell thereon. For example, bulky polymers such as polyvinylpyrrolidone (molecular weight of 55,000 g/mol) used during metal nanoparticle synthesis inhibit oxidation of metal nanoparticles. However, such stabilizers are not readily removable from the metal nanoparticles following synthesis. Without being limited to any particular theory, residual stabilizer can form an additional layer between the core formed by the metal nanoparticles and the metal halide or oxyhalide shell that detracts from the performance of the core-shell nanoparticle in the desired system. For example, it is desirable to maintain the conductivity of core- shell nanoparticles used as electrode material in an F-Shuttle battery. However, core-shell materials including an additional layer of residual stabilizer between the core and the shell will likely result in an increased space between electrode materials; the additional layer of residual stabilizer and/or the resulting increased space may decrease the conductivity of the core-shell material. Without wishing to be bound to any particular theory, the additional layer of stabilizer may impede contact between the core and the shell to conduct fluoride ion, while the absence of the stabilizer may increase the likelihood of conducting fluoride ion from the core to the shell.

[0063] Therefore, a stabilizer may be used in the synthesis of the metal nanoparticles used to form the core that is readily removable therefrom to minimize the amount of stabilizer on the surface of the core prior to formation of the metal halide or metal oxyhalide shell directly thereon. In a non-limiting example, the one or more stabilizers that may be used in the synthesis of the metal nanoparticles includes a molecular weight (either individually or a weight average) of less than 1000 g/mol, optionally less than 500 g/mol, optionally less than 375 g/mol, and optionally less than 350 g/mol. Illustrative examples include hexadecyltrimethylammonium bromide (CTAB) with a molecular weight of 364 g/mol, citric acid with a molecular weight of 192 g/mol, and mixtures thereof.

[0064] In some embodiments, the shell of the core-shell nanoparticles may be formed by mixing isolated metal nanoparticles used to form the core with, for example, a metal salt solution and a halide salt solution that react to form the metal halide shell on the core. The shell is deposited directly on the metal core and may entirely surround the core as shown in FIG. 1 A. In some embodiments, the metal salt used to form the shell is selected from the group consisting of alkali metal salts, alkaline earth metal salts, and transition metal salts. In certain embodiments, the metal salt used to form the shell is a transition metal salt. In certain embodiments, the metal salt used to form the shell is selected from the group consisting of lanthanum salts, cerium salts, and magnesium salts. In certain embodiments, the metal salt used to form the shell is selected from the group consisting of lanthanum salts and cerium salts. In certain embodiments, the metal salt is a lanthanum salt. In a preferred embodiment, the lanthanum salt is lanthanum nitrate. In some embodiments, the halide salt is sodium fluoride. In a non-limiting example, the shell comprises a metal fluoride or metal oxyfluoride containing material (i.e. CeF₃, CeOF, LaOF, LaF₃).

[0065] In some embodiments, the metal salt solution comprises two metal salts. In some such embodiments, one of the two metal salts is a barium salt. In some embodiments, the metal salt solution comprises a barium salt and a lanthanum salt. In some embodiments, the metal salt solution comprises barium nitrate and lanthanum nitrate. In some embodiments, the metal salt solution comprises barium nitrate and lanthanum nitrate in a ratio of about 1 : 10.

[0066] In other embodiments, the core (or electrode active material) maybe separated from the shell (or encapsulant) by a void space. Compositions and processes according to such embodiments may protect the electrode active material from side reactions with the electrolyte, allow ion conduction through an encapsulant, and have sufficient void space within the encapsulant and/or encapsulant expansion/contraction properties to accommodate the volume changes of the active material during charge and discharge, without permitting direct contact between the active material and the electrolyte.

[0067] The terms core and electrode active material are used interchangeably herein. Similarly, the terms shell and encapsulant are used interchangeably herein.

[0068] In other embodiments, the present disclosure is directed to an electrode comprising the core-shell nanoparticles disclosed herein. All aspects and embodiments described with respect to the core-shell nanoparticles and methods of making thereof apply with equal force to the electrode. In a non-limiting example, the electrode is part of an F-shuttle battery system.

[0069] In some embodiments, the present disclosure is directed to an electrochemically active structure, comprising: a core comprising an active material, and a fluoride-containing shell at least partially surrounding the active material, wherein the fluoride-containing shell comprises a first metal and a second metal, and the first metal is barium. All aspects described with respect to the aforementioned embodiments apply to the present embodiment with equal force, and vice versa.

[0070] In some aspects, the active material comprises copper nanoparticles.

[0071] In some aspects, the fluoride-containing shell is directly attached to the core.

[0072] In some aspects, the second metal is lanthanum.

[0073] In some aspects, the barium and the lanthanum are present in a ratio of x to 1- x.

[0074] In some aspects, x is about 0.03 to about 0.15.

[0075] In some aspects, x is about 0.03.

[0076] In some embodiments, the present disclosure is directed to a method of making coated metal nanoparticles, the method comprising: a) providing a water/metal nanoparticle mixture; b) exposing the water/metal nanoparticle mixture to an inert atmosphere; and c) forming a fluoride-containing shell around a metal nanoparticle core, wherein the fluoride-containing shell comprises a first metal and a second metal, and the first metal is barium. All aspects described with respect to the aforementioned embodiments apply to the present embodiment with equal force, and vice versa.

[0077] In some aspects, the metal nanoparticles comprise copper nanoparticles.

[0078] In some aspects, the fluoride-containing shell is directly attached to the core.

[0079] In some aspects, the second metal is lanthanum.

[0080] In some aspects, the barium and the lanthanum are present in a ratio of x to 1- x.

[0081] In some aspects, x is about 0.03 to about 0.15.

[0082] In some aspects, the forming the fluoride-containing shell comprises adding a first metal salt, a second metal salt, and a fluoride-containing salt to the water/metal nanoparticle mixture to create a fluoride-containing shell around the metal nanoparticle core, wherein the first metal is a barium salt.

[0083] In some aspects, the second metal is a lanthanum salt.

[0084] In some aspects, the first metal salt is barium nitrate and the second metal salt is lanthanum nitrate.

[0085] In some aspects, the barium nitrate and the lanthanum nitrate are used in a molar ratio of about 1 : 10.

[0086] In some embodiments, the present disclosure is directed to an electrode comprising: a core comprising copper nanoparticles, and a fluoride containing shell at least partially surrounding the copper nanoparticles, wherein the fluoride-containing shell comprises barium and lanthanum in a ratio of x to l-x. All aspects described with respect to the aforementioned embodiments apply to the present embodiment with equal force, and vice versa.

[0087] In some aspects, x is about 0.03 to about 0.15.

[0088] In some aspects, the present disclosure is directed to a fluoride shuttle battery comprising the electrode and a liquid electrolyte. Non-limiting examples of liquid electrolytes are described in U.S. Patent Application 15/228,876.

[0089] An“inert atmosphere” refers to a gaseous mixture that contains little or no oxygen and comprises inert or non-reactive gases or gases that have a high threshold before they react. An inert atmosphere may be, but is not limited to, molecular nitrogen or an inert gas, such as argon, or mixtures thereof.

[0090] A“reducing agent” is a substance that causes the reduction of another substance, while it itself is oxidized. Reduction refers to a gain of electron(s) by a chemical species, and oxidation refers to a loss of electron(s) by a chemical species.

[0091] A“metal salt” is an ionic complex wherein the cation(s) is(are) a positively charged metal ion(s) and the anion(s) is(are) a negatively charged ion(s).“Cation” refers to a positively charged ion, and“anion” refers to a negatively charged ion. In a“metal salt” according to the present disclosure, the anion may be any negatively charged chemical species. Metals in metal salts according to the present disclosure may include but are not limited to alkali metal salts, alkaline earth metal salts, transition metal salts, aluminum salts, or post-transition metal salts, and hydrates thereof.

[0092] “Alkali metal salts” are metal salts in which the metal ions are alkali metal ions, or metals in Group I of the periodic table of the elements, such as lithium, sodium, potassium, rubidium, cesium, or francium.

[0093] “Alkaline earth metal salts” are metal salts in which the metal ions are alkaline earth metal ions, or metals in Group II of the periodic table of the elements, such as beryllium, magnesium, calcium, strontium, barium, or radium.

[0094] “Transition metal salts” are metal salts in which the metal ions are transition metal ions, or metals in the d-block of the periodic table of the elements, including the lanthanide and actinide series. Transition metal salts include, but are not limited to, salts of scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, and lawrencium.

[0095] “Post-transition metal salts” are metal salts in which the metal ions are post transition metal ions, such as gallium, indium, tin, thallium, lead, bismuth, or polonium.

[0096] A“halide salt” is an ionic complex in which the anion(s) is(are) halide ion(s), including but not limited to fluoride ion(s), chloride ion(s), bromide ion(s), and iodide ion(s). A“fluoride salt” is an ionic complex in which the anion(s) is(are) fluoride ion(s). According to the present disclosure, the cation of the halide salt or the fluoride salt may be any positively charged chemical species.

[0097] A“metal fluoride” is an ionic complex in which the cation is one or more metal ion(s) and the anion(s) is(are) fluoride ion(s). According to some aspects of the present disclosure, the metal salt(s) and the fluoride salt react to create a metal fluoride shell around the metal nanoparticle core. Similarly, a“metal halide” is an ionic complex in which the cation is one or more metal ion(s) and the anion(s) is(are) halide ion(s).

[0098] A“fluoride-containing” salt is an ionic complex in which the anion(s) contain fluoride ion but are not limited to being solely fluoride. Instead,“fluoride-containing” salts include ionic complexes where the anion(s) contain fluoride itself in complex with other ions or atoms.“Fluoride-containing” salts suitable for use in aspects of the present disclosure include those known to persons of ordinary skill in the art, including, but not limited to, fluoride salts, non-metal fluoroanions such as tetrafluoroborate salts and hexafhiorophosphate salts, and oxyfluoride salts. In some aspects of the present disclosure, the fluoride-containing salts may include quaternary ammonium fluorides and fluorinated organic compounds. According to some aspects of the present disclosure, the metal salt and the fluoride-containing salt react to create a fluoride- containing shell around the metal nanoparticle core.

[0099] The term“electrode” refers to an electrical conductor where ions and electrons are exchanged with an electrolyte and an outer circuit.“Positive electrode” and“cathode” are used synonymously in the present description and refer to the electrode having the higher electrode potential in an electrochemical cell (i.e. higher than(xi) the negative electrode). “Negative electrode” and“anode” are used synonymously in the present description and refer to the electrode having the lower electrode potential in an electrochemical cell (i.e. lower than the positive electrode). Cathodic reduction refers to a gain of electron(s) of a chemical species, and anodic oxidation refers to the loss of electron(s) of a chemical species. Positive and negative electrodes of the present invention may be provided in a range of useful configurations and form factors as known in the art of electrochemistry and battery science, including thin electrode designs, such as thin film electrode configurations. Electrodes are manufactured as known in the art, including as disclosed in, for example, U.S. Pat. No. 4,052,539, and Oxtoby et ah, Principles of Modem Chemistry (1999), pp. 401-443.

[00100] The term“electrochemical cell” refers to devices and/or device components that convert chemical energy into electrical energy or vice versa. Electrochemical cells have two or more electrodes (e.g., positive and negative electrodes) and an electrolyte, wherein electrode reactions occurring at the electrode surfaces result in charge transfer processes. Electrochemical cells include, but are not limited to, primary batteries, secondary batteries, and electrolysis systems. General cell and/or battery construction is known in the art (see, e.g., Oxtoby et ah, Principles of Modern Chemistry (1999), pp. 401-443).

[00101] “Electrolyte” refers to an ionic conductor which can be in the solid state, the liquid state (most common), or more rarely a gas (e.g., plasma).

[00102] The present disclosure is directed generally to an electrochemically active structure comprising a core and a shell at least partially surrounding the core, wherein the core comprises an electrochemically active material and the shell comprises a shell material. The present disclosure is also directed to a method of making the electrochemically active structure as described herein as well as electrochemical cells comprising the electrochemically active structure as described herein.

[00103] The electrochemically active structure as described herein comprises a core, wherein the core comprises an electrochemically active material. As used herein, the term “electrochemically active material” refers to a material capable of acting as an electrode in a primary or secondary electrochemical cell, for example, in an ion battery system. According to some aspects, the electrochemically active material may comprise a material capable of acting as a cathode in a liquid type fluoride (F) shuttle battery.

[00104] According to some aspects, the electrochemically active material according to the present disclosure may be a lightweight material which provides high capacity and high energy densities. Examples of electrochemically active materials useful according to the present disclosure include, but are not limited to, metals such as copper (Cu), iron (Fe), lead (Pb), bismuth (Bi), cobalt (Co), tin (Sn), lanthanum (La), cerium (Ce), calcium (Ca), magnesium (Mg), lithium (Li), alloys thereof, oxides, fluorides thereof, and combinations thereof. According to some aspects, the electrochemically active material comprises copper, copper (II) fluoride (CuF₂), or a combination thereof.

[00105] According to some aspects, the electrochemically active material according to the present disclosure may be a lightweight material which provides high capacity and high energy densities. Examples of electrochemically active materials useful according to the present disclosure include, but are not limited to, metals such as copper (Cu), iron (Fe), lead (Pb), bismuth (Bi), cobalt (Co), tin (Sn), lanthanum (La), cerium (Ce), calcium (Ca), magnesium (Mg), lithium (Li), alloys thereof, oxides, fluorides thereof, and combinations thereof. According to some aspects, the electrochemically active material comprises copper, copper (II) fluoride (CuF₂), or a combination thereof.

[00106] According to some aspects, the core may have a selected shape. For example, the core may comprise a nanoparticle (e.g., a spherical nanoparticle), nanotube, nanowire, frame, flake, nanoporous sheet, thin film, foam, or a combination thereof. According to some aspects, the size of the core may be determined either by electron conductivity or F ion mobility. In an illustrative example, 20 nm may be the distance limit of F ion penetration in the core material. If the path of either an electron or F ion is greater than this distance limit (in this example, 20 nm), electron conductivity and/or F ion mobility will be reduced or prevented. As such, according to some aspects, the core may comprise at least one dimension that is less than or equal to about the distance limit. For example, the core may comprise a spherical nanoparticle having a diameter of less than or equal to about the distance limit, as such a spherical nanoparticle will provide a pathway for an electron or F ion that is less than or equal to about the distance limit in ah directions. It should be understood that the core may have one or more dimensions that are greater than about the distance limit so long as it has a pathway of about the distance limit or less in at least one direction. For example, the core may comprise a flake having dimensions in the X and Y directions of greater than about the distance limit and a dimension in the Z direction of less than or equal to about the distance limit. According to some aspects, the distance limit may be about 20 nm, optionally about 30 nm, optionally about 40 nm, and optionally about 50 nm. According to some aspects, the distance limit may be between about 20 and 80 nm, optionally between about 30 and 70 nm, and optionally between about 40 and 60 nm. According to some aspects, the distance limit corresponds at least in part to certain aspects of the electrochemically active structure, for example, its shell. In particular, a shell having a relatively low ionic resistance will provide for a longer distance limit as F ions are more easily able to traverse the shell to the core.

[00107] Examples of cores useful according to the present disclosure include, but are not limited to, a nanoparticle with a diameter of less than or equal to about the distance limit, a nanowire with at least one dimension of less than or equal to about the distance limit, a nanotube having a wall thickness of less than or equal to about the distance limit, a flake (e.g., a triangle, rectangle, square, circle, or oval) having a thickness of less than or equal to about the distance limit, a film having a thickness of less than or equal to about the distance limit, a foam having a pore wall thickness of less than or equal to about the distance limit, a sheet having a thickness of less than or equal to about the distance limit, a frame having a thickness of less than or equal to about the distance limit, a mesh having a wire thickness of less than or equal to about the distance limit, and combinations thereof.

[00108] According to some aspects, the core can include at least one dimension that is less than or equal to about 40 nm, optionally less than or equal to about 35 nm, optionally less than or equal to about 30 nm, optionally less than or equal to about 25 nm, optionally less than or equal to about 20 nm, optionally less than or equal to about 15 nm, and optionally less than or equal to about 10 nm. In some embodiments, the core can include at least one dimension from about 1-25 nm, optionally from about 1-20 nm, optionally from about 1-15 nm, optionally from about 1-10 nm, optionally from about 1-10 nm, and optionally from about 1-5 nm.

[00109] The electrochemically active structure further comprises a shell that at least partially surrounds the core. For example, the shell may surround the core such that at least about 50% of the core’s surface area is covered by the shell, optionally at least about 60%, optionally at least about 70%, optionally at least about 80%, optionally at least about 90%, optionally at least about 95%, and optionally at least about 100%. According to some aspects, the molecular coverage of the shell on the core may be between about 1 and 100 nm ², optionally between about 6 and 60 nm ².

[00110] In some embodiments, the shell at least partially surrounding the core includes a thickness, wherein the ratio of thickness between the thickness of the metal nanostructure core and the thickness of the shell layer is from about 10: 1 to about 1 : 1, optionally from about 9: 1 to about 2: 1, optionally from about 8: 1 to about 3:1, optionally from about 7: 1 to about 4: 1, and optionally from about 6: 1 to about 5: 1.

[00111] According to some aspects, the shell at least partially surrounding the core has a thickness from about 1 nm to about 10 nm, optionally from about 2 nm to about 9 nm, optionally from about 3 nm to about 8 nm, optionally from about 4 nm to about 7 nm, optionally from about 5 nm to about 6 nm, and optionally about 5 nm.

[00112] According to some aspects, the shell at least partially surrounding the core has a thickness about 1 nm to 1 micron, optionally no more than 500 nm, optionally no more than 200 nm, optionall no more than 100 nm, optionally no more than 50 nm, no more than 10 nm, optionally about no more than 9 nm, optionally about no more than 8 nm, optionally about no more than 7 nm, optionally about no more than 6 nm, optionally about no more than 5 nm, optionally about no more than 4 nm, optionally about no more than 3 nm, optionally about no more than 2 nm, and optionally about no more than 1 nm. Further wherein all ranges can optionally be described as about 1-500 nm, 1-200 nm, 1-100 nm, 1-50 nm, 1- 10 nm, 1-5 nm, and 1-2 nm.

[00113] According to some aspects, a metal nanostructure core capable of forming a metal fluoride having a theoretical capacity in a liquid electrolyte is provided, the metal nanostructure core including at least one lesser dimension, and a shell at least partially surrounding the core, the shell including a thickness, wherein the thickness of the shell and the lesser dimension of the nanostructure core are provided in a ratio wherein the capacity of the material in the liquid electrolyte is from about 5% to 90%, optionally about 10% to 75%, optionally about 15% to 60%, optionally about 20% to 50%, optionally about 25% to 45%, and optionally about 30% to 40%, of the theoretical capacity of the metal fluoride.

[00114] According to some aspects, the metal nanostructure core has a thickness of no more than 30 nm, optionally no more than 25 nm, optionally no more than 20 nm, optionally no more than 20 nm, optionally no more than 15 nm, optionally no more than 10 nm, optionally no more than 8 nm, optionally no more than 6 nm, and optionally no more than 5 nm.

[00115] According to some aspects, the shell may comprise a shell material that is compatible with a liquid type F-shuttle battery. For example, the shell material may be selected such that dissolution of the core material into the liquid electrolyte of the liquid type F-shuttle battery during charge and/or discharge may be reduced or eliminated. The shell material may be selected to further provide adequate charge time. As used herein, the term“charge time” refers to the length of time required for a discharged liquid type F-shuttle battery electrode to fully charge, that is, the length of time required for F in the fluoride conducting electrolyte to travel from the anode to the cathode during the charge of the battery. According to some aspects, the charge time may be between about 1 and 20 minutes, optionally been about 1 and 10 minutes, and optionally between about 3 and 5 minutes.

[00116] According to some aspects, the shell material may be selected in order to acceptably utilize the electrochemically active material comprised by the core during charge and/or discharge. It should be understood that utilization refers to the portion of the electrochemically active material that accepts F ions during charging and/or the portion of the electrochemically active material that is reduced during discharging. According to some aspects, by selecting a shell material having a relatively low ionic resistance as described herein, at least about 50% of the electrochemically active material may be utilized during charge and/or discharge, optionally at least about 60%, optionally at least about 70%, optionally at least about 80%, optionally at least about 90%, and optionally at least about 100%.

[00117] According to some aspects, the shell material may comprise a“soft shell” material. As used herein,“soft” refers to a material as described herein, and in particular, a material that includes at least one material capable of self-assembly as described herein. Examples of soft shell materials include, but are not limited to, surfactants, certain polymers, a non-surfactant molecule having one or more specific functional groups, and combinations thereof. According to some aspects, the shell material may comprise an organic material, and in particular, an organic material that includes at least one material capable of self-assembly as described herein. Examples of organic shell materials include, but are not limited to, organic soft shell materials such as organic surfactants, organic or organic molecule-containing polymers, non-surfactant organic molecules having one or more specific functional groups, and combinations thereof.

[00118] According to some aspects, the specific functional groups as described herein may be selected from the group consisting of -COOH, -NH₂, -COH, -OH, -SH, -PO3H, - SO3H, -CN, -NC, -R2P, -COO , -COO-OOCR, ene-diol, -CºN, -NºN⁺(BF₄ ), -Sac, -SR, -SSR, -CSSH, -S₂0₃ Na⁺, -SeH, -SeSeR, -R₂P=0, -P0₃ ²7-P(0)(0H) , -P0₄ ² , -NºC, - HC=CH₂, -CºCH, -S1H3, -S1CI3, -OCH₂CH3, formula (I), formula (II), formula (III), and combinations thereof, wherein formula (I) is:

A formula (I), formula (II) is:

formula (II), and formula (III) is:

formula (III) wherein R’ and R” are each independently an organic chain, particularly an organic chain capable of being partially or fully fluorinated, or an aromatic group, either alone or in combination with another R’ or R”, particularly an aromatic group substituted with one or more fluorophilic groups. Example organic chains useful for R’ and R” include, but are not limited to, -(CF₂)_nCF₃, (CFI₂CF₂)nCF3, and (CF₂CH₂0)_nCF₃. Examples of functional groups according to formula (III) having at least one aromatic group are shown below as formula (IV):

formula (IV), and as formula (Y):

formula (Y). [00119] It should be understood that each R’ and R” may be the same as another R’ or R”, or may be different. According to some aspects, each R’ may show acceptable fluorination characteristics and/or each R” may show acceptable stabilization characteristics. It should further be understood that the carbon atom having the unshared valence electrons in the carbene shown in formula (III) may be configured for attachment to one or more molecules comprised by the core, as described herein. Example materials comprising a functional group having formula (III) include those described in Smith et ah,“N-Heterocyclic Carbenes in Materials Chemistry.” Chem. Rev., 2019, 119, 4986- 5056, which is incorporated herein by reference in its entirety.

[00120] According to some aspects, the surfactant may comprise a surfactant useful for preparing the core as described herein, such as a surfactant having one or more functional groups selected from the group consisting of a polar head (e.g., a polar head comprising one or more of the specific functional groups as described herein), a carbon- containing tail (e.g., alkanes, alkynes, alkenes, and aromatic rings), a fluorocarbon- containing tail (e.g., aliphatic chains such as (CF₂)_n, (CHF)_n, (CFI₂CF₂)n, and (CH₂OCH₂CF₂)_n, and/or aromatic groups such as (C6-xF_x-)_n), and combinations thereof. Examples of surfactants useful according to the present disclosure may include, but are not limited to, oleylamine, oleic acid, tris(trimethylsilyl)silane, 3, 3, 4, 4, 5, 5, 6, 6, 7, 7, 8, 8, 9, 9,10,10,10-hep tadecafluorodecanethiol, 2-(trifluoromethoxy)-benzenethiol, P-[ 12-(2,3 ,4, 5,6-pentafluorophenoxy)dodecyl]-Phosphonic acid, P-(3, 3, 4, 4, 5, 5, 6, 6, 7, 7, 8, 8, 9, 9, 10, 10, lO-heptadecafluorodecyl)-Phosphonic acid, pentafluorobenzylphosphonic acid, perfluorododecanoic acid and combinations thereof. According to some aspects, the surfactant may comprise one or more surfactants useful in the production of the core.

[00121] According to some aspects, the certain polymers may comprise polymers capable of being formed via in-situ polymerization, particularly polymers capable of being formed via in-situ polymerization from their monomers or from shorter oligomeric species. Additionally or alternatively, the certain polymers may be capable of self-healing through hydrogen bonding. For example, the certain polymers may be capable of hydrogen bonding so as to autonomously and repeatedly“self-heal” imperfections in the shell, such as cracks and/or gaps that may result at least in part from volume expansion and/or contraction of the core during charge and discharge, as will be discussed in more detail below in regard to Fig. 28. Examples of such polymers include, but are not limited to, polyvinylpyrrolidone (PVP), poly(methyl methacrylate) (PMMA), amino-terminated, C=0 bond included cross linked polymers (P. Cordier, F. Tournilhac, C. Soulie-Ziakovic, L. Leibler, Nature 451, 977, (2008); B.C. Tee, C. Wang, R. Allen, Z. Bao, Nat Nanotechnol 7, 825, (2012)), and combinations thereof.

[00122] According to some aspects, the shell may comprise one or more monolayers. According to some aspects, the shell may comprise one, two, three, or more monolayers. According to some aspects, each of the monolayers may be the same or different.

[00123] According to some aspects of the present disclosure, the shell material may comprise inorganic materials, such as metal salts. Examples of the metal salts used to form the shell include alkali metal salts, alkaline earth metal salts, and transition metal salts. In certain embodiments, the metal salt used to form the shell includes lanthanum salts, cerium salts, and magnesium salts. In certain embodiments, the metal salt used to form the shell is selected from the group consisting of lanthanum salts and cerium salts. In certain embodiments, the metal salt is a lanthanum salt. In a preferred embodiment, the lanthanum salt is lanthanum nitrate. In some embodiments, the halide salt is sodium fluoride. In a non-limiting example, the shell comprises a metal fluoride or metal oxyfluoride containing material (i.e. CeF₃, CeOF, LaOF, LaF₃). In some embodiments, the shell of the core-shell nanoparticles may be formed by mixing isolated metal nanoparticles used to form the core with, for example, a metal salt solution and a halide salt solution that react to form the metal halide shell on the core.

[00124] In some embodiments, the metal salt solution comprises two metal salts. In some such embodiments, one of the two metal salts is a barium salt. In some embodiments, the metal salt solution comprises a barium salt and a lanthanum salt. In some embodiments, the metal salt solution comprises barium nitrate and lanthanum nitrate. In some embodiments, the metal salt solution comprises barium nitrate and lanthanum nitrate in a ratio of about 1 : 10.

I. Cu Nanoparticles Encapsulated in LaF₃ and Barium-Doped LaF₃ Shells

[00125] A method of making Cu nanoparticles encapsulated in LaF₃ or Barium-Doped

LaF₃ shells has been disclosed in U.S. Pat. Appl. No. 16/013,739 (published as U.S. Pat. Appl. Pub. No. 2018/0301764), which is incorporated herein by reference in its entirety.

[00126] Fig. 3A depicts TEM images of Cu@LaF₃ core-shell nanoparticles and Cu@Lao_.97Ba_0.03F2.97 core-shell nanoparticles, respectively. In Fig. 3A, the central black areas correspond to the copper core, and the peripheral black and white areas correspond to the LaF₃ or La0.97Ba0.05F2.97 shells. The figure shows homogeneous coverage of the copper core directly coated with the LaF₃ or La0_.97Ba0_.05F2.97 shells. [00127] Core-shell nanoparticles with shells of the formula Cu@La0.97Ba0.03F2.97 are shown schematically in Fig. 3B; Cu@LaF₃ is included for comparison. Initially, the copper nanoparticle core may be up to about 50 nm in diameter before use and the LaF₃ or La0_.97Ba0_.03F2.97 coating may be about 5 nm thick. The CuF2 layer that forms around the Cu core during battery charging can grow to a thickness of about 3 nm in Cu@LaF₃ nanoparticles. However, by doping Ba into the LaF₃ shell, the CuF2 layer can grow to a greater thickness, e.g. around 10 nm in Fig. 3B.

[00128] Figs. 4A and 4B demonstrate the capacity improvement achieved upon Ba- doping. Fig. 4A shows the voltage profile of the first charge-discharge cycle of a Cu@LaF₃ electrode or a Cu@La0.97Ba0.03F2.97 electrode, compared to the Ag/Ag⁺ reference electrode. The capacity delivery of the Ba-doped electrode (Cu@La0.97Ba0.03F2.97) reaches 95.2 mAh/g compared to only 50.2 mAh/g for Cu@LaF₃ (Fig. 4B). Thus, Ba-doping of the LaF₃ shell nearly doubles the capacity of cathodic electrode. With Ba doping, the ionic conductivity of the LaF₃ shell is improved about 100 times; see, e.g., M. Anji Reddy and M. Fichtner, Batteries based on fluoride shuttle, J Mater. Chem. 2011, 21, 17059-17062, which is incorporated herein by reference in its entirety. Fluoride ion can more readily travel through the shell to react with Cu to form CUF₂, and the amount of CuF2 formation directly determines the capacity of the battery. The more CuF2 that is formed, the higher the capacity of the battery. Therefore, the utilization of Cu can be nearly doubled by Ba-doping of the LaF₃ shell.

[00129] Cu or CUF₂ is useful as a cathode material for liquid type F-shuttle batteries. These materials are relatively inexpensive and are light weight, which provides a high capacity and a high energy density. Theoretical capacity of CuF₂ is 528 mAh/g. However, pure Cu or CuF₂ is easily dissolved into liquid electrolytes during charge and discharge. To solve this issue, a Cu core is coated with LaF₃ or Ba doped LaF₃ shell structures, which effectively prevents Cu from dissolution during charge/discharge cycling. For Cu@LaF₃, for example, the LaF₃ shell effectively prevents Cu from dissolution during charge/discharge. As a result, Cu can be converted to CuF₂ during charge, and CuF₂ can be reduced to Cu during discharge. With a Ba-doped shell (e.g., La_0.97Ba_0.03F_2.97), the ionic conductivity of the shell can be improved 100 times compared to that of a LaF₃ shell, i.e., the shell has low resistance. F ions more easily pass through the shell so that more Cu can be fluorinated to CuF₂ during charge. Capacity is doubled compared to the undoped LaF₃ shell. (See Figs. 4A and 4B and Fig. 5).

II. Designs of Cu Nanostructures [00130] Due to poor electrical and ionic conductivities of many metal fluorides, it is necessary to design the structures of the metal fluorides to fully utilize the active materials and achieve their specific capacities and energy densities.

[00131] In one embodiment, for better utilization of the Cu/CuF₂ electrode materials to achieve an energy density close to its theoretical capacity (i.e. 843.5 mAh/g for Cu and 528 mAh/g for CuF₂), structural designs tailored to satisfy the requirement of no more than 20 nm thickness of Cu nanomaterials along at least one direction or one axis of the Cu nanostructure are preferred. Among these structures, Cu may be the active material having a LaF₃ or Ba_xLai-_xF3-_x coating/coverage in the range of -5-20 nm.

[00132] Examples of such Cu nanostructures include: nanoparticles, nanotubes, nanowires, nanoframes, nanoflakes, nano porous, sheets, thin films and the like. According to some aspects, such Cu nanostructures can comprise Cu thin films with a thickness no more than 20 nm. In some embodiments, such Cu nanostructures can comprise Cu Nanofoams With A Porous Wall Having A Thickness No More Than 20 nm. In some embodiments, such Cu nanostructures can comprise Cu mesh with a wire having a thickness no more than 20 nm.

[00133] (i) Cu Nanoparticles (“NP”).

[00134] A structural design of Cu core nanoparticles is illustrated in Fig. 6 where the Cu core nanoparticles have a diameter no more than 20 nm and a LaF₃ or Ba_xLai_-xF_3-x coating/shell. In Fig. 6, in any direction, the thickness/diameter of Cu core nanoparticles is no more than 20 nm due to their spherical shape.

[00135] Example 1. Synthesis of 6 nm Cu Nanoparticles (“NP”)

[00136] NH₄OH (0.5 mL, 14.5 M) was added to a stirring solution of CuClr2 H₂0 (0.24 g, 1.4 mmol) and cetrimonium bromide (CTAB, 0.68 g, 1.87 mmol) in water (93 mL, DI) in an argon atmosphere at 23 °C. Hydrazine hydrate (50-60%, 3 mL, 17.66 M) was added to a solution of CTAB (0.68 g, 1.87 mmol) and citric acid monohydrate (0.036 g, 0.18 mmol) in water (57 mL, DI). The hydrazine solution was immediately transferred to a 60 mL syringe and added over 5 minutes via a syringe pump to the Cu precursor solution. Once the addition of the hydrazine solution was complete the argon line was removed and the reaction was stirred open to air. Once exposed to air a solution of citric acid monohydrate (0.21 g, 1.0 mmol) in water (5 mL) was injected all at once. The mixture was then stirred for 1 hour, open to air. The Cu NP were isolated via centrifuge (12,000 rpm for 5 min.), the supernatant was discarded and the Cu NP were washed with EtOH (10 mL) twice. The product exhibited small, broad Cu peaks by XRD. See Fig. 7. [00137] Example 2. Synthesis of 6 nm Cu Nanoparticle Shell

[00138] The Cu NP (6 nm) obtained in Example 1 was isolated and washed once with water (20 mL). The Cu NP was re-dispersed in water (300 mL) and a solution of La(N0₃)₃ 6H₂O (0.43 g, 1.0 mmol) in water (60 mL) was added and the mixture was stirred (60 min.) in an argon atmosphere. The sample was isolated (12,000 rpm for 10 min) and re- dispersed in water (300 mL). To the stirring solution NaF (0.042 g, 1.0 mmol) in water (60 mL) was injected at 6 mL/min then stirred (60 min.) in an argon atmosphere. The sample was isolated via centrifuge (12,000 rpm for 10 min) and washed twice with EtOH (20 mL). XRD showed complete oxidation of the Cu core sample to Cu₂0 with a LaF₃ shell. See Fig. 8. The TEM images of 6 nm Cu core NP and 6nm Cu core NP with a LaF₃ shell are depicted in Figs. 9A and 9B, respectively.

[00139] Example 3. Reduction of Cu₂0 to Cu in 6 nm Cu Core NP with A LaF₃ Shell.

[00140] The Cu₂0 in the core nanoparticles obtained in Example 2 was effectively reduced to Cu by a mixture of H₂ and N₂ gases under heat treatment of 300 °C for six hours. The particle size of Cu NP increased during the reduction reaction. XRD spectra of 6 nm Cu core NP with a LaF₃ shell after reduction reaction is shown in Fig. 10.

[00141] (ii) Cu Nanowires (“NW”) Encapsulated in LaF₃ or Ba-Doped LaF₃ Shells (“Hard Shells”).

[00142] The structural design of Cu core nano wires is illustrated in Fig. 11 where the Cu nanowires have a cross-sectional diameter no more than 20 nm and a LaF₃ or Ba_xLai- _XF_3-X coating. In Fig. 11, the cross-sectional diameter of Cu core in the nanowire is no more than 20 nm and the thickness of La_l-xBaxF_3-x/LaF₃ shell/coating is about 5 nm.

[00143] Example 4. Two Phase Shell Formation on Cu Nanowires

[00144] About 20 mg of Cu nanowires were re-dispersed in 50 ml toluene. A first portion of tetrabutylammonium bromide (0.322 g, 1.0 mmol) was added into the Cu nanowires toluene suspension. A solution of La(N0₃)₃ 6H₂0 (0.866 g, 2.0 mmol) in water (50 mL) was injected at 5 mL/min into the toluene suspension. This mixture was stirred very rapidly for 2 hours. The water layer was removed via a separatory funnel and a second portion of tetrabutylammonium bromide (0.322 g, 1.0 mmol) was added to the toluene layer. A solution of NaF (0.084 g, 2.0 mmol) in water (50 mL) was injected at 5 mL/min into the stirring toluene suspension. This mixture was stirred very rapidly for additional 2 hours. The water layer was removed via separatory funnel and ethanol (20 mL) was added to distribute the product. The product was isolated via centrifuge (12,000 rpm for 10 min) then washed twice with EtOH (20 mL).

[00145] As set forth above, the two phase shell formation method can be applied to nano wires. However, the applications of the same coating method is not limited to nanowires or relevant applications. Even further the core material is not limited to copper. In one example, The coated structures may be used as a cathode material in a Fluoride Shuttle battery. In another example, the Fluoride Shuttle battery comprises a liquid electrolyte.

[00146] The XRD spectra of Cu nanowires, a small amount of Cu₂0 after shell formation, and the LaF₃ shell of Cu nanowires are depicted in Fig. 14. Figs. 15A and 15B delineate SEM images of Cu nanowires prior to and after two phase LaF₃ shell formation, respectively. TEM images with different magnifications in Figs. 16A, 16B, and 16C show the formation of LaF₃ shells around Cu nanowires. In the images, the grey areas surrounding the Cu nanowires are the LaF₃ shells.

[00147] Fig. 17 shows the voltage profile of the charge-discharge cycle of an electrode made of Cu nano wires encapsulated in LaF₃ shells (CuNW@LaF₃) compared to the Ag/Ag⁺ reference electrode. The capacity delivery of electrode made of CuNW encapsulated in LaF₃ shells reaches 183 mAh/g compared to 95.2 mAh/g for Cu@Ba_xLai- _XF_3-X and 50.2 mAh/g for Cu@LaF₃, respectively. Thus, the electrode made of Cu nanowires encapsulated in LaF₃ shells nearly doubles the capacity of Cu@Ba_xLai_-xF_3-x and nearly has four times the capacity of Cu@LaF₃. Without wishing to be bound to any particular theory, it is believed that the amount of CuF₂ formation directly determines the capacity of the battery. The more CuF₂ that is formed, the higher the capacity of the battery can be achieved. Therefore, the utilization of Cu can be significantly increased by Cu nanowires coupled with LaF₃ encapsulation. In one embodiment, CuNW@LaF₃ can reach about 35% of theoretical capacity of CuF₂, whereas Cu@Ba_xLai_-xF_3-x and Cu@LaF₃ can reach about 18% and 9.5% of the theoretical capacity of CuF₂, respectively.

[00148] In addition, Fig. 18 shows the XRD spectra of CuNW@LaF₃ in initial condition, i.e., in an electrode before a use, and then after a charge (fluorination) and a subsequent discharge (defluorination), respectively. CuF₂ can be formed after charge and then reduced to Cu after discharge. Fig. 18 indicates that Cu in the form of nanowires coupled with LaF₃ shells can be cycled in liquid electrolytes.

[00149] (iii) Cu Nanotubes. [00150] The structural design of Cu nanotubes is illustrated in Fig. 21 where the Cu nanotubes have a Cu inner wall with a cross-sectional thickness of no more than 20 nm and a LaF₃ or Ba_xLai-_xF3-_x coating layer. In Fig. 21, the cross-sectional thickness of Cu inner wall of nanotubes is no more than 20 nm.

[00151] (iv) Cu Nanoflakes.

[00152] Cu flakes may take many shapes, such as triangle, rectangle, square, circle, oval etc. The structure of Cu nanoflakes is illustrated in Fig. 22 where the Cu nanoflakes have a minimum thickness of no more than 20 nm and a LaF₃ or Ba_xLai_-xF_3-x coating. In Fig. 22, at least along one direction or one axis, the thickness of the Cu nanoflakes is no more than 20 nm.

[00153] (v) Cu Nanoframes.

[00154] The structural design of Cu nanoflakes is illustrated in Fig. 23 where the Cu nanoframes have an inner layer of Cu with a thickness no more than 20 nm. In Fig. 23, the inner copper wall within the Cu nano frame has a thickness no more than 20 nm.

[00155] (vi) Cu Nanosheets With A Thickness No More Than 20 nm.

[00156] The structural design of Cu nanosheets is illustrated in Fig. 22 where the shortest direction of the Cu nanosheets has a thickness no more than 20 nm. In Fig. 22, the shortest direction of Cu nanosheets has a thickness no more than 20 nm.

III. Other Metal Materials Suitable for Making Nanostructures.

[00157] In the present disclosure, the metal nanostructures suitable for making cathodic electrode is not limited to copper. As shown in Fig. 1C, transition metals and any salts thereof can be used to prepare the nanostructures encapsulated in various coating layers as disclosed in the previous section. Suitable transition metal comprises metals in the d-block of the periodic table of the elements, including the lanthanide and actinide series. Transition metal salts include, but are not limited to, salts of scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, and lawrencium.

IV. Electrochemically Active Structure Encapsulated in Self- Assembled Shell (“Soft Shell”) [00158] Fig. 27A shows an example electrochemically active structure 11 according to aspects of the present disclosure. As show in Fig. 27 A, the electrochemically active structure 11 may comprise a core 12 as described herein and a monolayer 13 comprising a shell material as described herein. According to some aspects, the monolayer 13 may be, for example, a self-assembled monolayer (SAM) comprising a surfactant as described herein. It should be understood that in this example, monolayer 13 corresponds to the shell as described herein.

[00159] Fig. 27B shows an example electrochemically active structure 11 comprising a core 12 as described herein and a monolayer 13 comprising a shell material as described herein. Fig. 27B also shows a second monolayer 14 covering at least a portion of the first monolayer 13. The second monolayer 14 may also be a SAM that is either the same or different from the first monolayer 13. It should be understood that in this example, the first monolayer 13 and the second monolayer 14 may together correspond to the shell as described herein. Furthermore, the first and second monolayers can be self-assembled.

[00160] Fig. 27C shows an example electrochemically active structure 11 comprising a core 12 as described herein and a monolayer 13 comprising a shell material as described herein. Fig. 27C also shows a polymer layer 15 covering at least a portion of the monolayer 13. The polymer layer 15 may comprise any of the polymers as described herein. It should be understood that in this example, the monolayer 13 and the polymer layer 15 may together correspond to the shell as described herein.

[00161] It should be understood that while Figs. 27A-C show certain example shell configurations, the electrochemically active structure may comprise a shell having a different configuration. For example, the shell may comprise more than two SAMs and/or more than one polymer layer, wherein the position of the SAMs and/or polymer layer are in any arrangement with respect to each other.

[00162] According to some aspects, the shell may be configured to accommodate the volume change of the electrochemically active material between charged and discharged states. For example, Fig. 28 shows an example schematic of charging and discharging an electrochemically active structure 21 as described herein. As shown in Fig. 28, the electrochemically active structure 21 may comprise a core 22 and a shell comprising a SAM 23 and a polymer layer 24 as described herein. The core may comprise any core as described herein, for example, a Cu core. Fig. 28 shows a schematic of charging the electrochemically active structure 21, e.g., when F ions travel to a cathode comprising the electrochemically active structure 21. As shown in Fig. 28, F ions are able to traverse the shell to the core 22 such that at least a portion of the Cu core 22 is converted to CuF₂ 25. As the Cu in the Cu core 22 is converted to CuF₂ 25, the volume of the core may expand. Without wishing to be bound by theory, as the volume of the core expands, SAM 23 may defect or crack, thereby accommodating the change in volume. As shown in Fig. 28, as the electrochemically active structure 21 is discharged, the CuF₂ 25 may be reduced back to Cu 22, and the volume of the core may contract. As the volume contracts, the SAM 23 may self-assemble or "self-heal" to its original configuration.

[00163] Figs. 16A-16C show an example transmission electron microscope (TEM) image of an electrochemically active structure according to aspects of the present disclosure. In particular, Fig. 16A shows a nanowire having a shell as described herein. V. Cu Nanowire (CuNW) Encapsulated in Surfactant Shells (“Soft Shells”)

[00164] Cu nanowires can be encapsulated in surfactant soft shells. The soft shells comprises at least one organic surfactant. Suitable organic surfactants comprise one or more specific functional group, which may be selected from the group consisting of - COOH, -NH , -COH, -OH, -SH, -PO3H, -SO3H, -CN, -NC, -R₂P, -COO , -COO-OOCR, ene-diol,

R₂P=0, -

formula (I), formula (II), formula (III), an alkane, an alkyne, an alkene, an aromatic ring, and combinations therefore,

wherein formula (I) is:

formula (I),

formula (II) is:

formula (II),

and formula (III) is:

formula (III),

wherein R’ and R” are each independently an organic chain or an aromatic group, either alone or in combination with another R’ or R”. Examples of suitable surfactants include oleylamine, oleic acid, tris(trimethylsilyl)silane, 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10, lO-heptadecafluorodecanethiol, 2-(trifluoromethoxy)-benzenethiol, P-[l2-(2,3,4,5,6- pentafluorophenoxy)dodecyl]-Phosphonic acid, P-(3, 3, 4, 4, 5, 5, 6, 6, 7, 7, 8, 8, 9, 9, 10, 10,10- heptadecafluorodecyl)-Phosphonic acid, pentafluorobenzylphosphonic acid, perfluorododecanoic acid and combinations thereof. More specifically, the suitable surfactants are selected from oleylamine, oleic acid, tris(trimethylsilyl)silane, or a combination thereof. The structure of CuNW@soft shell is similar as that of Fig. 11, except that the shell layer is made of surfactants.

[00165] According to some aspects, the surfactant soft shells can comprise organic or organic molecule-containing polymers forming polymer shells; the structure of CuNW@soft shell comprising polymers is similar to that of Fig. 27A, except that the surfactant soft shell 13 comprises polymer. According to some aspects, the surfactant soft shells can comprise polymer shells as described for the“IV. Electrochemically Active Structure Encapsulated in Self-Assembled Shell” above. The structure of CuNW@soft shell with polymer shells is similar to that of Figs. 27B, 27C, and 28 except that a CuNW is at the core, the shell layer is made of surfactants, while the polymer layer may comprise any of the polymers as described herein. According to some aspects, Fig. 27C can represent a cross-section of a CuNW, and the monolayer 13 and the polymer layer 15 may together correspond to the shell as described herein. According to some aspects in Fig. 27C, the monolayer 13 and the polymer layer 15 may correspond to a surfactant shell and a polymer shell, respectfully. It should be understood that while Fig. 27C shows certain example shell configurations as described for CuNW, the shell may comprise a different configuration. For example, the shell may comprise a surfactant shell and a polymer shell in different arrangements. For example, the shell may comprise more than one surfactant shell and more than one polymer shell, wherein the position of the surfactant shell and the polymer shell are in any arrangement with respect to each other.

[00166] Example 5. Preparation of CuNW Encapsulated in Surfactant Shells

The method of synthesizing Cu nanowires has been reported in F Cui et ah,

Synthesis of Ultrathin Copper Nanowires Using Tris(trimethylsilyl)silane for High-

Performance and Low-Haze Transparent Conductors, Nano Letters 2015, 15, 7610-7615, the entirety of which is incorporated herein by reference. In this example, a solution of CuCh 2H₂0 (85 mg, 0.5 mmol) in oleylamine (5 g, 18.7 mmol) and oleic acid (0.1 g, 0.354 mmol) was sonicated in a glass vial until completely dissolved. Tris(trimethylsilyl)silane (0.5 g, 2.0 mmol) was added, and the mixture was heated up to 120 °C until the dark blue solution turned clear yellow. The mixture was heated further to 165 °C for 18 h. The Cu nanowires were isolated via centrifuge (12,000 rpm for 10 min.) and washed three times with toluene (10 mL). The XRD spectra and TEM images of the Cu nanowires produced in this example are illustrated in Figs. 12 and 13, respectively.

[00167] Example 6. Voltage Profile of the Charge-Discharge Cycle and XRD Characterization of A Cathode Made of CuNW@Soft Shell

[00168] A cathodic electrode was prepared using CuNW@soft shell nanomaterial of Example 5. The average cross-sectional diameter of CuNW core is about 20 nm. The voltage profile of the charge-discharge cycle of the CuNW@soft shell electrode is shown in Fig. 19. The Ag/Ag⁺ electrode was used as the reference in the experiment. According to Fig. 19, the capacity of 20 nm CuNW@soft shell cathode may reach above 200 mAh/g.

[00169] CuNW@soft shell electrode was further characterized by XRD and the experimental results are illustrated in Fig. 20. Fig. 20 shows the XRD spectra of CuNW@soft shell after a charge (fluorination) and after a subsequent discharge (defluorination), respectively. CuF₂ can be formed after charge and then reduced to Cu after discharge. Fig. 20 indicates that Cu in the form of nanowires coupled with surfactant soft shells can be cycled in liquid electrolytes.

[00170] Example 7. Comparison of Cathodes Made of Cu Nanostructures.

[00171] A series of cathodes having Cu nanostructures for F-shuttle batteries had been prepared. The Cu nanostructures used in the preparation of cathodes are CuNP@LaF₃ with a core having an average diameter about 50 nm, CuNP@La_0.97Ba_0.03F₂.97 with a core having an average diameter about 50 nm, CuNW@LaF₃ with a core having an average cross-sectional diameter about 20 nm, and CuNW@soft shells with a core having an average cross-sectional diameter about 20 nm.

[00172] Fig. 24 illustrates the voltage profiles of the charge-discharge cycles of a variety electrodes, which include about 50 nm CuNP@LaF₃, about 50 nm CuNP@Lao_.97Ba_0.03F_2.97, about 20 nm CuNW@LaF₃, and about 20 nm CuNW@soft shell, respectively. The Ag/Ag⁺ electrode was used as the reference in the experiment. In Fig. 24, capacities of 20 nm Cu nanowires encapsulated in either LaF₃ shells or in surfactant soft shells are clearly higher than 50 nm Cu nanoparticles encapsulated in either LaF₃ or La0.97Ba0.03F2.97 shells.

[00173] As shown in Fig. 25, the capacities of electrodes made of 50 nm CuNP@LaF₃, 50 nm CuNP@La0.97Ba0.03F2.97, 20 nm CuNW@LaF₃, and 20 nm CuNW@soft shell are 50.2, 95.2, 183, and 203 mAh/g, respectively. Thus, the electrodes made of Cu nanowires encapsulated in LaF₃ shells or soft shells nearly double the capacity of CuNP@La0.97Ba0.03F2.97 and nearly has four times the capacity of CuNP@LaF₃. As a comparison, the theoretical capacity of electrode made of CuF2 is about 528 mAh/g.

[00174] Furthermore, the capacity delivery of cathodes in Fig. 25 is normalized against the theoretical capacity of CuF2 to obtain percentile capacity of each electrode. The percentile capacities of all the tested electrodes are illustrated in Fig. 26. Fig. 26 indicates that capacities of electrodes made of 20 nm Cu nanowires encapsulated in LaF₃ shells and surfactant soft shells can reach 34.7% and 38.4% of theoretical capacity of CuF2, respectively.

[00175] While the aspects described herein have been described in conjunction with the example aspects outlined above, various alternatives, modifications, variations, improvements, and/or substantial equivalents, whether known or that are or may be presently unforeseen, may become apparent to those having at least ordinary skill in the art. Accordingly, the example aspects, as set forth above, are intended to be illustrative, not limiting. Various changes may be made without departing from the spirit and scope of the disclosure. Therefore, the disclosure is intended to embrace all known or later- developed alternatives, modifications, variations, improvements, and/or substantial equivalents.

[00176] Thus, the claims are not intended to be limited to the aspects shown herein, but are to be accorded the full scope consistent with the language of the claims, wherein reference to an element in the singular is not intended to mean“one and only one” unless specifically so stated, but rather“one or more.” All structural and functional equivalents to the elements of the various aspects described throughout this disclosure that are known or later come to be known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the claims. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the claims. No claim element is to be construed as a means plus function unless the element is expressly recited using the phrase“means for.” [00177] Further, the word“example” is used herein to mean“serving as an example, instance, or illustration.” Any aspect described herein as“example” is not necessarily to be construed as preferred or advantageous over other aspects. Unless specifically stated otherwise, the term“some” refers to one or more. Combinations such as“at least one of

A, B, or C,”“at least one of A, B, and C,” and“A, B, C, or any combination thereof’ include any combination of A, B, and/or C, and may include multiples of A, multiples of

B, or multiples of C. Specifically, combinations such as“at least one of A, B, or C,”“at least one of A, B, and C,” and“A, B, C, or any combination thereof’ may be A only, B only, C only, A and B, A and C, B and C, or A and B and C, where any such combinations may contain one or more member or members of A, B, or C. Nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the claims.

[00178] The examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how to make and use the present invention, and are not intended to limit the scope of what the inventors regard as their invention nor are they intended to represent that the experiments below are all or the only experiments performed. Efforts have been made to ensure accuracy with respect to numbers used (e.g. amounts, dimensions, etc.) but some experimental errors and deviations should be accounted for.

[00179] Moreover, all references throughout this application, for example patent documents including issued or granted patents or equivalents; patent application publications; and non-patent literature documents or other source material; are hereby incorporated by reference herein in their entireties, as though individually incorporated by reference.

Claims

CLAIMS What is claimed is:

1. A fluoride shuttle battery comprising: a cathode comprising a metal nanostructure core including at least one dimension that is less than or equal to 20 nm, and a shell at least partially surrounding the core;

an anode; and

a liquid electrolyte containing fluoride ions.

2. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core comprises a nanoparticle with a diameter of less than or equal to 20 nm.

3. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core comprises one or more cylindrical structures including a diameter of less than or equal to 20 nm and a length of greater than 20 nm.

4. The fluoride shuttle battery of claim 3, wherein the cylindrical structures comprise structures selected from nanotubes, nanowires, nanoframes, and combinations thereof.

5. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core comprises one or more sheetlike structures including a thickness of less than or equal to 20 nm and another dimension that is greater than 20 nm.

6. The fluoride shuttle battery of claim 5, wherein the sheetlike structures comprises structures selected from flake structure, sheet structure, fdm structure, and combinations thereof.

7. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core comprises a complex shape comprising interconnected metal portions and channels defining a network of pores wherein each channel comprises at least one dimension that is less than 25 nm.

8. The fluoride shuttle battery of claim 7, wherein the complex shape comprises porous nanosheets, nanoframes, or foams.

9. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core has a thickness of no more than 20 nm.

10. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core has a thickness of no more than 6 nm.

11. The fluoride shuttle battery of claim 1 , wherein the metal nanostructure core is enclosed by a Lai_-xBa_xF3-_x shell layer, wherein X = 0 - 0.5.

12. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core is enclosed by the Lai_-xBa_xF3-_x shell layer, wherein X = 0.

13. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core is enclosed by the Lai_-xBaxF3-x shell layer, wherein X = 0.03.

14. The fluoride shuttle battery of claim 1, wherein the Lai_-xBa_xF3-_x shell layer has a thickness of no more than 5 nm.

15. The fluoride shuttle battery of claim 1, wherein the ratio of thickness between the metal nanostructure core and the shell layer is from about 10:1 to about 1:1.

16. The fluoride shuttle battery of claim 15, wherein the ratio of thickness between the metal nanostructure core and the shell layer is about 4:1.

17. The fluoride shuttle battery of claim 15, wherein the ratio of thickness between the metal nanostructure core and the shell layer is about 1:1.

18. The fluoride shuttle battery of claim 1, wherein the metal is selected from a transitional metal, salts of the transition metal, and mixtures thereof.

19. The fluoride shuttle battery of claim 18, wherein the transition metal is selected from d-block of the periodic table of the elements, including the lanthanide and actinide series.

20. The fluoride shuttle battery of claim 18, wherein the transition metal is selected from scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, yttrium, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, lawrencium, and mixtures thereof.

21. The fluoride shuttle battery of claim 18, wherein the transition metal comprises copper.

22. The fluoride shuttle battery of claim 21, wherein the copper nanostructure core comprises a copper nanowire, the copper nanowire having an average cross- sectional diameter of no more than about 20 nm.

23. The fluoride shuttle battery of claim 22, wherein the copper nanowire is enclosed by a LaF₃ shell layer.

24. The fluoride shuttle battery of claim 23, wherein the copper nano wire enclosed by the LaF₃ shell has an energy capacity of about 183 mAh/g or of about 34.7% of a theoretical capacity of CuF₂.

25. The fluoride shuttle battery of claim 1, wherein the shell layer is a soft shell layer.

26. The fluoride shuttle battery of claim 25, wherein the soft shell layer comprises a surfactant.

27. The fluoride shuttle battery of claim 25, wherein the soft shell layer comprises a polymer or oligomer.

28. The fluoride shuttle battery of claim 26, wherein the surfactant comprises oleylamine, oleic acid, tris(trimethylsilyl)silane, or a combination thereof.

29. The fluoride shuttle battery of claim 27, wherein the polymer is selected from the group consisting of polyvinylpyrrolidone, poly(methyl methacrylate), and combinations thereof.

30. The fluoride shuttle battery of claim 25, wherein the shell comprises at least a first self-assembled monolayer.

31. The fluoride shuttle battery of claim 30, wherein the shell further comprises a second self-assembled monolayer, wherein the second self-assembled monolayer covers at least a portion of the first self-assembled monolayer.

32. The fluoride shuttle battery of claim 30, wherein the shell further comprises a polymer layer, wherein the polymer layer covers at least a portion of the first self- assembled monolayer.

33. The fluoride shuttle battery of claim 25, wherein the nanostructure core comprises a copper nanowire, the copper nanowire having an average cross-sectional diameter of no more than about 20 nm.

34. The fluoride shuttle battery of claim 33, wherein the copper nanowire is enclosed by a soft shell layer, the soft shell layer comprising a surfactant.

35. The fluoride shuttle battery of claim 25, wherein the soft shell layer is permeable to F ion.

36. The fluoride shuttle battery of claim 34, wherein the copper nanowire enclosed by the soft shell has an energy capacity of about 203 mAh/g or of about 38.4% of a theoretical capacity of CuF₂.

37. A fluoride shuttle battery comprising: an electrode comprising a metal nanostructure core including at least one dimension that is less than or equal to 25 nm, and a shell at least partially surrounding the core; and

a liquid electrolyte.

38. The fluoride shuttle battery of claim 37, wherein the metal nanostructure core comprises one or more cylindrical structures including a diameter of less than or equal to 25 nm and a length of greater than 25 nm.

39. The fluoride shuttle battery of claim 38, wherein the cylindrical structures are chosen from nanotube, nanowire, and nanoframe.

40. The fluoride shuttle battery of claim 37, wherein the metal nanostructure core comprises a sheetlike structure including a thickness of less than or equal to 25 nm and another dimension that is greater than 25 nm.

41. The fluoride shuttle battery of claim 40, wherein the sheetlike structure is flake structure, sheet structure, or fdm structure.

42. The fluoride shuttle battery of claim 1, wherein the metal nanostructure core comprises a complex shape comprising interconnected metal portions and channels defining a network of pores wherein each channel comprises at least one dimension that is less than 25 nm.

43. The fluoride shuttle battery of claim 7, wherein the network of pores are porous nanosheets, nanoframes, or foams.

44. The fluoride shuttle battery of claim 37, wherein the at least one dimension is from 1 to 20 nm.

45. The fluoride shuttle battery of claim 37, wherein the at least one dimension is from 1 to 10 nm.

46. The fluoride shuttle battery of claim 37, wherein the shell has a thickness from 1 nm to 1 micrometer.

47. The fluoride shuttle battery of claim 37, wherein the shell has a thickness from 1 nm to 200 nm.

48. A fluoride shuttle battery comprising: a liquid electrolyte containing fluoride ions; and

a cathode comprising a material comprising:

a metal nanostructure core capable of forming a metal fluoride having a theoretical capacity in the liquid electrolyte, the metal nanostructure core includes at least one lesser dimension, and a shell surrounding the core, the shell includes a thickness, wherein the thickness of the shell and the lesser dimension of the nanostructure core are provided in a ratio wherein the capacity of the material in the liquid electrolyte is from at least 25% to 45% of the theoretical capacity of the metal fluoride.