WO2018130200A1 - Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication - Google Patents

Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication Download PDF

Info

Publication number
WO2018130200A1
WO2018130200A1 PCT/CN2018/072379 CN2018072379W WO2018130200A1 WO 2018130200 A1 WO2018130200 A1 WO 2018130200A1 CN 2018072379 W CN2018072379 W CN 2018072379W WO 2018130200 A1 WO2018130200 A1 WO 2018130200A1
Authority
WO
WIPO (PCT)
Prior art keywords
rubber
parts
vulcanization
weight
rubber composition
Prior art date
Application number
PCT/CN2018/072379
Other languages
English (en)
Chinese (zh)
Inventor
徐涛
傅智盛
吴安洋
Original Assignee
杭州星庐科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN201810020833.2A external-priority patent/CN108299740B/zh
Application filed by 杭州星庐科技有限公司 filed Critical 杭州星庐科技有限公司
Priority to US16/477,414 priority Critical patent/US12152134B2/en
Priority to JP2019559148A priority patent/JP7152033B2/ja
Publication of WO2018130200A1 publication Critical patent/WO2018130200A1/fr

Abstract

L'invention concerne un composite de caoutchouc. Le composite de caoutchouc comprend un substrat de caoutchouc et un système réticulable. Le substrat de caoutchouc comprend les constituants suivants, en parties en poids : polyéthylène ramifié, dont la teneur est a : 0 < a ≤ 100 parties, caoutchouc éthylène propylène monomère, dont la teneur est b : 0 ≤ b < 100 parties, caoutchouc éthylène propylène diène monomère, dont la teneur est c : 0 ≤ c ≤ 100 parties, et, le substrat de caoutchouc correspondant à 100 parties en poids, le système réticulable, dont la teneur est d : 1 ≤ d ≤ 15 parties. Le système réticulable comprend au moins un agent de réticulation et/ou un agent auxiliaire de réticulation, le degré de ramification du polyéthylène ramifié n'est pas inférieur à 50 chaînes ramifiées/1000 atomes de carbone, la masse moléculaire moyenne en masse n'est pas inférieure à 50 000, et la viscosité Mooney n'est pas inférieure à 2 ml(1+4) à 125 °C. Le composite de caoutchouc résout efficacement le problème dans l'état de la technique d'un faible rendement de réticulation et d'une faible résistance mécanique, et simultanément acquiert de grandes performances d'isolation électrique et une grande résistance mécanique.
PCT/CN2018/072379 2017-01-13 2018-01-12 Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication WO2018130200A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US16/477,414 US12152134B2 (en) 2017-01-13 2018-01-12 Rubber composition, processing method thereof, and high-strength product using the same
JP2019559148A JP7152033B2 (ja) 2017-01-13 2018-01-12 ゴム組成物および加工方法、並びにそれを用いた高強度製品および製造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
CN201710025138 2017-01-13
CN201710025138.0 2017-01-13
CN201810020833.2A CN108299740B (zh) 2017-01-13 2018-01-10 橡胶组合物及加工方法，及应用其的高强度制品和生产方法
CN201810020833.2 2018-01-10

Publications (1)

Publication Number Publication Date
WO2018130200A1 true WO2018130200A1 (fr) 2018-07-19

Family

ID=62839314

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2018/072379 WO2018130200A1 (fr) 2017-01-13 2018-01-12 Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2018130200A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114106477A (zh) * 2020-09-01 2022-03-01 中国石油化工股份有限公司 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法
CN118994798A (zh) * 2024-09-05 2024-11-22 湖北联上科技有限公司 一种ul、cul电缆热固性绝缘材料

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1780876A (zh) * 2003-04-25 2006-05-31 美利肯公司 抗微生物树脂固化的橡胶制品和预硫化组合物
CN102086287A (zh) * 2009-12-03 2011-06-08 江苏润德医用材料有限公司 热塑性弹性体材料及由其制作的胶塞
CN102617938A (zh) * 2012-03-26 2012-08-01 兖矿集团有限公司 耐寒的电缆用乙丙绝缘材料
CN103980596A (zh) * 2014-05-13 2014-08-13 浙江大学 一种聚乙烯橡胶及其加工方法
CN104877225A (zh) * 2015-06-20 2015-09-02 浙江大学 一种气密层材料的制备方法及其原料配方

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1780876A (zh) * 2003-04-25 2006-05-31 美利肯公司 抗微生物树脂固化的橡胶制品和预硫化组合物
CN102086287A (zh) * 2009-12-03 2011-06-08 江苏润德医用材料有限公司 热塑性弹性体材料及由其制作的胶塞
CN102617938A (zh) * 2012-03-26 2012-08-01 兖矿集团有限公司 耐寒的电缆用乙丙绝缘材料
CN103980596A (zh) * 2014-05-13 2014-08-13 浙江大学 一种聚乙烯橡胶及其加工方法
CN104877225A (zh) * 2015-06-20 2015-09-02 浙江大学 一种气密层材料的制备方法及其原料配方

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114106477A (zh) * 2020-09-01 2022-03-01 中国石油化工股份有限公司 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法
CN114106477B (zh) * 2020-09-01 2023-07-21 中国石油化工股份有限公司 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法
CN118994798A (zh) * 2024-09-05 2024-11-22 湖北联上科技有限公司 一种ul、cul电缆热固性绝缘材料

Similar Documents

Publication Publication Date Title
JP7118450B2 (ja) ゴム組成物および加工方法、並びにそれを用いたゴムベルト、ゴムローラおよび製造方法
JP7152033B2 (ja) ゴム組成物および加工方法、並びにそれを用いた高強度製品および製造方法
WO2018130194A1 (fr) Composite de caoutchouc, procédé de traitement, produits en caoutchouc mettant en application le composite, et procédé de fabrication
JP7250341B2 (ja) ゴム組成物、それを用いた老化防止ゴム製品および製造方法
WO2018130197A1 (fr) Composite de caoutchouc, procédé de traitement, applications et procédé de fabrication de produits ignifuges
WO2018130195A1 (fr) Composite de caoutchouc, procédé de traitement, applications, procédé de fabrication des applications
JP7157464B2 (ja) ゴム組成物および加工方法、並びにそれを用いたゴムホースおよび製造方法
JP7162903B2 (ja) ゴム組成物及び加工方法、並びにそれを用いたブレーキ液耐性製品及び製造方法
JP7104426B2 (ja) ゴム組成物及び加工方法、並びにそれを用いたコンベアベルト及び製造方法
CN108314850A (zh) 橡胶组合物及加工方法，及应用其的橡胶制品和生产方法
WO2018130196A1 (fr) Composite de caoutchouc, applications dans un produit mousseux, et procédé de fabrication
WO2018130199A1 (fr) Composite de caoutchouc, procédé de traitement, tube de caoutchouc mettant en application un composite et procédé de fabrication
CN108299743B (zh) 橡胶组合物及加工方法与应用，及生产阻燃制品的方法
JP7156709B2 (ja) 光架橋によるゴム組成物およびその応用、並びに該応用の製造方法
WO2018130186A1 (fr) Composite de caoutchouc, procédé de traitement, élément d&#39;étanchéité mettant en application un composite et procédé de fabrication
WO2018130198A1 (fr) Composite de caoutchouc, procédé de traitement, composite d&#39;application de produit liquide résistant au freinage et procédé de fabrication
WO2018130191A1 (fr) Composite de caoutchouc à photoréticulation, applications et procédé de fabrication pour les applications
WO2018130187A1 (fr) Composite de caoutchouc, procédé de traitement, applications et procédé de fabrication de produits en caoutchouc à haute résistance
WO2020011004A1 (fr) Composition de caoutchouc polaire anti-vieillissement, procédé de traitement associé et application associée
WO2018130188A1 (fr) Composite de caoutchouc, procédé de traitement, courroie en caoutchouc et rouleau en caoutchouc utilisant le composite, et procédé de fabrication
CN108314851A (zh) 橡胶组合物及加工方法和应用，及该应用的生产方法
WO2018130189A1 (fr) Composite de caoutchouc, traitement, courroie transporteuse mettant en application un composite, et procédé de fabrication
WO2018130190A1 (fr) Matériau isolant non linéaire électroconducteur à base de caoutchouc et procédé de traitement correspondant
WO2018130200A1 (fr) Composite de caoutchouc, procédé de mise en œuvre, composite d&#39;application de produit à haute résistance et procédé de fabrication
WO2018130193A1 (fr) Composite de caoutchouc, procédé de traitement, applications, et élément d&#39;étanchéité de condensateur comprenant un composite

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18738448

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019559148

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18738448

Country of ref document: EP

Kind code of ref document: A1