WO2018116753A1 - Piston pour moteur à combustion interne, procédé de fabrication d'un piston pour moteur à combustion interne, et structure - Google Patents

Piston pour moteur à combustion interne, procédé de fabrication d'un piston pour moteur à combustion interne, et structure Download PDF

Info

Publication number
WO2018116753A1
WO2018116753A1 PCT/JP2017/042480 JP2017042480W WO2018116753A1 WO 2018116753 A1 WO2018116753 A1 WO 2018116753A1 JP 2017042480 W JP2017042480 W JP 2017042480W WO 2018116753 A1 WO2018116753 A1 WO 2018116753A1
Authority
WO
WIPO (PCT)
Prior art keywords
piston
sintered body
binder
combustion engine
internal combustion
Prior art date
Application number
PCT/JP2017/042480
Other languages
English (en)
Japanese (ja)
Inventor
高橋　智一
Original Assignee
日立オートモティブシステムズ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立オートモティブシステムズ株式会社 filed Critical 日立オートモティブシステムズ株式会社
Publication of WO2018116753A1 publication Critical patent/WO2018116753A1/fr

Abstract

L'invention concerne un piston destiné à un moteur à combustion interne, permettant une amélioration dans la contrôlabilité de la conductivité thermique. Le piston pour moteur à combustion interne comporte: une section de corps qui est formée d'un matériau métallique et munie d'une tête de piston et d'une partie de jupe, une partie de maintien étant formée dans la tête de piston du côté dirigé vers la chambre de combustion du moteur à combustion interne; et un corps fritté qui est disposé dans la partie de maintien et contient des particules creuses et un liant métallique, le corps fritté étant doté d'une partie de liant oxydé où le liant situé sur au moins la surface dirigée vers la chambre de combustion est oxydé.
PCT/JP2017/042480 2016-12-20 2017-11-28 Piston pour moteur à combustion interne, procédé de fabrication d'un piston pour moteur à combustion interne, et structure WO2018116753A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016247018A JP2018100625A (ja) 2016-12-20 2016-12-20 内燃機関のピストン、内燃機関のピストンの製造方法、及び構造体
JP2016-247018 2016-12-20

Publications (1)

Publication Number Publication Date
WO2018116753A1 true WO2018116753A1 (fr) 2018-06-28

Family

ID=62626345

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/042480 WO2018116753A1 (fr) 2016-12-20 2017-11-28 Piston pour moteur à combustion interne, procédé de fabrication d'un piston pour moteur à combustion interne, et structure

Country Status (2)

Country Link
JP (1) JP2018100625A (fr)
WO (1) WO2018116753A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115247603A (zh) * 2022-03-09 2022-10-28 广州汽车集团股份有限公司 氢气发动机活塞及其制造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000328292A (ja) * 1999-05-11 2000-11-28 Honda Motor Co Ltd Ｓｉ系アルミニウム合金の陽極酸化処理方法
JP2010185290A (ja) * 2009-02-10 2010-08-26 Toyota Central R&D Labs Inc 遮熱膜及びその形成方法
JP2015031226A (ja) * 2013-08-05 2015-02-16 トヨタ自動車株式会社 内燃機関とその製造方法
JP2015193915A (ja) * 2014-03-27 2015-11-05 スズキ株式会社 陽極酸化処理方法及び内燃機関の構造

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000328292A (ja) * 1999-05-11 2000-11-28 Honda Motor Co Ltd Ｓｉ系アルミニウム合金の陽極酸化処理方法
JP2010185290A (ja) * 2009-02-10 2010-08-26 Toyota Central R&D Labs Inc 遮熱膜及びその形成方法
JP2015031226A (ja) * 2013-08-05 2015-02-16 トヨタ自動車株式会社 内燃機関とその製造方法
JP2015193915A (ja) * 2014-03-27 2015-11-05 スズキ株式会社 陽極酸化処理方法及び内燃機関の構造

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115247603A (zh) * 2022-03-09 2022-10-28 广州汽车集团股份有限公司 氢气发动机活塞及其制造方法

Also Published As

Publication number Publication date
JP2018100625A (ja) 2018-06-28

Similar Documents

Publication Publication Date Title
CN105324570B (zh) 内燃机用活塞的制造方法及内燃机用活塞
US10221103B2 (en) Porous ceramic composite particle and method for preparing the same
JP2020076409A (ja) 付加的な製造技術を使用して作製されるピストン
JP2019508623A (ja) 対向ピストンエンジン用多層構造ピストンクラウン
US20090260594A1 (en) In-cylinder fuel-injection type internal combustion engine, piston for in-cylinder fuel-injection type internal combustion engine and process for manufacturing piston for in-cylinder fuel-injection type internal combustion engine
EP3440331B1 (fr) Piston avec insert thermiquement isolant et procédé de construction associé
WO2018116753A1 (fr) Piston pour moteur à combustion interne, procédé de fabrication d'un piston pour moteur à combustion interne, et structure
WO2018029903A1 (fr) Piston de moteur à combustion interne et procédé de fabrication de piston de moteur à combustion interne
WO2018147188A1 (fr) Piston pour moteur à combustion interne et son procédé de fabrication
JP2013087721A (ja) 遮熱膜の形成方法及び内燃機関
JP6760812B2 (ja) 内燃機関用ピストンおよび内燃機関用ピストンの製造方法
WO2018198786A1 (fr) Piston de moteur à combustion interne et procédé de commande du refroidissement d'un piston de moteur à combustion interne
JP2009287486A (ja) 内燃機関のピストン
JPS60119348A (ja) 内燃機関用ピストンおよびその製造方法
WO2014097924A1 (fr) Procédé de fabrication pour piston de moteur à combustion interne, dispositif de fabrication pour piston de moteur à combustion interne et moteur à combustion interne
WO2018037616A1 (fr) Piston pour moteur à combustion interne et procédé de fabrication dudit piston
WO2019049738A1 (fr) Piston de moteur à combustion interne, procédé de mesure de l'épaisseur de film d'un piston de moteur à combustion interne, et procédé de fabrication pour piston de moteur à combustion interne
JP2001240902A (ja) 低熱伝導率アルミニウム焼結材料及びその製造方法並びにピストン頂面材
JP2013129899A (ja) 断熱部材の製造方法およびこれにより製造された内燃機関
WO2018131356A1 (fr) Piston pour moteur à combustion interne
CN110894813B (zh) 气缸套及其制造方法和使用气缸套的气缸体的制造方法
JP2018178848A (ja) 内燃機関のピストン及び内燃機関のピストンの製造方法
WO2020003462A1 (fr) Procédé de fabrication de culasse, et matériau brut de culasse
CN113137316B (zh) 内燃机的活塞及其制造方法
EP4137612A1 (fr) Piston pour moteur à combustion interne et son procédé de fabrication

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17884109

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17884109

Country of ref document: EP

Kind code of ref document: A1

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载