WO2017208012A1 - Procédé d'assemblage de première et seconde pièces à l'aide d'éléments de fixation formés in situ et créés par faisceau laser ou faisceau d'électrons - Google Patents

Procédé d'assemblage de première et seconde pièces à l'aide d'éléments de fixation formés in situ et créés par faisceau laser ou faisceau d'électrons Download PDF

Info

Publication number
WO2017208012A1
WO2017208012A1 PCT/GB2017/051589 GB2017051589W WO2017208012A1 WO 2017208012 A1 WO2017208012 A1 WO 2017208012A1 GB 2017051589 W GB2017051589 W GB 2017051589W WO 2017208012 A1 WO2017208012 A1 WO 2017208012A1
Authority
WO
WIPO (PCT)
Prior art keywords
workpiece
hole
workpieces
filler
filler material
Prior art date
Application number
PCT/GB2017/051589
Other languages
English (en)
Inventor
Paola DE BONO
Original Assignee
The Welding Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by The Welding Institute filed Critical The Welding Institute
Publication of WO2017208012A1 publication Critical patent/WO2017208012A1/fr

Abstract

L'invention concerne un procédé d'assemblage de première et seconde pièces (1, 2). La première pièce (1) est conçue pour présenter un trou traversant qui passe d'un côté proximal à un côté distal de la première pièce (1). Les parties respectives des première et seconde pièces (1, 2) sont disposées les unes à côté des autres de manière à former une région d'assemblage de sorte que l'extrémité du trou traversant au niveau du côté distal de la première pièce (1) est adjacente à la partie de la seconde pièce (2) dans la région d'assemblage. Un matériau de remplissage est disposé dans le trou traversant, le matériau de remplissage pouvant former un joint soudé à la seconde pièce (2). Un faisceau de puissance est dirigé dans le trou traversant à partir du côté proximal de la première pièce (1), ce qui fait fondre le matériau de remplissage pour former une structure de verrouillage (9) dans le trou traversant qui est soudée à la seconde pièce (2) et qui fixe mécaniquement la première pièce (1) à la seconde pièce (2).
PCT/GB2017/051589 2016-06-03 2017-06-02 Procédé d'assemblage de première et seconde pièces à l'aide d'éléments de fixation formés in situ et créés par faisceau laser ou faisceau d'électrons WO2017208012A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1609751.1 2016-06-03
GB1609751.1A GB2550966A (en) 2016-06-03 2016-06-03 Joining method using in-situ formed fasteners

Publications (1)

Publication Number Publication Date
WO2017208012A1 true WO2017208012A1 (fr) 2017-12-07

Family

ID=56508045

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2017/051589 WO2017208012A1 (fr) 2016-06-03 2017-06-02 Procédé d'assemblage de première et seconde pièces à l'aide d'éléments de fixation formés in situ et créés par faisceau laser ou faisceau d'électrons

Country Status (2)

Country Link
GB (1) GB2550966A (fr)
WO (1) WO2017208012A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111819026A (zh) * 2018-03-05 2020-10-23 松下知识产权经营株式会社 接合结构以及接合方法
WO2022204089A1 (fr) * 2021-03-22 2022-09-29 Norma U.S. Holding Llc Raccord doté d'au moins une fenêtre de visualisation de soudure par points par résistance
WO2025061152A1 (fr) * 2023-09-22 2025-03-27 东华大学 Procédé de liaison pour un matériau composite à base de résine thermoplastique renforcée par des fibres continues et organe de raccordement formé

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6976572B2 (ja) * 2018-03-05 2021-12-08 伸和コントロールズ株式会社 ハニカムパネル及びその製造方法、並びに筐体
EP3556508B1 (fr) 2018-04-17 2020-11-25 C.R.F. Società Consortile per Azioni Procédé pour assembler un élément en matériau métallique et un élément en matériau plastique et composant hybride obtenu par ce procédé
CN110039209A (zh) * 2019-04-24 2019-07-23 首钢集团有限公司 一种异种金属的焊接方法
FR3110483B1 (fr) * 2020-05-20 2022-06-03 Arianegroup Sas Structure d’assemblage d’une pièce comprenant une première partie métallique et une deuxième partie en matériau composite à matrice organique
FR3110484B1 (fr) * 2020-05-20 2022-06-03 Arianegroup Sas Procédé d’assemblage d’une première partie métallique avec une deuxième partie en matériau composite à matrice organique, et pièce résultant d’un tel assemblage

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61116525A (ja) * 1984-11-13 1986-06-04 Toyota Motor Corp 合成樹脂材料の接合方法
DE19913436C1 (de) * 1999-03-25 2000-12-14 Erbsloeh Ag Schweißverbindung von Bauteilen aus unterschiedlichen Werkstoffen
JP2003311404A (ja) * 2002-04-23 2003-11-05 Hitachi Ltd タービン翼中子支持穴の封止溶接方法及びタービン翼
DE102010044886A1 (de) * 2010-09-09 2011-05-12 Daimler Ag Verfahren zum Fügen von zwei Bauteilen und Verbindung

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61116525A (ja) * 1984-11-13 1986-06-04 Toyota Motor Corp 合成樹脂材料の接合方法
DE19913436C1 (de) * 1999-03-25 2000-12-14 Erbsloeh Ag Schweißverbindung von Bauteilen aus unterschiedlichen Werkstoffen
JP2003311404A (ja) * 2002-04-23 2003-11-05 Hitachi Ltd タービン翼中子支持穴の封止溶接方法及びタービン翼
DE102010044886A1 (de) * 2010-09-09 2011-05-12 Daimler Ag Verfahren zum Fügen von zwei Bauteilen und Verbindung

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111819026A (zh) * 2018-03-05 2020-10-23 松下知识产权经营株式会社 接合结构以及接合方法
CN111819026B (zh) * 2018-03-05 2022-08-09 松下知识产权经营株式会社 接合结构以及接合方法
WO2022204089A1 (fr) * 2021-03-22 2022-09-29 Norma U.S. Holding Llc Raccord doté d'au moins une fenêtre de visualisation de soudure par points par résistance
WO2025061152A1 (fr) * 2023-09-22 2025-03-27 东华大学 Procédé de liaison pour un matériau composite à base de résine thermoplastique renforcée par des fibres continues et organe de raccordement formé

Also Published As

Publication number Publication date
GB201609751D0 (en) 2016-07-20
GB2550966A (en) 2017-12-06

Similar Documents

Publication Publication Date Title
WO2017208012A1 (fr) Procédé d'assemblage de première et seconde pièces à l'aide d'éléments de fixation formés in situ et créés par faisceau laser ou faisceau d'électrons
JP6646679B2 (ja) 同種材料及び異種材料を接合するための抵抗溶接ファスナ、装置及び方法
US10272524B2 (en) Laser conduction mode welding of aluminum alloys with cross dual laser beams
CN110914014B (zh) 用于使用焊接路径的组合激光焊接金属工件的方法
JP6448667B2 (ja) 抵抗溶接ファスナ、装置及び方法
US8253062B2 (en) System and methodology for zero-gap welding
US20140008328A1 (en) System and method for forming a joint with a hot wire
US10807193B2 (en) Method of laser beam localized-coating
JP6998513B2 (ja) 接合構造
CN109462986B (zh) 涂层钢的多束激光点焊
CN110582371B (zh) 提高焊接表面品质的光滑方法
CN110325316B (zh) 用于使激光焊接接头表面平滑的方法
EP2911822B1 (fr) Soudure laser avec apport de métal de pièces automobiles
CN110392620B (zh) 激光焊接包含表面氧化物涂层的轻金属工件的方法
CN108463308A (zh) 激光点焊镀层钢的方法
JP2018118306A (ja) 箔ベースの付加製造システムおよび方法
WO2019051273A1 (fr) Ébauches d'aluminium soudées au laser
CN110603115B (zh) 层叠造型部件的接合方法及结构体、以及层叠造型部件
CN106994554A (zh) 用于将包含钢的构件与包含铝的构件相接合的方法
Miller et al. Laser welding of aluminum alloys
Hajili Welding processes for joining dissimilar metals and plastics
Mazumder et al. Laser Beam Weld Design, Codes, and Quality Assessment
Gillner et al. High-precision and high-speed laser microjoining for electronics and microsystems
Bratt et al. Laser hybrid welding of advanced high strength steels for potential automotive applications
JPS61154780A (ja) 摩擦圧接方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17728620

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17728620

Country of ref document: EP

Kind code of ref document: A1

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载