WO2017019163A1 - Batteries au lithium à électrolyte multi-phase - Google Patents

Batteries au lithium à électrolyte multi-phase Download PDF

Info

Publication number
WO2017019163A1
WO2017019163A1 PCT/US2016/033967 US2016033967W WO2017019163A1 WO 2017019163 A1 WO2017019163 A1 WO 2017019163A1 US 2016033967 W US2016033967 W US 2016033967W WO 2017019163 A1 WO2017019163 A1 WO 2017019163A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrolyte
electrochemical cell
negative electrode
block copolymer
positive electrode
Prior art date
Application number
PCT/US2016/033967
Other languages
English (en)
Inventor
Hany Basam Eitouni
Russell Clayton Pratt
Original Assignee
Seeo, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US14/811,664 external-priority patent/US9893337B2/en
Application filed by Seeo, Inc. filed Critical Seeo, Inc.
Publication of WO2017019163A1 publication Critical patent/WO2017019163A1/fr

Abstract

Une batterie est construite avec une cathode qui comporte un électrolyte liquide fluoré, non polarisant qui ne pénètre pas dans le séparateur d'électrolyte polymère à l'état solide entre elle et l'anode à base de lithium. Cet ensemble permet d'améliorer la conduction ionique et permet d'éviter des gradients de concentration ionique nuisibles dans la cathode sans compromettre la résistance et la durabilité du séparateur.
PCT/US2016/033967 2015-07-28 2016-05-24 Batteries au lithium à électrolyte multi-phase WO2017019163A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US14/811,664 US9893337B2 (en) 2008-02-13 2015-07-28 Multi-phase electrolyte lithium batteries
US14/811,664 2015-07-28

Publications (1)

Publication Number Publication Date
WO2017019163A1 true WO2017019163A1 (fr) 2017-02-02

Family

ID=57884895

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/033967 WO2017019163A1 (fr) 2015-07-28 2016-05-24 Batteries au lithium à électrolyte multi-phase

Country Status (1)

Country Link
WO (1) WO2017019163A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10122049B2 (en) 2014-02-06 2018-11-06 Gelion Technologies Pty Ltd Gelated ionic liquid film-coated surfaces and uses thereof
CN109167080A (zh) * 2018-09-12 2019-01-08 哈尔滨工业大学（威海） 一种高电压锂热电池
CN112805853A (zh) * 2018-08-14 2021-05-14 赛伦能源公司 用于可再充电锌电池和电池组的受保护的金属锌电极和方法
CN115842094A (zh) * 2022-05-19 2023-03-24 宁德时代新能源科技股份有限公司 负极极片及其制备方法、二次电池、电池模块、电池包及用电装置
WO2024201348A1 (fr) * 2023-03-29 2024-10-03 Oxlid Ltd Système électrolytique

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020110739A1 (en) * 2000-05-26 2002-08-15 Mcewen Alan B. Non-flammable electrolytes
US20030181572A1 (en) * 2001-05-21 2003-09-25 Tan Lian S. Emulsion polymerization of fluorinated monomers
US20110281173A1 (en) * 2008-02-13 2011-11-17 Seeo, Inc. Multiple electrolyte electrochemical cells
US20130130069A1 (en) * 2006-04-04 2013-05-23 Scott Mullin High elastic modulus polymer electrolytes suitable for preventing thermal runaway in lithium batteries

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020110739A1 (en) * 2000-05-26 2002-08-15 Mcewen Alan B. Non-flammable electrolytes
US20030181572A1 (en) * 2001-05-21 2003-09-25 Tan Lian S. Emulsion polymerization of fluorinated monomers
US20130130069A1 (en) * 2006-04-04 2013-05-23 Scott Mullin High elastic modulus polymer electrolytes suitable for preventing thermal runaway in lithium batteries
US20110281173A1 (en) * 2008-02-13 2011-11-17 Seeo, Inc. Multiple electrolyte electrochemical cells

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10122049B2 (en) 2014-02-06 2018-11-06 Gelion Technologies Pty Ltd Gelated ionic liquid film-coated surfaces and uses thereof
CN112805853A (zh) * 2018-08-14 2021-05-14 赛伦能源公司 用于可再充电锌电池和电池组的受保护的金属锌电极和方法
CN109167080A (zh) * 2018-09-12 2019-01-08 哈尔滨工业大学（威海） 一种高电压锂热电池
CN115842094A (zh) * 2022-05-19 2023-03-24 宁德时代新能源科技股份有限公司 负极极片及其制备方法、二次电池、电池模块、电池包及用电装置
CN115842094B (zh) * 2022-05-19 2024-03-22 宁德时代新能源科技股份有限公司 负极极片及其制备方法、二次电池、电池模块、电池包及用电装置
WO2024201348A1 (fr) * 2023-03-29 2024-10-03 Oxlid Ltd Système électrolytique

Similar Documents

Publication Publication Date Title
US9136562B2 (en) Multiple electrolyte electrochemical cells
US10158109B2 (en) Multi-phase electrolyte lithium batteries
US9923231B2 (en) High energy lithium battery with separate anolyte and catholyte layers
US10461317B2 (en) Solid electrode including electrolyte-impregnated active material particles
CN107534158B (zh) 作为用于锂电池的电解质的peo和氟化聚合物的共聚物
US9017882B2 (en) Electrodes with solid polymer electrolytes and reduced porosity
EP3132482B1 (fr) Cellule électrochimique à électrolyte solide au lithium-soufre à longue durée de vie
US8999008B2 (en) Method of forming an electrode assembly
KR101499586B1 (ko) 상온형 Na/S 전지
US10014554B2 (en) Block copolymer electrolytes containing polymeric additives
US10044064B2 (en) Long cycle-life lithium sulfur solid state electrochemical cell
US20150303516A1 (en) Polymer composition with olefinic groups for stabilization of lithium sulfur batteries
WO2009103029A2 (fr) Electrodes comprenant des électrolytes polymères solides
WO2016205653A1 (fr) Anode de lithium revêtue de polymère multicouche pour batterie au métal lithium à haute densité
WO2017019163A1 (fr) Batteries au lithium à électrolyte multi-phase
WO2019050618A1 (fr) Revêtements de surface pour particules d'électrolyte en céramique
CN110997642A (zh) 取代的咪唑和苯并咪唑的锂盐
US10158146B2 (en) Block copolymer electrolytes containing polymeric additives
US11258102B2 (en) Fluorinated ionic liquids for multi-layer Li ion battery applications
CN109312075B (zh) 用于高压锂电池的聚烷氧基硅氧烷阴极电解液
US20200295401A1 (en) Grafted polyesters as electrolytes for lithium ion batteries
JPH10294130A (ja) 非水系電池用ハイブリッド電解質及び非水系電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16830969

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16830969

Country of ref document: EP

Kind code of ref document: A1