WO2016032844A1 - Latex copolymères cationiques utiles en tant qu'additifs pour des applications de champ pétrolifère - Google Patents

Latex copolymères cationiques utiles en tant qu'additifs pour des applications de champ pétrolifère Download PDF

Info

Publication number
WO2016032844A1
WO2016032844A1 PCT/US2015/046072 US2015046072W WO2016032844A1 WO 2016032844 A1 WO2016032844 A1 WO 2016032844A1 US 2015046072 W US2015046072 W US 2015046072W WO 2016032844 A1 WO2016032844 A1 WO 2016032844A1
Authority
WO
WIPO (PCT)
Prior art keywords
cationic
monomer
water
hydrogen
oil
Prior art date
Application number
PCT/US2015/046072
Other languages
English (en)
Inventor
Hongwei SHEN
Disha JAIN
Kurt J. MAGNI
Joseph Manna
Wen-Shiue YOUNG
Original Assignee
Dow Global Technologies Llc
Rohm And Haas Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies Llc, Rohm And Haas Company filed Critical Dow Global Technologies Llc
Publication of WO2016032844A1 publication Critical patent/WO2016032844A1/fr

Abstract

Des dispersions et des émulsions huile dans eau résultant d'opérations de l'industrie pétrolière sont désémulsionnées et clarifiées à l'aide d'une composition de clarification à base de copolymères cationiques. Ledit copolymère cationique comprend le produit de polymérisation de (i) un ou plusieurs monomères (méth)acryle(s), (ii) un monomère cationique, et (iii) éventuellement un ou plusieurs monomère(s) styrène(s) (substitué(s)).
PCT/US2015/046072 2014-08-28 2015-08-20 Latex copolymères cationiques utiles en tant qu'additifs pour des applications de champ pétrolifère WO2016032844A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201462043037P 2014-08-28 2014-08-28
US62/043,037 2014-08-28

Publications (1)

Publication Number Publication Date
WO2016032844A1 true WO2016032844A1 (fr) 2016-03-03

Family

ID=54064581

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2015/046072 WO2016032844A1 (fr) 2014-08-28 2015-08-20 Latex copolymères cationiques utiles en tant qu'additifs pour des applications de champ pétrolifère

Country Status (2)

Country Link
AR (1) AR102813A1 (fr)
WO (1) WO2016032844A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5006590A (en) 1988-10-14 1991-04-09 Kyoritsu Yuki Co., Ltd. Process for the preparation of dispersion of water-soluble cationic polymer
US5021167A (en) 1989-07-10 1991-06-04 Nalco Chemical Company Method for separating liquid from water using amine containing polymers
EP0617991A1 (fr) * 1993-03-01 1994-10-05 Nalco Chemical Company Récupération d'huile à partir de déchets fluides huileux et élimination d'huile des eaux résiduaires industrielles
EP0657478A2 (fr) * 1993-12-09 1995-06-14 Nalco Chemical Company Procédé de préparation de dispersion de polymères solubles dans l'eau
US5643460A (en) * 1994-01-14 1997-07-01 Nalco/Exxon Energy Chemicals, L. P. Method for separating oil from water in petroleum production
WO2000061501A1 (fr) * 1999-04-09 2000-10-19 Nalco Chemical Company Dispersion polymere a principes actifs superieurs pour favoriser la clarification, la deshydratation, et la retention et l'ecoulement
US20080216978A1 (en) 2007-03-09 2008-09-11 Steven Michael Baxter Cationic polymer latex
US7470744B2 (en) 2006-04-12 2008-12-30 Baker Hughes Incorporated Copolymers useful as demulsifiers and clarifiers
US20130259812A1 (en) 2010-12-20 2013-10-03 Rohm And Haas Company Cationic polymer latexes and uses
CN103980421A (zh) * 2014-05-30 2014-08-13 陕西科技大学 一种水基高分子页岩抑制剂及其制备方法

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5006590A (en) 1988-10-14 1991-04-09 Kyoritsu Yuki Co., Ltd. Process for the preparation of dispersion of water-soluble cationic polymer
US5021167A (en) 1989-07-10 1991-06-04 Nalco Chemical Company Method for separating liquid from water using amine containing polymers
EP0617991A1 (fr) * 1993-03-01 1994-10-05 Nalco Chemical Company Récupération d'huile à partir de déchets fluides huileux et élimination d'huile des eaux résiduaires industrielles
EP0657478A2 (fr) * 1993-12-09 1995-06-14 Nalco Chemical Company Procédé de préparation de dispersion de polymères solubles dans l'eau
US5643460A (en) * 1994-01-14 1997-07-01 Nalco/Exxon Energy Chemicals, L. P. Method for separating oil from water in petroleum production
WO2000061501A1 (fr) * 1999-04-09 2000-10-19 Nalco Chemical Company Dispersion polymere a principes actifs superieurs pour favoriser la clarification, la deshydratation, et la retention et l'ecoulement
US7470744B2 (en) 2006-04-12 2008-12-30 Baker Hughes Incorporated Copolymers useful as demulsifiers and clarifiers
US20080216978A1 (en) 2007-03-09 2008-09-11 Steven Michael Baxter Cationic polymer latex
US8192504B2 (en) 2007-03-09 2012-06-05 Rohm And Haas Company Cationic polymer latex
US20130259812A1 (en) 2010-12-20 2013-10-03 Rohm And Haas Company Cationic polymer latexes and uses
CN103980421A (zh) * 2014-05-30 2014-08-13 陕西科技大学 一种水基高分子页岩抑制剂及其制备方法

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
FW BILLMEYER, JR.: "Textbook of Polymer Science, second edition,", 1971

Also Published As

Publication number Publication date
AR102813A1 (es) 2017-03-29

Similar Documents

Publication Publication Date Title
CA2646373C (fr) Copolymeres utilises comme desemulsifiants et comme clarificateurs
CA1124612A (fr) Methode pour separer des emulsions d'huile dans l'eau
EP2319901B1 (fr) Séparation de phases huileuses et aqueuses dans des émulsions et des dispersions avec des polymères en tant qu'additifs
RU2340759C2 (ru) Разделение твердое-жидкость глинистых растворов на масляной основе
US5643460A (en) Method for separating oil from water in petroleum production
US4120815A (en) Polymeric demulsifiers
US4734205A (en) Hydrophobically associating polymers for oily water clean-up
EP0595156A1 (fr) Procédé pour la clarification de l'eau des champs pétrolifères avec des polymères de dispersion cationiques
US20050194323A1 (en) System and method for recovering oil from a waste stream
US12163095B2 (en) Copolymers useful as water clarifiers and for water-oil separation
EP2377590A2 (fr) Polymères utiles en tant que désémulsifiants et clarificateurs
US5851433A (en) Method of and composition for breaking oil and water emulsions in crude oil processing operations
US9981207B2 (en) Polymers useful as demulsifiers and clarifiers
US5449463A (en) Desalter wash water additive
WO2013155679A1 (fr) Procédé pour traiter des systèmes de liqueur de lavage dans des cokeries
WO2016032844A1 (fr) Latex copolymères cationiques utiles en tant qu'additifs pour des applications de champ pétrolifère
WO2016032841A1 (fr) Copolymères cationiques hydrosolubles utiles en tant qu'additifs pour des applications de champ pétrolifère
EP2879769B1 (fr) Copolymère à base d'imidazolium vinylique cationique pour séparer une émulsion huile dans l'eau
US5730905A (en) Method of resolving oil and water emulsions
AU2013296612A1 (en) N-vinylpyrrolidone-based cationic copolymer for separating an oil-in-water emulsion
JPH04284892A (ja) 液状有機物を含有する水の処理方法
MXPA06007576A (es) Aditivo surfactante-floculante para el tratamiento de aguas congenitas obtenidas del proceso de deshidratacion de aceites crudos.

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15759995

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15759995

Country of ref document: EP

Kind code of ref document: A1

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载