WO2016061450A1 - Constructions de collagène-alginate et leurs utilisations - Google Patents

Constructions de collagène-alginate et leurs utilisations Download PDF

Info

Publication number
WO2016061450A1
WO2016061450A1 PCT/US2015/055923 US2015055923W WO2016061450A1 WO 2016061450 A1 WO2016061450 A1 WO 2016061450A1 US 2015055923 W US2015055923 W US 2015055923W WO 2016061450 A1 WO2016061450 A1 WO 2016061450A1
Authority
WO
WIPO (PCT)
Prior art keywords
construct
pores
collagen
alginate
cells
Prior art date
Application number
PCT/US2015/055923
Other languages
English (en)
Inventor
Elliot L. Chaikof
Perla AYALA
Jeffrey Caves
Original Assignee
Beth Israel Deaconess Medical Center, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beth Israel Deaconess Medical Center, Inc. filed Critical Beth Israel Deaconess Medical Center, Inc.
Publication of WO2016061450A1 publication Critical patent/WO2016061450A1/fr

Abstract

L'invention concerne une construction artificielle pour la réparation et la régénération tissulaires comprenant plusieurs feuilles de collagène stratifiées en une pile, de multiples pores étant formés à l'intérieur de cette construction et un alginate étant incorporé dans les deux côtés de la construction. La construction de collagène-alginate peut fournir une meilleure intégration hôte lors de son implantation. L'alginate peut comprendre des cellules (par exemple des cellules souches mésenchymateuses), des facteurs de croissance et des cytokines qui peuvent améliorer la cicatrisation et favoriser la formation de nouveaux tissus. On peut ajuster les propriétés mécaniques de cette construction destinée à différentes applications de réparation tissulaire, en variant l'épaisseur et le nombre de feuilles de collagène, la dimension, les motifs et le nombre de pores, et d'autres paramètres. On peut concevoir cette construction de manière qu'elle possède la souplesse voulue, tout en lui conservant une résistance et une intégrité structurelle appropriées.
PCT/US2015/055923 2014-10-16 2015-10-16 Constructions de collagène-alginate et leurs utilisations WO2016061450A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201462064748P 2014-10-16 2014-10-16
US62/064,748 2014-10-16
US201562205488P 2015-08-14 2015-08-14
US62/205,488 2015-08-14

Publications (1)

Publication Number Publication Date
WO2016061450A1 true WO2016061450A1 (fr) 2016-04-21

Family

ID=55747394

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2015/055923 WO2016061450A1 (fr) 2014-10-16 2015-10-16 Constructions de collagène-alginate et leurs utilisations

Country Status (1)

Country Link
WO (1) WO2016061450A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107693834A (zh) * 2017-09-22 2018-02-16 青岛明月生物医用材料有限公司 一种负载胶原蛋白的海藻酸盐医用敷料及其制备方法
US11634448B2 (en) 2016-06-15 2023-04-25 The General Hospital Corporation Metabolic labeling and molecular enhancement of biological materials using bioorthogonal reactions
US11944723B2 (en) 2018-03-13 2024-04-02 Institut Quimic De Sarria Cets Fundacio Privada Vascular repair patch

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030133967A1 (en) * 2000-03-09 2003-07-17 Zbigniew Ruszczak Multilayer collagen matrix for tissue reconstruction
US20080050417A1 (en) * 2006-06-16 2008-02-28 Fmc Biopolymer As Alginate coated, collagen matrix cellular device, preparative methods, and uses thereof
US20140065198A1 (en) * 2001-01-16 2014-03-06 Vascular Therapies Llc Medical Implants and Methods for Regulating the Tissue Response to Vascular Closure Devices
US20140081070A1 (en) * 2010-09-10 2014-03-20 Fibralign Corporation Biodegradable Multilayer Constructs
US20140193477A1 (en) * 2012-10-11 2014-07-10 Emory University Collagen based materials and uses related thereto

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030133967A1 (en) * 2000-03-09 2003-07-17 Zbigniew Ruszczak Multilayer collagen matrix for tissue reconstruction
US20140065198A1 (en) * 2001-01-16 2014-03-06 Vascular Therapies Llc Medical Implants and Methods for Regulating the Tissue Response to Vascular Closure Devices
US20080050417A1 (en) * 2006-06-16 2008-02-28 Fmc Biopolymer As Alginate coated, collagen matrix cellular device, preparative methods, and uses thereof
US20140081070A1 (en) * 2010-09-10 2014-03-20 Fibralign Corporation Biodegradable Multilayer Constructs
US20140193477A1 (en) * 2012-10-11 2014-07-10 Emory University Collagen based materials and uses related thereto

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11634448B2 (en) 2016-06-15 2023-04-25 The General Hospital Corporation Metabolic labeling and molecular enhancement of biological materials using bioorthogonal reactions
CN107693834A (zh) * 2017-09-22 2018-02-16 青岛明月生物医用材料有限公司 一种负载胶原蛋白的海藻酸盐医用敷料及其制备方法
US11944723B2 (en) 2018-03-13 2024-04-02 Institut Quimic De Sarria Cets Fundacio Privada Vascular repair patch

Similar Documents

Publication Publication Date Title
US11338062B2 (en) Fiber-hydrogel composite surgical meshes for tissue repair
US20230405189A1 (en) Composite material for tissue restoration
US10092676B2 (en) Biohybrid composite scaffold
Wolf et al. Naturally derived and synthetic scaffolds for skeletal muscle reconstruction
Costa et al. Biologic scaffolds
US8535719B2 (en) Biohybrid elastomeric scaffolds and methods of use thereof
Priya et al. Skin tissue engineering for tissue repair and regeneration
Wu et al. An injectable extracellular matrix derived hydrogel for meniscus repair and regeneration
Shi et al. Regeneration of full-thickness abdominal wall defects in rats using collagen scaffolds loaded with collagen-binding basic fibroblast growth factor
Ayala et al. Engineered composite fascia for stem cell therapy in tissue repair applications
US20140356331A1 (en) Injectable cns-derived ecm for tissue reconstruction
Zhou et al. In vitro evaluation of poly (vinyl alcohol)/collagen blended hydrogels for regulating human periodontal ligament fibroblasts and gingival fibroblasts
US10130735B2 (en) Scaffold for cardiac patch
Ghosh et al. Single unit functionally graded bioresorbable electrospun scaffold for scar-free full-thickness skin wound healing
WO2016061450A1 (fr) Constructions de collagène-alginate et leurs utilisations
Jelodari et al. Decellularization of small intestinal submucosa
KR101714695B1 (ko) 가교화된 pva-ecm 복합체를 제조하는 방법 및 그에 의하여 제조된 pva-ecm 복합체
Carnes Tuning the Biophysical and Biochemical Cues of Fibrin Microthread Scaffolds Towards the Treatment of Volumetric Muscle Loss
Solanki et al. 17 Nanopolymer Scaffolds

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15851156

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15851156

Country of ref document: EP

Kind code of ref document: A1