WO2013084840A1 - Batterie rechargeable à électrolyte non aqueux et batterie assemblée utilisant celle-ci - Google Patents

Batterie rechargeable à électrolyte non aqueux et batterie assemblée utilisant celle-ci Download PDF

Info

Publication number
WO2013084840A1
WO2013084840A1 PCT/JP2012/081265 JP2012081265W WO2013084840A1 WO 2013084840 A1 WO2013084840 A1 WO 2013084840A1 JP 2012081265 W JP2012081265 W JP 2012081265W WO 2013084840 A1 WO2013084840 A1 WO 2013084840A1
Authority
WO
WIPO (PCT)
Prior art keywords
lithium
electrolyte secondary
secondary battery
nonaqueous electrolyte
positive electrode
Prior art date
Application number
PCT/JP2012/081265
Other languages
English (en)
Japanese (ja)
Inventor
立石　和幸
孝洋 大石
裕樹 澤田
充康 今▲崎▼
Original Assignee
株式会社カネカ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社カネカ filed Critical 株式会社カネカ
Publication of WO2013084840A1 publication Critical patent/WO2013084840A1/fr

Abstract

La présente invention a trait à une batterie au lithium-ion qui est dotée d'une électrode positive, d'une électrode négative, d'un séparateur et d'un électrolyte organique ; laquelle électrode positive contient un composé de lithium-manganèse qui est doté d'une structure de spinelle, laquelle électrode négative contient un oxyde complexe contenant du titanate de lithium qui est doté d'une structure de spinelle et lequel séparateur est un « tissu non-tissé de cellulose contenant une fibre de polyéthylène-téréphtalate » qui est doté d'une porosité inférieure à 50 % en volume. En utilisant une combinaison de cette description il est possible d'obtenir une batterie rechargeable à électrolyte non aqueux qui est dotée d'une stabilité de cycle supérieure.
PCT/JP2012/081265 2011-12-07 2012-12-03 Batterie rechargeable à électrolyte non aqueux et batterie assemblée utilisant celle-ci WO2013084840A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011268309 2011-12-07
JP2011-268309 2011-12-07

Publications (1)

Publication Number Publication Date
WO2013084840A1 true WO2013084840A1 (fr) 2013-06-13

Family

ID=48574207

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/081265 WO2013084840A1 (fr) 2011-12-07 2012-12-03 Batterie rechargeable à électrolyte non aqueux et batterie assemblée utilisant celle-ci

Country Status (3)

Country Link
JP (1) JPWO2013084840A1 (fr)
TW (1) TWI600195B (fr)
WO (1) WO2013084840A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015514284A (ja) * 2012-04-18 2015-05-18 エルジー・ケム・リミテッド 二次電池用電極及びそれを含む二次電池
WO2018139524A1 (fr) * 2017-01-26 2018-08-02 日本電気株式会社 Cellule secondaire
JP2020053163A (ja) * 2018-09-25 2020-04-02 三菱製紙株式会社 リチウムイオン電池の製造方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7377401B2 (ja) * 2019-04-25 2023-11-10 株式会社日本製鋼所 不織布、不織布の製造方法、固体電解質膜、固体電解質膜の製造方法、全固体電池および全固体電池の製造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007067389A (ja) * 2005-08-03 2007-03-15 Mitsubishi Paper Mills Ltd 電気化学素子用セパレータ
JP2007294164A (ja) * 2006-04-24 2007-11-08 Gs Yuasa Corporation:Kk 非水電解質二次電池
JP2010098074A (ja) * 2008-10-15 2010-04-30 Tomoegawa Paper Co Ltd 蓄電デバイス用セパレータ
JP2011210680A (ja) * 2010-03-30 2011-10-20 Tomoegawa Paper Co Ltd 電池用セパレータ
JP2011238427A (ja) * 2010-05-10 2011-11-24 Hitachi Maxell Energy Ltd 非水電解質電池

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007067389A (ja) * 2005-08-03 2007-03-15 Mitsubishi Paper Mills Ltd 電気化学素子用セパレータ
JP2007294164A (ja) * 2006-04-24 2007-11-08 Gs Yuasa Corporation:Kk 非水電解質二次電池
JP2010098074A (ja) * 2008-10-15 2010-04-30 Tomoegawa Paper Co Ltd 蓄電デバイス用セパレータ
JP2011210680A (ja) * 2010-03-30 2011-10-20 Tomoegawa Paper Co Ltd 電池用セパレータ
JP2011238427A (ja) * 2010-05-10 2011-11-24 Hitachi Maxell Energy Ltd 非水電解質電池

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015514284A (ja) * 2012-04-18 2015-05-18 エルジー・ケム・リミテッド 二次電池用電極及びそれを含む二次電池
US9508993B2 (en) 2012-04-18 2016-11-29 Lg Chem, Ltd. Electrode for secondary battery and secondary battery including the same
US10153480B2 (en) 2012-04-18 2018-12-11 Lg Chem, Ltd. Electrode for secondary battery and secondary battery including the same
WO2018139524A1 (fr) * 2017-01-26 2018-08-02 日本電気株式会社 Cellule secondaire
JPWO2018139524A1 (ja) * 2017-01-26 2019-11-14 日本電気株式会社 二次電池
JP7103234B2 (ja) 2017-01-26 2022-07-20 日本電気株式会社 二次電池
JP2020053163A (ja) * 2018-09-25 2020-04-02 三菱製紙株式会社 リチウムイオン電池の製造方法

Also Published As

Publication number Publication date
TW201332184A (zh) 2013-08-01
TWI600195B (zh) 2017-09-21
JPWO2013084840A1 (ja) 2015-04-27

Similar Documents

Publication Publication Date Title
JP6304774B2 (ja) 負極製造用ペーストの製造方法、リチウムイオン二次電池用負極の製造方法、リチウムイオン二次電池用負極およびリチウムイオン二次電池
CN107112584B (zh) 非水电解液二次电池和非水电解液二次电池的正极
JPWO2016098708A1 (ja) リチウムイオン二次電池
JP2020123460A (ja) プレドープ材、プレドープ材を含む正極、並びに、その正極を備えた非水電解質二次電池の製造方法、及び、金属酸化物の製造方法
JP2012174546A (ja) 非水電解質二次電池
JP2015118742A (ja) 非水電解質二次電池
JP2014006971A (ja) 非水電解質二次電池及びそれを用いた組電池
JP2012129095A (ja) 非水電解質二次電池用バイポーラ電極、および、それを用いた非水電解質二次電池。
JP2013098034A (ja) 非水電解質二次電池
JP2012156087A (ja) 非水電解質二次電池
WO2013084840A1 (fr) Batterie rechargeable à électrolyte non aqueux et batterie assemblée utilisant celle-ci
JP2017188424A (ja) リチウムイオン二次電池用正極活物質、及びそれを用いたリチウムイオン二次電池用正極並びにリチウムイオン二次電池
JP7003775B2 (ja) リチウムイオン二次電池
JP2015215947A (ja) 非水電解質二次電池用電極及び非水電解質二次電池
JP2014022321A (ja) 捕捉剤を含む非水電解質二次電池
JP7142301B2 (ja) 正極活物質およびそれを備えた電池
JP2013191484A (ja) 負極活物質層、その製造方法及び非水電解質二次電池
JP2017204334A (ja) 電極の製造方法、ならびに非水電解質二次電池および蓄電ユニット
JP2015187929A (ja) 非水電解質二次電池
JP5758731B2 (ja) 非水電解質二次電池
JP6244604B2 (ja) 非水電解質二次電池及びその製造方法
JP5726603B2 (ja) 非水電解質二次電池
JP2014238946A (ja) 非水電解質二次電池の製造方法及び製造された電池
JP2014072062A (ja) 非水電解質二次電池及び組電池
JP2014086382A (ja) 非水電解質二次電池の製造方法及びそれにより製造された電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12855980

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2013548223

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12855980

Country of ref document: EP

Kind code of ref document: A1

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载