WO2008111685A1 - Composition de cristaux liquides, lame à retard, dispositif d'affichage à cristaux liquides, et procédé de production de lame à retard - Google Patents

Composition de cristaux liquides, lame à retard, dispositif d'affichage à cristaux liquides, et procédé de production de lame à retard Download PDF

Info

Publication number
WO2008111685A1
WO2008111685A1 PCT/JP2008/055155 JP2008055155W WO2008111685A1 WO 2008111685 A1 WO2008111685 A1 WO 2008111685A1 JP 2008055155 W JP2008055155 W JP 2008055155W WO 2008111685 A1 WO2008111685 A1 WO 2008111685A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
formula
substituted
hydrogen atom
carbon atoms
Prior art date
Application number
PCT/JP2008/055155
Other languages
English (en)
Inventor
Yi Li
Hideyuki Nishikawa
Yuta Takahashi
Masataka Yoshizawa
Takafumi Hosokawa
Original Assignee
Fujifilm Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2008042759A external-priority patent/JP5221980B2/ja
Application filed by Fujifilm Corporation filed Critical Fujifilm Corporation
Priority to US12/529,841 priority Critical patent/US8053040B2/en
Publication of WO2008111685A1 publication Critical patent/WO2008111685A1/fr

Abstract

L'invention concerne une composition comprenant au moins un composé de cristaux liquides et au moins un polymère. Le polymère comprend une unité constitutive représentée par une formule suivante (a) et une unité constitutive dérivée d'un monomère pourvu d'un ou de plusieurs groupes fluoroaliphatiques : où Mp représente un groupe trivalent constituant, pour toute ou partie, une chaîne principale polymère ; L représente une liaison simple ou un groupe de liaison divalent ; et X représente un groupe cyclique condensé aromatique substitué ou non substitué.
PCT/JP2008/055155 2007-03-14 2008-03-13 Composition de cristaux liquides, lame à retard, dispositif d'affichage à cristaux liquides, et procédé de production de lame à retard WO2008111685A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/529,841 US8053040B2 (en) 2007-03-14 2008-03-13 Liquid crystal composition, retardation plate, liquid crystal display device, and process for producing retardation plate

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2007-064952 2007-03-14
JP2007064952 2007-03-14
JP2008042759A JP5221980B2 (ja) 2007-03-14 2008-02-25 液晶組成物、位相差板、液晶表示装置、及び位相差板の製造方法
JP2008-042759 2008-02-25

Publications (1)

Publication Number Publication Date
WO2008111685A1 true WO2008111685A1 (fr) 2008-09-18

Family

ID=39759613

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2008/055155 WO2008111685A1 (fr) 2007-03-14 2008-03-13 Composition de cristaux liquides, lame à retard, dispositif d'affichage à cristaux liquides, et procédé de production de lame à retard

Country Status (1)

Country Link
WO (1) WO2008111685A1 (fr)

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63205306A (ja) * 1987-02-23 1988-08-24 Mitsui Petrochem Ind Ltd 酸素透過体
JPH023407A (ja) * 1987-12-31 1990-01-09 Minnesota Mining & Mfg Co <3M> 弗素及び発色団含有重合体
JP2005225990A (ja) * 2004-02-13 2005-08-25 Ipposha Oil Ind Co Ltd 光学フィルム用添加剤、それを含む光学フィルム、それを用いた偏光板及び液晶表示装置
JP2005533902A (ja) * 2002-07-26 2005-11-10 スリーエム イノベイティブ プロパティズ カンパニー 染色フルオロポリマー
JP2006126768A (ja) * 2004-09-30 2006-05-18 Fuji Photo Film Co Ltd 光学異方性フィルム、それを用いた偏光板及び液晶表示装置
JP2006233191A (ja) * 2005-01-27 2006-09-07 Fuji Photo Film Co Ltd 塗布組成物、光学フィルム、反射防止フィルム、偏光板およびそれらを用いた画像表示装置
JP2007217656A (ja) * 2006-01-23 2007-08-30 Fujifilm Corp 組成物、位相差板、液晶表示装置および、位相差板の製造方法
JP2007272185A (ja) * 2006-03-10 2007-10-18 Fujifilm Corp 組成物、位相差板、液晶表示装置、平均チルト角調整剤、平均チルト角の調整方法

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63205306A (ja) * 1987-02-23 1988-08-24 Mitsui Petrochem Ind Ltd 酸素透過体
JPH023407A (ja) * 1987-12-31 1990-01-09 Minnesota Mining & Mfg Co <3M> 弗素及び発色団含有重合体
JP2005533902A (ja) * 2002-07-26 2005-11-10 スリーエム イノベイティブ プロパティズ カンパニー 染色フルオロポリマー
JP2005225990A (ja) * 2004-02-13 2005-08-25 Ipposha Oil Ind Co Ltd 光学フィルム用添加剤、それを含む光学フィルム、それを用いた偏光板及び液晶表示装置
JP2006126768A (ja) * 2004-09-30 2006-05-18 Fuji Photo Film Co Ltd 光学異方性フィルム、それを用いた偏光板及び液晶表示装置
JP2006233191A (ja) * 2005-01-27 2006-09-07 Fuji Photo Film Co Ltd 塗布組成物、光学フィルム、反射防止フィルム、偏光板およびそれらを用いた画像表示装置
JP2007217656A (ja) * 2006-01-23 2007-08-30 Fujifilm Corp 組成物、位相差板、液晶表示装置および、位相差板の製造方法
JP2007272185A (ja) * 2006-03-10 2007-10-18 Fujifilm Corp 組成物、位相差板、液晶表示装置、平均チルト角調整剤、平均チルト角の調整方法

Similar Documents

Publication Publication Date Title
US8053040B2 (en) Liquid crystal composition, retardation plate, liquid crystal display device, and process for producing retardation plate
JP4756082B2 (ja) レターデーションと厚みが制御されたセルロースアセテートフイルムを用いた液晶表示装置
JP4076454B2 (ja) 光学補償シート、偏光板および画像表示装置
KR101249546B1 (ko) 광학 이방성 필름, 휘도 향상 필름, 적층 광학 필름, 및이를 이용한 화상 표시 장치
KR101182614B1 (ko) 광학 보상 필름, 편광판 및 액정 표시 장치
US7989037B2 (en) Composition, retardation plate, and liquid-crystal display device
WO2007083848A1 (fr) Composition, plaque de retardement, dispositif d’affichage a cristaux liquides et procede de fabrication de la plaque de retardement
JP2002006138A (ja) 光学補償シートおよびその製造方法
US20130057809A1 (en) Optically-compensatory sheet, polarizing plate and liquid crystal display device
JP2002303722A (ja) 光学補償シート
JP4316131B2 (ja) 光学補償フイルムの製造方法
US7153548B2 (en) Compound, retardation plate and method for forming optically anisotropic layer
US7311949B2 (en) Composition, optical film, polarizing plate and liquid crystal display
US20040109114A1 (en) Retarder and circular polarizer
JP5069530B2 (ja) 組成物、位相差板、液晶表示装置および、位相差板の製造方法
US7767286B2 (en) Polarizing plate and liquid crystal display device
US20100188616A1 (en) Liquid-crystal display device
JP2009193046A (ja) 光学補償フィルム、偏光板、及び液晶表示装置
JP4637599B2 (ja) 光学異方性膜及び液晶表示装置
JP2008133355A (ja) ポリマー、組成物、位相差板、楕円偏光板および液晶表示装置
JP2007231193A (ja) ポリマー、及びそれを含有する組成物、ならびにそれを用いた位相差板及び液晶表示装置
JP3916950B2 (ja) 光学積層体、及びその製造方法、並びに円偏光板
WO2008111685A1 (fr) Composition de cristaux liquides, lame à retard, dispositif d&#39;affichage à cristaux liquides, et procédé de production de lame à retard
US20070002232A1 (en) Optical compensation film, polarizing plate and liquid crystal display device
US7250116B2 (en) Liquid crystal composition, polymerization product, retardation plate and ellipsoidally polarizing plate

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08722527

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 12529841

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08722527

Country of ref document: EP

Kind code of ref document: A1