WO2008012869A1 - Tissu de doublureà élasticité de type tramée et son procédé de fabrication - Google Patents

Tissu de doublureà élasticité de type tramée et son procédé de fabrication Download PDF

Info

Publication number
WO2008012869A1
WO2008012869A1 PCT/JP2006/314641 JP2006314641W WO2008012869A1 WO 2008012869 A1 WO2008012869 A1 WO 2008012869A1 JP 2006314641 W JP2006314641 W JP 2006314641W WO 2008012869 A1 WO2008012869 A1 WO 2008012869A1
Authority
WO
WIPO (PCT)
Prior art keywords
weft
warp
lining
yarn
fabric
Prior art date
Application number
PCT/JP2006/314641
Other languages
English (en)
French (fr)
Inventor
Masanori Nakagawa
Ryozo Ueno
Original Assignee
Asahi Kasei Fibers Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Kasei Fibers Corporation filed Critical Asahi Kasei Fibers Corporation
Priority to JP2008526623A priority Critical patent/JP4819123B2/ja
Priority to CN2006800554044A priority patent/CN101501258B/zh
Priority to KR1020087028419A priority patent/KR101101452B1/ko
Priority to PCT/JP2006/314641 priority patent/WO2008012869A1/ja
Priority to EP06781553A priority patent/EP2045381B1/en
Publication of WO2008012869A1 publication Critical patent/WO2008012869A1/ja

Description

明 細 書
緯ストレッチ裏地及びその製造法
技術分野
[0001] 本発明は、特定の緯ストレッチ裏地及びその製造法に関する。
背景技術
[0002] 近年、衣料分野に於いて着用快適感を求める気運が高まり、ストレッチを謳った商 品が数多く見られるようになった。特に表地として使われる織物のストレッチ化が進行 し、それらに併せるかたちで裏地や芯地等の副資材にもストレッチ性が要求されるよ うになつた。そのため、裏地でも各種方法によりストレッチを持たせた商品がある。
[0003] 例えば、糸自体がゴムのように伸びるスパンデッタス糸を芯糸に用い、その周りにマ ルチフィラメントを卷きつけたカバリング糸を利用する方法が一般的に知られている。 この方法で得られた裏地は地厚感ゃフカツキ感が出易ぐ且つ、滑りも悪くなるため 裏地としてはそれ程波及していない。他の手段としては仮撚加工糸の嵩高性や捲縮 性を利用したものゃ仮撚加工糸の追撚糸や撚糸の解撚カを利用したもの等が挙げ られる。これらの方法で得られる裏地もフカツキ感ゃザラツキ感、シボ感等が発現し、 裏地としての品位は低 、ものであった。
[0004] 一方、特許文献 1には、経緯糸共に無撚糸を用いて、 5%以上、 12%未満の緯スト レツチ性を有する裏地が記載されている。また特許文献 2には、緯糸にポリトリメチレ ンテレフタレート糸を用いて、 3%以上、 30%未満の緯ストレッチ性を有する裏地が 記載されている。特許文献 1は緯糸に曲げ柔らカ 、もの（細単糸、偏平糸等）を用い ることで緯クリンプを発現させるものである。特許文献 2は緯糸に伸縮糸を用いて緯ク リンブを発現させる。しかし、これらの方法では平滑性を保持したまま高ストレッチ化 することは困難である。
[0005] これらのように従来、緯方向にストレッチ性を有する裏地として、緯糸に伸縮性糸（ 弾性糸、有撚糸等）を用いるもの、経緯無撚糸で緯糸に曲げ柔らかい糸を用いるも の等が提案されている。しかし、最近の表地のストレッチは 15%〜20%前後ものが 増えてきており、前述の裏地で表地の伸びに対応させるためにこのように、良好な滑 り性とストレッチ性を充分満たし、最近の表地の高ストレッチ化に対応できる裏地が無 いのが実状である。
[0006] 特許文献 1 :国際公開 WO99Z31309号明細書
特許文献 2：特開 2001— 172843号公報
発明の開示
発明が解決しょうとする課題
[0007] 本発明の目的は、滑り性を損ねることなく緯方向の伸びが大きなストレッチ性を有す る着用快適性に優れた裏地を提供することにある。即ち、係る滑り性やストレッチ性能 の他に裏地の表面構造の尺度となるクリンプ指数を制御することにより着用時の着脱 性や縫目滑脱性、及び、動作追従性などが優れた裏地の提供を可能ならしめるもの である。
[0008] 本発明の更なる目的は、前記機能を有するポリエステル系長繊維 100%の裏地、 ポリエステル系長繊維とセルロース系長繊維の交織裏地、及びセルロース系長繊維
100%の裏地を提供することにある。
課題を解決するための手段
[0009] 本発明者らは前記課題を解決するために、裏地の緯伸び率に直接反映する織物 中の緯糸クリンプ率を如何に高めるかを詳細に検討した結果、無撚糸を緯糸に用い た上で、経糸に適度な撚りを掛けることで生機に効率的に緯糸クリンプを付与するこ とが可能となり、付与された生機中の緯糸クリンプ率の高さが前駆体となって、後ェ 程 (精練'熱処理 ·セット)でストレッチ率に繋がる織物中の緯糸クリンプ率が容易に増 加することを見出し、本発明に到達したものである。ここで言うクリンプ率とは、生機や 最終仕上げ品の織物の緯方向に 20cmの印を付けた後、織物力も取り出した緯糸に 繊度の 1Z10の荷重を掛け、その時の印間長さ (L)から次式で算出される値である。
クリンプ率（％) = { (L— 20)Z20} X 100 (3)
即ち、本発明は、以下の通りである。
[0010] [1]下式（1)で定義される撚り係数 (K)が 2000以上、 15000以下のポリエステル 系長繊維又はセルロース系長繊維を経糸に、実質的に無撚のポリエステル系長繊 維又はセルロース系長繊維を緯糸に用いてなる織物からなり、緯伸び率が 8%以上 、 20%以下、表面の動摩擦係数が 0. 20以上、 0. 40以下、下式（2)で定義されるク リンブ指数 (C)が 0. 007以上、 0. 015以下であることを特徴とする緯ストレッチ裏地
K= (0. 9 X D) 0 5 XT (1)
C=製品の緯糸のクリンプ率 Z{M X (D) ° 5} (2) 式中、 Dは経糸繊度 (dtex)、 Tは撚糸回数 (tZm)、 Mは経糸密度 (本 Z2. 54cm )を意味する。
ここで、緯伸び率と動摩擦係数は後述する KES (カトーテック社製)法で計測される 値を意味する。
[0011] [2]織物の緯伸び率が 12%以上、 20%以下である上記 [1]記載の緯ストレッチ裏 地。
[0012] [3]セルロース系長繊維がキュプラアンモ-ゥムレーヨン長繊維、ビスコース法レー ヨン長繊維及び精製セルロース長繊維である上記 [1]記載の緯ストレッチ裏地。
[0013] [4]ポリエステル系長繊維がポリエチレンテレフタレート系長繊維である上記 [1]〜
[3]の 、ずれかに記載の緯ストレッチ裏地。
[0014] [5]生機状態で織物にアルカリ水溶液を付与した後、該織物を生機幅に対して 5〜
30%の幅入れした状態で熱処理することを特徴とする上記 [1]〜 [3]の 、ずれかに 記載の緯ストレッチ裏地の製造方法。
発明の効果
[0015] 本発明の裏地織物は、適度なストレッチ性を有するので着用時の圧迫性が低く運 動追従性にも優れる。また、滑脱が起こり難く保型性にも優れる。また、滑り性も良好 なため着脱が容易であるば力りか動き易さの点でも優れる。
図面の簡単な説明
[0016] [図 1]比較例 2における織物断面形状の電子顕微鏡写真である。
[図 2]実施例 7における織物断面形状の電子顕微鏡写真である。
発明を実施するための最良の形態
[0017] 本発明について、以下具体的に説明する。
[0018] 本発明の第一の特徴は、撚り係数 (K)が 2000以上、 15000以下のポリエステル 系長繊維又はセルロース系長繊維を経糸に、実質的に無撚のポリエステル系長繊 維又はセルロース系長繊維を緯糸に用いる点にある。
[0019] 緯糸に無撚糸（原糸）を用いる場合、織物の緯伸び率は緯糸のクリンプ率にほぼ対 応することから、如何に緯糸に効率的にクリンプを付けるかが重要となる。本発明者ら は種々の検討からポリエステル系長繊維またはセルロース系長繊維にぉ ヽて生機段 階での緯糸のクリンプ率の大小が後工程 (精練工程、熱処理工程)で発現する緯糸 のクリンプ率と相関することを見出した。すなわち、生機の緯糸クリンプ率が大きいも の程、最終製品の緯ストレッチ率が大きくなる。
[0020] 従って、生機の緯糸クリンプ率を何らかの手段で高められれば、緯ストレッチ率を向 上させる事が可能となる。本願発明者らはその手段を種々検討した結果、経糸に撚り を与える事で生機の緯糸クリンプ率が向上し、それが最終製品の緯糸クリンプ率の向 上に繋がる事、即ち、緯伸びに反映されることを見出し本発明に到達したものである
[0021] 経糸と緯糸が共に長繊維の無撚糸（原糸）からなる織物の場合、織物中の経糸と緯 糸の断面形状は、長繊維を構成する数十本の単糸間の拘束力が弱いため経糸と緯 糸は互いに相手糸に押え付けられ共に扁平となる。この場合、生機の緯糸クリンプ率 は極めて低いものとなり、後工程を如何に工夫しても高いストレッチを達成させる事は できない。
[0022] 本発明で緯糸が無撚糸（原糸）使いでも従来技術より緯ストレッチ率が向上した技 術ポイントは、（1)経糸を特定条件で有撚ィヒさせる事により、経糸に使われる長繊維 の単糸を収束させ、経糸の断面形状を円形化せしめる事で緯糸のクリンプを形成し 易くした事、（2)経糸の有撚ィ匕で緯糸対比経糸の曲げ硬さを高め、曲げ柔かい緯糸 側にクリンプを付き易くした事、にある。即ち、経糸に特定条件の撚りをかける事で経 糸の断面形状を真円化させると共に曲げ硬さを高め、生機段階の緯糸に、より一層ク リンブが付き易くする事に成功し、本発明の緯ストレッチ裏地の創出が可能となった。 経糸の有撚化と緯糸の原糸使いが必須要件であり、後述するが緯糸には原糸の中 でも曲げ柔か 、ものを使用することが好まし 、。
[0023] 従来の織物および本発明の裏地に用いられる織物の断面形状を比較するために、 後述する比較例 2の織物断面の電子顕微鏡写真を図 1に、実施例 7の織物断面の電 子顕微鏡写真を図 2にそれぞれ示す。これらの写真は、夫々染色前の精練幅入れ · 乾燥後の織物を、経糸断面が現われるようにカットし、金属蒸着した後電子顕微鏡で 観察した (この形態が最終仕上がり品の形態にほぼ近ぐ精練'仕上げ加工前の生 機状態での形態もこれらと相似形態を取っている)ものであり、経糸の断面形状と緯 糸のクリンプ形態を示す。
[0024] 経糸の断面形状を比較すると、後述する撚り係数 (K) = 7100である撚糸を経糸に 用いた実施例 7と、撚り係数 (K) = 1050であって実質的に無撚に近い糸を経糸に 用いた比較例 2とでは、経糸断面の形状が異なり、それに伴い緯糸のクリンプ形態も 大幅に違っている事が判る。
[0025] 本発明に用いられる織物の経糸における好ましい撚糸条件は、撚糸回数および経 糸の繊度等によっても変化するため、本願発明では下記式（1)で示す撚り係数 (K) で規定している。
撚り係数 (K) = (0. 9 X D) °- 5 XT (1)
式中、 Dは経糸繊度 (dtex)、 Tは撚糸回数 (tZm)を意味する。
[0026] 本発明では 2000以上、 15000以下の範囲の撚り係数 (K)の糸が経糸に用いられ る事を特徴とする。撚り係数 (K)が 2000未満の場合は無撚使いよりクリンプが形成さ れやすいものの、経糸断面の形状がやや扁平になるので充分なストレッチ裏地を得 ることが出来ない。
[0027] 一方、撚り係数が 15000を越えると解撚し易くなりシボの発生やふかつき感が出易 くなつたり、見掛けの繊度が低下するため透け感が高まったり、ハリ感が出たりするの で好ましくない。
[0028] 本発明に用いられる織物の緯糸に使用できる繊維としては、上述の撚り係数を有 するポリエステル系長繊維又はセルロース系長繊維が挙げられる。
[0029] 本発明の経糸に用いられるポリエステル系長繊維としては、ポリエチレンテレフタレ ート、ポリブチレンテレフタレートなどのホモポリマー、これらポリマーらのポリエステノレ 共重合体などの繊維形成性を有するポリエステル重合体からなる繊維が用いられる 。滑り性等の面力もポリエチレンテレフタレートからなる繊維が好ましい。繊維中に制 電剤、難燃剤、耐熱剤、耐光剤、酸化チタン等の添加剤が添加されていても何ら差し 支えはない。繊維の断面形状は特に制限されるものではなぐ丸型の他に三角型、 L 型、 Y型、 T型、の多角形型でも良いし、多葉型、中空型や扁平型、不定形型など任 ,S (？ある。
[0030] また、経糸に用いられるセルロース系長繊維には、銅アンモニア法レーヨン、ピスコ ース法レーヨン、ポリノジックレーヨン、竹を原料とするセルロースなどの再生セルロー ス繊維、有機溶剤 (Nメチルモルフォリン Nオキサイド)紡糸される精製セルロース繊 維ゃジアセテートやトリアセテートなどのアセテート繊維などが代表例として挙げられ る。滑り性及び風合いの点力も銅アンモニア法レーヨン長繊維、ビスコース法レーヨン 長繊維、ポリノジックレーヨン長繊維が好ましい。
[0031] 経糸に用いられるポリエステル系長繊維、セルロース系長繊維の繊度は好ましくは 33〜133デシテックス（(¾6 ）、ょり好ましくは56〜110(¾6 でぁる。単糸繊度は特 に限定されるものではないが好ましくは 0. 5〜10dtex、より好ましくは 0. 5〜5dtex である。
[0032] 一方、本発明の緯糸に使用できる繊維としては、実質的に仮撚りゃ撚糸等が施さ れていない無撚のポリエステル系長繊維又はセルロース系長繊維の原糸が挙げられ る。これらの原糸は実質的に無撚である力 フィラメントを収束させるためにインターレ ースの付与や軽度の撚り（10〜200tZm程度）をかけたりしても構わない。
[0033] 本発明の緯糸に用いられるポリエステル系長繊維としては、ポリエチレンテレフタレ ート、ポリブチレンテレフタレートなどのホモポリマー、これらポリマーらのポリエステノレ 共重合体などの繊維形成性を有するポリエステル重合体からなる繊維が用いられる 。滑り性等の面力もポリエチレンテレフタレートからなる繊維が好ましい。繊維中に制 電剤、難燃剤、耐熱剤、耐光剤、酸化チタン等の添加剤が添加されていても何ら差し 支えはない。
[0034] また、緯糸に用いられるセルロース系長繊維は、銅アンモニア法レーヨン、ピスコ一 ス法レーヨン、ポリノジックレーヨン、竹を原料とするセルロースなどの再生セルロース 繊維、有機溶剤 (Nメチルモルフォリン Nオキサイド)紡糸される精製セルロース繊維 ゃジアセテートやトリアセテートなどのアセテート繊維などが挙げられる。滑り性及び 風合いの点力 銅アンモニア法レーヨン長繊維、ビスコース法レーヨン長繊維、ポリノ ジックレーヨン長繊維が好まし 、。
[0035] 緯糸に用いられるポリエステル系長繊維、セルロース系長繊維の繊度は好ましくは 33〜133デシテックス（(¾6 ）、ょり好ましくは56〜110(¾6 でぁる。単糸繊度は特 に限定されるものではないが好ましくは 0. 5〜10dtex、より好ましくは 0. 5〜5dtex である。
[0036] 繊維の断面形状は特に制限されるものではないが、緯伸びを効率良く発現させる には曲げ柔かい原糸を用いた方が望ましい。丸断面形状の場合は単糸繊度が小さ V、すなわち単糸径が小さ 、方が好まし 、し、扁平度の高!、原糸を用いることが特に 好ましい。扁平形状は特に限定されないが、単なる扁平型ではなく W型、 I型、ブーメ ラン型、波型、串団子型等、実質的に扁平であり特定の方向に曲げ柔かい断面構造 を有する原糸が特に好ましい。
[0037] 経糸と緯糸の素材の組み合わせには、ポリエステル系長繊維 100%の裏地、セル ロース系長繊維 100%の裏地、および、ポリエステル系長繊維とセルロース系長繊維 の交織裏地 2種、計 4種の組み合わせが存在するが何ら制限はな 、。
[0038] 本発明の第二の特徴は、裏地に用いられる織物の緯伸び率が 8%以上、 20%以 下、織物表面の動摩擦係数が 0. 20以上、 0. 40以下、クリンプ指数 (C)が 0. 007 以上、 0. 015以下である点にある。
[0039] 本発明の目的である着用時の縫目の滑脱や圧迫感を抑制ならびに着用快適性に 優れた裏地を得るためには、裏地の緯方向の伸びと裏地表面の動摩擦係数が上記 の特定範囲に設計された織物でなければならない。即ち、本発明の裏地の緯伸びは 8%以上、 20%以下が好ましぐ更に好ましくは 10%以上、 20%以下、特に好ましく は 12%以上、 20%以下である。本発明裏地の緯伸び率は、撚り係数 (経糸繊度、撚 り数)や織物密度や加工条件 (幅入れ率）によって制御'調整することができる。
[0040] 従来の 5〜10%程度の緯伸びを有する表地に対して、裏地に必要とされる緯伸び は「きせ (着心地を阻害しな!、ために表地のサイズより大きめに裏地を裁断し縫目近 辺で裏地を折り返し、裏地にゆとりを持たせること）」の存在や表地の保型性を考慮す ると、表地の緯伸びの 7割程度（3. 5〜7%)で充分対応可能である。しかし、前述し たように最近の表地の伸びは 15〜20%前後のものが主流となりつつあり、これらのス トレツチ表地に対応するためには裏地としてそれ以上の緯伸びが必要である。本発 明者らが緯伸び 15%の表地に緯伸びの異なる裏地を付けて着用試験を行った結果 、裏地の伸びとしては 8%以上あれば動作時にも圧迫感や不快感を感じることがな ヽ ことを確認した。一方、裏地の緯伸びが 20%を超えると緯糸のクリンプが大きくなるた め、表面のざらつきが増し滑り性が低下するので着用快適感が損なわれ望ましくない
[0041] また、裏地として必要とされる性能であるホッレ耐久性や緯糸の目よれ等を満足す るためには、（2)式で示されるクリンプ指数 (C)が特定の範囲に収まって 、る事が望 ましい。
クリンプ指数 (C) =製品の緯糸のクリンプ率 Z{M X (D)0 5} (2)
式中、 Dは経糸繊度 (dtex)、 Mは経糸密度 (本 Zインチ）を意味する。
[0042] クリンプ指数は、織物の緯伸びと経糸のカバーファクターに関して裏地の表面構造 を特定する尺度である。本発明裏地の織物単位でのクリンプ指数としては、 0. 007 以上、 0. 015以下の範囲にある事が好ましい。 0. 007未満になると緯糸のクリンプ 率が低く緯伸びが 8%未満の裏地となったり、経糸密度が多すぎたり経糸繊度が太 すぎると風合いが硬くなるので好ましくない。一方、 0. 015を越える場合は緯糸のタリ ンプ率が大きすぎるか経糸密度が少なすぎたり、経糸繊度が小さすぎて緯糸の緩ん だ織物構造となるため目よれやホッレが発生し易くなるので好ましくない。
[0043] 一方、着用快適感を左右する裏地特性として滑り性が挙げられる。滑り性を満足な ものにするためには裏地の動摩擦係数を 0. 20以上、 0. 40以下の範囲にする事が 必要である。
[0044] 緯伸び率と比例して動摩擦係数も高くなる傾向にあるが、 0. 40以下であれば着用 感を損ねるものではない。 0. 4を越えると着脱性や肌触り性が悪く裏地としては好ま しくない。また、 0. 20未満の場合、例えばスカートを着用して椅子等に腰掛けた場 合に表地や素肌やパンティストキングなどとの滑りが良すぎる為に、スカートの裾部な どがずれ易くなつたり、体勢が崩れ易くなつたりするなどの支障をきたすので好ましく ない。 [0045] 本発明の裏地の織物組織としては、平織、綾織、朱子織などが挙げられる。何れの 織組織を採用するかは裏地の用途領域、要求特性などによって適宜決定すればよ い。例えば、婦人服に関しては、薄くてソフトな風合いが好まれることから、特に平組 織の裏地とする事が好ましい。紳士服の場合には、滑りとある程度の厚み感が必要と なるので綾組織の裏地とする事が好まし 、。
[0046] 本発明の裏地は後述する方法によって製造することができる。製造法は基本的に は引用文献 1に記載されている方法と同様で、生機を処理するに当たって生機の幅 に対して精練前又は精練後に 5〜30%の幅入れ熱処理を行なえばよい。即ち、緯 方向（幅方向）より経方向がより緊張状態となる状態で幅入れ処理することにより、緯 糸密度の増加を極力抑えながら経糸密度の増加に伴う織物の幅方向の組織収縮（ 緯糸にタリンプを形成させる）を起こさせることにより達成できるものである。
[0047] 緯糸がポリエステル系長繊維の場合、生機織物を精練前又は精練後に生機幅に 対して 5〜30%の幅入れした状態で 160°C〜210°Cの熱処理を行うことで本発明裏 地を達成することができる。これは、生機織物中に形成された緯糸のクリンプと、ポリ エステル系長繊維の熱収縮率とを利用して、緯糸に高度にクリンプを形成させて緯 伸びを発現させる原理からなる。例えば、織物の加工時に熱処理機として一般的に 用いられて 、るピンテンター型のヒートセッターで熱処理する場合、製織後または精 練後の織物の両端を固定した状態で熱処理するが、その固定した幅を製織後または 精練後の織物幅より狭くして、且つ、経方向により緊張させた状態で処理すればよい 。ここで精練とは、製織後の織物に付着している油剤や経糸糊剤などを除去するェ 程である。この精練で用いられる処理液としては、水または界面活性剤とアルカリを 含む水溶液がよい。装置としては、織物の精練で一般的に使用されているオープン ソーパー型連続精練機、液流染色機、浴中懸垂型連続精練機、ゥインス精練機、ソ フサ一精練機などを用いれば良 、。
[0048] 幅入れ熱処理及び精練を終了した後は、裏地の一般的な加工工程である染色、仕 上げ工程が適用される。風合いをよりソフトにする場合には、染色前にアルカリ減量 加工を行っても差し支えな 、。ポリエステル系長繊維の染色加工は通常の裏地の加 ェ方法が適用され、液流型染色機、ジッガー染色機、ビーム染色機、ゥインス染色機 などが使用できる。仕上げ加工についても同様で通常の裏地の加工方法を採用す ればよい。この仕上げ工程で、付加的に仕上げ剤として帯電防止剤、撥水剤、吸汗 剤などを付与する事ができる。又、織物表面の光沢、平滑性、風合いを改善するため にカレンダー処理やエンボス処理などを適用する事もできる。
[0049] 緯糸にポリエステル系長繊維、経糸にセルロース系長繊維を用いた交織織物の場 合の染色加工では、まず上記と同様な方法で幅入れ、精練した後にポリエステル系 長繊維の染色を行う。次いで、セルロース系長繊維の染色を行う。この場合、ポリエス テル系長繊維を染色した染色機と同機を用いて染色しても良いし、コールドパッドバ ツチ法やパッドスチーム法ゃジッガー法による別の染色機を用いて染色する事もでき る。
[0050] また、緯糸がセルロース系長繊維の場合、生機状態で織物に水、スチーム、アル力 リ水溶液を付与した後、該織物を生機幅に対して 5〜15%の幅入れした状態で 100 °C〜 210°Cの熱処理を行えばよ!/、。これは生機織物中に形成された緯糸のクリンプ とセルロース系長繊維が水によって生起する膨潤作用を最大限に利用して緯糸に高 度にクリンプを形成させて緯伸び発現させる原理力 なる。セルロース系長繊維が酢 酸セルロースの場合は、精練前に織物を生機幅に対して 5〜15%の幅入れした状 態で 160°C〜 210°Cの熱処理を行えば良 、。これは生機織物中に形成された緯糸 のクリンプと酢酸セルロース繊維の熱収縮率とを利用して緯糸に高度にクリンプを形 成させて緯伸び発現させる原理からなる。
[0051] 精練前の生機織物に水を付与するには、織物に均一に水を付与できる方法、例え ば、浸漬法ゃスプレー法やキスロール法などが挙げられる。加工コストや加工安定性 を考慮すると、浸漬法が好ましい。セルロース系長繊維の膨潤を更に大きくするため に水酸化ナトリウムや水酸化カリウム、炭酸ナトリウムなどのアルカリ性ィ匕合物を lOwt %程度まで添加する事もできる。水付与後に熱処理機として一般的に用いられてい るピンテンター型のヒートセッターで熱処理する場合、製織後または精練後の織物の 両端を固定した状態で熱処理する。その固定した幅を製織後または精練後の織物 幅より狭くして、且つ、経方向により緊張させた状態で処理すれば良い。幅入れ熱処 理及び精練を終了した後は、裏地の一般的な加工工程である染色、仕上げ工程が 適用される。
[0052] 本発明の裏地は、上述された方法で得られた織物を用いることで、好適に得られる 実施例
[0053] 以下、本発明を実施例で具体的に説明するが、本発明は実施例のみに限定される ものではない。尚、測定方法、評価方法等は下記の通りである。
[0054] (1)緯伸び率の評価
カトーテック（株）製の KES— FBIを用いて、 20cm X 20cmの織物を把持長（L) 5 cm、引っ張り速度 0. 2mmZ秒で緯方向に伸長し、 490NZmの応力下での伸び E (%)を次式により算出した。
E (%) = ( A L/L) X 100 (4)
ここで Δ Lは 490NZm応力下で伸びた長さ（cm)である。
[0055] (2)動摩擦係数の評価
力トーテック (株）の KES— SEを用いて、金巾 3号精練上がりの綿布を摩擦面寸法 が lcmX 1cmで重量が 25gの摩擦子に取り付けて、 5cmZminの速度で固定した 裏地の表面上を滑らせ、その時の摩擦抵抗力から次式によって動摩擦係数（ ）を 求めたものである。式中の Aは測定器に掲示された摩擦抵抗力の平均値 (gf)、 Bは 摩擦子の重量 (g)をそれぞれ表わす。なお、摩擦係数は裏地の経糸方向に滑らした 値と緯糸方向に滑らせたときの値の平均値を裏地の動摩擦係数とした。
動摩擦係数（ ） =AZB (5)
(3)織物中の緯糸クリンプ率
織物 (生機、仕上げ後の織物、裏地製品）中の緯糸クリンプ率は、織物の緯糸方向 に 20cmの印を付けた後、織物を分解して取り出した緯糸に繊度の 1Z10の荷重を かけ、そのときの印間長さ L (cm)を計測して次式により算出した。
緯糸のクリンプ率（％) ={(1^— 20) 720} 100 (3)
(4)縫目滑脱
JIS— L— 1096法 (B法）に準拠して測定した。着用時には緯方向に応力が加わり 易 、ので緯方向の滑脱 (緯糸が滑脱する発生する緯糸上の経糸のズレ量)を計測し た。経方向 10cm (幅）、緯方向 17cm (長さ）のピースを長さの半分に折り、縫い代 lc mで本縫いし（針 11番、糸 50番ポリエステル糸、 5針 Zcm)、折り目を切断した。この ピースを引っ張り試験で定荷重（5kgZ2. 54cm)の負荷を掛け、無荷重で 1時間後 に 0. 5kg/2. 54cmの荷重を掛けその時の縫目ズレ量を縫目滑脱量とした。値は n = 3の平均値で算出した。
[0056] 以下、実施例 1〜5、比較例 1に於いて、経糸にポリエステル系長繊維を用いた場 合の実例を開示する。
[0057] 〔実施例 1〕
経糸に撚り係数 (K)力 260の 56dtexZ24fのポリエチレンテレフタレート長繊維（ 鞘芯構造の制電糸）、緯糸に断面形状が W型をした 56dtexZ30fポリエチレンテレ フタレート長繊維 (長径と短径の長さの比は約 3： 1)の無撚糸を用いて、経糸密度 12 2本 Z2. 54cm,緯糸密度 99本 Z2. 54cmの平織物を製織した。
[0058] この生機をピンテンターにより、 190°C X 30秒の条件で生機織物幅に対して 15% の幅入れを行った。次にオープンソーパー型の連続精練機を用いて、 90°Cの水酸 化ナトリウム 5gZlとノ-オン系界面活性剤 2gZlを含む浴で精練した後、湯洗 (80°C ) ·脱水 ·乾燥（120°C)した。引き続き、パッドスチーム法にて水酸ィ匕ナトリウム 125g Zl、ネオレート NA30 (日華化学社製：アルキルホスフェート系浸透剤 lOg/1)を含 む処理液を含浸 ·絞液 (絞り率 40wt%)して連続アルカリ減量を行い、常法にて中和 •湯洗 ·乾燥を行った。染色は液流染色機を用い、分散染料 (C. I DISPERSE B LUE 291： l%owf)とデイスパー TL (明成化学社製、：タモール型分散剤 lg/1) と PH調整剤（酢酸: 0. 5ccZD力もなる浴で 130°C X 30分染色し、その後還元洗浄 を経て染色織物を得た。力かる織物を NKガード FGN800 (日華化学社製、フッ素系 撥水剤： lwt%)とミユウロン AS222 (ミヨシ油脂社製、カチオン系制電剤： lwt%)か らなる水溶液を用いて、パッドドライキュア法 (予備乾燥 100°C X 1分、本乾燥 180°C X 30秒)で仕上げられた織物を使用して裏地を得た。物性結果を表 1に示す。
[0059] 〔実施例 2〕
経糸に撚り係数 (K)力 260の 56dtexZ24fのポリエチレンテレフタレート長繊維（ 鞘芯構造の制電糸）、緯糸に断面形状が W型をした 84dtexZ30fポリエチレンテレ フタレート長繊維 (長径と短径の長さの比は約 3： 1)の無撚糸を用いて、経糸密度 11
7本 Z2. 54cm,緯糸密度 80本 Z2. 54cmの平織物を製織した。
[0060] この生機をピンテンターにより、 195°C X 30秒の条件で生機織物幅に対して 18% の幅入れを行った。精練 ·連続アルカリ減量 ·染色 ·仕上げ加工は実施例 1と同様の 方法で行い裏地を得た。物性結果を表 1に示す。
[0061] 〔実施例 3〕
経糸に撚り係数 (K)が 7100の 56dtexZ24fのポリエチレンテレフタレート長繊維（ 鞘芯構造の制電糸）、緯糸に丸断面の 84dtexZ70fポリエチレンテレフタレート長繊 維の無撚糸を用いて、経糸密度 120本 Z2. 54cm、緯糸密度 82本 Z2. 54cmの平 織物を製織した。
[0062] この生機をピンテンターにより、 190°C X 30秒の条件で生機織物幅に対して 16% の幅入れを行った。精練 ·アルカリ減量 ·染色 ·仕上げ加工は実施例 1と同様の方法 で行い裏地を得た。物性結果を表 1に示す。
[0063] 〔実施例 4〕
経糸に撚り係数 (K)が 7100の 56dtexZ24fのポリエチレンテレフタレート長繊維（ 鞘芯構造の制電糸）、緯糸に 84dtexZ45fのキュプラアンモ-ゥムレーヨン長繊維を 用いて、経糸密度 120本 Z2. 54cm、緯糸密度 85本 Z2. 54cmの平織物を製織し た。
[0064] この生機を 25°Cの水に約 5秒浸漬した後、脱液機にて絞り率 48%にしたあと連続 的にピンテンターにて、製織後の織物幅に対して 14%の幅入れを 170°C X 30秒の 条件で行った。精練は実施例 1と同様にオープンソーパー型連続精練機を用いて行 つた。染色は液流染色機を用いて 130°Cで 60分行った。染色条件は浴比 1 : 20、浴 PH5. 5、薬剤としては分散染料（C. I DISPERSE BLUE 291 : l%owf)、直 接染料（C. I DIRECT BLUE 291： l%owf)、デイスパー TL (明成化学社製、 タモール型分散剤： lgZD、硫酸ナトリウム 50gZlを用いた。仕上げ加工はパッドド ライキュア法で、スミテックスレジン NF— 500K (住友化学社製、ノンホルマリン系榭 脂： 5wt%)、スミテックス ACC X— 110 (住友化学社製、金属塩系触媒： 1. 5wt% )、ニツカ MS— IF (日華化学社製、メチロールアミド系柔軟剤： lwt%)を用いて、デ イッブ. -ップ後、予備乾燥（100°C X 1分)し架橋のための熱処理（160°C X 90秒） を行い、裏地を得た。物性結果を表 1に示す。
[0065] 〔実施例 5〕
実施例 3において緯糸に 84dtexZ36f丸型断面のポリエチレンテレフタレート長繊 維を用いる以外は、すべて実施例 2と同様の方法で行い裏地を得た。物性結果を表
1に示す。
[0066] 〔比較例 1〕
実施例 1の経糸が 56dtexZ24fのポリエチレンテレフタレート長繊維（鞘芯構造の 制電糸）の無撚糸使い以外は、すべて実施例 1と同様の方法で行い裏地を得た。物 性結果を表 1に示す。
[0067] 以下の実施例 6〜13、比較例 2〜4に於いて、経糸にセルロース系長繊維を用い た場合の実例を開示する。
[0068] 〔実施例 6〜8〕
経糸に撚り係数 (K)が 2100 (実施例 6)と 4260 (実施例 7)と 7100 (実施例 8)の 56 dtexZ30fのキュプラアンモ-ゥムレーヨン長繊維、緯糸に 56dtexZ45fのキュプラ アンモ-ゥムレーヨン長繊維の無撚糸を用いて、経糸密度 136本 Z2. 54cm,緯糸 密度 103本 Z2. 54cmの平織物を製織した。
[0069] この生機を製織後の織物幅に対しておよそ 12%の幅入れを行うためにオープンソ 一パー型の連続精練機を用いて、 30°Cの 3. 15wt%水酸ィ匕ナトリウム水溶液（5° ボーメ）に浸漬した後、湯洗 (80°C) ·水洗を繰り返し脱水 ·乾燥（120°C)させた。実 質的な幅入れ率は、撚り係数が高くなるほど高くなつた（実施例 6は 9. 5%、実施例 7 は 10. 2%、実施例 8は 11. 2%) o染色はコールドバッチ法で 25°Cで 15時間行った 。染料にはビュルスルフォン系反応染料（SUMIFIX NAVY BLUE GS : l%ow f)を、水酸ィ匕ナトリウム lOgZlを用いた。引き続く仕上げ加工は実施例 4の処方に準 じて実施し、裏地を得た。但し、榭脂と触媒濃度は 2倍量使用した。物性結果を表 2 に示す。
[0070] 〔比較例 2〜3〕
経糸に撚り係数 (K)が 1060 (比較例 2)と 16300 (比較例 3)の 56dtexZ30fのキ ュプラアンモ-ゥムレーヨン長繊維、緯糸に 56dtexZ45fのキュプラアンモ-ゥムレ 一ヨン長繊維の無撚糸を用いて、経糸密度 136本 Z2. 54cm,緯糸密度 103本 Z2 . 54cmの平織物を製織した。
この生機を実施例 6の方法の準じて精練 '幅入れ、染色、仕上げ加工を行い、裏地を 得た。物性結果を表 2に示す。
[0071] 〔実施例 9〕
経糸に撚り係数 (K)が 14100の 66dtexZ36fのキュプラアンモ-ゥムレーヨン長 繊維を SSZZ2本交互使!、で用い、緯糸に 84dtexZ45fのキュプラアンモ-ゥムレ 一ヨン長繊維を用いて、経糸密度 118本 Z2. 54cm、緯糸密度 83本 Z2. 54cmの 平織物を製織した。この生機を実施例 6の方法の準じて精練 ·幅入れ、染色、仕上げ 加工を行い、裏地を得た。物性結果を表 2に示す。
[0072] 〔実施例 10〕
経糸に撚り係数 (K)が 14200の 84dtexZ45fのキュプラアンモ-ゥムレーヨン長 繊維を SSZZ2本交互使!、で用い、緯糸に 84dtexZ45fのキュプラアンモ-ゥムレ 一ヨン長繊維の無撚糸を用いて、経糸密度 113本 Z2. 54cm,緯糸密度 72本 Z2.
54cmの平織物を製織した。この生機を実施例 6の方法の準じて精練 '幅入れ、染色
、仕上げ加工を行い、裏地を得た。物性結果を表 3に示す。
[0073] 〔比較例 4〕
実施例 10の経糸が 84dtexZ45fのキュプラアンモ-ゥムレーヨン長繊維の無撚使 い以外は、すべて実施例 10と同様の方法で行い裏地を得た。物性結果を表 3に示 す。
[0074] 〔実施例 11〕
経糸に撚り係数 (K)が 7100の 56dtexZ30fのキュプラアンモ-ゥムレーヨン長繊 維、緯糸に断面形状が W型をした 84dtexZ30fポリエチレンテレフタレート長繊維 ( 長径と短径の長さの比は約 3 : 1)の無撚糸を用いて、経糸密度 136本 Z2. 54cm, 緯糸密度 85本 Z2. 54cmの平織物を製織した。
[0075] この生機をピンテンターにより、 190°C X 30秒の条件で生機織物幅に対して 12% の幅入れを行った。精練は実施例 1と同様にオープンソーパー型連続精練機を用い て行った。染色は液流染色機を用いて 130°Cで 60分行った。染色条件は浴比 1 : 20 、浴 PH5. 5、薬剤としては分散染料（C. I DISPERSE BLUE 291 : l%owf)、 直接染料（C. I DIRECT BLUE 291 : l%owf)、デイスパー TL (明成化学社製 、タモール型分散剤： lgZD、硫酸ナトリウム 50gZlを用いた。仕上げ加工はパッドド ライキュア法で、スミテックスレジン NF— 500K (住友化学社製、ノンホルマリン系榭 脂： 5wt%)、スミテックス ACC X— 110 (住友化学社製、金属塩系触媒： 1. 5wt% )、ニツカ MS— IF (日華化学社製、メチロールアミド系柔軟剤： lwt%)を用いて、デ イッブ. -ップ後、予備乾燥（100°C X 1分)し架橋のための熱処理（160°C X 90秒） を行い、裏地を得た。物性結果を表 3に示す。
[0076] 〔実施例 12〕
経糸に撚り係数 (K)が 5200の 84dtexZ33fのビスコース法レーヨン長繊維、緯糸 に 110dtexZ44fのピスコース法レーョン長繊維の無撚糸を用いて、経糸密度 136 本 Z2. 54cm,緯糸密度 71本 Z2. 54cmの綾織物を製織した。
[0077] この生機を実施例 6に準拠して精練 '幅入れ、染色、仕上げ加工を行い、裏地を得 た。物性結果を表 3に示す。
[0078] 〔実施例 13〕
経糸に撚り係数が 7100の 56dtexZ30fのキュプラアンモ-ゥムレーヨン長繊維、 緯糸に 84dtexZ20fのジアセテート長繊維の無撚糸を用いて、経糸密度 136本 Z2 . 54cm,緯糸密度 80本 Z2. 54cmの平織物を製織した。
[0079] 生機を 25°Cの水に約 5秒浸漬した後、脱液機で絞り率 51%にしたあと連続的にピ ンテンターにて、製織後の織物幅に対して 10%の幅入れを 190°C X 30秒の条件で 行った。精練は実施例 1に準拠して行った。染色はジッガー染色法で分散染料 (C. I
DISPERSE BLUE 291： l%owf)とデイスパー TL (明成化学社製、タモール 型分散剤： lgZDを用いて 95°Cで 1時間ジアセテートを染めた後、直接染料 (C. I DIRECT BLUE 291： l%owf)と硫酸ナトリウム 50gZlを用いてキュプラアンモ- ゥムレーヨンを染めた。仕上げ力卩ェはパッドドライキュア法で、スミテックスレジン NF - 500K (住友化学社製、ノンホルマリン系榭脂： 5wt%)、スミテックス ACC X— 11 0 (住友化学社製、金属塩系触媒： 1. 5wt%)、ニツカ MS— IF (日華化学社製、メチ ロールアミド系柔軟剤： lwt%)を用いて、ディップ' -ップ後、予備乾燥（100°CX 1 分)し架橋のための熱処理（160°C X 90秒)を行 、、裏地を得た。物性結果を表 3に 示す。
[0080] [表 1]
Figure imgf000018_0001
[0081] [表 2] 実施例 6 実施倒 7 実施俩 8 実施例 Θ 比較例 2 比較例 3 経糸撚糸回数 s300 s600 s 1000 s S1825 s 150 S2300
(t/m)
聽数 2100 Ξ60 71(H) 14100 1060 16300 生機密度 (経/緯） 136/103 136 Ί03 136/103 118/83 136/103 136/103 本 ,S!, 54cm
製品密度（経/ !*) 150X105 146/106 156/107 本/ ¾, 54cm
緯伸び率 (%) 10,】 12,4 12.1 17.6 7.7
動摩擦係数 0.28 J 0.315 0.306 0.291 0.280 0.483 縫目滑脱抵抗 (nun) 0.7 0.7 0.7 0.2 0.7 0.5 目よれ状態 問題なし 問題なし 聞題なし 隱なし 問題なし 題なし クリンプ指数 0, 0085 0,0103 0,0102 O.OH2 0.0068 0.0082 備考 シボ感 ·ザラ ツキ感あり [0082] [表 3]
Figure imgf000019_0001
産業上の利用可能性
[0083] 本発明の目的は、滑り性を損ねることなく緯方向の伸びが 8%以上のストレッチ裏地 を提供することにあり、力かる性能により着用時の縫目の滑脱や圧迫感の少ない着 用快適性に優れた裏地の提供を可能ならしめるものである。本発明の裏地は特に表 地のストレッチ率が 15%以上の衣料の裏地に好適である。

Claims

請求の範囲
[1] 下記（1)で定義される撚り係数 (K)が 2, 000以上、 15, 000以下のセルロース系 長繊維又はポリエステル系長繊維を経糸に、無撚のセルロース系長繊維又はポリェ ステル系長繊維を緯糸に用いてなる織物からなり、緯伸び率が 8%以上、 20%未満 、表面の動摩擦係数が 0. 20以上、 0. 40以下、下記（2)で定義されるクリンプ指数 ( C)が 0. 007以上、 0. 015以下である事を特徴とする緯ストレッチ裏地。
K= (0. 9 X D) 0 5 XT (1)
C=製品の緯糸のクリンプ率 Z{M X (D) ° 5} (2)
式中、 Dは経糸繊度 (dtex)、 Tは撚糸回数 (tZm)、 Mは経糸密度 (本 Z2. 54cm) を意味する。
[2] 織物の緯伸び率が 12%以上、 20%以下である請求項 1記載の緯ストレッチ裏地。
[3] 緯糸がセルロース系長繊維である請求項 1記載の緯ストレッチ裏地。
[4] セルロース系長繊維がキュプラアンモ-ゥムレーヨン長繊維、ビスコース法レーヨン 長繊維及び精製セルロース長繊維の 、ずれかである請求項 1〜3の ヽずれかに記 載の緯ストレッチ裏地。
[5] ポリエステル系長繊維がポリエチレンテレフタレート系長繊維である請求項 1〜3の
V、ずれかに記載の緯ストレッチ裏地。
[6] 生機状態で織物にアルカリ水溶液を付与した後、該織物を生機幅に対して 5〜30
%の幅入れした状態で熱処理することを特徴とする請求項 1〜3のいずれかに記載 の緯ストレッチ裏地の製造方法。
PCT/JP2006/314641 2006-07-25 2006-07-25 Tissu de doublureà élasticité de type tramée et son procédé de fabrication WO2008012869A1 (fr)