WO2003101425A2 - Articles polymeres contenant des agents therapeutiques - Google Patents

Articles polymeres contenant des agents therapeutiques Download PDF

Info

Publication number
WO2003101425A2
WO2003101425A2 PCT/US2003/017536 US0317536W WO03101425A2 WO 2003101425 A2 WO2003101425 A2 WO 2003101425A2 US 0317536 W US0317536 W US 0317536W WO 03101425 A2 WO03101425 A2 WO 03101425A2
Authority
WO
WIPO (PCT)
Prior art keywords
nanoarticle
hydrogel
scaffold
building blocks
nano
Prior art date
Application number
PCT/US2003/017536
Other languages
English (en)
Other versions
WO2003101425A3 (fr
WO2003101425A8 (fr
Inventor
Stephen E. Barry
Andrew A. Goodwin
Rachel Decor
Original Assignee
Alnis Biosciences, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alnis Biosciences, Inc. filed Critical Alnis Biosciences, Inc.
Priority to EP03741863A priority Critical patent/EP1531868A2/fr
Priority to CA002487720A priority patent/CA2487720A1/fr
Priority to AU2003273272A priority patent/AU2003273272A1/en
Priority to JP2004508783A priority patent/JP2005535604A/ja
Publication of WO2003101425A2 publication Critical patent/WO2003101425A2/fr
Priority to US10/995,880 priority patent/US20050129769A1/en
Publication of WO2003101425A3 publication Critical patent/WO2003101425A3/fr
Publication of WO2003101425A8 publication Critical patent/WO2003101425A8/fr

Abstract

La présente invention concerne des articles polymères hydrophiles comprenant une structure polymère et un ou plusieurs agents thérapeutiques, tels que des molécules médicamenteuses ou de conjugués médicamenteux. Les articles peuvent en outre éventuellement comprendre des éléments de reconnaissance qui se fixent à des structures biomoléculaires exprimées sur certaines cellules ou sur certains tissus, pour faciliter le ciblage et/ou l'administration.
PCT/US2003/017536 2002-06-03 2003-06-03 Articles polymeres contenant des agents therapeutiques WO2003101425A2 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP03741863A EP1531868A2 (fr) 2002-06-03 2003-06-03 Agents therapeutiques contenant des nano-polymeres
CA002487720A CA2487720A1 (fr) 2002-06-03 2003-06-03 Agent therapeutique contenant des nanoarticles polymeriques
AU2003273272A AU2003273272A1 (en) 2002-06-03 2003-06-03 Therapeutic agent-containing polymeric nanoarticles
JP2004508783A JP2005535604A (ja) 2002-06-03 2003-06-03 治療剤を含むポリマーナノ物品
US10/995,880 US20050129769A1 (en) 2002-06-03 2004-11-22 Polymeric articles for carrying therapeutic agents

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US38553702P 2002-06-03 2002-06-03
US60/385,537 2002-06-03
US46316203P 2003-04-16 2003-04-16
US60/463,162 2003-04-16

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US10/995,880 Continuation-In-Part US20050129769A1 (en) 2002-06-03 2004-11-22 Polymeric articles for carrying therapeutic agents

Publications (3)

Publication Number Publication Date
WO2003101425A2 true WO2003101425A2 (fr) 2003-12-11
WO2003101425A3 WO2003101425A3 (fr) 2005-03-17
WO2003101425A8 WO2003101425A8 (fr) 2005-04-28

Family

ID=29715373

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/017536 WO2003101425A2 (fr) 2002-06-03 2003-06-03 Articles polymeres contenant des agents therapeutiques

Country Status (5)

Country Link
EP (1) EP1531868A2 (fr)
JP (1) JP2005535604A (fr)
AU (1) AU2003273272A1 (fr)
CA (1) CA2487720A1 (fr)
WO (1) WO2003101425A2 (fr)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005027873A3 (fr) * 2003-06-20 2005-06-23 Alnis Biosciences Inc Nanoarticles therapeutiques
WO2005065724A1 (fr) * 2003-12-30 2005-07-21 Alnis Biosciences, Inc. Preparations a base de complexes d'ions paramagnetiques
WO2005070471A3 (fr) * 2004-01-20 2006-03-30 Alnis Biosciences Inc Articles comprenant un materiau magnetique et des agents bioactifs
JP2008542295A (ja) * 2005-05-27 2008-11-27 ロイヤー バイオメディカル， インク． 生体再吸収性ポリマーマトリックス、ならびにその作製および使用方法
EP2111872A3 (fr) * 2004-07-05 2009-12-23 Complex Biosystems GmbH Hydrogel de conjugués polymères promédicamenteux
CN101864071A (zh) * 2010-05-21 2010-10-20 北京中海康医药科技发展有限公司 聚乙二醇-二硬脂酰磷脂酰乙醇胺衍生物及其制备方法
US7968085B2 (en) 2004-07-05 2011-06-28 Ascendis Pharma A/S Hydrogel formulations
WO2013036931A1 (fr) 2011-09-08 2013-03-14 Western University Of Health Sciences Liposomes ciblés en thérapie cancéreuse
US9023370B2 (en) 2008-12-16 2015-05-05 Fundacio Privada Institut Catala De Nanotecnologia Conjugates comprising nanoparticles coated with platinum containing compounds
US9133276B2 (en) 2010-09-17 2015-09-15 Sanofi-Aventis Deutschland Gmbh Prodrugs comprising an exendin linker conjugate
US9138462B2 (en) 2009-07-31 2015-09-22 Sanofi-Aventis Deutschland Gmbh Prodrugs comprising an insulin linker conjugate
US9265723B2 (en) 2009-07-31 2016-02-23 Sanofi-Aventis Deutschland Gmbh Long acting insulin composition
US9295736B2 (en) 2007-09-24 2016-03-29 Bar Ilan University Polymer nanoparticles coated by magnetic metal oxide and uses thereof
US9434610B2 (en) 2008-10-07 2016-09-06 Rexahn Pharmaceuticals, Inc. HPMA—docetaxel conjugates and uses therefore
WO2017201407A1 (fr) * 2016-05-20 2017-11-23 Massachusetts Institute Of Technology Particule hydrogel d'aldéhyde dextrane réticulé par la cystamine, contenant de la doxorubicine conjuguée à l'imine et un peptide rgd pour la chimiothérapie
US10285943B2 (en) 2010-12-02 2019-05-14 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
US11666515B2 (en) 2018-03-28 2023-06-06 Greenmark Biomedical Inc. Phosphate crosslinked starch nanoparticle and dental treatments

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BR112012008772A2 (pt) * 2009-10-13 2017-06-20 Rexahn Pharmaceuticals Inc sistemas poliméricos para a liberação de agentes anti-câncer
PL221351B1 (pl) * 2012-03-14 2016-03-31 Politechnika Warszawska Sposób otrzymywania nanocząstek polisacharydowych

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05507948A (ja) * 1990-04-18 1993-11-11 ユニバーシティ オブ ユタ リサーチ ファウンデーション アゾ結合を含み、ｐＨ依存性膨潤を示す、架橋したヒドロゲルに基づいた、結腸を標的にした経口薬の投薬形態
US5562099A (en) * 1990-10-05 1996-10-08 Massachusetts Institute Of Technology Polymeric microparticles containing agents for imaging
WO1994018955A1 (fr) * 1993-02-22 1994-09-01 Alza Corporation Compositions destinees a l'apport oral d'agents actifs
US5980883A (en) * 1996-10-02 1999-11-09 Kuraray Co., Ltd. Polymer gel for medical use
US6632457B1 (en) * 1998-08-14 2003-10-14 Incept Llc Composite hydrogel drug delivery systems
EP1194171A2 (fr) * 1999-09-02 2002-04-10 Rice University Materiaux hydrogels produisant du monoxyde d'azote
AU2001255356A1 (en) * 2000-04-14 2001-10-30 Alnis Biosciences, Inc. High affinity peptide-containing nanoparticles

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005027873A3 (fr) * 2003-06-20 2005-06-23 Alnis Biosciences Inc Nanoarticles therapeutiques
WO2005065724A1 (fr) * 2003-12-30 2005-07-21 Alnis Biosciences, Inc. Preparations a base de complexes d'ions paramagnetiques
WO2005070471A3 (fr) * 2004-01-20 2006-03-30 Alnis Biosciences Inc Articles comprenant un materiau magnetique et des agents bioactifs
US9056126B2 (en) 2004-07-05 2015-06-16 Ascendis Pharma A/S Hydrogel formulations
EP2111872A3 (fr) * 2004-07-05 2009-12-23 Complex Biosystems GmbH Hydrogel de conjugués polymères promédicamenteux
EP1781335B1 (fr) * 2004-07-05 2021-01-13 Ascendis Pharma GmbH Conjugués d'hydrogel
US7968085B2 (en) 2004-07-05 2011-06-28 Ascendis Pharma A/S Hydrogel formulations
US10029015B2 (en) 2004-07-05 2018-07-24 Ascendis Pharma A/S Hydrogel formulations
EP2594291A1 (fr) * 2004-07-05 2013-05-22 Ascendis Pharma GmbH Hydrogel
JP2008542295A (ja) * 2005-05-27 2008-11-27 ロイヤー バイオメディカル， インク． 生体再吸収性ポリマーマトリックス、ならびにその作製および使用方法
JP2013155204A (ja) * 2005-05-27 2013-08-15 Royer Biomedical Inc 生体再吸収性ポリマーマトリックス、ならびにその作製および使用方法
US9295736B2 (en) 2007-09-24 2016-03-29 Bar Ilan University Polymer nanoparticles coated by magnetic metal oxide and uses thereof
US9434610B2 (en) 2008-10-07 2016-09-06 Rexahn Pharmaceuticals, Inc. HPMA—docetaxel conjugates and uses therefore
US9023370B2 (en) 2008-12-16 2015-05-05 Fundacio Privada Institut Catala De Nanotecnologia Conjugates comprising nanoparticles coated with platinum containing compounds
US9457066B2 (en) 2009-07-31 2016-10-04 Sanofi-Aventis Deutschland Gmbh Prodrugs comprising an insulin linker conjugate
US9265723B2 (en) 2009-07-31 2016-02-23 Sanofi-Aventis Deutschland Gmbh Long acting insulin composition
US9138462B2 (en) 2009-07-31 2015-09-22 Sanofi-Aventis Deutschland Gmbh Prodrugs comprising an insulin linker conjugate
CN101864071A (zh) * 2010-05-21 2010-10-20 北京中海康医药科技发展有限公司 聚乙二醇-二硬脂酰磷脂酰乙醇胺衍生物及其制备方法
US9133276B2 (en) 2010-09-17 2015-09-15 Sanofi-Aventis Deutschland Gmbh Prodrugs comprising an exendin linker conjugate
US10285943B2 (en) 2010-12-02 2019-05-14 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
US11369570B2 (en) 2010-12-02 2022-06-28 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
EP2763658A4 (fr) * 2011-09-08 2015-08-12 Univ Western Health Sciences Liposomes ciblés en thérapie cancéreuse
US9808425B2 (en) 2011-09-08 2017-11-07 Western University Of Health Sciences Targeted liposomes in cancer therapy
WO2013036931A1 (fr) 2011-09-08 2013-03-14 Western University Of Health Sciences Liposomes ciblés en thérapie cancéreuse
WO2017201407A1 (fr) * 2016-05-20 2017-11-23 Massachusetts Institute Of Technology Particule hydrogel d'aldéhyde dextrane réticulé par la cystamine, contenant de la doxorubicine conjuguée à l'imine et un peptide rgd pour la chimiothérapie
US11666515B2 (en) 2018-03-28 2023-06-06 Greenmark Biomedical Inc. Phosphate crosslinked starch nanoparticle and dental treatments

Also Published As

Publication number Publication date
AU2003273272A1 (en) 2003-12-19
WO2003101425A3 (fr) 2005-03-17
JP2005535604A (ja) 2005-11-24
EP1531868A2 (fr) 2005-05-25
WO2003101425A8 (fr) 2005-04-28
AU2003273272A8 (en) 2003-12-19
CA2487720A1 (fr) 2003-12-11

Similar Documents

Publication Publication Date Title
WO2003101425A2 (fr) Articles polymeres contenant des agents therapeutiques
Khandare et al. Multifunctional dendritic polymers in nanomedicine: opportunities and challenges
JP2022191364A (ja) ポリマーナノ粒子およびその調整のプロセス
Nakamura et al. Two step mechanisms of tumor selective delivery of N-(2-hydroxypropyl) methacrylamide copolymer conjugated with pirarubicin via an acid-cleavable linkage
Mezghrani et al. Hepatocellular carcinoma dually-targeted nanoparticles for reduction triggered intracellular delivery of doxorubicin
US20060127310A1 (en) Amplification of biotin-mediated targeting
Ma et al. Copolymers containing carbohydrates and other biomolecules: design, synthesis and applications
Sunasee et al. Therapeutic potential of carbohydrate-based polymeric and nanoparticle systems
JP2003531930A (ja) 両親媒性大環状誘導体およびそれらの類似体
Mukwaya et al. Saccharide‐based nanocarriers for targeted therapeutic and diagnostic applications
US20040126900A1 (en) High affinity peptide- containing nanoparticles
Hudlikar et al. Controlled multi‐functionalization facilitates targeted delivery of nanoparticles to cancer cells
Nie et al. In vitro and in vivo evaluation of stimuli-responsive vesicle from PEGylated hyperbranched PAMAM-doxorubicin conjugate for gastric cancer therapy
JPH06505755A (ja) 重合体誘導体結合アンスラサイクリン配糖体を含有する医薬組成物及びその製造方法
Wali et al. Tailoring the supramolecular structure of amphiphilic glycopolypeptide analogue toward liver targeted drug delivery systems
US20050129769A1 (en) Polymeric articles for carrying therapeutic agents
US6054492A (en) Fluorinated copolymeric pharmaceutical adjuncts
CN101249266A (zh) 纳米肝靶向两亲性嵌段共聚物给药系统及制备方法
JP2019123773A (ja) 修飾されたスチレン−無水マレイン酸共重合体及びその使用
JPWO2006028129A1 (ja) 医薬品製剤
Wu et al. Enhanced drug delivery to hepatocellular carcinoma with a galactosylated core–shell polyphosphoester nanogel
CA2553647A1 (fr) Articles comprenant un materiau magnetique et des agents bioactifs
WO2005065724A1 (fr) Preparations a base de complexes d'ions paramagnetiques
Tang et al. Synthesis, characterization, and in vitro and in vivo evaluation of a novel pectin–adriamycin conjugate
KR20180107745A (ko) 기체 발포형 마이셀 및 이의 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 10995880

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 2487720

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2004508783

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 2003741863

Country of ref document: EP

CFP Corrected version of a pamphlet front page
CR1 Correction of entry in section i

Free format text: IN PCT GAZETTE 50/2003 UNDER (71) THE NAME/ADDRESS SHOULD READ "ALNIS BIOSCIENCES, INC."

WWP Wipo information: published in national office

Ref document number: 2003741863

Country of ref document: EP

WWW Wipo information: withdrawn in national office