WO2001000377A1 - Procede de production de pieces en bois comprimees - Google Patents

Procede de production de pieces en bois comprimees Download PDF

Info

Publication number
WO2001000377A1
WO2001000377A1 PCT/FI2000/000600 FI0000600W WO0100377A1 WO 2001000377 A1 WO2001000377 A1 WO 2001000377A1 FI 0000600 W FI0000600 W FI 0000600W WO 0100377 A1 WO0100377 A1 WO 0100377A1
Authority
WO
WIPO (PCT)
Prior art keywords
compressed
wooden
wooden piece
heat treatment
temperature
Prior art date
Application number
PCT/FI2000/000600
Other languages
English (en)
Inventor
Pertti Viitaniemi
Saila JÄMSÄ
Paavo Kontinen
Pentti Ek
Original Assignee
Valtion Teknillinen Tutkimuskeskus
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=8554986&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2001000377(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Valtion Teknillinen Tutkimuskeskus filed Critical Valtion Teknillinen Tutkimuskeskus
Priority to EP00944077A priority Critical patent/EP1198329A1/fr
Priority to AU58313/00A priority patent/AU5831300A/en
Publication of WO2001000377A1 publication Critical patent/WO2001000377A1/fr

Abstract

L'invention concerne un procédé de fabrication de pièces en bois comprimées consistant à leur donner une forme souhaitée, à les acheminer vers une installation de traitement thermique à une température accrue de manière à durcir la forme modifiée par compression, à comprimer les pièces de bois à une température accrue, les pièces étant sous compression jusqu'à ce que leur humidité soit réduite à moins de 15 %, à les chauffer ensuite à une pression atmosphérique normale en présence d'une vapeur à une température dépassant 180 °C jusqu'à ce que la perte de poids soit au moins d'environ 3 %. On peut, selon cette invention, améliorer la stabilité des dimensions du bois comprimé, réduire au minimum le gonflement des pièces lors de leur immersion dans l'eau. De plus, une fois séchées, les pièces reprennent leur épaisseur originale à la différence des pièces de bois comprimées traditionnelles qui gonflent.
PCT/FI2000/000600 1999-06-29 2000-06-29 Procede de production de pieces en bois comprimees WO2001000377A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP00944077A EP1198329A1 (fr) 1999-06-29 2000-06-29 Procede de production de pieces en bois comprimees
AU58313/00A AU5831300A (en) 1999-06-29 2000-06-29 Process for producing compressed wood pieces

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FI991483 1999-06-29
FI991483A FI110241B (fi) 1999-06-29 1999-06-29 Menetelmä puristettujen puukappaleiden valmistamiseksi

Publications (1)

Publication Number Publication Date
WO2001000377A1 true WO2001000377A1 (fr) 2001-01-04

Family

ID=8554986

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/FI2000/000600 WO2001000377A1 (fr) 1999-06-29 2000-06-29 Procede de production de pieces en bois comprimees

Country Status (4)

Country Link
EP (1) EP1198329A1 (fr)
AU (1) AU5831300A (fr)
FI (1) FI110241B (fr)
WO (1) WO2001000377A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL1023232C2 (nl) * 2003-04-22 2004-10-26 Franciscus Antonius Ma Heijden Werkwijze voor het produceren van massief houten planken of balken.
WO2005049291A1 (fr) * 2003-11-21 2005-06-02 Teknocomp Oy Procede et appareil de traitement du bois ou de produits ligneux
CN115990926A (zh) * 2022-07-13 2023-04-21 上海星衡木业有限公司 一种提升木材硬度的加工方法及应用

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1994020273A1 (fr) * 1993-03-10 1994-09-15 Jaakko Kause Procede de production de bois fortement comprime
WO1994026485A1 (fr) * 1993-05-18 1994-11-24 Valtion Teknillinen Tutkimuskeskus Procede de sechage et de compression pour la mise en forme du bois

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1994020273A1 (fr) * 1993-03-10 1994-09-15 Jaakko Kause Procede de production de bois fortement comprime
WO1994026485A1 (fr) * 1993-05-18 1994-11-24 Valtion Teknillinen Tutkimuskeskus Procede de sechage et de compression pour la mise en forme du bois

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL1023232C2 (nl) * 2003-04-22 2004-10-26 Franciscus Antonius Ma Heijden Werkwijze voor het produceren van massief houten planken of balken.
WO2005049291A1 (fr) * 2003-11-21 2005-06-02 Teknocomp Oy Procede et appareil de traitement du bois ou de produits ligneux
CN115990926A (zh) * 2022-07-13 2023-04-21 上海星衡木业有限公司 一种提升木材硬度的加工方法及应用

Also Published As

Publication number Publication date
FI991483A7 (fi) 2000-12-30
FI110241B (fi) 2002-12-31
EP1198329A1 (fr) 2002-04-24
AU5831300A (en) 2001-01-31
FI991483A0 (fi) 1999-06-29

Similar Documents

Publication Publication Date Title
CA2162374C (fr) Methode pour ameliorer la resistance a la biodegradation et la stabilite dimensionnelle de produits cellulosiques
US5605767A (en) Hardened and fire retardant wood products
Ding et al. Influence of steam pressure on physical and mechanical properties of heat-treated Mongolian pine lumber
US4606388A (en) Process for densifying low density woods
Gao et al. Effects of pressurized superheated-steam heat treatment on set recovery and mechanical properties of surface-compressed wood
FI91947C (fi) Menetelmä puun muotokuivaamiseksi
Ferrari et al. A Revaluation of Turkey Oak Wood (Quercus cerris L.) Through Combined Steaming and Thermo-vacuum Treatments.
Li et al. Chemical analysis of densification, drying, and heat treatment of Scots pine (Pinus sylvestris L.) through a hot-pressing process
Jebrane et al. Comparative study of two softwood species industrially modified by Thermowood® and thermo-vacuum process
JP2004522623A (ja) 木材を処理及び乾燥する方法
Dos Santos et al. Properties of thermo-mechanically treated wood from Pinus caribaea var. hondurensis.
Ninane et al. Physical, mechanical, and decay resistance properties of heat-treated wood by Besson® process of three European hardwood species
Korkut et al. The effects of heat treatment on physical and technological properties and surface roughness of European Hophornbeam (Ostrya carpinifolia Scop.) wood
US20080256824A1 (en) Method of Treating a Piece of Wood at an Elevated Temperature
WO2001000377A1 (fr) Procede de production de pieces en bois comprimees
Zhao et al. Effects of steam treatment on bending properties and chemical composition of moso bamboo (Phyllostachys pubescens)
EP0197674B1 (fr) Procédé pour densifier des bois de basse densité
Kim Environmentally-friendly wood modification: physical and mechanical properties of Jabon wood (Anthocephalus cadamba) as affected by oil heat treatment
Hamzah et al. Assessment of oil palm wood quality improvement through integrated treatment process as function of sawing pattern and slab thickness
EP1597039B1 (fr) Procede de traitement de pieces en bois
NO813990L (no) Fremgangsmaate for dimensjonsstabilisering av pressede trematerialer
Albert et al. Influence of Densification Treatment on The Morphology and Density Profile of Paraserianthes falcataria Laminas.
RU2837866C1 (ru) Способ паротермической обработки древесины
Nazerian et al. Physical and mechanical properties of laminated veneer lumber manufactured by poplar veneer
O'Connor Improving wood strength and stiffness through viscoelastic thermal compression

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2000944077

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2000944077

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWW Wipo information: withdrawn in national office

Ref document number: 2000944077

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: JP

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载