WO1999038034A1 - Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles - Google Patents

Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles Download PDF

Info

Publication number
WO1999038034A1
WO1999038034A1 PCT/US1998/011135 US9811135W WO9938034A1 WO 1999038034 A1 WO1999038034 A1 WO 1999038034A1 US 9811135 W US9811135 W US 9811135W WO 9938034 A1 WO9938034 A1 WO 9938034A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
adhesion
enhancing
ceramer
composition
Prior art date
Application number
PCT/US1998/011135
Other languages
English (en)
Inventor
Zayn Bilkadi
Peter L. Erickson
Original Assignee
Minnesota Mining And Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining And Manufacturing Company filed Critical Minnesota Mining And Manufacturing Company
Priority to EP98925100A priority Critical patent/EP1051645A1/fr
Priority to AU77124/98A priority patent/AU7712498A/en
Priority to KR1020007008142A priority patent/KR20010034387A/ko
Priority to JP2000528886A priority patent/JP2002501118A/ja
Priority to CA002318900A priority patent/CA2318900A1/fr
Publication of WO1999038034A1 publication Critical patent/WO1999038034A1/fr

Abstract

L'invention concerne un revêtement conférant une adhérence améliorée, qui comporte une matrice organique contenant des particules d'oxyde inorganique dispersées dans celle-ci. Le revêtement est formé à partir d'une composition de précurseur qui comprend une composition de céramère. Une composition de céramère peut comporter au moins un monomère éthyléniquement insaturé, un agent de pontage de monomères de silane organofonctionnel facultatif, et des particules colloïdales inorganiques qui comprennent au moins de la silice. Une autre composition de céramère comporte un agent de pontage de monomères de silane organofonctionnel et des particules colloïdales inorganiques qui comprennent au moins de la silice.
PCT/US1998/011135 1998-01-27 1998-06-02 Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles WO1999038034A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP98925100A EP1051645A1 (fr) 1998-01-27 1998-06-02 Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles
AU77124/98A AU7712498A (en) 1998-01-27 1998-06-02 Adhesion-enhancing coatings for optically functional coatings materials
KR1020007008142A KR20010034387A (ko) 1998-01-27 1998-06-02 광학적 작용성 코팅 소재를 위한 접착력 증가 코팅
JP2000528886A JP2002501118A (ja) 1998-01-27 1998-06-02 光機能性コーティング材料用接着強化コーティング
CA002318900A CA2318900A1 (fr) 1998-01-27 1998-06-02 Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US1399198A 1998-01-27 1998-01-27
US09/013,991 1998-01-27

Publications (1)

Publication Number Publication Date
WO1999038034A1 true WO1999038034A1 (fr) 1999-07-29

Family

ID=21762907

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1998/011135 WO1999038034A1 (fr) 1998-01-27 1998-06-02 Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles

Country Status (6)

Country Link
EP (1) EP1051645A1 (fr)
JP (1) JP2002501118A (fr)
KR (1) KR20010034387A (fr)
AU (1) AU7712498A (fr)
CA (1) CA2318900A1 (fr)
WO (1) WO1999038034A1 (fr)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001048095A1 (fr) * 1999-12-28 2001-07-05 Dsm N.V. Composition photodurcissable et produits durcis
US6458462B1 (en) 2000-12-13 2002-10-01 3M Innovative Properties Company Sporting goods having a ceramer coating
EP1283107A2 (fr) 2001-07-17 2003-02-12 LINTEC Corporation Feuille avec un revêtement dur
US6749813B1 (en) 2000-03-05 2004-06-15 3M Innovative Properties Company Fluid handling devices with diamond-like films
EP1384736A4 (fr) * 2001-03-21 2004-07-21 Hoya Corp Objets moules transparents, element optique, lentilles plastiques, et leurs procedes de production
KR100496557B1 (ko) * 2000-11-30 2005-06-22 호야 가부시키가이샤 증착 조성물의 제조방법, 증착 조성물 및 반사방지막을갖는 광학부품의 제조방법
KR100553010B1 (ko) * 2000-11-13 2006-02-16 호야 가부시키가이샤 증착 조성물, 그것을 이용한 반사방지막의 형성방법 및광학부재
US7101616B2 (en) 2001-09-11 2006-09-05 3M Innovative Properties Company Smudge resistant nanocomposite hardcoats and methods for making same
US7304112B2 (en) 2004-10-01 2007-12-04 3M Innovative Properties Company Azlactone telechelic polymer
US7332546B2 (en) 2004-10-01 2008-02-19 3M Innovative Properties Company Ring-opened azlactone telechelic polymer
WO2009023169A1 (fr) * 2007-08-10 2009-02-19 Nano Terra Inc. Revêtements structurés à résistance aux traces et procédés pour les réaliser et les utiliser
US7496255B2 (en) 2000-03-05 2009-02-24 3M Innovative Properties Company Radiation-transmissive films on glass articles
US20200032080A1 (en) * 2016-09-28 2020-01-30 Posco Solution composition for surface treatment of steel sheet and surface-treated steel sheet using same
CN113433603A (zh) * 2018-06-29 2021-09-24 唯亚威通讯技术有限公司 具有功能分子的光学器件
CN114649195A (zh) * 2022-03-10 2022-06-21 西安应用光学研究所 一种光学基底表面ito薄膜的高效去除方法
CN115260762A (zh) * 2022-09-02 2022-11-01 乌镇实验室 聚醚酰亚胺介电复合材料及其制备方法、应用

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100888563B1 (ko) * 2008-01-16 2009-03-12 천광조명 주식회사 고반사율을 갖는 고천정 반사판

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60163001A (ja) * 1984-02-03 1985-08-24 Asahi Glass Co Ltd 合成樹脂製レンズ
JPS6151101A (ja) * 1984-08-21 1986-03-13 Toray Ind Inc 被覆透明導電パネル
JPH03145602A (ja) * 1989-11-01 1991-06-20 Seiko Epson Corp 積層体およびその製造方法
WO1996023243A1 (fr) * 1995-01-23 1996-08-01 Essilor International Compagnie Generale D'optique Procede conferant une resistance a l'impact a des lentilles oculaires en plastique, composition utilisee a cet effet et lentilles ainsi traitees
JPH08295846A (ja) * 1995-03-01 1996-11-12 Seiko Epson Corp コーティング用組成物および積層体

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60163001A (ja) * 1984-02-03 1985-08-24 Asahi Glass Co Ltd 合成樹脂製レンズ
JPS6151101A (ja) * 1984-08-21 1986-03-13 Toray Ind Inc 被覆透明導電パネル
JPH03145602A (ja) * 1989-11-01 1991-06-20 Seiko Epson Corp 積層体およびその製造方法
WO1996023243A1 (fr) * 1995-01-23 1996-08-01 Essilor International Compagnie Generale D'optique Procede conferant une resistance a l'impact a des lentilles oculaires en plastique, composition utilisee a cet effet et lentilles ainsi traitees
JPH08295846A (ja) * 1995-03-01 1996-11-12 Seiko Epson Corp コーティング用組成物および積層体

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Section Ch Week 8540, Derwent World Patents Index; Class A28, AN 85-246682, XP002078489 *
DATABASE WPI Section Ch Week 8617, Derwent World Patents Index; Class A85, AN 86-109331, XP002078490 *
DATABASE WPI Section Ch Week 9704, Derwent World Patents Index; Class A14, AN 97-038134, XP002078488 *
PATENT ABSTRACTS OF JAPAN vol. 015, no. 372 (P - 1254) 19 September 1991 (1991-09-19) *

Cited By (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001048095A1 (fr) * 1999-12-28 2001-07-05 Dsm N.V. Composition photodurcissable et produits durcis
US7496255B2 (en) 2000-03-05 2009-02-24 3M Innovative Properties Company Radiation-transmissive films on glass articles
US6749813B1 (en) 2000-03-05 2004-06-15 3M Innovative Properties Company Fluid handling devices with diamond-like films
KR100553010B1 (ko) * 2000-11-13 2006-02-16 호야 가부시키가이샤 증착 조성물, 그것을 이용한 반사방지막의 형성방법 및광학부재
KR100496557B1 (ko) * 2000-11-30 2005-06-22 호야 가부시키가이샤 증착 조성물의 제조방법, 증착 조성물 및 반사방지막을갖는 광학부품의 제조방법
US6458462B1 (en) 2000-12-13 2002-10-01 3M Innovative Properties Company Sporting goods having a ceramer coating
EP1384736A4 (fr) * 2001-03-21 2004-07-21 Hoya Corp Objets moules transparents, element optique, lentilles plastiques, et leurs procedes de production
EP1283107B1 (fr) * 2001-07-17 2012-04-18 Lintec Corporation Feuille avec un revêtement dur
EP1283107A2 (fr) 2001-07-17 2003-02-12 LINTEC Corporation Feuille avec un revêtement dur
US7101616B2 (en) 2001-09-11 2006-09-05 3M Innovative Properties Company Smudge resistant nanocomposite hardcoats and methods for making same
US7932325B2 (en) 2004-10-01 2011-04-26 3M Innovative Properties Company Azlactone telechelic polymer
US7642321B2 (en) 2004-10-01 2010-01-05 3M Innovative Properties Company Ring-opened azlactone telechelic polymer
US7649054B2 (en) 2004-10-01 2010-01-19 3M Innovative Properties Company Azlactone telechelic polymer
US7304112B2 (en) 2004-10-01 2007-12-04 3M Innovative Properties Company Azlactone telechelic polymer
US7332546B2 (en) 2004-10-01 2008-02-19 3M Innovative Properties Company Ring-opened azlactone telechelic polymer
WO2009023169A1 (fr) * 2007-08-10 2009-02-19 Nano Terra Inc. Revêtements structurés à résistance aux traces et procédés pour les réaliser et les utiliser
US20200032080A1 (en) * 2016-09-28 2020-01-30 Posco Solution composition for surface treatment of steel sheet and surface-treated steel sheet using same
US11939489B2 (en) * 2016-09-28 2024-03-26 Posco Co., Ltd Solution composition for surface treatment of steel sheet and surface-treated steel sheet using same
CN113433603A (zh) * 2018-06-29 2021-09-24 唯亚威通讯技术有限公司 具有功能分子的光学器件
CN113433603B (zh) * 2018-06-29 2023-05-09 唯亚威通讯技术有限公司 具有功能分子的光学器件
CN114649195A (zh) * 2022-03-10 2022-06-21 西安应用光学研究所 一种光学基底表面ito薄膜的高效去除方法
CN115260762A (zh) * 2022-09-02 2022-11-01 乌镇实验室 聚醚酰亚胺介电复合材料及其制备方法、应用
CN115260762B (zh) * 2022-09-02 2023-11-21 乌镇实验室 聚醚酰亚胺介电复合材料及其制备方法、应用

Also Published As

Publication number Publication date
CA2318900A1 (fr) 1999-07-29
JP2002501118A (ja) 2002-01-15
AU7712498A (en) 1999-08-09
EP1051645A1 (fr) 2000-11-15
KR20010034387A (ko) 2001-04-25

Similar Documents

Publication Publication Date Title
WO1999038034A1 (fr) Revetements conferant une adherence amelioree a des matieres de revetement optiquement fonctionnelles
US6261700B1 (en) Ceramer containing a brominated polymer and inorganic oxide particles
EP1187881B1 (fr) Compositions de ceramere et cerameres antistatiques resistant a l'abrasion obtenues a partir de celles-ci
AU744976B2 (en) Ceramer containing a brominated polymer and inorganic oxide particles
KR101529355B1 (ko) 폴리(알킬렌 옥사이드) 반복 단위를 갖는 퍼플루오로폴리에테르 중합체를 포함하는 하드코트
KR101009821B1 (ko) 반사방지 코팅 조성물, 반사방지 필름 및 이의 제조방법
TWI518156B (zh) 抗反射及抗炫塗佈組成物、抗反射及抗炫薄膜以及其製備方法
EP1194931B1 (fr) Compositions cerameres aqueuses et cerameres antistatiques resistants a l'abrasion obtenus a partir desdites compositions
EP1471120B1 (fr) Composition de revêtement protectrice, article revêtu et stratifie multicouches
JP4590705B2 (ja) 反射防止積層体
US20080176973A1 (en) Solar control multilayer film
KR20100080788A (ko) 표면 개질된 고굴절률 나노입자를 포함하는 자기-조립 반사방지 코팅
CN104837908A (zh) 纳米结构化材料及其制备方法
WO2012005542A2 (fr) Film antiréfléchissant et procédé pour fabriquer celui-ci
KR20140015443A (ko) 입자 크기가 큰 건식 실리카를 포함하는 반사 방지 필름
JP2009533535A (ja) 硬化性フルオロアルキルシリコーン組成物
US20080057262A1 (en) Low-Reflection Material
JP4736234B2 (ja) 反射防止積層体の製造方法
JP2020510563A (ja) 疎水性シランを含むコーティング及び物品
JP4747421B2 (ja) 反射防止積層体
JP2002513839A (ja) 耐摩耗性および防汚性のあるセラマー組成物
JP4649690B2 (ja) 反射防止積層体およびその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref document number: 2318900

Country of ref document: CA

Ref country code: CA

Ref document number: 2318900

Kind code of ref document: A

Format of ref document f/p: F

WWE Wipo information: entry into national phase

Ref document number: 1020007008142

Country of ref document: KR

Ref document number: 77124/98

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 1998925100

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1998925100

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1020007008142

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1998925100

Country of ref document: EP

WWR Wipo information: refused in national office

Ref document number: 1020007008142

Country of ref document: KR