WO1999052972A1 - Composition pour scellage pelable en polyolefine et couche de scellement - Google Patents

Composition pour scellage pelable en polyolefine et couche de scellement Download PDF

Info

Publication number
WO1999052972A1
WO1999052972A1 PCT/US1999/008320 US9908320W WO9952972A1 WO 1999052972 A1 WO1999052972 A1 WO 1999052972A1 US 9908320 W US9908320 W US 9908320W WO 9952972 A1 WO9952972 A1 WO 9952972A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
polymer
layer
weight percent
heat seal
Prior art date
Application number
PCT/US1999/008320
Other languages
English (en)
Other versions
WO1999052972A9 (fr
Inventor
Timothy J. Pope
Laura K. Mergenhagen
Original Assignee
The Dow Chemical Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by The Dow Chemical Company filed Critical The Dow Chemical Company
Priority to AU36469/99A priority Critical patent/AU3646999A/en
Publication of WO1999052972A1 publication Critical patent/WO1999052972A1/fr
Publication of WO1999052972A9 publication Critical patent/WO1999052972A9/fr

Abstract

La présente invention concerne une composition de scellage à l'oléfine et une couche de scellement présentant des caractéristiques de scellement à chaud permettant une ouverture facile. La composition de l'invention et la couche de scellement sont faites d'au moins un polymère d'éthylène, et pour au moins 25 % de la masse de la composition ou de la couche, d'au moins un polymère de polybutylène, d'un additif silicique ou calcique, d'un agent glissant, et de quantités éventuelles d'un polymère d'éthylène intervenant comme résine vecteur d'additif. Le polymère d'éthylène préféré est un polymère d'éthylène à ramifications homogènes, le polymère de polybutylène présentant un faible degré de cristallinité, ou une teneur élevée en comonomères. En tant que couche de scellement, la composition fait preuve d'excellentes propriétés de tenue à chaud des soudures, d'un coefficient de frottement relativement bas et de propriétés d'obturation particulièrement remarquables. En effet, la résistance du thermoscellage se situe dans la plage des 270 à 640 g/cm (1,5 à 3,5 livres par pouce) de largeur pour 100 °C, l'écart moyen statistique de la résistance du thermoscellage entre 100 °C et 130 °C n'excédant pas 16,5 %. Cette composition convient pour des applications nécessitant un scellage pelable constant et stable dans de larges fenêtres de scellage comme dans le cas notamment des garnitures intérieures des boîtes de céréales.
PCT/US1999/008320 1998-04-15 1999-04-15 Composition pour scellage pelable en polyolefine et couche de scellement WO1999052972A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU36469/99A AU3646999A (en) 1998-04-15 1999-04-15 Peelable-seal polyolefin composition and sealant layer

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US8185098P 1998-04-15 1998-04-15
US60/081,850 1998-04-15

Publications (2)

Publication Number Publication Date
WO1999052972A1 true WO1999052972A1 (fr) 1999-10-21
WO1999052972A9 WO1999052972A9 (fr) 2000-01-27

Family

ID=22166799

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1999/008320 WO1999052972A1 (fr) 1998-04-15 1999-04-15 Composition pour scellage pelable en polyolefine et couche de scellement

Country Status (3)

Country Link
AR (1) AR019067A1 (fr)
AU (1) AU3646999A (fr)
WO (1) WO1999052972A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1572455A2 (fr) * 2002-11-22 2005-09-14 Brpp, Llc Barriere amelioree pour la conservation de saveur
WO2006019921A1 (fr) * 2004-07-15 2006-02-23 E.I. Dupont De Nemours And Company Composition comprenant des copolymères d'éthylène et des polyoléfines
US7871696B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US7871697B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
WO2012129045A1 (fr) 2011-03-18 2012-09-27 The Procter & Gamble Company Pellicules polymères multicouches et leurs procédés de fabrication
WO2013172978A1 (fr) * 2012-05-18 2013-11-21 Toray Plastics (America), Inc. Emballage de céréales en polyester sans migration
US8642144B2 (en) 2008-05-28 2014-02-04 Bemis Company, Inc. Innerliner with nylon skin layer
WO2015178927A1 (fr) * 2014-05-23 2015-11-26 Bemis Company, Inc. Emballage pelable
EP2346930B1 (fr) * 2008-10-01 2017-12-06 Dow Global Technologies LLC Films barrière et leur procédé de fabrication et d'utilisation
WO2018226582A1 (fr) * 2017-06-09 2018-12-13 Dow Global Technologies Llc Compositions à base d'éthylène à faible coefficient de frottement
CN109265594A (zh) * 2017-07-17 2019-01-25 中国石油天然气股份有限公司 乙丙丁三元共聚聚丙烯及其制备方法和应用
US10287077B2 (en) 2010-02-26 2019-05-14 Intercontinental Great Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
US11338563B2 (en) * 2017-06-09 2022-05-24 Dow Global Technologies Llc Multilayer films and laminates containing slip agents

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9232808B2 (en) 2007-06-29 2016-01-12 Kraft Foods Group Brands Llc Processed cheese without emulsifying salts
EP2539414A1 (fr) 2010-02-26 2013-01-02 Kraft Foods Global Brands LLC Emballage refermable utilisant un adhésif à faible adhérence
US9533472B2 (en) 2011-01-03 2017-01-03 Intercontinental Great Brands Llc Peelable sealant containing thermoplastic composite blends for packaging applications

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4795767A (en) * 1987-09-30 1989-01-03 Union Carbide Corporation Can carrier composition
WO1996012762A1 (fr) * 1994-10-21 1996-05-02 The Dow Chemical Company Compositions de polyolefines a forte resistance a la chaleur, faible degagement d'hexane et module d'elasticite controlable
WO1997048554A1 (fr) * 1996-06-21 1997-12-24 The Dow Chemical Company Compositions d'etancheite et couches de scellage detachables

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4795767A (en) * 1987-09-30 1989-01-03 Union Carbide Corporation Can carrier composition
WO1996012762A1 (fr) * 1994-10-21 1996-05-02 The Dow Chemical Company Compositions de polyolefines a forte resistance a la chaleur, faible degagement d'hexane et module d'elasticite controlable
WO1997048554A1 (fr) * 1996-06-21 1997-12-24 The Dow Chemical Company Compositions d'etancheite et couches de scellage detachables

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1572455A4 (fr) * 2002-11-22 2007-06-27 Brpp Llc Barriere amelioree pour la conservation de saveur
EP1572455A2 (fr) * 2002-11-22 2005-09-14 Brpp, Llc Barriere amelioree pour la conservation de saveur
US7235306B2 (en) 2002-11-22 2007-06-26 Brpp, Llc Flavor barrier
JP2008506556A (ja) * 2004-07-15 2008-03-06 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー エチレンコポリマー及びポリオレフィンを含む組成物
AU2005275079B2 (en) * 2004-07-15 2010-12-09 E.I. Dupont De Nemours And Company Composition comprising ethylene copolymers and polyolefins
WO2006019921A1 (fr) * 2004-07-15 2006-02-23 E.I. Dupont De Nemours And Company Composition comprenant des copolymères d'éthylène et des polyoléfines
US7871696B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US7871697B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US8110286B2 (en) 2006-11-21 2012-02-07 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US8470397B2 (en) 2006-11-21 2013-06-25 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
CN103213756A (zh) * 2006-11-21 2013-07-24 卡夫食品环球品牌有限责任公司 包装膜中可剥离的复合热塑性密封剂
CN103213756B (zh) * 2006-11-21 2015-07-15 洲际大品牌有限责任公司 包装膜中可剥离的复合热塑性密封剂
US8642144B2 (en) 2008-05-28 2014-02-04 Bemis Company, Inc. Innerliner with nylon skin layer
EP2346930B1 (fr) * 2008-10-01 2017-12-06 Dow Global Technologies LLC Films barrière et leur procédé de fabrication et d'utilisation
US10287077B2 (en) 2010-02-26 2019-05-14 Intercontinental Great Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
WO2012129045A1 (fr) 2011-03-18 2012-09-27 The Procter & Gamble Company Pellicules polymères multicouches et leurs procédés de fabrication
WO2013172978A1 (fr) * 2012-05-18 2013-11-21 Toray Plastics (America), Inc. Emballage de céréales en polyester sans migration
WO2015178927A1 (fr) * 2014-05-23 2015-11-26 Bemis Company, Inc. Emballage pelable
US10857754B2 (en) 2014-05-23 2020-12-08 Bemis Company, Inc. Peelable package
WO2018226582A1 (fr) * 2017-06-09 2018-12-13 Dow Global Technologies Llc Compositions à base d'éthylène à faible coefficient de frottement
CN110709462A (zh) * 2017-06-09 2020-01-17 陶氏环球技术有限责任公司 低摩擦系数的乙烯类组合物
US11338563B2 (en) * 2017-06-09 2022-05-24 Dow Global Technologies Llc Multilayer films and laminates containing slip agents
US11466147B2 (en) 2017-06-09 2022-10-11 Dow Global Technologies Llc Low coefficient of friction ethylene-based compositions
CN110709462B (zh) * 2017-06-09 2023-03-31 陶氏环球技术有限责任公司 低摩擦系数的乙烯类组合物
CN109265594A (zh) * 2017-07-17 2019-01-25 中国石油天然气股份有限公司 乙丙丁三元共聚聚丙烯及其制备方法和应用
CN109265594B (zh) * 2017-07-17 2021-07-30 中国石油天然气股份有限公司 乙丙丁三元共聚聚丙烯及其制备方法和应用

Also Published As

Publication number Publication date
WO1999052972A9 (fr) 2000-01-27
AR019067A1 (es) 2001-12-26
AU3646999A (en) 1999-11-01

Similar Documents

Publication Publication Date Title
US5874139A (en) Multilayer polyolefin with balanced sealant properties
AU739746B2 (en) Polyolefin compositions with balanced sealant properties and improved modulus and method for same
AU771820B2 (en) Polymer compositions which exhibit high hot tack
CA2231449C (fr) Nouvelles enveloppes pour le conditionnement de matieres fluides
EP0665863A1 (fr) Film d'emballage
WO1999052972A1 (fr) Composition pour scellage pelable en polyolefine et couche de scellement
JPH0957916A (ja) 共押出フィルム
US20010028929A1 (en) Films having improved sealing properties
US6228201B1 (en) Pinhole-resistant extrusion method
WO1998029249A1 (fr) Films ayant de meilleures proprietes d'etancheification
WO1999051433A1 (fr) Composition adhesive polymere destinee aux interpolymeres de polychlorure de vinylidene
CA2350962A1 (fr) Film multicouche en polyolefine comprenant une couche non externe de polypropylene syndiotactique
MXPA99004434A (en) Polyolefin compositions with balanced sealant properties and improved modulus and method for same
AU1193202A (en) Polyolefin compositions with balanced sealant properties and improved modulus and method for same
CA2341390A1 (fr) Emballages contenant des liquides a etancheite amelioree

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
AK Designated states

Kind code of ref document: C2

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: C2

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

COP Corrected version of pamphlet

Free format text: PAGES 55-57, DESCRIPTION, REPLACED BY NEW PAGES 55-57; PAGES 1/21-21/21; DRAWINGS, REPLACED BY NEW PAGES 1/18-18/18; DUE TO LATE TRANSMITTAL BY THE RECEIVING OFFICE

NENP Non-entry into the national phase

Ref country code: KR

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase