WO1998052995A1 - Procede servant a preparer une macromolecule a chaine ramifiee, macromolecule a chaine ramifiee et ses utilisations - Google Patents

Procede servant a preparer une macromolecule a chaine ramifiee, macromolecule a chaine ramifiee et ses utilisations Download PDF

Info

Publication number
WO1998052995A1
WO1998052995A1 PCT/NL1998/000284 NL9800284W WO9852995A1 WO 1998052995 A1 WO1998052995 A1 WO 1998052995A1 NL 9800284 W NL9800284 W NL 9800284W WO 9852995 A1 WO9852995 A1 WO 9852995A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
type
isocyanate
process according
macromolecule
Prior art date
Application number
PCT/NL1998/000284
Other languages
English (en)
Inventor
Rudolfus Antonius Theodorus Maria Van Benthem
Johan Franz Gradus Antonius Jansen
Dirk Armand Wim Stanssens
Original Assignee
Dsm N.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dsm N.V. filed Critical Dsm N.V.
Priority to AU76766/98A priority Critical patent/AU7676698A/en
Publication of WO1998052995A1 publication Critical patent/WO1998052995A1/fr

Abstract

L'invention concerne un procédé servant à préparer une molécule à chaîne ramifiée et consistant à (a) effectuer la réaction d'un noyau moléculaire avec un composé de premier type contenant un groupe isocyanate primaire et un groupe isocyanate tertiaire; (b) effectuer la réaction du produit obtenu avec un composé de deuxième type contenant un premier groupe réactif, dont on peut effectuer la réaction avec un isocyanate tertiaire, et un ou plusieurs groupes réagissant avec un isocyanate primaire, ainsi qu'avec un isocyanate tertiaire dans une mesure moindre que le premier groupe réactif, ladite réaction étant suivie par l'exécution alternée des étapes (c) et (b); (c) effectuer la réaction du produit obtenu à l'étape (b) avec un composé de premier type. L'invention concerne également des macromolécules pouvant être obtenues au moyen de ce procédé et leur utilisation.
PCT/NL1998/000284 1997-05-21 1998-05-18 Procede servant a preparer une macromolecule a chaine ramifiee, macromolecule a chaine ramifiee et ses utilisations WO1998052995A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU76766/98A AU7676698A (en) 1997-05-21 1998-05-18 Method for the production of a branched macromolecule, the branched macromolecule and uses thereof

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
NL1006097 1997-05-21
NL1006097A NL1006097C2 (nl) 1997-05-21 1997-05-21 Werkwijze voor het vervaardigen van een vertakt macromolecule, het vertakte macromolecule en toepassingen van het vertakte macromolecule.

Publications (1)

Publication Number Publication Date
WO1998052995A1 true WO1998052995A1 (fr) 1998-11-26

Family

ID=19765002

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/NL1998/000284 WO1998052995A1 (fr) 1997-05-21 1998-05-18 Procede servant a preparer une macromolecule a chaine ramifiee, macromolecule a chaine ramifiee et ses utilisations

Country Status (3)

Country Link
AU (1) AU7676698A (fr)
NL (1) NL1006097C2 (fr)
WO (1) WO1998052995A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1026185A1 (fr) * 1999-02-04 2000-08-09 Basf Aktiengesellschaft Dendrimères et polyuréthanes hautement ramifiés
EP1167413A1 (fr) * 2000-06-23 2002-01-02 Basf Aktiengesellschaft Produits de polyaddition de polyisocyanates ayant une fonctionnalité élevée
US7176271B2 (en) 2002-02-06 2007-02-13 Basf Aktiengesellschaft Method for the production of highly functional, highly branched polyureas
WO2007107478A1 (fr) * 2006-03-22 2007-09-27 Basf Se Substrat enduit de polyurethanne ramifie pour procede d'impression electrophotographique
US7645855B2 (en) 2003-11-04 2010-01-12 Basf Aktiengesellschaft Highly functional, highly branched polyureas

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19524045A1 (de) * 1995-07-01 1997-01-02 Basf Ag Hochfunktionalisierte Polyurethane
WO1997036857A1 (fr) * 1996-04-02 1997-10-09 University Of South Florida Procede pour utiliser des liaisons isocyanate pour former des polymeres a multicouches superposees

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19524045A1 (de) * 1995-07-01 1997-01-02 Basf Ag Hochfunktionalisierte Polyurethane
WO1997036857A1 (fr) * 1996-04-02 1997-10-09 University Of South Florida Procede pour utiliser des liaisons isocyanate pour former des polymeres a multicouches superposees

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1026185A1 (fr) * 1999-02-04 2000-08-09 Basf Aktiengesellschaft Dendrimères et polyuréthanes hautement ramifiés
KR100569047B1 (ko) * 1999-02-04 2006-04-10 바스프 악티엔게젤샤프트 수지상 및 고도로 분지된 폴리우레탄
EP1167413A1 (fr) * 2000-06-23 2002-01-02 Basf Aktiengesellschaft Produits de polyaddition de polyisocyanates ayant une fonctionnalité élevée
US6632914B2 (en) 2000-06-23 2003-10-14 Basf Aktiengesellschaft Polyfunctional polyisocyanate polyadducts
US7176271B2 (en) 2002-02-06 2007-02-13 Basf Aktiengesellschaft Method for the production of highly functional, highly branched polyureas
US7645855B2 (en) 2003-11-04 2010-01-12 Basf Aktiengesellschaft Highly functional, highly branched polyureas
WO2007107478A1 (fr) * 2006-03-22 2007-09-27 Basf Se Substrat enduit de polyurethanne ramifie pour procede d'impression electrophotographique

Also Published As

Publication number Publication date
NL1006097C2 (nl) 1998-11-25
AU7676698A (en) 1998-12-11

Similar Documents

Publication Publication Date Title
WO2015173110A1 (fr) Catalyseurs pour la synthèse de composés oxazolidinone
NZ235503A (en) Ring opening polymerisation of lactones and lactides using yttrium and/or rare earth metal compounds as catalysts; catalysts, films and coated articles
WO2010043354A1 (fr) Nouveaux catalyseurs pour la reaction entre un isocyanate et un alcool
CN111282597B (zh) 一种催化剂及其制备方法和应用、环状二氧化碳基聚碳酸酯及其制备方法
US20180009933A1 (en) Cyclic dynamic polyureas for polymeric urea processing
US20110046301A1 (en) Synthesis of urethanes and polyurethanes catalysed by carbenes
US20120184706A1 (en) Method for synthesizing polyesters in an acidic ionic liquid medium
CN116283667B (zh) 一种功能型异氰酸酯交联剂及其制备方法
EP3194461B1 (fr) Polymère organique durcissable comprenant au moins une unité d'acylurée, sa préparation et son utilisation
WO1998052995A1 (fr) Procede servant a preparer une macromolecule a chaine ramifiee, macromolecule a chaine ramifiee et ses utilisations
US2954365A (en) Process for the production of isocyanate polymerization products
EP2649083A1 (fr) Complexes de zirconium à base de carbène n-hétérocyclique, à utiliser dans la polymérisation de lactone par ouverture de cycle
SU944507A3 (ru) Способ получени катионоактивных полиуретанов
CN101921380A (zh) 一种聚丙烯酸酯-氨酯共聚物及其制备方法
JP6461016B2 (ja) トリアジンカルバマートの製造方法
CN110563941B (zh) 一种医药用生物可降解高分子材料聚己内酯的制备方法
CN113861234A (zh) 一种络合物催化剂及其制备方法和在制备聚碳酸酯中的应用
CN108641073B (zh) 一种三核有机亚锡金属催化剂及其制备方法和应用
WO2021064416A1 (fr) Procédé de formation d'un polymère conjugué
US4571310A (en) Process for preparing alkoxyphosphonitrile compounds
CN114249850B (zh) 一种丁二酮骨架含二苯甲基氟取代的二亚胺镍(ⅱ)催化剂及其制备方法和应用
CA3124279A1 (fr) Procede de preparation d'amides et d'esthers de l'acide 2-((2-hydroxypanoyl)oxy)propanoique
CA2087939A1 (fr) Methode servant a preparer des polyesters aromatiques
EP0177059B1 (fr) Polyisocyanates modifiés ayant la structure du biuret et procédé de préparation
CN116082260A (zh) 催化剂及其制备方法和脂肪族异氰酸酯聚合物的制备方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AU BA BB BG BR CA CN CU CZ EE GE HU ID IL IS JP KP KR LC LK LR LT LV MG MK MN MX NO NZ PL RO SG SI SK SL TR TT UA US UZ VN YU

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 1998550262

Format of ref document f/p: F

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载