WO1997037802A1 - Procede de granulation - Google Patents

Procede de granulation Download PDF

Info

Publication number
WO1997037802A1
WO1997037802A1 PCT/BE1997/000040 BE9700040W WO9737802A1 WO 1997037802 A1 WO1997037802 A1 WO 1997037802A1 BE 9700040 W BE9700040 W BE 9700040W WO 9737802 A1 WO9737802 A1 WO 9737802A1
Authority
WO
WIPO (PCT)
Prior art keywords
zone
flow
liquid
region
edge
Prior art date
Application number
PCT/BE1997/000040
Other languages
English (en)
Inventor
Paul Hippoliet Isidoor Kestens
Jan Hendrik Labuschagne
Johannes Hendrik Bothma
Stephanus Albertus Venter
Original Assignee
Consolidated Metallurgical Industries Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Consolidated Metallurgical Industries Limited filed Critical Consolidated Metallurgical Industries Limited
Priority to EP97915207A priority Critical patent/EP0909229A1/fr
Priority to AU22820/97A priority patent/AU2282097A/en
Publication of WO1997037802A1 publication Critical patent/WO1997037802A1/fr

Abstract

L'invention a trait à un procédé de production de métal de structure granuleuse, de matte, ou de matériau similaire. Ce procédé consiste à produire une source de matériau en fusion dans un réservoir, à préparer une plaque distributrice (26), pourvue d'au moins un rebord (32) et placée au-dessus d'une masse de liquide de refroidissement (12), puis à faire sortir le métal en fusion du réservoir, à le faire passer sur la plaque distributrice, à le faire s'écouler au-dessus du bord susmentionné et à le transférer dans la masse de liquide de refroidissement. Il est créé, de préférence, une zone de flux liquide dans la masse de liquide de refroidissement. Cette zone possède un premier secteur à vélocité prédéfinie et un autre secteur, au moins, à plus grande vélocité. On fait pénétrer le flux de métal en fusion dans le premier secteur de la zone avant de le laisser passer dans l'autre secteur.
PCT/BE1997/000040 1996-04-04 1997-04-03 Procede de granulation WO1997037802A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP97915207A EP0909229A1 (fr) 1996-04-04 1997-04-03 Procede de granulation
AU22820/97A AU2282097A (en) 1996-04-04 1997-04-03 Granulation method

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
ZA96/2726 1996-04-04
ZA962726 1996-04-04
ZA968995 1996-10-25
ZA96/8995 1996-10-25
ZA96/9637 1996-11-18
ZA969637 1996-11-18

Publications (1)

Publication Number Publication Date
WO1997037802A1 true WO1997037802A1 (fr) 1997-10-16

Family

ID=27420994

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/BE1997/000040 WO1997037802A1 (fr) 1996-04-04 1997-04-03 Procede de granulation

Country Status (4)

Country Link
EP (1) EP0909229A1 (fr)
CN (1) CN1219897A (fr)
AU (1) AU2282097A (fr)
WO (1) WO1997037802A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107119186B (zh) * 2017-04-28 2018-07-17 重庆市永川区益锐机械有限责任公司 液态铜锍的分级粒化设备

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR896046A (fr) * 1942-04-15 1945-02-09 Metallwerk Olsberg G M B H Procédé et appareil pour granuler les alliages métalliques, en particulier de grande viscosité
FR905767A (fr) * 1943-06-24 1945-12-13 Arbed Vereinigte Hu Ttenwerke Procédé de fabrication de grains ou morceaux de fer brut, et dispositif y relatif
US4192673A (en) * 1978-12-19 1980-03-11 Hyuga Smelting Co., Ltd. Method of manufacturing granulated ferronickel
EP0522844A2 (fr) * 1991-07-08 1993-01-13 Elkem A/S Procédé pour la granulation de métal fondu

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR896046A (fr) * 1942-04-15 1945-02-09 Metallwerk Olsberg G M B H Procédé et appareil pour granuler les alliages métalliques, en particulier de grande viscosité
FR905767A (fr) * 1943-06-24 1945-12-13 Arbed Vereinigte Hu Ttenwerke Procédé de fabrication de grains ou morceaux de fer brut, et dispositif y relatif
US4192673A (en) * 1978-12-19 1980-03-11 Hyuga Smelting Co., Ltd. Method of manufacturing granulated ferronickel
EP0522844A2 (fr) * 1991-07-08 1993-01-13 Elkem A/S Procédé pour la granulation de métal fondu

Also Published As

Publication number Publication date
CN1219897A (zh) 1999-06-16
AU2282097A (en) 1997-10-29
EP0909229A1 (fr) 1999-04-21

Similar Documents

Publication Publication Date Title
RU2036050C1 (ru) Способ гранулирования расплавленного металла
US4359434A (en) Process for granulating molten material
US4936375A (en) Continuous casting of ingots
US3669181A (en) Pouring apparatus with submerged deflector plates for continuous casting
KR102340801B1 (ko) 용융된 재료의 과립화를 위한 턴디쉬 배열체 및 노즐
CS238359B2 (en) Melted material drops hardening acceleration method and equipment for execution of this method
US3542351A (en) Spray refining
MX2011008947A (es) Produccion de particulas metalicas esfericas.
JPH11512150A (ja) 金属塊の製造
JP2703818B2 (ja) 溶融体を噴霧する方法及び該方法を使用する装置
CA1125964A (fr) Methode et appareillage pour la fabrication de poudre par granulation d'un metal fondu
US3908735A (en) Method and device for the continuous casting of killed steel with artificial wildness
WO1997037802A1 (fr) Procede de granulation
CA1136365A (fr) Methode d'extraction de granulats et de materiaux analogues, et dispositif pour la mise en oeuvre de ladite methode
WO2003106012A1 (fr) Procede et dispositif de granulation de metal en fusion
US5379989A (en) Tundish with improved flow control
NZ196765A (en) Refining molten metal using sparging gas
US3023454A (en) Hydraulic quenching and granulation of molten materials
RU2113317C1 (ru) Устройство для получения металлических гранул
JP7397499B2 (ja) タンディッシュに衝撃パッドを利用する溶融金属の鋳造方法
Forwald et al. Method for Granulating Molten Metal
JP2002146412A (ja) 溶融スラグ用樋
JPH0217733Y2 (fr)
JP3520640B2 (ja) 溶融金属中の非金属介在物除去方法
KR100485404B1 (ko) 박형슬라브를연속주조하기위한부분침수노즐

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 97194933.6

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AT AU AZ BA BB BG BR BY CA CH CN CU CZ CZ DE DE DK DK EE EE ES FI FI GB GE GH HU IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SK TJ TM TR TT UA UG US UZ VN YU AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1997915207

Country of ref document: EP

NENP Non-entry into the national phase

Ref document number: 97535682

Country of ref document: JP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1997915207

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: CA

WWW Wipo information: withdrawn in national office

Ref document number: 1997915207

Country of ref document: EP

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载