WO1997008260A1 - Film adhesif autocollant, antistatique et optiquement transparent - Google Patents

Film adhesif autocollant, antistatique et optiquement transparent Download PDF

Info

Publication number
WO1997008260A1
WO1997008260A1 PCT/US1996/007669 US9607669W WO9708260A1 WO 1997008260 A1 WO1997008260 A1 WO 1997008260A1 US 9607669 W US9607669 W US 9607669W WO 9708260 A1 WO9708260 A1 WO 9708260A1
Authority
WO
WIPO (PCT)
Prior art keywords
acrylate
vinyl
sensitive adhesive
antistatic
optically clear
Prior art date
Application number
PCT/US1996/007669
Other languages
English (en)
Inventor
James N. Kellen
Gustav Gutman
Richard J. Goetz
Original Assignee
Minnesota Mining And Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining And Manufacturing Company filed Critical Minnesota Mining And Manufacturing Company
Priority to AU65404/96A priority Critical patent/AU6540496A/en
Publication of WO1997008260A1 publication Critical patent/WO1997008260A1/fr

Abstract

Film adhésif autocollant, antistatique, pouvant être enlevé. Ce film se compose d'une base polymère souple et transparente portant, sur au moins l'une de ces faces, un mélange adhésif de microparticules non-susceptibles de charge triboélectrique. Ce mélange est constitué de microparticules conductrices, polymères, intrinsèquement collantes, dispersibles dans un solvant sans être solubles dans un tel solvant, et élastomères. Ces microparticules sont revêtues sur leur surface d'un matériau conducteur ionique réalisé à partir d'un polymère capable de former un électrolyte polymère, et au moins un sel ionique choisi dans le groupe constitué par les sels de métaux alcalins et les sels de métaux alcalino-terreux, ces microparticules ayant un diamètre moyen d'au moins un micromètre, et à partir d'un copolymère acrylique non particulaire. L'adhésif présente une adhésion à l'acier se situant entre environ 0,1 Newton/100 mm (N/100 mm) à environ 5 N/100 mm, et un indice de transmission optique d'au moins 80 % environ.
PCT/US1996/007669 1995-08-22 1996-07-11 Film adhesif autocollant, antistatique et optiquement transparent WO1997008260A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU65404/96A AU6540496A (en) 1995-08-22 1996-07-11 Optically clear antistatic pressure-sensitive adhesive film

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US261995P 1995-08-22 1995-08-22
US60/002,619 1995-08-22
US66150596A 1996-06-11 1996-06-11
US08/661,505 1996-06-11

Publications (1)

Publication Number Publication Date
WO1997008260A1 true WO1997008260A1 (fr) 1997-03-06

Family

ID=26670629

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/007669 WO1997008260A1 (fr) 1995-08-22 1996-07-11 Film adhesif autocollant, antistatique et optiquement transparent

Country Status (2)

Country Link
AU (1) AU6540496A (fr)
WO (1) WO1997008260A1 (fr)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999029795A1 (fr) * 1997-12-05 1999-06-17 Minnesota Mining And Manufacturing Company Film adhesif autocollant antistatique optiquement clair
EP1085567A1 (fr) * 1999-09-14 2001-03-21 Sony Chemicals Corporation CSV assemblage et materiel de connexion utilisé dans le meme
WO2001036558A3 (fr) * 1999-11-17 2002-01-10 3M Innovative Properties Co Adhesif rempli de particules organiques
WO2003011958A1 (fr) * 2001-08-02 2003-02-13 3M Innovative Properties Company Adhesifs autocollants antistatiques optiquement transparents
JP2006307238A (ja) * 2004-04-19 2006-11-09 Nitto Denko Corp 粘着剤組成物および粘着シート類
WO2006123638A1 (fr) * 2005-05-20 2006-11-23 Nitto Denko Corporation Composition d'adhesif sensible a la pression, feuille d'adhesif sensible a la pression, et film protecteur de surface
DE102005029722A1 (de) * 2005-06-24 2006-12-28 Tesa Ag Halogenfreie selbstklebende Schutzfolie
EP1802724A1 (fr) * 2004-10-21 2007-07-04 LG Chem, Ltd. Composition auto-adhesive acrylique a bonnes proprietes antistatiques
US7491758B2 (en) 2004-06-01 2009-02-17 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheet and surface protecting film
WO2009126532A2 (fr) * 2008-04-11 2009-10-15 3M Innovative Properties Company Feuille adhésive transparente et dispositif d’affichage d’image la comportant
US7658992B2 (en) * 2004-05-24 2010-02-09 Nitto Denko Corporation Surface protection film-attached optical film and image display
US7691925B2 (en) 2004-03-08 2010-04-06 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets and surface protecting film
US7799853B2 (en) 2005-09-05 2010-09-21 Nitto Denko Corporation Adhesive composition, adhesive sheet, and surface protective film
US7842742B2 (en) 2004-07-26 2010-11-30 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets, and surface protecting film
US9850395B2 (en) 2009-07-07 2017-12-26 Ak Steel Properties, Inc. Polymer coated metallic substrate and method for making
US10401988B2 (en) 2011-01-18 2019-09-03 Aevoe Corp. Touch screen protector
US10738172B2 (en) 2009-12-17 2020-08-11 3M Innovative Properties Company Display panel assembly and methods of making same

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995004356A1 (fr) * 1993-07-28 1995-02-09 Minnesota Mining And Manufacturing Company Microparticules conductrices et bandes autoadhesives fabriquees a partir de celles-ci
WO1996020983A1 (fr) * 1994-12-29 1996-07-11 Minnesota Mining And Manufacturing Company Rubans auto-adhesifs pour applications electroniques

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995004356A1 (fr) * 1993-07-28 1995-02-09 Minnesota Mining And Manufacturing Company Microparticules conductrices et bandes autoadhesives fabriquees a partir de celles-ci
WO1996020983A1 (fr) * 1994-12-29 1996-07-11 Minnesota Mining And Manufacturing Company Rubans auto-adhesifs pour applications electroniques

Cited By (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999029795A1 (fr) * 1997-12-05 1999-06-17 Minnesota Mining And Manufacturing Company Film adhesif autocollant antistatique optiquement clair
EP1085567A1 (fr) * 1999-09-14 2001-03-21 Sony Chemicals Corporation CSV assemblage et materiel de connexion utilisé dans le meme
US6903463B1 (en) 1999-09-14 2005-06-07 Sony Chemicals Corporation COG-assembly and connecting material to be used therein
WO2001036558A3 (fr) * 1999-11-17 2002-01-10 3M Innovative Properties Co Adhesif rempli de particules organiques
US6342561B1 (en) 1999-11-17 2002-01-29 3M Innovative Properties Company Organic particulate-filled adhesive
US6635704B2 (en) 1999-11-17 2003-10-21 3M Innovative Properties Company Organic particulate-filled adhesive
CN100351294C (zh) * 2001-08-02 2007-11-28 3M创新有限公司 光学透明和抗静电的压敏粘合剂
WO2003011958A1 (fr) * 2001-08-02 2003-02-13 3M Innovative Properties Company Adhesifs autocollants antistatiques optiquement transparents
KR100908941B1 (ko) * 2001-08-02 2009-07-22 쓰리엠 이노베이티브 프로퍼티즈 컴파니 광학적으로 투명한 대전방지 감압성 접착제
US7691925B2 (en) 2004-03-08 2010-04-06 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets and surface protecting film
JP2006307238A (ja) * 2004-04-19 2006-11-09 Nitto Denko Corp 粘着剤組成物および粘着シート類
US7658992B2 (en) * 2004-05-24 2010-02-09 Nitto Denko Corporation Surface protection film-attached optical film and image display
US7491758B2 (en) 2004-06-01 2009-02-17 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheet and surface protecting film
US7846999B2 (en) 2004-07-26 2010-12-07 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets, and surface protecting film
US7989525B2 (en) 2004-07-26 2011-08-02 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets, and surface protecting film
US7842742B2 (en) 2004-07-26 2010-11-30 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive sheets, and surface protecting film
EP1802724A1 (fr) * 2004-10-21 2007-07-04 LG Chem, Ltd. Composition auto-adhesive acrylique a bonnes proprietes antistatiques
EP1802724A4 (fr) * 2004-10-21 2007-10-17 Lg Chemical Ltd Composition auto-adhesive acrylique a bonnes proprietes antistatiques
US8404344B2 (en) * 2005-05-20 2013-03-26 Nitto Denko Corporation Pressure sensitive adhesive composition, pressure sensitive adhesive sheet and surface protective film
WO2006123638A1 (fr) * 2005-05-20 2006-11-23 Nitto Denko Corporation Composition d'adhesif sensible a la pression, feuille d'adhesif sensible a la pression, et film protecteur de surface
DE102005029722A1 (de) * 2005-06-24 2006-12-28 Tesa Ag Halogenfreie selbstklebende Schutzfolie
US7799853B2 (en) 2005-09-05 2010-09-21 Nitto Denko Corporation Adhesive composition, adhesive sheet, and surface protective film
WO2009126532A3 (fr) * 2008-04-11 2009-12-03 3M Innovative Properties Company Feuille adhésive transparente et dispositif d’affichage d’image la comportant
WO2009126532A2 (fr) * 2008-04-11 2009-10-15 3M Innovative Properties Company Feuille adhésive transparente et dispositif d’affichage d’image la comportant
US9850395B2 (en) 2009-07-07 2017-12-26 Ak Steel Properties, Inc. Polymer coated metallic substrate and method for making
US9951244B2 (en) 2009-07-07 2018-04-24 Ak Steel Properties, Inc. Polymer coated metallic substrate and method for making
US10683431B2 (en) 2009-07-07 2020-06-16 Ak Steel Properties, Inc. Polymer coated metallic substrate and method for making
US10738172B2 (en) 2009-12-17 2020-08-11 3M Innovative Properties Company Display panel assembly and methods of making same
US10401988B2 (en) 2011-01-18 2019-09-03 Aevoe Corp. Touch screen protector

Also Published As

Publication number Publication date
AU6540496A (en) 1997-03-19

Similar Documents

Publication Publication Date Title
US5508107A (en) Pressure-sensitive adhesive tapes for electronics applications
EP0711448B1 (fr) Microparticules conductrices et bandes autoadhesives fabriquees a partir de celles-ci
EP0758366B1 (fr) Bande adhesive autocollante, antistatique resistant a de hautes temperatures
US5885708A (en) Antistatic latex adhesives
WO1997008260A1 (fr) Film adhesif autocollant, antistatique et optiquement transparent
EP0444354B1 (fr) Microsphères creuses polymères d'acrylates ne contenant pas d'acide avec des cavités multiples
AU627607B2 (en) Pressure-sensitive adhesive comprising hollow tacky microspheres and macromonomer-containing binder copolymer
EP0563055B1 (fr) Reseaux polymeres a interpenetration auto-adhesifs
EP1007596B1 (fr) Composition adhesive imprimable par contact et procede de preparation
US5914186A (en) High temperature resistant antistatic pressure-sensitive adhesive tape
WO2009058630A2 (fr) Adhésifs thermiquement conducteurs et ruban adhésif les utilisant
KR20150061580A (ko) 도전성 점착 테이프, 전자 부재 및 점착제
US6017624A (en) Pressure sensitive adhesive film having differential adhesive properties and method of making the same
WO1999029795A1 (fr) Film adhesif autocollant antistatique optiquement clair
WO2005073332A1 (fr) Composition adhesive decollable
JP2003171560A (ja) 粘着付与樹脂エマルション及びその製造方法、並びに水系感圧性接着剤組成物
KR102659187B1 (ko) 점착 시트
JP2014224208A (ja) 粘着テープ
JP2003138235A (ja) 隠蔽性を有する粘着剤組成物及びそれを用いた粘着シート
CA2205848C (fr) Rubans auto-adhesifs pour applications electroniques
CA2187316C (fr) Bande adhesive autocollante, antistatique resistant a de hautes temperatures
JP2006008827A (ja) 粘着剤用複合樹脂組成物水性分散体及び粘着剤組成物

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BB BG BR BY CA CH CN CZ DE DK EE ES FI GB GE HU IS JP KE KG KP KR KZ LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载