WO1996025992A1 - Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers - Google Patents

Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers Download PDF

Info

Publication number
WO1996025992A1
WO1996025992A1 PCT/US1996/001891 US9601891W WO9625992A1 WO 1996025992 A1 WO1996025992 A1 WO 1996025992A1 US 9601891 W US9601891 W US 9601891W WO 9625992 A1 WO9625992 A1 WO 9625992A1
Authority
WO
WIPO (PCT)
Prior art keywords
passivated
matrix
chromatographic media
porous
monomer
Prior art date
Application number
PCT/US1996/001891
Other languages
English (en)
Other versions
WO1996025992A9 (fr
Inventor
Pierre Girot
Egisto Boschetti
Original Assignee
Biosepra, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Biosepra, Inc. filed Critical Biosepra, Inc.
Priority to AU49215/96A priority Critical patent/AU4921596A/en
Publication of WO1996025992A1 publication Critical patent/WO1996025992A1/fr
Publication of WO1996025992A9 publication Critical patent/WO1996025992A9/fr

Abstract

L'invention a pour objet des supports solides poreux modifiés et des procédés de préparation et d'utilisation de ces derniers. En particulier, l'invention concerne des supports poreux passivés qui sont caractérisés par une forte capacité de sorption réversible ne s'accompagnant sensiblement d'aucune adsorption non spécifique de biomolécules ni d'aucune interaction avec ces dernières. La passivation est effectuée au moyen d'un mélange de passivation comprenant un monomère principal, un agent de passivation comprenant de la polyéthylénimine et un agent de réticulation . Lors de la polymérisation, ce mélange se traduit par l'élimination sensible de l'interaction non spécifique avec les biomolécules indésirable.
PCT/US1996/001891 1995-02-22 1996-02-13 Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers WO1996025992A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU49215/96A AU4921596A (en) 1995-02-22 1996-02-13 Passivated porous polymer supports and methods for the preparation and use of same

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US394,014 1989-08-15
US39401495A 1995-02-22 1995-02-22

Publications (2)

Publication Number Publication Date
WO1996025992A1 true WO1996025992A1 (fr) 1996-08-29
WO1996025992A9 WO1996025992A9 (fr) 1997-01-16

Family

ID=23557184

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/001891 WO1996025992A1 (fr) 1995-02-22 1996-02-13 Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers

Country Status (2)

Country Link
AU (1) AU4921596A (fr)
WO (1) WO1996025992A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019213040A1 (fr) * 2018-04-30 2019-11-07 Nitto Denko Corporation Polymères d'affinité et procédés pour réduire les taux de purine dans des mélanges complexes
WO2022140437A1 (fr) * 2020-12-22 2022-06-30 California Institute Of Technology Membranes composites fonctionnelles pour chromatographie et catalyse

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4335017A (en) * 1975-12-15 1982-06-15 United Kingdom Atomic Energy Authority Composite materials comprising deformable xerogel within the pores of particulate rigid supports useful in chromatography
US5268097A (en) * 1992-06-19 1993-12-07 Sepracor Inc. Passivated and stabilized porous mineral oxide supports and method for the preparation and use of same

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4335017A (en) * 1975-12-15 1982-06-15 United Kingdom Atomic Energy Authority Composite materials comprising deformable xerogel within the pores of particulate rigid supports useful in chromatography
US5268097A (en) * 1992-06-19 1993-12-07 Sepracor Inc. Passivated and stabilized porous mineral oxide supports and method for the preparation and use of same

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019213040A1 (fr) * 2018-04-30 2019-11-07 Nitto Denko Corporation Polymères d'affinité et procédés pour réduire les taux de purine dans des mélanges complexes
WO2022140437A1 (fr) * 2020-12-22 2022-06-30 California Institute Of Technology Membranes composites fonctionnelles pour chromatographie et catalyse

Also Published As

Publication number Publication date
AU4921596A (en) 1996-09-11

Similar Documents

Publication Publication Date Title
US5906734A (en) Passivated porous polymer supports and methods for the preparation and use of same
US5393430A (en) Passivated and stabilized porous mineral oxide supports and methods for the preparation and use of same
US5445732A (en) Passivated porous polymer supports and methods for the preparation and use of same
US5470463A (en) Passivated porous supports and methods for the preparation and use of same
US5906747A (en) Separation of molecules from dilute solutions using composite chromatography media having high dynamic sorptive capacity at high flow rates
AU681590B2 (en) Passivated and stabilized porous supports and methods for the preparation and use of same
CA2049298C (fr) Materiaux a film pour la chromatographie
EP3570974B1 (fr) Milieu chromatographique multimodal pour la séparation de protéines
WO2012015379A1 (fr) Procédé de greffage pour améliorer la performance de phases stationnaires de chromatographie
WO1998033572A1 (fr) Procede d'adsorption/separation et support pour adsorption/separation
US20140263011A1 (en) Novel chromatographic media based on allylamine and its derivative for protein purification
JP5280604B2 (ja) 多孔性支持体の後修飾
AU5381700A (en) Process for making fluorinated polymer adsorbent particles
JP2005510593A5 (fr)
Hedhammar et al. Chromatographic methods for protein purification
EP1507808B1 (fr) Particules polymeres macroporeuses reticulees
WO1996025992A1 (fr) Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers
WO1996025992A9 (fr) Supports polymeres poreux passives et procedes de preparation et d'utilisation de ces derniers
Sakata et al. Chromatographic removal of host cell DNA from cellular products using columns packed with cationic copolymer beads
Svec Organic Polymer Support Materials
Svec University of California at Berkeley Berkeley, California
Lloyd et al. Polymers and their Application in Liquid Chromatography
EP1084150A1 (fr) Cationites carboxyliques et leurs procedes de fabrication

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AU AZ BB BG BR BY CA CN CZ EE FI GE HU IS JP KG KP KR KZ LK LR LS LT LV MD MG MK MN MX NO NZ PL RO RU SG SI SK TJ TM TR TT UA UZ VN AZ BY KG KZ RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
COP Corrected version of pamphlet

Free format text: PAGE 45,DESCRIPTION,REPLACED BY A NEW PAGE 45;PAGES 1/6-6/6,DRAWINGS,REPLACED BY NEW PAGES 1/5-5/5;DUE TO LATE TRANSMITTAL BY THE RECEIVING OFFICE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)