WO1996003232A1 - Appareil d'assemblage d'un materiau en feuille et assemblage obtenu - Google Patents

Appareil d'assemblage d'un materiau en feuille et assemblage obtenu Download PDF

Info

Publication number
WO1996003232A1
WO1996003232A1 PCT/US1994/008413 US9408413W WO9603232A1 WO 1996003232 A1 WO1996003232 A1 WO 1996003232A1 US 9408413 W US9408413 W US 9408413W WO 9603232 A1 WO9603232 A1 WO 9603232A1
Authority
WO
WIPO (PCT)
Prior art keywords
punch
sheet
segment
sheets
die
Prior art date
Application number
PCT/US1994/008413
Other languages
English (en)
Inventor
Xinrong Wu
Original Assignee
Btm Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Btm Corporation filed Critical Btm Corporation
Priority to AU75147/94A priority Critical patent/AU7514794A/en
Priority to EP94925111A priority patent/EP0783384B1/fr
Priority to PCT/US1994/008413 priority patent/WO1996003232A1/fr
Priority to JP8505700A priority patent/JPH10503427A/ja
Priority to DE69431490T priority patent/DE69431490T2/de
Priority to US08/530,202 priority patent/US5984563A/en
Publication of WO1996003232A1 publication Critical patent/WO1996003232A1/fr

Abstract

L'appareil de la présente invention servant à assembler un matériau en feuille est un pointeau profilé (38). Ce pointeau profilé (38) sert à renforcer un assemblage entre au moins deux feuilles de matériau (16 et 18), en créant un segment profilé (122) dans au moins une de ces feuilles de matériau. Pendant la formation de ce segment profilé (122), le matériau est déplacé sous l'effet d'une force vers un autre segment de matériau, qui est élargi vers l'extérieur afin de s'enclencher avec la feuille de matériau adjacente.
PCT/US1994/008413 1994-07-22 1994-07-22 Appareil d'assemblage d'un materiau en feuille et assemblage obtenu WO1996003232A1 (fr)

Priority Applications (6)

Application Number Priority Date Filing Date Title
AU75147/94A AU7514794A (en) 1994-07-22 1994-07-22 Apparatus for joining sheet material and joint formed therein
EP94925111A EP0783384B1 (fr) 1994-07-22 1994-07-22 Procede et appareil d'assemblage d'un materiau en feuille et assemblage obtenu
PCT/US1994/008413 WO1996003232A1 (fr) 1994-07-22 1994-07-22 Appareil d'assemblage d'un materiau en feuille et assemblage obtenu
JP8505700A JPH10503427A (ja) 1994-07-22 1994-07-22 薄板材の結合装置、およびこの装置で成形された結合部
DE69431490T DE69431490T2 (de) 1994-07-22 1994-07-22 Verfhren und gerät zum verbinden von blechen und darin hergestellte verbindung
US08/530,202 US5984563A (en) 1994-07-22 1994-07-22 Apparatus for joining sheet material and joint formed therein

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US1994/008413 WO1996003232A1 (fr) 1994-07-22 1994-07-22 Appareil d'assemblage d'un materiau en feuille et assemblage obtenu

Publications (1)

Publication Number Publication Date
WO1996003232A1 true WO1996003232A1 (fr) 1996-02-08

Family

ID=22242784

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1994/008413 WO1996003232A1 (fr) 1994-07-22 1994-07-22 Appareil d'assemblage d'un materiau en feuille et assemblage obtenu

Country Status (5)

Country Link
EP (1) EP0783384B1 (fr)
JP (1) JPH10503427A (fr)
AU (1) AU7514794A (fr)
DE (1) DE69431490T2 (fr)
WO (1) WO1996003232A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001000347A3 (fr) * 1999-06-25 2001-07-26 Tox Pressotechnik Gmbh Procede et dispositif pour assembler des plaques superposees
GB2369316A (en) * 2000-11-28 2002-05-29 Colin Maxwell Wade Ductile material lance joiner

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010099740A (ja) * 2009-12-28 2010-05-06 Ricoh Elemex Corp 板状部材の締結方法
JP2012035279A (ja) * 2010-08-04 2012-02-23 Asmo Co Ltd 金属部材のかしめ接合方法及び金属部材のかしめ接合装置
JP6505618B2 (ja) * 2016-02-05 2019-04-24 株式会社東芝 摩擦攪拌接合方法および接合体

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3828517A (en) * 1971-10-27 1974-08-13 V Johnson Metal layer rivetform and two layer assembly
JPS63177931A (ja) * 1987-01-16 1988-07-22 Masataka Matsumura 厚板に薄板をカシメで結合する方法とそのための装置
JPS63192524A (ja) * 1987-02-03 1988-08-09 Sharp Corp 金属板の接合装置
US4831704A (en) * 1985-09-14 1989-05-23 Eugen Rapp Apparatus for connecting thin plates
US4928370A (en) * 1988-03-19 1990-05-29 Eckold Gerd Juergen Tool set for connecting superposed sheet metal work pieces
US5051020A (en) * 1989-11-13 1991-09-24 Tech-Line Engineering Co. Leak proof joint
US5177861A (en) * 1980-09-08 1993-01-12 Btm Corporation Apparatus for joining sheet material
DE4317278A1 (de) * 1992-05-29 1993-12-02 Vaillant Joh Gmbh & Co Blechteil-Verbindung
US5305517A (en) * 1991-09-23 1994-04-26 Schleicher Louis C Apparatus for forming clinch joints
US5315743A (en) * 1990-05-18 1994-05-31 Tech-Line Engineering Co. Apparatus for forming a clinch joint

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5155897A (en) * 1989-11-13 1992-10-20 Tech-Line Engineering Co. Leak proof joint and method and apparatus for forming same
US5119966A (en) * 1990-09-14 1992-06-09 Rheem Manufacturing Company Simplified hinge apparatus and associated joining methods
SE9301097D0 (sv) * 1993-03-31 1993-03-31 Attexor Equipements Sa A method for joining together two or several overlaying sheet formed members, an apparatus for carrying out said method and a joint resulting from said method

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3828517A (en) * 1971-10-27 1974-08-13 V Johnson Metal layer rivetform and two layer assembly
US5177861A (en) * 1980-09-08 1993-01-12 Btm Corporation Apparatus for joining sheet material
US4831704A (en) * 1985-09-14 1989-05-23 Eugen Rapp Apparatus for connecting thin plates
JPS63177931A (ja) * 1987-01-16 1988-07-22 Masataka Matsumura 厚板に薄板をカシメで結合する方法とそのための装置
JPS63192524A (ja) * 1987-02-03 1988-08-09 Sharp Corp 金属板の接合装置
US4928370A (en) * 1988-03-19 1990-05-29 Eckold Gerd Juergen Tool set for connecting superposed sheet metal work pieces
US5051020A (en) * 1989-11-13 1991-09-24 Tech-Line Engineering Co. Leak proof joint
US5315743A (en) * 1990-05-18 1994-05-31 Tech-Line Engineering Co. Apparatus for forming a clinch joint
US5305517A (en) * 1991-09-23 1994-04-26 Schleicher Louis C Apparatus for forming clinch joints
DE4317278A1 (de) * 1992-05-29 1993-12-02 Vaillant Joh Gmbh & Co Blechteil-Verbindung

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP0783384A4 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001000347A3 (fr) * 1999-06-25 2001-07-26 Tox Pressotechnik Gmbh Procede et dispositif pour assembler des plaques superposees
GB2369316A (en) * 2000-11-28 2002-05-29 Colin Maxwell Wade Ductile material lance joiner
GB2369316B (en) * 2000-11-28 2003-01-15 Colin Maxwell Wade Ductile material lance joiner

Also Published As

Publication number Publication date
EP0783384A1 (fr) 1997-07-16
EP0783384A4 (fr) 1998-01-07
JPH10503427A (ja) 1998-03-31
DE69431490D1 (de) 2002-11-07
EP0783384B1 (fr) 2002-10-02
AU7514794A (en) 1996-02-22
DE69431490T2 (de) 2003-06-26

Similar Documents

Publication Publication Date Title
US5984563A (en) Apparatus for joining sheet material and joint formed therein
US5408735A (en) Method for forming a clinch joint
US5208973A (en) Apparatus for joining sheet material
US5051020A (en) Leak proof joint
US6338601B1 (en) Punch rivet, riveted joints produced with it, riveting tool and method of producing a riveted joint
US4400965A (en) Forming integral flanges in a sheet apparatus therefore
US5177861A (en) Apparatus for joining sheet material
US4459735A (en) Joining sheet metal
US5581860A (en) Apparatus for joining sheet material
CA1139742A (fr) Methode et dispositif de faconnage de rabats a meme une tole
US5027996A (en) Method of manufacturing a hollow shaft with internal swellings of revolution and shaft obtained by this method
US5155897A (en) Leak proof joint and method and apparatus for forming same
US5678970A (en) Self-coining fastener
GB2189175A (en) Apparatus for joining sheet material
US20030221474A1 (en) Method and apparatus for cold forging a trailer hitch receiving housing
GB2087284A (en) Apparatus for and method of joining sheet metal and sheet metal so joined
DE4404659C5 (de) Verfahren zum Herstellen einer Nietverbindung sowie Werkzeug zur Durchführung des Verfahrens
EP0783384B1 (fr) Procede et appareil d'assemblage d'un materiau en feuille et assemblage obtenu
GB2281527A (en) Cold forming method and apparatus
US20050056075A1 (en) Process for press forming metal tubes
US4399196A (en) Integral flanges in a sheet
AU2004238826A1 (en) Process for press forming metal tubes
JP3549607B2 (ja) 車両用ドアビームおよびその製造方法
JP5355874B2 (ja) パイプと被接合部材との接合方法
SU984598A1 (ru) Заготовка дл изготовлени полых цилиндрических изделий

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR BY CA CH CN CZ DE DK ES FI GB HU JP KP KR KZ LK LU LV MG MN MW NL NO NZ PL PT RO RU SD SE SK UA US UZ VN

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 08530202

Country of ref document: US

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 1994925111

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1994925111

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: CA

WWG Wipo information: grant in national office

Ref document number: 1994925111

Country of ref document: EP

点击 这是indexloc提供的php浏览器服务,不要输入任何密码和下载