WO1994015745A1 - Procede permettant d'enlever une bande dure d'une tige de forage et de recharger celle-ci - Google Patents
Procede permettant d'enlever une bande dure d'une tige de forage et de recharger celle-ci Download PDFInfo
- Publication number
- WO1994015745A1 WO1994015745A1 PCT/US1994/000257 US9400257W WO9415745A1 WO 1994015745 A1 WO1994015745 A1 WO 1994015745A1 US 9400257 W US9400257 W US 9400257W WO 9415745 A1 WO9415745 A1 WO 9415745A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- wire
- arc
- weld
- flux
- Prior art date
Abstract
Procédé permettant, par soudage à l'arc sous flux, de remplacer une bande dure par de la matière, pour conserver la résistance d'une tige de forage. Afin d'obtenir de meilleurs résultats, lors du rechargement de la tige de forage après que la bande dure a été enlevée, il est possible de commander certaines variables du processus, à savoir: les volts par fil, les ampères, la vitesse d'avance du fil (206), la vitesse de déplacement de la torche, la longueur libre de l'électrode et la hauteur de flux (204). On utilise, pour mettre en ÷uvre le procédé de soudage à l'arc sous flux, un fil à flux incorporé, en alliage comprenant du nickel, du molybdène et du chrome.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US259193A | 1993-01-04 | 1993-01-04 | |
US002,591 | 1993-01-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1994015745A1 true WO1994015745A1 (fr) | 1994-07-21 |
Family
ID=21701511
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1994/000257 WO1994015745A1 (fr) | 1993-01-04 | 1994-01-04 | Procede permettant d'enlever une bande dure d'une tige de forage et de recharger celle-ci |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO1994015745A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ITRM20090448A1 (it) * | 2009-09-02 | 2011-03-03 | Univ Catania | Dispositivo e metodo di controllo di una saldatrice, in particolare per una fabbricazione a mezzo di apporto di materiale |
US9869132B2 (en) | 2015-02-04 | 2018-01-16 | National Oilwell Varco, L.P. | Wellsite hardfacing with particle distribution and method of using same |
US9909395B2 (en) | 2015-09-21 | 2018-03-06 | National Oilwell DHT, L.P. | Wellsite hardfacing with distributed hard phase and method of using same |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3596041A (en) * | 1969-07-31 | 1971-07-27 | Stoody Co | Roller rebuilding system |
US3890482A (en) * | 1970-03-24 | 1975-06-17 | Gurtler Hebert & Co Inc | Apparatus for welding together substantially vertically extending pipe sections |
US3999036A (en) * | 1975-03-07 | 1976-12-21 | Viktor Alexeevich Muratov | Powder-cored strip electrode for surfacing with abrasion-resistant composite alloys |
US4214145A (en) * | 1979-01-25 | 1980-07-22 | Stoody Company | Mild steel, flux-cored electrode for arc welding |
US4432313A (en) * | 1982-05-27 | 1984-02-21 | Trw Inc. | Aluminum base material with hard facing deposit |
US4673796A (en) * | 1985-12-09 | 1987-06-16 | Weld Mold Company | Arc welding electrode |
US5192851A (en) * | 1988-02-05 | 1993-03-09 | Commonwealth Scientific And Industrial Research Organization And Welding Industries Limited | Cored electrode wires |
-
1994
- 1994-01-04 WO PCT/US1994/000257 patent/WO1994015745A1/fr active Application Filing
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3596041A (en) * | 1969-07-31 | 1971-07-27 | Stoody Co | Roller rebuilding system |
US3890482A (en) * | 1970-03-24 | 1975-06-17 | Gurtler Hebert & Co Inc | Apparatus for welding together substantially vertically extending pipe sections |
US3999036A (en) * | 1975-03-07 | 1976-12-21 | Viktor Alexeevich Muratov | Powder-cored strip electrode for surfacing with abrasion-resistant composite alloys |
US4214145A (en) * | 1979-01-25 | 1980-07-22 | Stoody Company | Mild steel, flux-cored electrode for arc welding |
US4432313A (en) * | 1982-05-27 | 1984-02-21 | Trw Inc. | Aluminum base material with hard facing deposit |
US4673796A (en) * | 1985-12-09 | 1987-06-16 | Weld Mold Company | Arc welding electrode |
US5192851A (en) * | 1988-02-05 | 1993-03-09 | Commonwealth Scientific And Industrial Research Organization And Welding Industries Limited | Cored electrode wires |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ITRM20090448A1 (it) * | 2009-09-02 | 2011-03-03 | Univ Catania | Dispositivo e metodo di controllo di una saldatrice, in particolare per una fabbricazione a mezzo di apporto di materiale |
WO2011027238A1 (fr) * | 2009-09-02 | 2011-03-10 | Universita' Degli Studi Di Catania | Dispositif et procédé de commande d'une machine à souder, notamment pour la fabrication par dépôt de matière |
US9869132B2 (en) | 2015-02-04 | 2018-01-16 | National Oilwell Varco, L.P. | Wellsite hardfacing with particle distribution and method of using same |
US9909395B2 (en) | 2015-09-21 | 2018-03-06 | National Oilwell DHT, L.P. | Wellsite hardfacing with distributed hard phase and method of using same |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO1994008747A1 (fr) | Inclinaison et enlevement de la bande dure pour tige de forage | |
EP1004389B1 (fr) | Dispositif de soudage à court-circuit | |
US4918283A (en) | Method of and apparatus for conducting plasma welding | |
US7397015B2 (en) | Metal cored electrode for open root pass welding | |
KR900007801B1 (ko) | 내마모성 표면재료를 부착시키는 용접장치 및 방법과 용접 비이드를 가진 금속기재(基材) | |
JP2912693B2 (ja) | アルミニウム基材加工物のガス金属アーク溶接方法 | |
MX2014006637A (es) | Método y sistema de soldadura de arco giratorio con electrodo negativo de cc. | |
US4162389A (en) | Welding apparatus | |
CA1254955A (fr) | Electrode tubulaire fourree, et methode de decoupage des metaux a l'arc electrique | |
US20020079301A1 (en) | High deposition submerged arc welding system | |
EP0691173B1 (fr) | Soudage a l'arc de plasma et instrument a cet effet | |
US5945014A (en) | Method of arc welding heavy steel plates | |
Holliday | Gas-metal arc welding | |
Cunat | The welding of stainless steels | |
WO1994015745A1 (fr) | Procede permettant d'enlever une bande dure d'une tige de forage et de recharger celle-ci | |
CN113070553B (zh) | 碳钢管道药芯焊丝全位置机动焊mag打底焊接工艺 | |
US3854028A (en) | High speed vertical electro-slag welding | |
KR102021893B1 (ko) | 자동 용접장치로 튜브시트 용접 시 제어알고리즘을 이용한 용착 제어 방법 | |
Reutzel | Advantages and disadvantages of arc and laser welding | |
JP7258110B1 (ja) | 溶接方法および開先構造 | |
KR102228164B1 (ko) | 그루브 폭 변동에 대한 적응제어 방법 | |
Allgood | Submerged arc welding | |
JPS5934477B2 (ja) | 溶接方法 | |
WO2024119060A1 (fr) | Chalumeau de soudage avec guide d'électrode à fil | |
Sivabalan | CHAPTER-2 SUBMERGED ARC WELDING (SAW)-AN OVERVIEW |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): CA |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
122 | Ep: pct application non-entry in european phase | ||
NENP | Non-entry into the national phase |
Ref country code: CA |