WO1993025596A1 - Resine pour revetements pulverulents s'utilisant en tant que couche de finissage dans l'industrie automobile et substrats revetus - Google Patents
Resine pour revetements pulverulents s'utilisant en tant que couche de finissage dans l'industrie automobile et substrats revetus Download PDFInfo
- Publication number
- WO1993025596A1 WO1993025596A1 PCT/NL1993/000120 NL9300120W WO9325596A1 WO 1993025596 A1 WO1993025596 A1 WO 1993025596A1 NL 9300120 W NL9300120 W NL 9300120W WO 9325596 A1 WO9325596 A1 WO 9325596A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin
- group
- acrylate
- unsaturated
- meth
- Prior art date
Abstract
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU45878/93A AU4587893A (en) | 1992-06-10 | 1993-06-07 | Resin for powder coatings for use as a top coat in the automotive industry and top-coated automotive substrates |
EP93916272A EP0644905A1 (fr) | 1992-06-10 | 1993-06-07 | Resine pour revetements pulverulents s'utilisant en tant que couche de finissage dans l'industrie automobile et substrats revetus |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
BE9200542 | 1992-06-10 | ||
BE9200542A BE1005993A3 (nl) | 1992-06-10 | 1992-06-10 | Hars voor poedercoatings toepasbaar in de automobielindustrie. |
Publications (2)
Publication Number | Publication Date |
---|---|
WO1993025596A1 true WO1993025596A1 (fr) | 1993-12-23 |
WO1993025596B1 WO1993025596B1 (fr) | 1994-02-17 |
Family
ID=3886317
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/NL1993/000120 WO1993025596A1 (fr) | 1992-06-10 | 1993-06-07 | Resine pour revetements pulverulents s'utilisant en tant que couche de finissage dans l'industrie automobile et substrats revetus |
Country Status (6)
Country | Link |
---|---|
EP (1) | EP0644905A1 (fr) |
CN (1) | CN1082083A (fr) |
AU (1) | AU4587893A (fr) |
BE (1) | BE1005993A3 (fr) |
TW (1) | TW233305B (fr) |
WO (1) | WO1993025596A1 (fr) |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1995023120A1 (fr) * | 1994-02-24 | 1995-08-31 | Dsm N.V. | Composition de resine durcissable liquide pour fibres optiques |
US5484850A (en) * | 1993-11-03 | 1996-01-16 | Basf Aktiengesellschaft | Copolymers crosslinkable by a free radical method |
US5527859A (en) * | 1993-11-03 | 1996-06-18 | Basf Aktiengesellschaft | Preparation of copolymers crosslinkable by a free radical method |
EP0796873A4 (fr) * | 1995-10-06 | 1999-11-03 | Nippon Catalytic Chem Ind | Sirop (meth)acrylique, procede d'elaboration de ce sirop et procede d'elaboration d'un materiau de moulage contenant un tel sirop |
WO2000008067A1 (fr) * | 1998-08-07 | 2000-02-17 | Basf Coatings Ag | Laque en poudre a structure de base fonctionnalisee, durcissable par un rayonnement haute energie et/ou par la chaleur |
WO2000008107A1 (fr) * | 1998-08-04 | 2000-02-17 | Basf Coatings Ag | Dispersion aqueuse contenant un vernis clair pulverulent |
EP1170109A1 (fr) * | 2000-07-05 | 2002-01-09 | Mitsubishi Rayon Co., Ltd. | Compositions photodurcissables, feuilles phodurcissables et objet moulé contenant celles-ci, procédés et production |
US6384102B1 (en) | 1996-10-25 | 2002-05-07 | Ucb S.A. | Powder compositions with semi-crystalline polyester and acrylic copolymer base containing ethylenically unsaturated groups |
WO2002018456A3 (fr) * | 2000-08-25 | 2002-05-30 | Johnson Polymer Inc | Procede de production de polymeres reactifs par post-modification en ligne et produits correspondants |
EP1443059A1 (fr) * | 2003-02-02 | 2004-08-04 | Solutia Italy S.r.l. | Résines pour compositions de revêtements sous forme de poudre |
WO2005108513A1 (fr) * | 2004-05-07 | 2005-11-17 | Cytec Surface Specialties, S.A. | Compositions de revetements en poudre peu brillantes durcissables par rayonnement |
US7122595B1 (en) | 1999-02-25 | 2006-10-17 | Basf Coatings Ag | Powder-slurry that can be hardened by actinic radiation or by thermal means, method for producing said slurry and use of the same |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE19544930C2 (de) * | 1995-12-01 | 1999-08-12 | Inventa Ag | Verfahren zur Herstellung von Pulverlacken sowie Verwendung des verfahrensgemäß hergestellten Pulverlacks |
TWI350999B (en) | 2006-06-29 | 2011-10-21 | Realtek Semiconductor Corp | Multimedia data processing apparatus |
CN112175486B (zh) * | 2020-09-30 | 2021-11-16 | 安徽省华安进出口有限公司 | 一种消光粉末涂料 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2163660A1 (de) * | 1971-12-21 | 1973-07-05 | Ford Werke Ag | Mit elektronenstrahlen haertbare kautschukhaltige anstrichmittel |
US3974303A (en) * | 1973-07-27 | 1976-08-10 | Kansai Paint Company, Ltd. | Method for forming coating films |
EP0029596A1 (fr) * | 1979-11-21 | 1981-06-03 | E.I. Du Pont De Nemours And Company | Composition de revêtement contenant un grand nombre de particules solides à base d'un polymère acrylique à bas poids moléculaire et un agent réticulant à base de résine azotée et substrat ainsi revêtu |
EP0480120A2 (fr) * | 1990-10-12 | 1992-04-15 | Mitsui Toatsu Chemicals, Inc. | Composition de résine pour revêtement en poudre |
-
1992
- 1992-06-10 BE BE9200542A patent/BE1005993A3/nl not_active IP Right Cessation
-
1993
- 1993-06-01 TW TW82104362A patent/TW233305B/zh active
- 1993-06-07 WO PCT/NL1993/000120 patent/WO1993025596A1/fr not_active Application Discontinuation
- 1993-06-07 AU AU45878/93A patent/AU4587893A/en not_active Abandoned
- 1993-06-07 EP EP93916272A patent/EP0644905A1/fr not_active Withdrawn
- 1993-06-09 CN CN 93108409 patent/CN1082083A/zh active Pending
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2163660A1 (de) * | 1971-12-21 | 1973-07-05 | Ford Werke Ag | Mit elektronenstrahlen haertbare kautschukhaltige anstrichmittel |
US3974303A (en) * | 1973-07-27 | 1976-08-10 | Kansai Paint Company, Ltd. | Method for forming coating films |
EP0029596A1 (fr) * | 1979-11-21 | 1981-06-03 | E.I. Du Pont De Nemours And Company | Composition de revêtement contenant un grand nombre de particules solides à base d'un polymère acrylique à bas poids moléculaire et un agent réticulant à base de résine azotée et substrat ainsi revêtu |
EP0480120A2 (fr) * | 1990-10-12 | 1992-04-15 | Mitsui Toatsu Chemicals, Inc. | Composition de résine pour revêtement en poudre |
Non-Patent Citations (1)
Title |
---|
CHEMICAL ABSTRACTS, vol. 86, no. 20, 16 May 1977, Columbus, Ohio, US; abstract no. 141733d, OZAWA HIROSHI ET AL. 'RESIN POWDER COATING COMPOSITIONS' page 93 ;column 1 ; * |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5484850A (en) * | 1993-11-03 | 1996-01-16 | Basf Aktiengesellschaft | Copolymers crosslinkable by a free radical method |
US5527859A (en) * | 1993-11-03 | 1996-06-18 | Basf Aktiengesellschaft | Preparation of copolymers crosslinkable by a free radical method |
WO1995023120A1 (fr) * | 1994-02-24 | 1995-08-31 | Dsm N.V. | Composition de resine durcissable liquide pour fibres optiques |
US6191229B1 (en) | 1995-10-06 | 2001-02-20 | Nippon Shokubai Co., Ltd. | (Meth)acryl syrup, method of manufacturing the same, and method of manufacturing molding material including the same |
EP0796873A4 (fr) * | 1995-10-06 | 1999-11-03 | Nippon Catalytic Chem Ind | Sirop (meth)acrylique, procede d'elaboration de ce sirop et procede d'elaboration d'un materiau de moulage contenant un tel sirop |
US6384102B1 (en) | 1996-10-25 | 2002-05-07 | Ucb S.A. | Powder compositions with semi-crystalline polyester and acrylic copolymer base containing ethylenically unsaturated groups |
US6485793B1 (en) | 1998-08-04 | 2002-11-26 | Basf Coatings Ag | Aqueous dispersion of transparent powder coating material |
WO2000008107A1 (fr) * | 1998-08-04 | 2000-02-17 | Basf Coatings Ag | Dispersion aqueuse contenant un vernis clair pulverulent |
WO2000008067A1 (fr) * | 1998-08-07 | 2000-02-17 | Basf Coatings Ag | Laque en poudre a structure de base fonctionnalisee, durcissable par un rayonnement haute energie et/ou par la chaleur |
US6541535B1 (en) | 1998-08-07 | 2003-04-01 | Basf Coatings Ag | High powered radiation and/or thermal hardening coating powder with a functionalized based structure |
US7122595B1 (en) | 1999-02-25 | 2006-10-17 | Basf Coatings Ag | Powder-slurry that can be hardened by actinic radiation or by thermal means, method for producing said slurry and use of the same |
EP1170109A1 (fr) * | 2000-07-05 | 2002-01-09 | Mitsubishi Rayon Co., Ltd. | Compositions photodurcissables, feuilles phodurcissables et objet moulé contenant celles-ci, procédés et production |
US6646022B2 (en) | 2000-07-05 | 2003-11-11 | Mitsubishi Rayon Co., Ltd. | Photocuring resin compositions, photocuring sheets and molded article using the same, and processes of production thereof |
CN1308356C (zh) * | 2000-08-25 | 2007-04-04 | 约翰逊聚合物公司 | 通过管内改性方法连续生产反应性聚合物的工艺过程及其产物 |
WO2002018456A3 (fr) * | 2000-08-25 | 2002-05-30 | Johnson Polymer Inc | Procede de production de polymeres reactifs par post-modification en ligne et produits correspondants |
US7230048B1 (en) | 2000-08-25 | 2007-06-12 | Basf Corporation | Process for continuous production of reactive polymers with in-line post-modification and products thereof |
EP1443059A1 (fr) * | 2003-02-02 | 2004-08-04 | Solutia Italy S.r.l. | Résines pour compositions de revêtements sous forme de poudre |
US7390849B2 (en) | 2003-02-02 | 2008-06-24 | Surface Specialties Italy S.R.L. | Powder coating composition |
WO2005108513A1 (fr) * | 2004-05-07 | 2005-11-17 | Cytec Surface Specialties, S.A. | Compositions de revetements en poudre peu brillantes durcissables par rayonnement |
US7816420B2 (en) | 2004-05-07 | 2010-10-19 | Cytec Surface Specialties, S.A. | Radiation curable low gloss powder coating compositions |
Also Published As
Publication number | Publication date |
---|---|
AU4587893A (en) | 1994-01-04 |
EP0644905A1 (fr) | 1995-03-29 |
BE1005993A3 (nl) | 1994-04-12 |
TW233305B (fr) | 1994-11-01 |
CN1082083A (zh) | 1994-02-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP4574867B2 (ja) | モノマーおよび重合法 | |
WO1993025596A1 (fr) | Resine pour revetements pulverulents s'utilisant en tant que couche de finissage dans l'industrie automobile et substrats revetus | |
WO1992022615A1 (fr) | Enduits a base de polymeres et de resines epoxydes contenant des groupes carboxyles | |
US4981885A (en) | Polymer dispersions, process for their preparation, and their use as binders | |
JPH09221578A (ja) | 耐環境腐食性コーティング用の水性コーティング組成物 | |
US5969054A (en) | High solids polyurethane binder compositions containing grafted polyacrylate polyols | |
JP2002322429A (ja) | 流動改変剤を有するコーティング組成物および流動改変剤および複層コーティング | |
AU693515B2 (en) | Polymer | |
US4605719A (en) | Liquid, curable coating composition based on a hydroxyl groups-containing addition polymer as binder | |
US3947528A (en) | Additives for powder resins | |
EP0156210A2 (fr) | Compositions de résines réticulables à base de polymères vinyliques renfermant des groupes amines tertiaires | |
EP2089436A1 (fr) | Polymérisation de polymères acryliques dans des diluants réactifs | |
US5770667A (en) | Functional copolymers of low molar mass, processes for their preparation, and their use | |
JPH05501125A (ja) | 多層被覆を得る方法、水性被覆組成物及び水に希釈可能なポリアクリレート樹脂の製法 | |
US5576405A (en) | Liquid-resin, process for the production thereof and its use | |
US20020156221A1 (en) | High solids acrylic resin | |
CA2325946C (fr) | Nouvelles compositions de liant a forte teneur en solides et utilisation de ces produits | |
US20020156220A1 (en) | High solids acrylic resin | |
JPH04220410A (ja) | ハイブリッドポリマーの水性分散物及びそれより得られるコーティング組成物 | |
JPH06329984A (ja) | 物理的迅速乾燥結合剤混合物および木材支持体を塗布するためのそれらの使用 | |
JPS5940846B2 (ja) | 非水系不飽和樹脂組成物 | |
WO1997019118A1 (fr) | Polymeres dispersibles dans l'eau et leur utilisation dans des systemes aqueux | |
JP3861680B2 (ja) | ポリオレフィン系樹脂用活性エネルギー線硬化型プライマー組成物 | |
JPH04233926A (ja) | ハイブリッドポリマ−、それより得られる水性分散物及びコ−ティング組成物 | |
CA2020166A1 (fr) | Polymeres pour revetements ultra-brillants |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AU BB BG BR CA CZ FI HU JP KP KR KZ LK MG MN MW NO NZ PL RO RU SD SK UA US VN |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 1993916272 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1993916272 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: CA |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1993916272 Country of ref document: EP |