Mode I fracture toughness of co-cured and secondary bonded composite jointsMohan et al., 2014
View PDF- Document ID
- 8304413967806017959
- Author
- Mohan J
- Ivanković A
- Murphy N
- Publication year
- Publication venue
- International Journal of Adhesion and Adhesives
External Links
Snippet
The mode I fracture toughness of a single co-cured and two secondary bonded joint systems were determined using the double cantilever beam test. The initiation values of fracture toughness from the PTFE film insert and a mode I crack-tip were considered as well as …
- 210000001503 Joints 0 title abstract description 30
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Mohan et al. | Mode I fracture toughness of co-cured and secondary bonded composite joints | |
| Mariam et al. | Influence of hydrothermal ageing on the mechanical properties of an adhesively bonded joint with different adherends | |
| Mohan et al. | Mixed-mode fracture toughness of co-cured and secondary bonded composite joints | |
| Katsiropoulos et al. | Fracture toughness and shear behavior of composite bonded joints based on a novel aerospace adhesive | |
| Mohan et al. | Effect of prepreg storage humidity on the mixed-mode fracture toughness of a co-cured composite joint | |
| Löbel et al. | A hybrid bondline concept for bonded composite joints | |
| Pegorin et al. | Influence of z-pin length on the delamination fracture toughness and fatigue resistance of pinned composites | |
| Brunner et al. | A status report on delamination resistance testing of polymer–matrix composites | |
| Akpinar et al. | Effect of nanostructured reinforcement of adhesive on thermal cycling performance of a single-lap joint with composite adherends | |
| Koutras et al. | Influence of temperature on the strength of resistance welded glass fibre reinforced PPS joints | |
| Majerski et al. | The comparison of effects of hygrothermal conditioning on mechanical properties of fibre metal laminates and fibre reinforced polymers | |
| Kousourakis et al. | The effect of self-healing hollow fibres on the mechanical properties of polymercomposites | |
| Shahverdi et al. | Experimental investigation of R-ratio effects on fatigue crack growth of adhesively-bonded pultruded GFRP DCB joints under CA loading | |
| Thunga et al. | Adhesive repair of bismaleimide/carbon fiber composites with bisphenol E cyanate ester | |
| Li et al. | Effect of CFRP surface topography on the adhesion and strength of composite-composite and composite-metal joints | |
| Kanerva et al. | Interface modification of glass fibre–polyester composite–composite joints using peel plies | |
| Budhe et al. | Influence of pre-bond moisture in the adherents on the fracture toughness of bonded joints for composite repairs | |
| Agius et al. | Rapidly cured out-of-autoclave laminates: Understanding and controlling the effect of voids on laminate fracture toughness | |
| Sales et al. | Analysis of hygrothermal effects on mixed mode I/II interlaminar fracture toughness of carbon composites joints | |
| Abdel-Monsef et al. | Effect of environment conditioning on mode II fracture behaviour of adhesively bonded joints | |
| Tauheed et al. | Mode I fracture R-curve and cohesive law of CFRP composite adhesive joints | |
| Amedewovo et al. | A methodology for online characterization of the deconsolidation of fiber-reinforced thermoplastic composite laminates | |
| Brito et al. | Mode I interlaminar fracture toughness analysis of Co-bonded and secondary bonded carbon fiber reinforced composites joints | |
| Srinivasan et al. | Fatigue performance of wind turbine rotor blade epoxy adhesives | |
| Cui et al. | Inter-fibre failure of through-thickness reinforced laminates in combined transverse compression and shear load |