US20130340825A1

US20130340825A1 - Dye-Sensitized Solar Cell with Ordered Tin Oxide Composite Nanostructure Electrodes

Info

Publication number: US20130340825A1
Application number: US14/012,159
Authority: US
Inventors: Jong-Jan Lee; Karen Yuri Nishimura; Wei Pan; Sean Andrew Vail
Original assignee: Sharp Laboratories of America Inc
Current assignee: Sharp Laboratories of America Inc
Priority date: 2010-09-28
Filing date: 2013-08-28
Publication date: 2013-12-26

Abstract

A dye-sensitized solar cell (DSC) is provided, made from an anode layer of tin oxide (SnO₂) coated titanium oxide (TiO₂) nanostructures that overlie a substrate top surface. A dye overlies the anode layer, and a cathode overlies the dye. The cathode may be a hole conducting layer having a solid state phase or a redox electrolyte, with a counter electrode. The TiO₂nanostructures may be TiO₂nanoparticles, TiO₂nanowires, or TiO₂nanotubes. In the case of TiO₂nanowires or TiO₂nanotubes, their center axes are perpendicular to the substrate top surface. Regardless of the TiO₂nanostructure morphology, the SnO₂coating thickness is in the range of 2 to 10 nanometers (nm). In one aspect, the SnO₂coated TiO₂nanostructures have a dielectric layer shell, which may have a thickness in the range of 0.3 to 2 nm.

Description

RELATED APPLICATIONS

This application is a Continuation-in-part (CIP) of a patent application entitled, TANDEM DYE-SENSITIZED SOLAR CELL AND METHOD FOR MAKING SAME, invented by Lee et al., Ser. No. 12/892,779, filed Sep. 28, 2010. This application is incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention
This invention generally relates to photovoltaic energy cells and, more particularly, to a dye-sensitized solar cell (DSSC or DSC) formed from a tin oxide coated titanium oxide nanostructure electrode.
2. Description of the Related Art
FIG. 1 is a partial cross-sectional view of typical DSC structure (prior art). DSCs had typically exhibited low conversion efficiencies until a breakthrough in 1991 by professor Grätzel and co-workers using a nanocrystalline titanium oxide (TiO₂) electrode modified with a photon absorbing dye. In modern DSC cells, the photoanode TiO₂electrode is fabricated on a transparent conducting oxide (TCO), a monolayer of absorbed dye on a TiO₂surface, a platinum (Pt) counter-electrode, and an electrolyte solution with a dissolved iodine ion/tri-iodide ion redox couple between the electrodes. The structure shown in FIG. 1 has successfully demonstrated an energy conversion efficiency that exceeded 7% in 1991 (B. O'Regan and M. Gratzel, “A low cost high efficiency solar cell based on dye-sensitized colloidal TiO2 films,” Nature, 353, 737-740, Oct. 24, 1991), 10% in 1993 (M. K. Nazeeruddin et al., J. Am. Chem. Soc., 115, 6382-6390, 1993), and 11.1% (L. Han et al., “High efficiency of dye-sensitized solar cell and module,” IEEE 4^thWorld Conference on Photovoltaic Energy Conversion, 179-182, 1996).
In order to sensitize the TiO₂, a dye molecule is attached to the TiO₂surface. When the dye molecule absorbs a photon, an electron is excited to the lowest unoccupied molecular orbital (LUMO) and is subsequently injected into the conduction band of the TiO₂. As a result of this, the dye molecule is transformed to its oxidized state. The injected electron percolates through the porous nanocrystalline structure to the TCO (negative electrode, anode) and finally through an external load to the counter electrode (positive electrode, cathode, and Pt). At the counter electrode, the electron is transferred to tri-iodide in the electrolyte to yield iodine (I₃ ₋+2e⁻→3I⁻). The cycle is closed by reduction of the oxidized dye by the iodine in the electrolyte.
In another aspect of solar cell technology, the most frequently explored strategy for achieving higher efficiency in solar cells has focused on the use of a tandem cell structure, through which individual cells can be tuned to a particular frequency of the spectrum. This allows the cells to be stacked such that layers capable of capturing shorter wavelengths are located on top, while longer wavelengths of light are allowed to pass through the top and travel to the lower layers. For DSC cells, several tandem cell concepts and structures have been proposed. One proposal suggests a random mixture of two or more dyes with different absorption spectra (molecular cocktail). So far, this approach has not led to higher efficiency cells when compared to the best (single) dye with broad absorption characteristics.
As noted above, a DSC is typically composed of a mesoporous TiO₂electrode sensitized with a photon absorbing dye, which is in turn contacted by a redox-active hole transporting medium. Photoexcitation of the sensitizer leads to electron transfer from the excited dye to TiO₂conduction band, and the oxidized dye is regenerated via hole-transfer to the redox active medium. The photoelectron generation, charge transfer, and dye regeneration are well studied. The charge transfer from the excited dye to TiO₂conduction hand depends upon the anchoring function group of the dye and the energy difference between the excited dye and the TiO₂conduction band. In principle, a more efficient electron transfer occurs for the system with a larger energy difference.
In addition, for a dye to absorb longer wavelengths, the energy difference between the ground state (highest occupied molecular orbital, HOMO) and the excited state (lowest unoccupied molecular orbital, LUMO) must be reduced. For instance, for a dye to be able to absorb wavelengths shorter than 700 nanometers (nm), its bandgap (energy difference between HOMO and LUMO) is around 1.8 electron volts (eV). For a dye to absorb wavelengths shorter than 1050 nm, its bandgap is around 1.2 eV. When the bandgap of the dye shrinks, the LUMO level drops, and the energy difference (between the excited dye (LUMO level) and the TiO₂conduction band) decreases, leading to a decreased likelihood of charge injection.
FIG. 2 illustrates the band structure of various metal oxides and semiconductors (prior art). Shown are the band positions of several semiconductors in contact with an aqueous electrolyte at a pH 1. The lower edge of the conduction hand (top) and the upper edge of the valence band (bottom) are presented along with the bandgap in electron volts. On the right side the standard potentials of several redox couples are presented against the standard hydrogen electrode (NHE or SHE) potential.
Comparing to the TiO₂conduction band (E_C), ZnO has a 0.1-0.2 eV lower E_C. The favorable E_Clevel and ease of fabricating ZnO nanostructures, makes ZnO a common replacement for TiO₂as a photoanode in DSC development. However, ZnO is very active and unstable, and the energy difference from TiO₂is too small for many applications. Other oxides, e.g., WO₃and Fe₂O₃are potential candidates, but not much related development has been done on these materials. On the other hand, SnO₂has an E_Cof about 0.6 eV below that of TiO₂. Several published papers suggest that SnO₂may be a suitable photoanode for DSC application. In addition, bulk SnO₂has a mobility of up to 240 centimeters squared per volt-seconds (cm²/V-s), which is 100 times that of TiO₂. Of course, for a DSC incorporating bare SnO₂with no surface treatment, the regeneration of the oxidized photosensitizer from the hole conductor (or the redox couple) is often not sufficiently fast, and the recombination of the conduction band electrons with the oxidized photosensitizer is incomplete. However, some reports suggest that with the incorporation of thin (sub nm) interfacial layers of wide bandgap “insulating” oxides, such as MgO or Al₂O₃, between the SnO₂and photosensitizer, suppress the back reaction and can enable a significant enhancement in the photovoltaic conversion efficiency.
Mesoporous SnO₂electrodes made of SnO₂nanoparticles have been described and good DSC performance was reported. Nevertheless, DSC electrodes made of one-dimensional SnO₂nanostructures, such as nanowire, nanoribbon, and nanotube have advantages, such as a faster charge transfer. Four examples of one-dimensional SnO₂nanostructures are provided below. As used herein, a “one-dimensional structure” is essentially a structure in the shape of a Line, such as a wire, tube, or rod having a high aspect ratio between the length and diameter. In some aspects, the ratio is greater than 10:1.

SnO₂Nanowire

SnO₂nanowires can be synthesized with sizes ranging from 20-200 nm in diameter and lengths up to a few tens of micrometers depending on the growth conditions. In one method, the growth of nanowires follows that of a self catalytic vapor-liquid-solid (VLS) mechanism. Quartz substrates with tin metal powders are placed in the center zone of a tubular quartz reactor. The reactor is then heated to temperatures of 850-950° C. at ambient pressure and under a continuous flow of argon. At these elevated temperatures, the metal powders melt and form a thin film on the substrates. The branching and interconnectivity of nanowires is promoted by providing Sn droplets intermittently for secondary nucleation. This is done by fluctuating the temperatures of both the Sn source and the substrate. The precursor for nanowire growth is pure Sn metal.

SnO₂Nanotubes

SnO₂nanotubes can be synthesized by template-directed electrodeposition using nuclear track etching of polycarbonate membranes with a nominal pore diameter of 50 or 100 nm. The rated thickness and pore density are 6 μm and 6×108 pores cm⁻², respectively. One side of the polycarbonate membrane is first coated with a 500 nm thick layer of gold by sputtering to create a seed layer. The electrical contact is made to the membrane working electrode using a conductive copper tape. The resultant template is placed in an electrolyte cell, such that an area of 1 cm²is exposed to the electrolyte. Platinum gauze is used as the counter electrode and a Ag/AgCl (3 M KCl) electrode serves as the reference electrode. Electrochemical synthesis is performed under a potentiostatic mode using a multichannel potentio/galvanostat. The electrolyte consists of 20 mM tin chloride, 0.1 M sodium nitrate, and 75 mM nitric acid in distilled (DI) water. SnO₂is deposited on the templates using a fixed potential of −0.4 V (versus Ag/AgCl) with varying deposition times. Following deposition, the gold seed layer used as the working electrode is mechanically removed and the membrane rinsed in DI water. The nanotubes are released by dissolving the polycarbonate membrane in dichloromethane. The suspension is centrifuged, the nanotubes washed three times with dichloromethane, and finally suspended in isopropanol. The resultant SnO₂nanotubes are annealed in air at 400° C. for 4 hours to investigate the effect of annealing on the crystal structure of the nanotubes.

Single Crystalline SnO₂Nanoribbons

The experimental apparatus used for the synthesis of SnO₂nanoribbons consists of a horizontal alumina tube furnace, a rotary pump, and a gas supply. SnO or SnO₂powder is used as the source material, placed in an alumina crucible, with the crucible being located at the center of the alumina tube. Several alumina substrates are placed downstream inside the alumina tube for collecting the growth products. After evacuating the alumina tube to 2×10⁻³Torr, thermal evaporation is conducted at 1000° C. for SnO powders, or 1350° C. for the SnO₂powders, for 2 hours under a pressure of 300 Torr and Ar gas flow rate of 50 standard cubic centimeters per minute (sccm). A white-color, fuzzy looking product is collected in a region where the temperature is in the range of 900-950° C. Electron diffraction analysis reveals that each nanoribbon is single crystalline SnO₂without dislocation.

Single Crystalline SnO₂Nanowires

In one method, a horizontal quartz tube is mounted inside a high-temperature tube furnace. A mixture of active carbon powder 1.2 grams (g) and fine SnO₂powder 5 g are placed on a quartz crucible and Si substrates (deposited with thin 5 nm Au) are placed downstream of the furnace. After the wafer is inserted into the center of the quartz tube, the quartz tube is first evacuated by a vacuum pump. Next, the furnace is rapidly heated up to 700° C. from room temperature under a N₂flow at a rate of about 100 sccm. The pressure is kept at 200 Torr and the heating lasts for 240 minutes. Subsequently, the furnace is cooled to room temperature naturally, and the products are collected on the substrates from different regions of the furnace. All these regions have the same temperature of 700° C. It is observed that thick, white, cotton-wool-like products are deposited on the surfaces of the substrates. Scanning electron microscope (SEM) images of the resulting product indicate single crystalline SnO₂nanowires.
Some of the previously discussed one-dimensional SnO₂nanostructures exhibit a single crystalline structure. DSC cells have been successfully fabricated with these one-dimensional nanostructures. As discussed above, thin (sub nm) interfacial layers of wide bandgap “insulating” oxides are needed to suppress the hack reaction. However, there are challenges with using these one-dimensional SnO₂nanostructure; for example (1) they are random powder-like structures and (2) synthesis temperatures are very high.
It would be advantageous to produce SnO₂as an ordered, one dimensional nanostructures using a low temperature process.

SUMMARY OF THE INVENTION

Disclosed herein are titanium oxide (TiO₂) nanostructures covered with tin oxide (SnO₂), resulting in an ordered, one-dimensional nanostructure. As used herein, a set of “ordered” structures are formed in a uniform direction. Thus, “ordered one-dimensional” structures are line-like structures having a high aspect ratio of length to diameter, such as a wire, tube, or rod aligned in a uniform direction. That is, a set of one-dimensional structures have center axes aligned in parallel. The electrical properties, especially focusing on the conduction hand, are controlled by the SnO₂. The SnO₂covered TiO₂nanostructures can be used for single junction dye-sensitized solar cells (DSCs) and tandem junction DSCs. In the case of tandem junction DSCs cell, the SnO₂coated TiO₂nanostructures can replace the TiO₂nanostructure anode layer of some conventional devices.
Accordingly, a DSC is provided, made from a substrate having a top surface. An anode layer of SnO₂coated TiO₂nanostructures overlies the substrate top surface. A dye overlies the anode layer, and a cathode overlies the dye. The cathode may be made from a hole conducting layer having a solid state phase or a liquid phase redox electrolyte, with a counter electrode. The TiO₂nanostructures may be TiO₂nanoparticles, TiO₂nanowires, or TiO₂nanotubes. In the case of TiO₂nanowires or TiO₂nanotubes, their center axes are perpendicular to the substrate top surface. Regardless of the TiO₂nanostructure morphology, the SnO₂coating thickness is in the range of 2 to 10 nanometers (nm). In one aspect, the SnO₂coated TiO₂nanostructures have a dielectric layer shell, which may have a thickness in the range of 0.3 to 2 nm. The dielectric layer shell may be a material such as niobium oxide (NbO₃), aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), or TiO₂, to name a few examples.
Additional details of the above-described DSC, a tandem DSC, and a composite nanostructure are provided below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partial cross-sectional view of typical DSC structure (prior art).

FIG. 2 illustrates the band structure of various metal oxides and semiconductors (prior art).

FIGS. 3A through 3D are partial cross-sectional views of a composite nanostructure.

FIG. 4 is a partial cross-sectional view depicting a dye-sensitized solar cell (DSC).

FIG. 5 is a partial cross-sectional view depicting the DSC of FIG. 4 in greater detail.

FIGS. 6A through 6C are partial cross-sectional views of a tandem DSC.

FIGS. 7A and 7B respectively depict plan and partial cross-sectional views of a first step in the fabrication of SnO₂coated TiO₂nanostructures before measurement.

FIGS. 8A and 8B respectively depict plan and partial cross-sectional views of a second step in the fabrication of SnO₂coated TiO₂nanostructures.

FIGS. 9A through 9F are graphs of work functions measured on three separate TiO₂/FTO samples before (FIGS. 9A-9C) and after (FIGS. 9D-9F) SnO₂coating treatment.

FIG. 10 is a diagram depicting the band structure relationship between TiO₂, SnO₂, a first dye, and a second dye.

DETAILED DESCRIPTION

FIGS. 3A through 3D are partial cross-sectional views of a composite nanostructure. The composite nanostructure 300 comprise a titanium oxide (TiO₂) nanostructure core 302 and a tin oxide (SnO₂) coating 304 covering the core 302. The SnO₂coating 304 has a thickness 306 in the range of 2 to 10 nanometers (nm). In FIG. 3A, the TiO₂nanostructure core 302 is a nanowire morphology, in FIG. 3B, the morphology is a nanotube, and in FIG. 3C the morphology is a nanoparticle.
The composite nanostructure of FIG. 3D additionally comprises a dielectric layer shell 308 overlying the SnO₂coating 304. Here the TiO₂nanostructure core 302 is shown as a nanowire, but it could just as well be a nanotube or nanoparticle. The dielectric layer shell 308 has a thickness 310 in the range of 0.3 to 2 nm, Some examples of the dielectric layer shell 308 material include niobium oxide (NbO₃), aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), and TiO₂. Other materials, especially metal oxide materials may possibly be used.
FIG. 4 is a partial cross-sectional view depicting a dye-sensitized solar cell (DSC). The DSC 400 comprises a substrate 402 having a top surface 404. An anode layer 406 comprising SnO₂coated TiO₂nanostructures, identified in FIGS. 3A-3D as composite structures 300, overlie the substrate top surface. The substrate 402 may be made from a transparent conductive oxide (TCO) material, such as In₂O₃—SnO₂(indium tin oxide or ITO), tin oxide (SnO₂), zinc oxide (ZnO). aluminum/gallium doped zinc oxide (ZnO:Al(Ga)), a carbon nanotube layer, a graphene layer, or fluorine doped tin oxide (SnO₂:F or FTO). A dye 407 overlies the anode layer 406, and a cathode 408 overlies the dye. The cathode 408 is comprised of a first material 410, which may be a hole conducting layer having a solid state phase or a redox electrolyte having a liquid phase, overlying the dye 407. Although the dye 407 is depicted as a separate layer, it should be understood that the dye may permeate into the SnO₂coated TiO₂nanostructures of the anode layer 406. Similarly, it should be understood that the first material 410 may permeate into the SnO₂coated TiO₂nanostructures of the anode layer 406 and be in contact with the dye 407.
A counter electrode 412 overlies the first material 410. For example, the first material may be a redox electrolyte that includes iodine and/or tri-iodine. As used herein, the orientation of the DSC 400 is relative. Therefore, the term “underlie” may alternatively be understood to mean “overlie” or in direct physical contact, depending upon the orientation of the DSC 400.
In one aspect, the substrate 402 is formed overlying glass 416 and acts as an external electrode, in another aspect, the counter electrode 412 acts as an external electrode and can be made from a metal such as platinum (Pt), platinum/aluminum (Pt/Al), silver (Ag), gold (Au), or carbon. The external electrodes are configured to be connected to other DSCs or electrical circuitry (not shown) such as a DC-to-AC inverter.
As explained above in the descriptions of FIGS. 3A-3D, the TiO₂nanostructures, referred to as TiO₂nanostructure cores 302 in FIGS. 3A-3D, may be TiO₂nanoparticles (FIG. 3C), TiO₂nanowires (FIG. 3A), or TiO₂nanotubes (FIG. 3B). Referring still to FIGS. 3A-3D, the SnO₂coating thickness 306 on the TiO₂nanostructures 302 is in the range of 2 to 10 nm. In some aspects, the TiO₂nanostructure acts as a “backbone” to make an ordered one-dimensional nanostructure. The SnO₂coating on the surface of TiO₂improves the charge transfer from the excited dye to SnO₂conduction band.
Further, as shown in FIG. 3D, the SnO₂coated TiO₂nanostructures 300 may further comprise a dielectric layer shell 308 overlying the SnO₂coating 304. The dielectric layer shell 308 has a thickness 310 in the range of 0.3 to 2 nm. Some examples of the dielectric layer shell 308 material include niobium oxide (NbO₃), aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), and TiO₂. Other materials, especially metal oxide materials may possibly be used. Since the SnO₂surface may exhibit high charge recombination, the thin layer of dielectric layer may be used to inhibit charge recombination. Note that the dielectric layer 308 is much thinner than the SnO₂coating 304, and it does not affect the charge transfer from the excited dye 407 to SnO₂conduction band.
FIG. 5 is a partial cross-sectional view depicting the e DSC of FIG. 4 in greater detail. In the case where the TiO₂nanostructures 302 are TiO₂nanowires or TiO₂nanotubes, they have a center axis 500 perpendicular to the substrate top surface 404. That is, the SnO₂coated TiO₂nanostructures 300 are ordered in a direction perpendicular to the substrate top surface 404.
FIGS. 6A through 6C are partial cross-sectional views of a tandem DSC. The tandem DSC 600 comprises a first photovoltaic (PV) cell 602 and a second PV cell 604. The first PV cell 602 includes a first anode layer 406 of SnO₂coated TiO₂nanostructures. The SnO₂coated TiO₂nanostructures are labeled with reference designator 300 in FIG. 4. Details of the SnO₂coated TiO₂nanostructures have been presented above in the descriptions of FIGS. 3A-3D and 4, and are not repeated here in the interest of brevity. As noted above in the description of FIG. 4, the first anode layer 406 is typically formed overlying a substrate (see FIG. 4, reference designator 402). A first dye 407 overlies the first anode layer 406, and a first cathode 408 overlying the first dye 407. As noted above in the description of FIG. 4, the first cathode 408 comprises a first material 410, which may be a solid state phase hole conducting layer and or liquid phase redox electrolyte, overlying the first dye 407, and a counter electrode 412 overlying the first material.
The second PV cell 604 includes a second anode layer 606 of TiO₂nanostructures. Note: the TiO₂nanostructures that make up the second anode layer 606 are not coated with tin oxide. A second dye 608 overlies the second anode 606, and a second cathode 610 overlies the second dye 608. The second cathode 610 may be formed from one of the above-described first materials and a counter electrode. An electrical connection 612 exists between the first PV cell 602 and the second PV cell 604. The electrical connection 612 may be a parallel connection, as shown in FIG. 6A, or a series connection, as described below. Either the second anode 606 of the second PV cell 604, or the second cathode 610 (as shown in FIG. 6A), is configured to initially accept incident light 612. Typically, the first dye 407 has a first bandgap and the second dye 608 has a second bandgap, larger than, or equal to the first bandgap.
FIG. 10 is a diagram depicting the band structure relationship between TiO₂, SnO₂, a first dye, and a second dye. Only the Ec is shown for TiO₂and SnO₂(refer to FIG. 2). Note, the terms Ec and Ev are used for crystalline structures, while LUMO and HOMO are used for molecules. Conventional dye-sensitized solar cells have a dye bandgap (LUMO to HOMO) of around 1.7 eV, and can absorb wavelengths shorten than 750 nm well, using a TiO₂nanostructured anode, in order to improve absorption for longer wavelengths, the bandgap of the dye (LUMO to HOMO) must be smaller than 1.7 eV. As the bandgap gets smaller, the distance (energy drop) from the LUMO of the smaller bandgap dye to TiO₂Ec becomes smaller (ΔV3 in the figure). Further, the charge injection from the dye to Ec is easier if the energy drop is larger. For this reason, SnO₂is used in conjunction with the smaller bandgap dye. From the figure, you can see ΔV2 is larger than ΔV3, so the change injection to SnO₂is easier than injection to TiO₂.
In a tandem PV cell, the light preferably initially intersects the larger bandgap material of the second PV cell (604, FIGS. 6A-6C). Photons having less energy (longer wavelength) than the bandgap (Eg) of the second PV cell pass through, and can be absorbed by the first PV cell (602, FIG. 6A-6C) with the smaller Eg material.
In one aspect, the series connection is made using a transparent conductive adhesive. For example, organic adhesives may be used such as: poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) or similar polymers based upon the PEDCOT scaffolding such as Aedotron™ and Oligotron™ (TDA Research, Inc.), polythiophene derivatives, polyaniline, polypyrrole, polyacetylene, polyphenylenevinylene, polyphenylene sulfides, etc., which may contain other additives to increase conductivity and/or adhesion properties. Further, otherwise nonconductive or low conductivity adhesive polymers may be used that are appropriately doped with metals, metal nanoparticles, carbon nanotubes, etc., in order to increase conductivity.
Although not explicitly shown, the second PV cell 604 may be formed on glass substrate with intervening external electrodes made from a transparent conductive oxide (TCO) layer and a metal, as is conventional. The TCO layer can be selected from the following materials: SnO₂:F (FTO), In₂O₃—SnO₂(ITO), ZnO, ZnO:Al(Ga), carbon nanotube layer and graphene layer.
FIG. 6B depicts the first anode 406 of the first PV cells 602 connected in series with the e second cathode 610 of the second PV cell 604. In this aspect, the tandem DSC 600 is configured so that the second anode 606 initially accepts incident light 612. FIG. 6C depicts the first cathode 408 of the first PV cell 602 connected in series with the second anode 606 of the second PV cell 604. In this aspect, the tandem DSC 600 is configured so that the second cathode 610 initially accepts incident light 612.
It should be understood that there are a number of ways of mechanically configuring the tandem DSC 600. The first and second PV cells 602/604 may be fabricated as a single module. Alternatively, the first and second PV cells 602/604 may be fabricated as separate modules, and connected together, mechanically and electrically, upon installation. In another aspect, the e first and second PV cells 602/604 may be fabricated as separate modules and electrically connected at a DC-to-AC inverter.
Using SnO₂coated TiO₂nanostructures, it is possible to design a nanostructured electrode that exhibits the electrical properties of SnO₂, such as the conduction band E_Cand electrical conductivity, while simultaneously exhibiting the physical properties of TiO₂nanostructure, such as morphology, as well as bond and transfer characteristics. Experimental data is provided below, of coating a SnO₂layer on a planar TiO₂film for ease of characterization.
FIGS. 7A and 7B respectively depict plan and partial cross-sectional views of a first step in the fabrication of SnO₂coated TiO₂nanostructures before measurement. Blanket TiO ₂ 700 was sputtered onto fluorine-doped tin oxide (FTO) 702. A masked portion of FTO 702 was left uncoated.
FIGS. 8A and 8B respectively depict plan and partial cross-sectional views of a second step in the fabrication of SnO₂coated TiO₂nanostructures. The sample of FIGS. 7A and 7B was soaked in Tin(IV) isopropoxide and annealed to form SnO ₂ 800 prior to measurement.
As described by Diamant et al (Coordination Chemistry Reviews 248 (2004) 1271-1276), nanoporous TiO₂can be coated with SnO₂by dipping in a 50 mM Sn-isopropoxide solution, and then annealing at 500° C. for 30 minutes. For an initial experiment, 50 mM Tin(IV) isopropoxide in anhydrous isopropanol was prepared. Samples of sputtered/annealed TiO₂film on FTO glass were soaked for 30 seconds, air-dried, and annealed at 500° C. for 30 minutes in ambient. The SnO₂layer thickness is very thin due to short processing time (30 second), and it is difficult to accurately determine the correct thickness since the film is coated on a rough substrate (FTO glass). Kelvin probe measurements were used to determine the work function of the film before and after the SnO₂coating procedure.
The Kelvin probe is a non-contact, vibrating capacitor instrument used to measure the work function difference between materials. The work function is indicative of surface condition and can reveal information regarding surface contamination, charging, oxidation, etc. The Kelvin probe utilizes a “calibration disk” consisting of a gold surface which is used to measure a “reference” work function Au_(ref). From this reference, the following can be calculated:
Φ_{(probe tip)}=Au_{(theoretical)}−Au_(ref)
Φ_(sample)=Φ_(tip)+Φ_{(as measured on sample)}
where Au(theoretical)=5.1 to 5.47 eV
FIGS. 9A through 9F are graphs of work functions measured on three separate TiO₂/FTO samples before (FIGS. 9A-9C) and after (FIGS. 9D-9F) SnO₂coating treatment. The work function difference, measured using the Kelvin probe, decreased to ˜200 meV (1 meV=0.001 eV) for each sample. The work function difference between TiO₂and FTO is measured to be between ˜400 to 700 meV, which agrees well with the reported work function number. After coating with SnO₂, the work function difference is ˜200 meV. Note that the potential value of the SnO₂/TiO₂/FTO surface (after coating) is similar to the value of the FTO surface (before coating). This observation is in accordance with expectation, as the work function of SnO₂should be similar to FTO. Interestingly, the work function of SnO₂-coated FTO also increased Slightly. This indicates that the coated SnO₂film is so thin so that the surface potential is affected by the film under the SnO₂.
A tin oxide (SnO₂) coated titanium oxide (TiO₂) composite nanostructure has been provided along with a DSC device made from the SnO₂coated TiO₂nanostructures. Particular materials, device structures, and process details have been presented as examples to illustrate the invention. However, the invention is not limited to just these examples. Other variations and embodiments of the invention will occur to those skilled in the art.

Claims

We claim:

1. A dye-sensitized solar cell (DSC) comprising:

a substrate having a top surface;

an anode layer comprising tin oxide (SnO₂) coated titanium oxide nanostructures overlying the substrate top surface;

a dye overlying the anode layer; and,

a cathode overlying the dye.

2. The DSC of claim 1 wherein the cathode comprises:

a first material, selected from a group consisting of a hole conducting layer having a solid state phase and a redox electrolyte having a liquid phase, overlying the dye; and,

a counter electrode overlying the first material.

3. The DSC of claim 1 wherein the TiO₂nanostructures are selected from a group consisting of TiO₂nanoparticles, TiO₂nanowires, and TiO₂nanotubes.

4. The DSC of claim 1 wherein the TiO₂nanostructures are selected from a group consisting of TiO₂nanowires and TiO₂nanotubes, having a center axes perpendicular to the substrate top surface.

5. The DSC of claim 1 wherein the SnO₂coating thickness on the TiO₂nanostructures is in a range of 2 to 10 nanometers (nm).

6. The DSC of claim 1 wherein the SnO₂coated TiO₂nanostructures have a dielectric layer shell.

7. The DSC of claim 6 wherein the dielectric layer shell has a thickness in a range of 0.3 to 2 nm.

8. The DSC of claim 6 wherein the dielectric layer shell is a material selected from a group consisting of niobium oxide (NbO₃), aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), and TiO₂.

9. A tandem dye-sensitized solar cell (DSC) comprising:

a first photovoltaic (PV) cell including:

a first anode layer of tin oxide (SnO₂) coated titanium oxide (TiO₂) nanostructures;

a first dye overlying the first anode layer;

a first cathode overlying the first dye;

a second PV cell including:

a second anode layer of TiO₂nanostructures;

a second dye overlying the second anode;

a second cathode overlying the second dye;

an electrical connection between the first PV cell and the second PV cell; and,

wherein an electrode of the second PV cell, selected from a group consisting of the second anode and second cathode, is configured to initially accept incident light.

10. The tandem DSC of claim 9 wherein the electrical connection between the first PV cell and the second PV cell is selected from a group consisting of a series connection and a parallel connection.

11. The tandem DSC of claim 9 wherein the first dye has a first bandgap; and,

wherein the second dye has a second bandgap, larger than, or equal to the first bandgap.

12. The tandem DSC of claim 9 wherein the first anode layer SnO₂coating thickness is in a range of 2 to 10 nanometers (nm).

13. The tandem DSC of claim 9 wherein the first anode layer SnO₂coated TiO₂nanostructures have a dielectric layer shell.

14. The tandem DSC of claim 13 wherein the dielectric layer shell has a thickness in a range of 0.3 to 2 nm.

15. The tandem DSC of claim 13 wherein the dielectric layer shell is a material selected from a group consisting of niobium oxide (NbO₃) aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), and TiO₂.

16. The tandem DSC of claim 9 wherein the first cathode comprises:

a first material, selected from a group consisting of a solid state phase hole conducting layer and a liquid phase redox electrolyte, overlying the first dye; and,

a counter electrode overlying the first material.

17. A composite nanostructure comprising:

a titanium oxide (TiO₂) nanostructure core; and,

a tin oxide (SnO₂) coating covering the core.

18. The composite nanostructure of claim 17 wherein the SnO₂coating thickness is in a range of 2 to 10 nanometers (nm).

19. The composite nanostructure of claim 17 further comprising:

a dielectric layer shell overlying the SnO₂coating.

20. The composite nanostructure of claim 19 wherein the dielectric layer shell has a thickness in a range of 0.3 to 2 nm.

21. The composite nanostructure of claim 19 wherein the dielectric layer shell is a material selected from a group consisting of niobium oxide (NbO₃), aluminum oxide (Al₂O₃), magnesium oxide (MgO), silicon dioxide (SiO₂), and TiO₂.

22. The composite nanostructure of claim 17 wherein the TiO₂nanostructure core is a morphology selected from a group consisting of TiO₂nanoparticles, TiO₂nanowires, and TiO₂nanotubes.