US20090038678A1 - Thin film iii-v compound solar cell - Google Patents

Thin film iii-v compound solar cell Download PDF

Info

Publication number
US20090038678A1
US20090038678A1 US12/167,588 US16758808A US2009038678A1 US 20090038678 A1 US20090038678 A1 US 20090038678A1 US 16758808 A US16758808 A US 16758808A US 2009038678 A1 US2009038678 A1 US 2009038678A1
Authority
US
United States
Prior art keywords
thin film
solar cell
compound solar
iii
film iii
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/167,588
Other languages
English (en)
Inventor
Noren Pan
Glen Hillier
Duy Phach Vu
Rao Tatavarti
Christopher Youtsey
David McCallum
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Microlink Devices Inc
Original Assignee
Microlink Devices Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Microlink Devices Inc filed Critical Microlink Devices Inc
Priority to US12/167,588 priority Critical patent/US20090038678A1/en
Publication of US20090038678A1 publication Critical patent/US20090038678A1/en
Assigned to MICROLINK DEVICES, INC. reassignment MICROLINK DEVICES, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HILLIER, GLEN, MARTIN, GENEVIEVE, MCCALLUM, DAVID, PAN, NOREN, TATAVARTI, RAO, YOUTSEY, CHRISTOPHER, VU, DUY PHACH
Assigned to NASA reassignment NASA CONFIRMATORY LICENSE (SEE DOCUMENT FOR DETAILS). Assignors: MICROLINK DEVICES INC.
Assigned to U.S. DEPARTMENT OF ENERGY reassignment U.S. DEPARTMENT OF ENERGY CONFIRMATORY LICENSE (SEE DOCUMENT FOR DETAILS). Assignors: MICROLINK DEVICES, INC
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F71/00—Manufacture or treatment of devices covered by this subclass
    • H10F71/127—The active layers comprising only Group III-V materials, e.g. GaAs or InP
    • H10F71/1276—The active layers comprising only Group III-V materials, e.g. GaAs or InP comprising growth substrates not made of Group III-V materials
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F10/00—Individual photovoltaic cells, e.g. solar cells
    • H10F10/10—Individual photovoltaic cells, e.g. solar cells having potential barriers
    • H10F10/14—Photovoltaic cells having only PN homojunction potential barriers
    • H10F10/142—Photovoltaic cells having only PN homojunction potential barriers comprising multiple PN homojunctions, e.g. tandem cells
    • H10F10/1425—Inverted metamorphic multi-junction [IMM] photovoltaic cells
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F71/00—Manufacture or treatment of devices covered by this subclass
    • H10F71/127—The active layers comprising only Group III-V materials, e.g. GaAs or InP
    • H10F71/1272—The active layers comprising only Group III-V materials, e.g. GaAs or InP comprising at least three elements, e.g. GaAlAs or InGaAsP
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F71/00—Manufacture or treatment of devices covered by this subclass
    • H10F71/139—Manufacture or treatment of devices covered by this subclass using temporary substrates
    • H10F71/1395—Manufacture or treatment of devices covered by this subclass using temporary substrates for thin-film devices
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y02E10/544—Solar cells from Group III-V materials

Definitions

  • the present invention concerns photovoltaic devices. More specifically, the present invention concerns III-V compound based photovoltaic devices and epitaxial lift-off methodologies in the fabrication of III-V compound based photovoltaic devices.
  • III-V compound based photovoltaic devices are epitaxially grown on substrates and remain affixed thereto throughout fabrication and deployment as a solar cell.
  • the substrates can be approximately 150 ⁇ m thick. Having substrates with such thickness may introduce a number of undesirable consequences for a solar cell.
  • the thick substrate can make up a large percentage of the overall weight of the resulting solar cell.
  • weight and size of a solar cell can be significant given the liftoff capability of the selected launch vehicle.
  • the substrate increases the thermal impedance between the solar cell and a heat sink on which the substrate and solar cell may be mounted.
  • the increased thermal impedance results in higher junction temperatures in the solar cell, which, in turn, reduces the efficiency of the solar cell.
  • the substrate serves no purpose other than as a mechanical support for the solar cell.
  • the substrate thickness of approximately 150 ⁇ m, it is typically necessary to remove, mechanically or chemically, part of the substrate, which amounts to further waste.
  • a 150 ⁇ m thick substrate is rigid, which means that the solar cell cannot be mounted on a curved surface and cannot be rolled up for easy storage.
  • the substrate of a solar cell be as thin as possible to reduce the weight and to increase the thermal conductivity
  • thin substrates can also present undesirable difficulties. If the substrate is too thin, the III-V compound solar cell can become so fragile that it is very difficult to handle.
  • GaAs Gallium Arsenide
  • a layer of Gallium Arsenide (GaAs) that is 100 mm in diameter, but only 2-10 ⁇ m thick, tends to crack and break when subjected to even very gentle handling. This consideration applies particularly to whole wafers of III-V compound solar cells. That is, the thinner the substrate, the more difficult it becomes to fabricate whole wafers of III-V compound solar cells without a decrease in yield due to breakage and handling damage.
  • a thin film III-V compound solar cell and methodologies for fabrication of thin film III-V compound solar cells that utilizes a removable and reusable substrate in the fabrication process is desirable.
  • the present invention teaches different structures for thin film III-V compound solar cells free of a substrate and methodologies for fabrication of the same.
  • one or more thin film III-V compound solar cells are epitaxially grown on a sacrificial layer formed on a substrate.
  • the one or more thin film III-V compound solar cells are separated from the substrate by an epitaxial lift-off technique.
  • a metallized layer, polymer layer, or metal/polymer layer is applied to the thin film III-V compound solar cell before the thin film III-V compound solar cell is separated or lifted from the substrate.
  • the sacrificial layer is removed.
  • the metallized layer, polymer layer, or metal/polymer layer allows the thin film III-V compound solar cell to flex without being damaged.
  • the fabrication methodologies taught herein are particularly useful for large-scale fabrication and lift off of thin film III-V solar cells. That is, the fabrication methodologies taught herein are well suited to lift off large area wafers up to 6-inch diameter, which is the largest diameter available for GaAs wafers. Liftoff has been performed on wafers up to 6 inches in diameter.
  • a method for fabrication of a thin film III-V compound solar cell. The method involves providing a substrate. A sacrificial layer is formed on the substrate. A thin film III-V compound solar cell having a single junction is then formed on the sacrificial layer. A backing layer is then formed on the thin film III-V compound solar cell. Once the backing layer is formed, the sacrificial layer is removed from between the thin film III-V compound solar cell and the substrate to separate the thin film III-V compound solar cell from the substrate.
  • a method for forming a multi-junction thin film III-V compound solar cell.
  • the method involves providing a substrate.
  • a sacrificial layer is formed on the substrate.
  • a first III-V compound solar cell junction is formed on the sacrificial layer.
  • a second III-V compound solar cell junction is formed on the first solar cell junction.
  • a backing layer is formed on the second III-V compound solar cell junction. Once the backing layer is formed, the sacrificial layer is removed from between the first solar cell junction and the substrate to separate the multi-junction thin film III-V compound solar cell from the substrate.
  • a method for forming a thin film III-V compound solar cell.
  • the method involves providing a substrate that was previously used in the fabrication of a III-V compound solar cell.
  • a sacrificial layer is formed on the substrate.
  • the thin film III-V compound solar cell is formed on the sacrificial layer.
  • a backing layer is formed the thin film III-V compound solar cell. Once the backing layer is formed, the sacrificial layer may be removed from between the thin film III-V compound solar cell and the substrate to separate the thin film III-V compound solar cell from the substrate.
  • a method for forming a plurality of thin film III-V compound solar cells includes providing a substrate, forming a sacrificial layer on the substrate, forming a full wafer-sized III-V compound solar cell on the sacrificial layer and removing the sacrificial layer from between the wafer-sized solar cell and the substrate to separate the wafer-sized III-V compound solar cell from the substrate on a wafer sized scale.
  • a method for forming a flexible III-V compound solar cell includes receiving a substrate previously used to form a III-V compound solar cell, forming a sacrificial layer on the reused substrate, forming a wafer-sized flexible III-V compound solar cell on the sacrificial layer, forming a backing layer on the solar cell and removing the sacrificial layer from between the solar cell and the substrate to separate the wafer-sized solar cell from the substrate on a wafer sized scale.
  • a method for forming a thin film multiple junction III-V compound solar cell includes the steps of forming a first thin film III-V compound solar cell on a first substrate and forming a second thin film III-V compound solar cell on a second substrate.
  • the method includes the steps of removing by epitaxial lift off one of the first thin film III-V compound solar cell from the first substrate or the second thin film III-V compound solar cell from the second substrate, wafer bonding the first and the second thin film III-V compound solar cell to form a wafer bonded thin film multiple junction III-V compound solar cell and removing by epitaxial lift off the wafer bonded thin film III-V compound solar cell from the remaining substrate.
  • a thin film III-V compound solar cell free of a substrate includes an active layer and a backing layer formed on the active layer.
  • the thin film III-V compound solar cell is initially formed on a substrate and the substrate is subsequently removed to leave the thin film III-V compound solar cell free of the substrate.
  • a thin film III-V compound solar cell free of a substrate includes a plurality of active layers and a backing layer formed on a surface of the active layer having the lowest bandgap energy level.
  • the thin film III-V compound solar cell is formed on a substrate and the substrate is subsequently removed to leave the thin film III-V compound solar cell free of the substrate.
  • another thin film III-V compound solar cell free of a substrate is disclosed.
  • the thin film III-V compound solar cell includes a GaAs active layer and a GaInP active layer.
  • the thin film III-V compound solar cell is formed on a substrate and the substrate is subsequently removed to leave the thin film III-V compound solar cell free of the substrate.
  • another thin film III-V compound solar cell free of a substrate includes a GaInAs active layer and a GaInAsP active layer.
  • the thin film III-V compound solar cell is formed on a substrate and the substrate is subsequently removed to leave the thin film III-V compound solar cell free of the substrate.
  • a wafer bonded thin film III-V compound solar cell free of a substrate includes a GaInAs active layer, a GaInAsP active layer, a GaAs active layer, an AlGaInP active layer, a GaInP active layer, an AlGaInP active layer and a backing layer.
  • the wafer bonded thin film III-V compound solar cell is formed on a substrate and the substrate is subsequently removed to leave the wafer bonded thin film III-V compound solar cell free of the substrate.
  • FIG. 1 is a cross-sectional view of an exemplary stack up of a thin film III-V compound solar cell having a structure in accordance with the teachings of the present invention
  • FIG. 2 is a perspective view of an exemplary array of thin film III-V compound solar cells formed on a wafer in accordance the teachings of the present invention
  • FIG. 3 is a flow diagram depicting steps taken to fabricate a thin film III-V compound solar cell using epitaxial lift-off (ELO) in accordance with the teachings of the present invention
  • FIG. 4A depicts the thin film III-V solar cell of FIG. 1 before ELO;
  • FIG. 4B depicts the thin film III-V solar cell of FIG. 1 after ELO and after further processing in accordance with the teachings of the present invention
  • FIG. 5 is a cross-sectional view of one exemplary stack-up of a thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention
  • FIG. 6 is a cross-sectional view of another exemplary stack up of a thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention.
  • FIG. 7 is an exemplary flow diagram depicting steps taken to fabricate a thin film multiple junction III-V compound solar cell using epitaxial lift-off (ELO) in accordance with the teachings of the present invention
  • FIG. 8A is a cross-sectional view of another exemplary stack up of a wafer bonded thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention.
  • FIG. 8B is a cross-sectional view of another exemplary stack up of a wafer bonded thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention.
  • FIG. 8C is a cross-sectional view of another exemplary stack up of a wafer bonded thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention.
  • FIG. 8D is a cross-sectional view of another exemplary stack up of a wafer bonded thin film multiple junction III-V compound solar cell as taught in accordance with the teachings of the present invention.
  • FIG. 9 is a graph graphically depicting a comparison of the Current v. Bias characteristics of a thin film III-V compound solar cell fabricated in accordance with the teachings herein and a conventionally fabricated III-V compound solar cell having a substrate attached thereto;
  • FIG. 10 is graph graphically depicting the Current v. Bias characteristics of a thin film III-V compound solar cell fabricated in accordance with the teachings herein before and after temperature cycling;
  • FIG. 11 is graph graphically depicting the Current v. Bias characteristics of a thin film III-V compound solar cell with and without an antireflection coating formed thereon as fabricated in accordance with the teachings of the present invention.
  • the present invention discloses thin film III-V compound solar cells and methodologies for fabricating such solar cell devices.
  • the thin film III-V compound solar cells as taught herein are free of a substrate once fabrication is complete.
  • an epitaxial lift-off method is used which allows a thin film III-V compound solar cell to be separated from the substrate.
  • a metallized layer, polymer layer, or metal/polymer layer formed on a surface of an active layer of the thin film III-V compound solar cell provides structural support in the absence of the substrate.
  • the resulting thin film III-V compound solar cell is thinner, lighter, and more flexible than substrate supported solar cell devices (i.e., conventional solar cells) allowing for larger size, such as wafer scale components and wafer scale lift-off of thin film III-V compound solar cells.
  • the substrate can be reused with appropriate repolishing to restore the surface condition in the fabrication of another thin film III-V compound solar cell device.
  • FIG. 1 depicts an exemplary thin film III-V compound solar cell device 100 as taught by the present invention.
  • the thin film III-V compound solar cell 100 includes an active layer 110 A and a backing layer 120 formed on a first surface of the active layer 110 A.
  • the thin film III-V compound solar cell 100 may include additional metallization, an antireflection coating and other like features as discuss below.
  • one active layer i.e., single junction
  • the thin film III-V compound solar cells and the methods of fabricating the same may involve thin film III-V compound solar cells with one active layer, two active layers, three active layers, four active layers or any suitable number of active layers (i.e., single junction and multiple junction thin film III-V compound solar cells).
  • active layer refers to a layer or region of a thin film III-V compound solar cell having a certain band gap energy characteristic, which uses a certain portion of the solar spectrum to generate electricity.
  • each active layer in a multiple junction solar cell device has a different band gap energy characteristic.
  • the reference designation 110 A refers generically to a first active layer of a thin film III-V compound solar cell and does not imply or expressly teach that each first active layer discussed and depicted has the same structure, doping, III-V compound composition, performance, thickness and the like.
  • the reference designation 110 B refers generically to a second active layer of a thin film III-V compound solar cell and does not imply or expressly teach that each second active layer discussed and depicted has the same structure, doping, III-V compound composition, performance, thickness and the like.
  • the reference designation 110 C refers generically to a third active layer of a thin film III-V compound solar cell and does not imply or expressly teach that each third active layer discussed and depicted has the same structure, doping, III-V compound composition, performance, thickness and the like.
  • the reference designation 110 D refers generically to a fourth active layer of a thin film III-V compound solar cell and does not imply or expressly teach that each fourth active layer discussed and depicted has the same structure, doping, III-V compound composition, performance, thickness and the like.
  • the first active layer 110 A of the thin film III-V compound solar cell 100 is formed of one or more III-V compounds.
  • the first active layer 110 A is formed of Gallium Arsenide (GaAs), Gallium Indium Phosphide (GaInP), Gallium Indium Arsenide (GaInAs), Gallium Indium Arsenide Phosphide (GaInAsP), or any other suitable III-V compound.
  • the thin film III-V compound solar cell 100 may have more than one active layer.
  • the active layer may include multiple sub-layers.
  • the backing layer 120 may be formed of a metal, a polymer, or a composite of metal and polymer.
  • the backing layer 120 provides support for the first active layer 110 A when the thin film III-V compound solar cell 100 is separated from a substrate 400 during and after epitaxial lift off (ELO).
  • the substrate 400 serves as a base providing a suitable lattice structure onto which the thin film III-V solar cell 100 is formed.
  • FIG. 4A illustrates one example of the substrate 400 .
  • the substrate 400 may formed from Gallium Arsenide (GaAs), Indium Phosphide (InP), Gallium Phosphide (GaP), Gallium Antimonide (GaSb) or any other suitable III-V compound. As is taught herein, the substrate 400 can be recycled and reused to form another thin film III-V compound solar cell.
  • FIG. 2 depicts an array 110 of thin film III-V solar cells formed on a wafer 150 using the methodologies taught by the present invention.
  • an array 110 of thin film III-V compound solar cells as disclosed herein are often fabricated on a wafer 150 .
  • One of the advantages of the methodologies taught by the present invention is that an entire wafer of a thin film III-V compound solar cell may be lifted from the substrate 400 and further processed to form the array 110 without increasing the risk of damaging the structure of the thin film II-V compound solar cell due to handling.
  • an array 110 of the thin film III-V compound solar cells may be formed after the epitaxial lift off process disclosed herein.
  • the thin film III-V compound solar cell fabricated in accordance with the teachings herein are flexible once lifted off the substrate 400 .
  • FIG. 3 is a block flow diagram of an exemplary method for fabricating thin film III-V solar cells in accordance with the teachings of the present invention.
  • Those skilled in the art will appreciate that to facilitate explanation of one exemplary fabrication methodology one thin film III-V solar cell is discussed. Nonetheless, the fabrication methodology is equally applicable to a thin film III-V solar cell that may have one or more active layers.
  • FIG. 3 is discussed in relation to FIGS. 4A and 4B , which depict exemplary stages in the fabrication of the thin film III-V compound solar cell 100 .
  • the fabrication methodology of the thin film III-V compound solar cell 100 as taught herein involves growing epitaxial layers on a provided substrate.
  • the substrate 400 is provided.
  • the substrate 400 may be a new substrate or may be a substrate that was previously used to fabricate on or more thin film III-V compound solar cells. That is, as is explained below, the substrate 400 is separated from the thin film III-V compound solar cell 100 at some point in the fabrication process and may be recycled and reused to fabricate another thin film III-V solar cell.
  • a sacrificial layer 420 is formed on the substrate 400 .
  • the sacrificial layer 420 is formed on the substrate 400 using a Metal-Organic Chemical Vapor Deposition (MOCVD) methodology, a Molecular Beam Epitaxy (MBE) methodology or any other suitable methodology for forming an epitaxial layer.
  • MOCVD Metal-Organic Chemical Vapor Deposition
  • MBE Molecular Beam Epitaxy
  • the sacrificial layer 420 is lattice matched to the substrate 400 .
  • pseudomorphic or mismatched lattice structures may be implemented.
  • a buffer layer may be used to facilitate growth of mismatched lattice structures.
  • the sacrificial layer could be placed directly on top of the buffer layer, which would permit the removal of the buffer layer along with the substrate in the liftoff process.
  • the sacrificial layer 420 is formed of a material that can be removed using a process such as an epitaxial lift-off (ELO) process.
  • the sacrificial layer 420 is formed of Aluminum Gallium Arsenide (e.g., Al x Ga 1-x As where x>80%) that is n-type or p-type doped.
  • the sacrificial layer 420 is formed of Indium Aluminum Arsenide (e.g., In 0.52 Al 0.48 As) that is n-type or p-type doped.
  • the sacrificial layer 420 is formed of Aluminum Arsenide Antimonide (e.g., AlAs 0.5 Sb 0.5 ) that is n-type or p-type doped, or any other suitable III-V compound.
  • the sacrificial layer 420 is formed of Aluminum Phosphide Antimonide (e.g., AlPxSb 1-x ) that is n-type or p-type doped, or any other suitable III-V compound.
  • the sacrificial layer 420 can have a thickness of approximately 10-200 nm.
  • step 330 the first active layer 110 A is formed on the sacrificial layer 420 .
  • step 330 is repeated “N” number of times, where “N” is an integer, to form multiple active layers or a thin film multiple junction III-V compound solar cell with “N” junctions or active layers.
  • step 340 the backing layer 120 is formed on a surface of the last formed active layer that opposes the substrate 400 . The result of these steps can be seen in FIG. 4A .
  • the backing layer 120 has a thickness of 10-50 ⁇ m, which allows for some flexibility while still providing support.
  • the backing layer 120 is formed of a polymer. Suitable materials for a polymer layer include, but are not limited to polyimide and kapton.
  • the backing layer 120 is formed of metal. Suitable materials for the backing layer 120 include, but are not limited to, Gold, Copper, Aluminum, Titanium, Platinum, Silver, Tungsten, and other alloys. Those skilled in the art will appreciate that other embodiments may be possible.
  • the backing layer 120 is a compound of metal and polymer.
  • step 350 the sacrificial layer 420 is removed from between the first active layer 110 A and the substrate 400 by epitaxial lift off to release the thin film III-V compound solar cell 100 from the substrate 400 .
  • the stack up of the released thin film III-V compound solar cell 100 is depicted in FIG. 1 , before any further processing.
  • step 355 the substrate 400 may be processed and reused to fabricate another thin film III-V compound solar cell as taught herein.
  • step 360 the released thin film III-V compound solar cell 100 is inverted and mounted to a workpiece holder 450 for further processing. That is, the backing layer 120 abuts a surface of the workpiece holder 450 to allow further processing of the active layers.
  • FIG. 4B depicts the thin film III-V compound solar cell 100 mounted to the workpiece holder 450 .
  • the last added active layer for example, the first active layer 110 A is processed to form metallized conductors 140 .
  • the active layers may be etched to remove portions thereof.
  • an antireflection coating 130 (for example, a zinc sulfide/magnesium fluoride coating or other suitable antireflection coating) is formed on a surface of the last added active layer opposing the backing layer 120 .
  • the antireflection coating 130 is formed on the surface of the first active layer 110 A opposing the backing layer 120 .
  • additional processing may be performed such as wafer probing, wafer bonding, testing of individual or groups of thin film III-V compound solar cells, slicing of the wafer to produce individual thin film III-V compound solar cells, packaging of the individual thin film III-V compound solar cells, formation of thin film multiple junction III-V compound solar cells and other like processes.
  • the one or more active layers of the thin film III-V compound solar cells taught herein may be formed of one or more III-V compounds.
  • a thin film III-V compound solar cell may have one or more active layers formed of Gallium Arsenide (GaAs), Gallium Indium Phosphide (GaInP), Gallium Indium Arsenide (GaInAs), Gallium Indium Arsenide Phosphide (GaInAsP), Aluminum Gallium Indium Phosphide (AlGaInP), Indium Phosphide (InP) or any suitable III-V compound.
  • GaAs Gallium Arsenide
  • GaInP Gallium Indium Phosphide
  • GaInAs Gallium Indium Arsenide
  • GaInAsP Gallium Indium Arsenide Phosphide
  • AlGaInP Aluminum Gallium Indium Phosphide
  • InP Indium Phosphide
  • the first active layer 110 A is lattice matched to the sacrificial layer 420 , lattice matched to the substrate 400 or lattice matched to both the sacrificial layer 420 and the substrate 400 .
  • the first active layer 110 A is formed on the sacrificial layer 420 using Metal-Organic Chemical Vapor Deposition (MOCVD).
  • MOCVD Metal-Organic Chemical Vapor Deposition
  • the first active layer 110 A is formed on the sacrificial layer 420 using Molecular Beam Epitaxy (MBE).
  • the thin film III-V compound solar cells taught herein may have more than one active layer. That is, the thin film III-V compound solar cells taught herein may be thin film multiple junction III-V compound solar cells. As described herein, each active layer (i.e., junction) in a thin film multiple junction III-V compound solar cell has a different bandgap energy value.
  • FIGS. 5 , 6 and 8 A- 8 D depict stack ups of some exemplary thin film multiple junction III-V compound solar cells free of a substrate and formed in accordance with the teachings herein.
  • FIG. 5 depicts one exemplary thin film multiple junction III-V compound solar cell 101 fabricated in accordance with the teachings of the present invention.
  • the thin film multiple junction III-V compound solar cell 101 is depicted prior to deposition of the metal layer and removal of the sacrificial layer 420 .
  • the thin film multiple junction III-V compound solar cell 101 can include a metal back layer 120 , an antireflection coating 130 and metallized conductors 140 after further processing in accordance with the teachings of the present invention.
  • the thin film multiple junction solar cell 101 includes a first active layer 110 A and a second active layer 110 B.
  • the thin film multiple junction III-V compound solar cell 101 can include a metal back layer 120 , an antireflection coating 130 and metallized conductors 140 .
  • the first active layer 110 A of the thin film multiple junction solar cell 101 may be formed of Gallium Arsenide (GaAs) having a thickness of between about 100 nm and 3000 nm and having a bandgap energy of about 1.42 eV.
  • GaAs Gallium Arsenide
  • the second active layer 110 B of the thin film multiple junction solar cell 101 is formed of Gallium Indium Phosphide (GaInP) having a thickness of between about 50 nm and 1500 nm and having a bandgap energy of about 1.85 eV.
  • GaInP Gallium Indium Phosphide
  • the exemplary thin film multiple junction III-V compound solar cell 101 may be formed on the sacrificial layer 420 .
  • the sacrificial layer 420 for the thin film multiple junction solar cell 101 may be formed of Aluminum Gallium Arsenide (Al x Ga 1-x As, where x>80%) having a thickness of between about 1 nm and 200 nm and having either a p-type or an n-type doping.
  • the sacrificial layer 420 may be formed on the substrate 400 .
  • the substrate 400 on which the exemplary thin film multiple junction III-V compound solar cell 101 is formed and latter removed may be GaAs.
  • FIG. 6 depicts another exemplary thin film multiple junction III-V compound solar cell 102 fabricated in accordance with the teachings of the present invention.
  • the thin film multiple junction III-V compound solar cell 102 is depicted prior to deposition of the metal layer and removal of the sacrificial layer 420 .
  • the thin film multiple junction III-V compound solar cell 102 can include a metal back layer 120 , an antireflection coating 130 and metallized conductors 140 after further processing in accordance with the teachings of the present invention.
  • the thin film multiple junction solar cell 102 includes a first active layer 110 A and a second active layer 110 B.
  • the thin film multiple junction III-V compound solar cell 102 can include a metal back layer 120 , an antireflection coating 130 and metallized conductors 140 .
  • the first active layer 110 A of the thin film multiple junction III-V compound solar cell 102 may be formed of Gallium Indium Arsenide (GaInAs) having a thickness of between about 100 nm and 5000 nm.
  • GaInAs first active layer 110 A has a bandgap energy of about 0.75 eV.
  • the second active layer 110 B of the thin film multiple junction III-V compound solar cell 102 may be formed of Gallium Indium Arsenide Phosphide (GaInAsP) on the first active layer 110 A.
  • GaInAsP second active layer 110 B may have a thickness of between about 100 nm and 5000 nm and have bandgap energy in the range of between about 0.95-1.00 eV.
  • the exemplary thin film multiple junction III-V compound solar cell 102 may be formed on the sacrificial layer 420 .
  • the sacrificial layer 420 on which the thin film multiple junction III-V compound solar cell 102 is formed may be Indium Aluminum Arsenide (In 0.52 Al 0.48 As) having a thickness of between about 1 nm and 200 nm and having either a p-type or n-type doping.
  • the sacrificial layer 420 on which for the exemplary thin film multiple junction III-V compound solar cell 102 is formed may be Aluminum Arsenide Antimonide (AlAs 0.5 Sb 0.5 ) having a thickness of between about 1 nm and 200 nm and having either a p-type or a n-type doping.
  • the sacrificial layer 420 may be formed on the substrate 400 .
  • the substrate 400 for the exemplary thin film multiple junction III-V compound solar cell 102 may be Indium Phosphide (InP).
  • the first active layer 110 A, the second active layer 110 B, the sacrificial layer 420 and the substrate 400 of the thin film multiple junction III-V compound solar cell 102 may be formed using Metal-Organic Chemical Vapor Deposition (MOCVD) or Molecular Beam Epitaxy (MBE) as discussed above.
  • MOCVD Metal-Organic Chemical Vapor Deposition
  • MBE Molecular Beam Epitaxy
  • thin film multiple junction III-V compound solar cells having more than two active layers are possible in accordance with the teachings of the present invention.
  • thin film multiple junction III-V compound solar cells having three and four active layers may be formed in accordance with the teachings discussed herein.
  • multiple layers may be formed one on top of another in accordance with the steps discussed in relation to FIG. 3 .
  • wafer bonding may be used to join multiple independently formed thin film multiple junction III-V compound solar cells, for example, in accordance with the teachings of the present invention, it is possible to wafer-bond the thin film multiple junction III-V compound solar cell 101 and the thin film multiple junction III-V compound solar cell 102 to form a thin film multiple junction III-V compound solar cell having four active layers.
  • An example of wafer bonding is discussed in relation to FIG. 7 .
  • FIG. 7 is a block flow diagram depicting formation of a thin film III-V compound multiple junction solar cell from other independently formed thin film III-V compound multiple junction solar cells, for example, the thin film III-V compound multiple junction solar cells depicted in FIGS. 5 and 6 .
  • a first thin film III-V compound solar cell is formed.
  • the first thin film III-V compound solar cell may be a single junction solar cell, for example, the thin film III-V compound solar cell 100 or may be a multiple junction solar cell, for example, the thin film multiple junction III-V solar cell 101 or the thin film multiple junction III-V solar cell 102 .
  • the first thin film III-V compound solar cell may be formed in accordance with steps 310 - 350 depicted in FIG. 3 .
  • step 340 may be skipped or bypassed during formation of the first thin film III-V compound solar cell.
  • the reason for skipping or bypassing step 340 is because the formation of the backing layer 120 would interfere with the wafer bonding process that takes place in step 730 below.
  • step 350 may be skipped or bypassed during formation of the first thin film III-V compound solar cell.
  • the sacrificial layer may be removed in step 742 once the first thin film III-V compound solar cell and a second thin film III-V compound solar cell are wafer bonded.
  • a second thin film III-V compound solar cell is formed.
  • the second thin film III-V compound solar cell may be a single junction solar cell, for example, the thin film III-V compound solar cell 100 or may be a multiple junction solar cell, for example, the thin film multiple junction III-V solar cell 101 or the thin film multiple junction III-V solar cell 102 .
  • Those skilled in the art will appreciate that other thin film III-V compound solar cell structures are possible in addition to those discussed in relation to FIGS. 1 , 5 and 6 .
  • the second thin film III-V compound solar cell may be formed in accordance with steps 310 - 350 depicted in FIG. 3 .
  • step 340 may be skipped or bypassed during formation of the second thin film III-V compound solar cell.
  • the reason for skipping or bypassing step 340 is because the formation of the backing layer 120 would interfere with the wafer bonding process that takes place in step 730 below.
  • step 350 may be skipped or bypassed during formation of the second thin film III-V compound solar cell.
  • the sacrificial layer may be removed in step 742 once the first thin film III-V compound solar cell and the second thin film III-V compound solar cell are wafer bonded.
  • steps 710 and 720 may be carried out in parallel fashion or in serial fashion.
  • the first and second thin film III-V compound solar cells are wafer bonded to form a wafer bonded thin film multiple junction III-V compound solar cell 103 .
  • the first and second thin film III-V compound solar cells are wafer bonded to form the wafer bonded thin film multiple junction III-V compound solar cell 100 D.
  • either the first thin film III-V compound solar cell or the second thin film III-V compound solar cell may undergo formation of the backing layer 120 in step 340 and, in turn, an epitaxial lift off process as in step 350 to remove the sacrificial layer 420 .
  • the lifted off thin film III-V compound solar cell with the backing layer 120 is wafer bonded to a surface of an active layer of the other thin film III-V solar cell, which is affixed to the substrate 400 .
  • the wafer bonding may employ a direct wafer bonding methodology that is accomplished by placing one wafer over the other and heating the combined stack to high temperatures (e.g., temperatures >300° C.) under uniformly applied high pressure.
  • the wafer bonding methodology may also involve wafer surface preparation such as cleaning and removal of large particles on the surface. Atomically flat surfaces are needed for wafer bonding. Smoothing of the surfaces can be achieved either by polishing or by chemical etching.
  • a bonding layer is employed between the two surfaces being bonded. In some embodiments, no bonding layer is employed between the two surfaces being bonded.
  • the wafer bonded thin film multiple junction III-V compound solar cell 100 D includes a first active layer 110 A, a second active layer 110 B, a third active layer 110 C and a fourth active layer 110 D.
  • the first active layer 110 A of the wafer bonded thin film multiple junction III-V compound solar cell 100 D is formed of Gallium Indium Arsenide (GaInAs) having a thickness of between about 100 nm and 5000 nm and having a bandgap energy of about 0.75 eV;
  • the second active layer 110 B of the wafer bonded thin film multiple junction III-V compound solar cell 100 D is formed of Gallium Indium Arsenide Phosphide (GaInAsP) having a thickness of between about 100 nm and 3000 nm and having a bandgap energy of between about 0.95-1.00 eV;
  • the third active layer 110 C of the wafer bonded thin film multiple junction III-V compound solar cell 100 D is formed of Gallium Arsenide (GaAs) having a thickness of between about 100 nm and 3000 nm and having a bandgap energy of about 1.42 eV;
  • the epitaxial stack up described above is merely exemplary and that the epitaxial stack up depicted in FIG. 8A is not limited to four active layers or junctions, but may include fewer active layers or junctions, for example, two or three active layers or junctions. In like manner, the epitaxial stack up depicted in FIG. 8A is not limited to four active layers or junctions, but may include more active layers or junctions, for example, five, six, seven or more active layers or junctions.
  • FIG. 8B-8D Other examples of a wafer bonded thin film multiple junction III-V compound solar cell 100 D are depicted in FIG. 8B-8D .
  • FIG. 8B depicts the wafer bonded thin film multiple junction III-V compound solar cell 100 D with two active layers 110 A and 110 B.
  • FIG. 8C depicts the wafer bonded thin film multiple junction III-V compound solar cell 100 D with three active layers 110 A, 110 B and 110 C.
  • FIG. 8D depicts the wafer bonded thin film multiple junction III-V compound solar cell 100 D with five active layers 110 A, 110 B, 110 C, 110 D and 110 E.
  • the wafer bonded thin film multiple junction III-V compound solar cell 100 D is not limited to any particular number of active layers and is not limited to any particular III-V compound stack up or structure.
  • the backing layer 120 is formed after the first and second III-V compound solar cells are wafer bonded.
  • some embodiments include a step 740 .
  • the backing layer 120 is formed on the wafer bonded thin film multiple junction III-V compound solar cell 100 D.
  • the backing layer 120 may also be formed earlier in the process of forming a wafer bonded thin film multiple junction III-V compound solar cell, for example, in step 340 on either the first thin film III-V compound solar cell or the second thin film III-V compound solar cell, but not both.
  • Formation of the backing layer 120 is performed on the active layer or junction having the lowest bandgap energy from amongst the multiple active layers or junctions of the wafer bonded thin film multiple junction III-V compound solar cell 100 D. If formation of the backing layer occurs before or as part of wafer bonding in step 730 , the thin film III-V compound solar cell having the backing layer 120 formed thereon would be removed from the substrate on which it was formed by the epitaxial lift off process of step 340 . The lifted off thin film III-V compound solar cell would be wafer bonded to the other thin film III-V compound solar cell.
  • the backing layer 120 has a thickness of 10-50 ⁇ m, which allows for some flexibility while still providing support.
  • the backing layer 120 is formed of a polymer. Suitable materials for a polymer layer include, but are not limited to polyimide and kapton.
  • the backing layer 120 is formed of metal. Suitable materials for the backing layer 120 include, but are not limited to, Gold, Copper, Aluminum, Titanium, Platinum, Silver, Tungsten, and other alloys. Those skilled in the art will appreciate that other embodiments may be possible.
  • the backing layer 120 is a compound of metal and polymer.
  • the backing layer 120 may be formed on the active layer having the lowest bandgap energy level by plating, evaporation, sputtering, spin coating, or screen-printing. Plating is done either by electrodeposition or electrode less deposition. Formation of the backing layer 120 on the selected active layer having the lowest bandgap energy level assists in increasing the efficiency of a thin film multiple junction III-V compound solar cell of the present invention by recycling photons that are not fully absorbed in the overlying layers via reflection. Additionally, the backing layer 120 provides structural support, thermal dissipation and transfer for the thin film multiple junction III-V compound solar cells of the present invention.
  • step 742 the remaining sacrificial layer or layers are removed in the manner of step 350 .
  • the wafer bonding had taken place without ELO being performed on one of the thin film multiple junction III-V compound solar cells, that the sacrificial layers would be removed in sequence.
  • a backing layer would be applied to the surface from which the substrate had been removed.
  • step 745 the wafer bonded thin film multiple junction III-V compound solar cell 100 D is mounted to a workpiece holder for further processing.
  • a surface the active layer having the highest bandgap energy is metallized to form at least metallized conductors 140 .
  • the metallized conductors 140 may be bus bars or other conductors for interconnecting two or more wafer bonded thin film multiple junction III-V compound solar cells.
  • step 760 an antireflection coating 130 is applied to a surface of the active layer having the highest bandgap energy level of the wafer bonded thin film multiple junction III-V compound solar cell 100 D.
  • the first active layer 110 A or layers, for example, any of the active layers 110 A- 110 D, are separated from the substrate 400 .
  • This lift off and removal of the sacrificial layer 420 is referred to as epitaxial lift-off (ELO).
  • the removal of the sacrificial layer 420 is performed by etching. In such embodiments, this may involve immersing the substrate 400 , sacrificial layer 420 , the various active layers 110 A- 110 D and the backing support layer 120 in an acid etch solution to dissolve the sacrificial layer 420 .
  • the type of acid etch solution depends on the materials used in the substrate 400 , the sacrificial layer 420 , the active layers 110 A- 110 D and the backing layer 120 .
  • An example of a suitable acid etch solution is a solution of approximately 10-25% Hydrofluoric Acid at 50° C.
  • One skilled in the art will appreciate that other suitable etch solutions and methods are possible.
  • the backing layer 120 provides the flexibility to be able to separate and handle individual thin film III-V compound solar cells and a full or partial wafer of thin film III-V solar cells free of a substrate.
  • a thin film III-V compound solar cell formed by using the epitaxial lift-off methodology described herein has performance characteristics similar to conventional solar cells that are affixed to substrates.
  • the thin film III-V compound solar cells as taught herein do not suffer from the drawbacks suffered by such conventional solar cells affixed to a substrate.
  • FIG. 9 graphically depicts a comparison of Current v. Bias (IV) curves for a thin film single junction Gallium Arsenide (GaAs) solar cell manufactured using the epitaxial lift-off method (ELO) disclosed herein and a conventional single junction Gallium Arsenide (GaAs) solar cell affixed to a substrate.
  • the graph 1000 depicts the IV characteristics for the thin film single junction GaAs solar cell formed in accordance with the teachings herein with plot 1010 .
  • the graph 1000 depicts the IV characteristics for the single junction GaAs solar cell affixed to the substrate with plot 1020 .
  • Comparison of the IV plot 1010 and the IV plot 1020 shows that there is no degradation in the IV characteristics of the thin film single junction GaAs solar cell formed in accordance with the teachings herein. Rather, the thin film single junction GaAs solar cell formed in accordance with the teachings herein exhibits improved IV performance characteristics.
  • Solar cells manufactured using the ELO methods of the present invention are also quite robust against thermal shock. To test this, solar cells fabricated using the ELO method taught in the present invention was thermally shocked using liquid nitrogen (LN2).
  • LN2 liquid nitrogen
  • FIG. 10 graphically depicts the measured IV performance characteristics of a thin film III-V compound solar cell formed in accordance with the teachings herein before and after the LN2 cycling.
  • Plot 1120 depicts the measured IV performance characteristics of the thin film III-V compound solar cell formed in accordance with the teachings herein before the LN2 cycling.
  • Plot 1110 depicts the measured IV performance characteristics of the thin film III-V compound solar cell formed in accordance with the teachings herein after the LN2 cycling.
  • a review of the before and after IV performance characteristics show no apparent differences in the IV curves. This suggests that the thin film III-V solar cells formed in accordance with the teachings herein are robust and not susceptible to damage by the thermal shock.
  • FIG. 11 graphically depicts Current v. Bias (IV) performance characteristics from a thin film Gallium Indium Phosphide (GaInP) single junction solar cell formed in accordance with the teachings herein.
  • the IV performance characteristics graphically depicted in FIG. 11 includes a first plot 1210 depicting the measured IV performance characteristics of the GaInP single junction solar cell with the antireflection coating 130 .
  • the thin film III-V solar cell fabrication methodology disclosed herein is not limited to one III-V compound, but rather is well suited for use with a variety of III-V compounds to form thin film III-V compound solar cells free of a substrate.
  • the ELO methodology as taught by the present invention it is possible to create a thin film III-V compound solar cell that performs as well, if not better than, solar cells created using conventional methods and without requiring the thin film III-V compound solar cell to remain affixed to the substrate after fabrication.
  • An additional benefit is that the removed substrate can then be reused to form another thin film III-V compound solar cell.
  • the resulting thin film III-V compound solar cells are lighter, less wasteful and more flexible than those produced using conventional methods.

Landscapes

  • Photovoltaic Devices (AREA)
  • Crystals, And After-Treatments Of Crystals (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Sustainable Energy (AREA)
  • Chemical Vapour Deposition (AREA)
US12/167,588 2007-07-03 2008-07-03 Thin film iii-v compound solar cell Abandoned US20090038678A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/167,588 US20090038678A1 (en) 2007-07-03 2008-07-03 Thin film iii-v compound solar cell

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US95818607P 2007-07-03 2007-07-03
US4585008P 2008-04-17 2008-04-17
US12/167,588 US20090038678A1 (en) 2007-07-03 2008-07-03 Thin film iii-v compound solar cell

Publications (1)

Publication Number Publication Date
US20090038678A1 true US20090038678A1 (en) 2009-02-12

Family

ID=40226434

Family Applications (4)

Application Number Title Priority Date Filing Date
US12/167,588 Abandoned US20090038678A1 (en) 2007-07-03 2008-07-03 Thin film iii-v compound solar cell
US12/167,583 Active 2029-02-25 US7994419B2 (en) 2007-07-03 2008-07-03 Methods for fabricating thin film III-V compound solar cell
US13/165,318 Active US10923617B2 (en) 2007-07-03 2011-06-21 Methods for fabricating thin film III-V compound solar cell
US17/170,133 Active 2029-12-05 US11901476B2 (en) 2007-07-03 2021-02-08 Methods for fabricating thin film III-V compound solar cell

Family Applications After (3)

Application Number Title Priority Date Filing Date
US12/167,583 Active 2029-02-25 US7994419B2 (en) 2007-07-03 2008-07-03 Methods for fabricating thin film III-V compound solar cell
US13/165,318 Active US10923617B2 (en) 2007-07-03 2011-06-21 Methods for fabricating thin film III-V compound solar cell
US17/170,133 Active 2029-12-05 US11901476B2 (en) 2007-07-03 2021-02-08 Methods for fabricating thin film III-V compound solar cell

Country Status (8)

Country Link
US (4) US20090038678A1 (fr)
EP (2) EP2168171A4 (fr)
JP (2) JP5576273B2 (fr)
KR (2) KR20100047246A (fr)
CN (2) CN101785115B (fr)
CA (2) CA2692126A1 (fr)
SG (2) SG182989A1 (fr)
WO (2) WO2009005824A1 (fr)

Cited By (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100047959A1 (en) * 2006-08-07 2010-02-25 Emcore Solar Power, Inc. Epitaxial Lift Off on Film Mounted Inverted Metamorphic Multijunction Solar Cells
US20100116327A1 (en) * 2008-11-10 2010-05-13 Emcore Corporation Four junction inverted metamorphic multijunction solar cell
WO2010062991A1 (fr) 2008-11-26 2010-06-03 Microlink Devices, Inc. Pile solaire dotée d'un orifice de surface inférieure permettant de s'engager avec la couche émettrice
US20100203730A1 (en) * 2009-02-09 2010-08-12 Emcore Solar Power, Inc. Epitaxial Lift Off in Inverted Metamorphic Multijunction Solar Cells
US20100310775A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Spalling for a Semiconductor Substrate
US20100307572A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Heterojunction III-V Photovoltaic Cell Fabrication
US20100307591A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Single-Junction Photovoltaic Cell
US20110048516A1 (en) * 2009-06-09 2011-03-03 International Business Machines Corporation Multijunction Photovoltaic Cell Fabrication
US20110048517A1 (en) * 2009-06-09 2011-03-03 International Business Machines Corporation Multijunction Photovoltaic Cell Fabrication
US7939428B2 (en) 2000-11-27 2011-05-10 S.O.I.Tec Silicon On Insulator Technologies Methods for making substrates and substrates formed therefrom
US20110155231A1 (en) * 2009-12-31 2011-06-30 Tzer-Perng Chen Multi-junction solar cell
US20110186910A1 (en) * 2009-09-10 2011-08-04 The Regents Of The University Of Michigan Methods of preparing flexible photovoltaic devices using epitaxial liftoff, and preserving the integrity of growth substrates used in epitaxial growth
US20120091474A1 (en) * 2010-10-13 2012-04-19 NuPGA Corporation Novel semiconductor and optoelectronic devices
US8278133B2 (en) 2010-04-20 2012-10-02 Panasonic Corporation Method for joining a film onto a substrate
EP2515349A1 (fr) * 2011-04-18 2012-10-24 Everphoton Energy Corporation Paquet de cellule solaire III-V et son procédé de fabrication
US20120285520A1 (en) * 2011-05-13 2012-11-15 International Business Machines Corporation Wafer bonded solar cells and fabrication methods
US8497421B2 (en) * 2011-08-26 2013-07-30 Institute Of Nuclear Energy Research Atomic Energy Council, Executive Yuan Lift-off structure for substrate of a photoelectric device and method thereof
US20140034699A1 (en) * 2012-08-02 2014-02-06 King Abdulaziz City For Science And Technology Method for improving quality of spalled material layers
KR20140043805A (ko) * 2011-07-06 2014-04-10 더 리젠츠 오브 더 유니버시티 오브 미시간 에피택셜 리프트 오프 및 냉간 용접 결합된 반도체 태양 전지를 사용한 일체형 태양열 집열기
US8778199B2 (en) 2009-02-09 2014-07-15 Emoore Solar Power, Inc. Epitaxial lift off in inverted metamorphic multijunction solar cells
EP2831929A1 (fr) * 2012-03-28 2015-02-04 Soitec Fabrication de dispositifs de cellule solaire multi-jonctions
US20150122313A1 (en) * 2012-03-28 2015-05-07 Soitec Manufacture of multijunction solar cell devices
US9650148B2 (en) 2012-02-15 2017-05-16 Microlink Devices, Inc. Integration of high-efficiency, lightweight solar sheets onto unmanned aerial vehicle for increased endurance
US10141469B1 (en) * 2016-10-17 2018-11-27 Stc.Unm Radially stacked solar cells based on 2D atomic crystals and methods for their production
DE102012209891B4 (de) 2011-06-15 2018-12-13 Globalfoundries Inc. Verfahren für eine gesteuerte Entfernung einer Halbleiterelementschicht von einem Grundsubstrat
US10490688B2 (en) 2011-10-11 2019-11-26 Soitec Multi junctions in a semiconductor device formed by different deposition techniques
US10811551B2 (en) 2016-11-22 2020-10-20 Korea Research Institute Of Standards And Science Tandem solar cell including metal disk array
US10923617B2 (en) 2007-07-03 2021-02-16 Microlink Devices, Inc. Methods for fabricating thin film III-V compound solar cell
US10957808B2 (en) 2017-11-28 2021-03-23 Korea Research Institute Of Standards And Science Flexible double-junction solar cell
US11398575B2 (en) * 2017-04-07 2022-07-26 Microlink Devices, Inc. Back-contact thin film semiconductor device structures and methods for their production

Families Citing this family (51)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9634172B1 (en) 2007-09-24 2017-04-25 Solaero Technologies Corp. Inverted metamorphic multijunction solar cell with multiple metamorphic layers
US9117966B2 (en) 2007-09-24 2015-08-25 Solaero Technologies Corp. Inverted metamorphic multijunction solar cell with two metamorphic layers and homojunction top cell
US10381501B2 (en) 2006-06-02 2019-08-13 Solaero Technologies Corp. Inverted metamorphic multijunction solar cell with multiple metamorphic layers
US10381505B2 (en) 2007-09-24 2019-08-13 Solaero Technologies Corp. Inverted metamorphic multijunction solar cells including metamorphic layers
GB2467935B (en) 2009-02-19 2013-10-30 Iqe Silicon Compounds Ltd Formation of thin layers of GaAs and germanium materials
GB2467934B (en) * 2009-02-19 2013-10-30 Iqe Silicon Compounds Ltd Photovoltaic cell
US20100248413A1 (en) * 2009-03-31 2010-09-30 David Strand Monolithic Integration of Photovoltaic Cells
KR101108245B1 (ko) * 2010-03-24 2012-01-31 광주과학기술원 화합물 반도체 태양 전지의 제조 방법
WO2012018997A2 (fr) * 2010-08-06 2012-02-09 Semprius, Inc. Matières et procédés permettant de démouler des dispositifs à semi-conducteur composé imprimables
CN102376788A (zh) * 2010-08-11 2012-03-14 朱忻 用于太阳能电池的多层薄膜及其制备方法和用途
WO2012021880A2 (fr) * 2010-08-13 2012-02-16 Solexel, Inc. Appareil et procédé de fabrication répétée de substrats semi-conducteurs à couches minces au moyen d'un gabarit
KR101163154B1 (ko) * 2010-09-30 2012-07-06 광주과학기술원 고효율 연성 캘코파이럿계 화합물 반도체 박막태양전지의 제조 방법
US9425249B2 (en) 2010-12-01 2016-08-23 Alliance For Sustainable Energy, Llc Coincident site lattice-matched growth of semiconductors on substrates using compliant buffer layers
WO2012074523A1 (fr) 2010-12-01 2012-06-07 Alliance For Sustainable Energy, Llc Procédés de fabrication de semi-conducteurs autoportants à l'aide de couches tampons sacrificielles et de substrats recyclables
US8643062B2 (en) 2011-02-02 2014-02-04 Transphorm Inc. III-N device structures and methods
CN102655177A (zh) * 2011-03-02 2012-09-05 亿芳能源科技股份有限公司 Iii-v族太阳能电池封装件及其制法
CA2840517A1 (fr) * 2011-06-29 2013-06-27 Stephen R. Forrest Couches de protection de gravure sacrificielle pour reutilisation de tranches apres arrachage epitaxial
CN102299210A (zh) * 2011-09-14 2011-12-28 中国科学院苏州纳米技术与纳米仿生研究所 倒装薄膜太阳能电池的制作方法
US8541315B2 (en) 2011-09-19 2013-09-24 International Business Machines Corporation High throughput epitaxial lift off for flexible electronics
US8492187B2 (en) 2011-09-29 2013-07-23 International Business Machines Corporation High throughput epitaxial liftoff for releasing multiple semiconductor device layers from a single base substrate
CN103035775A (zh) * 2011-09-29 2013-04-10 北儒精密股份有限公司 太阳能电池组及其制造方法
US20150255668A1 (en) * 2011-09-30 2015-09-10 Microlink Devices, Inc. Thin film inp-based solar cells using epitaxial lift-off
KR101309924B1 (ko) 2012-03-21 2013-09-17 주식회사 포스코 광소자 제조방법
JP2015133339A (ja) * 2012-04-25 2015-07-23 パナソニック株式会社 光電変換装置
US8569097B1 (en) 2012-07-06 2013-10-29 International Business Machines Corporation Flexible III-V solar cell structure
JP2014060382A (ja) 2012-08-20 2014-04-03 Toshiba Corp 光電変換素子、光電変換システムおよび光電変換素子の製造方法
US8748324B1 (en) 2013-02-26 2014-06-10 The Boeing Company Systems and methods for separating components of a multilayer stack of electronic components
CN104009047B (zh) * 2013-02-27 2017-10-24 中国科学院苏州纳米技术与纳米仿生研究所 一种倒装结构的激光光伏电池及其制作方法
KR101455724B1 (ko) * 2013-04-24 2014-11-03 한국광기술원 실리콘 기판을 재활용한 고효율 iii-v 태양전지와 광전소자 및 그의 제조방법
KR101455723B1 (ko) * 2013-04-24 2014-11-04 한국광기술원 실리콘기판을 재활용한 고효율 iii-v 나노 막대 태양전지 및 그의 제조방법
KR101926621B1 (ko) * 2013-05-20 2018-12-07 엘지전자 주식회사 화합물 반도체 태양전지의 제조 방법
US9831363B2 (en) * 2014-06-19 2017-11-28 John Farah Laser epitaxial lift-off of high efficiency solar cell
US9340895B1 (en) 2013-06-27 2016-05-17 The Boeing Company Systems and methods for separating components of a multilayer stack of electronic components
CN103489958B (zh) * 2013-08-27 2015-09-02 湖南红太阳光电科技有限公司 一种柔性硅基砷化镓电池的制备方法
CN103594539B (zh) * 2013-10-22 2016-02-10 扬州乾照光电有限公司 一种柔性多结GaAs太阳电池及其制备方法
US10141465B2 (en) 2014-04-04 2018-11-27 The Regents Of The University Of Michigan Epitaxial lift-off processed GaAs thin-film solar cells integrated with non-tracking mini-compound parabolic concentrators
CN104538284A (zh) * 2014-12-30 2015-04-22 西安交通大学 一种在硅片上集成化合物半导体器件的工艺
KR102533932B1 (ko) 2015-03-18 2023-05-17 더 리젠츠 오브 더 유니버시티 오브 미시간 사전 패터닝된 메사들을 통한 스트레인 경감 에피택셜 리프트-오프
KR101743017B1 (ko) 2015-05-19 2017-06-05 한국과학기술연구원 고속 에피택셜 리프트오프와 iii-v족 직접 성장용 템플릿을 이용한 반도체 소자의 제조 방법 및 이에 의해 제조된 반도체 소자
KR101633871B1 (ko) * 2015-06-08 2016-06-28 한국광기술원 3-5족 화합물 반도체 제조방법
US9653308B2 (en) 2015-08-28 2017-05-16 International Business Machines Corporation Epitaxial lift-off process with guided etching
CN105470115B (zh) * 2015-12-08 2018-10-23 中国电子科技集团公司第十八研究所 一种将砷化镓外延层转移至金属柔性衬底的方法
WO2018013193A2 (fr) 2016-04-18 2018-01-18 Microlink Devices, Inc. Intégration de feuilles solaires légères à haute rendement sur un véhicule aérien sans pilote pour une endurance accrue
US12249667B2 (en) 2017-08-18 2025-03-11 Solaero Technologies Corp. Space vehicles including multijunction metamorphic solar cells
JP6652111B2 (ja) 2017-07-18 2020-02-19 トヨタ自動車株式会社 太陽電池の製造方法
US20190181289A1 (en) 2017-12-11 2019-06-13 Solaero Technologies Corp. Multijunction solar cells
JP6937050B2 (ja) * 2018-08-09 2021-09-22 中国科学院蘇州納米技術与納米▲ファン▼生研究所 フレキシブル太陽電池の製造方法
KR20200021772A (ko) * 2018-08-21 2020-03-02 엘지전자 주식회사 화합물 반도체 태양전지 및 이의 제조 방법
US10717610B1 (en) * 2019-02-06 2020-07-21 National Presort, Inc. Mechanically locking diverter
KR102193767B1 (ko) * 2019-07-23 2020-12-21 고려대학교 산학협력단 다층 페로브스카이트 구조체의 제조방법과, 이로부터 제조된 다층 페로브스카이트 구조체 및 태양전지
CN119008811A (zh) * 2024-10-25 2024-11-22 南昌凯迅光电股份有限公司 一种空间用多结太阳电池及其制备方法

Citations (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4661712A (en) * 1985-05-28 1987-04-28 Varian Associates, Inc. Apparatus for scanning a high current ion beam with a constant angle of incidence
US4816420A (en) * 1980-04-10 1989-03-28 Massachusetts Institute Of Technology Method of producing tandem solar cell devices from sheets of crystalline material
US4846931A (en) * 1988-03-29 1989-07-11 Bell Communications Research, Inc. Method for lifting-off epitaxial films
US5336909A (en) * 1991-08-16 1994-08-09 Kabushiki Kaisha Toshiba Bipolar transistor with an improved collector structure
US5458694A (en) * 1992-04-15 1995-10-17 Picogiga Societe Anonyme Multispectral photovoltaic component comprising a stack of cells, and method of manufacture
US5853497A (en) * 1996-12-12 1998-12-29 Hughes Electronics Corporation High efficiency multi-junction solar cells
US6043520A (en) * 1998-04-02 2000-03-28 Mitsubishi Denki Kabushiki Kaisha III-V heterojunction bipolar transistor having a GaAs emitter ballast
US20010016366A1 (en) * 1997-01-29 2001-08-23 Sharp Kabushiki Kaisha Method for fabricating semiconductor light emitting element
US20030025179A1 (en) * 2001-07-20 2003-02-06 Microlink Devices, Inc. Graded base GaAsSb for high speed GaAs HBT
US20030047289A1 (en) * 1999-12-13 2003-03-13 Claude Jaussaud Intermediate suction support and its utilisation or producing a thin film structure
US20030136956A1 (en) * 2002-01-18 2003-07-24 Nec Compound Semiconductor Devices, Ltd. Heterojunction bipolar transistor and semiconductor integrated circuit device using the same
US20040118451A1 (en) * 2002-05-24 2004-06-24 Wladyslaw Walukiewicz Broad spectrum solar cell
US20040166681A1 (en) * 2002-12-05 2004-08-26 Iles Peter A. High efficiency, monolithic multijunction solar cells containing lattice-mismatched materials and methods of forming same
US20040206389A1 (en) * 2003-04-21 2004-10-21 Sharp Kabushiki Kaisha Compound solar battery and manufacturing method thereof
US20050172996A1 (en) * 2004-02-05 2005-08-11 Advent Solar, Inc. Contact fabrication of emitter wrap-through back contact silicon solar cells
US6946309B2 (en) * 1997-06-03 2005-09-20 Lumileds Lighting U.S., Llc III-Phosphide and III-Arsenide flip chip light-emitting devices
US6974521B2 (en) * 2000-10-18 2005-12-13 Katholieke Universiteit Nijmegen Method for separating a film and a substrate
US20060054900A1 (en) * 2004-09-09 2006-03-16 Sharp Kabushiki Kaisha Compound semiconductor device epitaxial growth substrate, semiconductor device, and manufacturing method thereof
US20060144435A1 (en) * 2002-05-21 2006-07-06 Wanlass Mark W High-efficiency, monolithic, multi-bandgap, tandem photovoltaic energy converters
US20060162768A1 (en) * 2002-05-21 2006-07-27 Wanlass Mark W Low bandgap, monolithic, multi-bandgap, optoelectronic devices
US20070032089A1 (en) * 2004-06-04 2007-02-08 The Board Of Trustees Of The University Of Illinois Printable Semiconductor Structures and Related Methods of Making and Assembling
US20090044860A1 (en) * 2007-07-03 2009-02-19 Microlink Devices, Inc. Methods for fabricating thin film iii-v compound solar cell
US7687886B2 (en) * 2004-08-19 2010-03-30 Microlink Devices, Inc. High on-state breakdown heterojunction bipolar transistor

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63107073A (ja) * 1986-06-26 1988-05-12 Matsushita Electric Ind Co Ltd 薄膜太陽電池の製造法
JP2680582B2 (ja) * 1987-10-19 1997-11-19 三洋電機株式会社 光起電力装置の製造方法
JPH02291135A (ja) 1989-05-01 1990-11-30 Sumitomo Electric Ind Ltd ヘテロ接合バイポーラトランジスタ
JPH06310521A (ja) 1993-04-23 1994-11-04 Nippon Telegr & Teleph Corp <Ntt> バイポーラトランジスタ
JP3292894B2 (ja) 1993-05-12 2002-06-17 日本電信電話株式会社 集積化受光回路
US5557146A (en) * 1993-07-14 1996-09-17 University Of South Florida Ohmic contact using binder paste with semiconductor material dispersed therein
JPH07161727A (ja) 1993-12-02 1995-06-23 Hitachi Ltd ヘテロバイポーラトランジスタ
GB2330687B (en) * 1997-10-22 1999-09-29 Printable Field Emitters Ltd Field emission devices
US6455186B1 (en) * 1998-03-05 2002-09-24 Black & Decker Inc. Battery cooling system
US7022556B1 (en) * 1998-11-11 2006-04-04 Semiconductor Energy Laboratory Co., Ltd. Exposure device, exposure method and method of manufacturing semiconductor device
US6320206B1 (en) * 1999-02-05 2001-11-20 Lumileds Lighting, U.S., Llc Light emitting devices having wafer bonded aluminum gallium indium nitride structures and mirror stacks
AU3594000A (en) * 1999-03-01 2000-09-21 Sensors Unlimited Inc. Epitaxially grown p-type diffusion source for photodiode fabrication
US6380480B1 (en) * 1999-05-18 2002-04-30 Nippon Sheet Glass Co., Ltd Photoelectric conversion device and substrate for photoelectric conversion device
JP2003504877A (ja) * 1999-07-13 2003-02-04 アイトゲネーシシエ テクニシエ ホッホシューレ （エーテーハー） 可撓性薄層太陽電池
US6340788B1 (en) * 1999-12-02 2002-01-22 Hughes Electronics Corporation Multijunction photovoltaic cells and panels using a silicon or silicon-germanium active substrate cell for space and terrestrial applications
US6274402B1 (en) 1999-12-30 2001-08-14 Sunpower Corporation Method of fabricating a silicon solar cell
JP2001326229A (ja) 2000-05-12 2001-11-22 Toshiba Corp ヘテロ接合バイポーラトランジスタ及びその製造方法
US6956283B1 (en) * 2000-05-16 2005-10-18 Peterson Kenneth A Encapsulants for protecting MEMS devices during post-packaging release etch
US20020092558A1 (en) 2001-01-18 2002-07-18 Kim Seong Bae Integrated thin film cell and fabrication method thereof
GB0114896D0 (en) 2001-06-19 2001-08-08 Bp Solar Ltd Process for manufacturing a solar cell
JP4471584B2 (ja) * 2003-04-28 2010-06-02 シャープ株式会社 化合物太陽電池の製造方法
US20060226440A1 (en) 2003-09-04 2006-10-12 Pan Janet L Use of deep-level transitions in semiconductor devices
JP2005142532A (ja) * 2003-10-14 2005-06-02 Matsushita Electric Ind Co Ltd 窒化物半導体素子の製造方法
CN1938866A (zh) * 2004-03-31 2007-03-28 罗姆股份有限公司 叠层型薄膜太阳能电池及其制造方法
WO2006015185A2 (fr) * 2004-07-30 2006-02-09 Aonex Technologies, Inc. Cellule solaire a triple jonction gainp/gaas/si obtenue par liaison de tranches et transfert de couches
JP4397792B2 (ja) * 2004-11-10 2010-01-13 シャープ株式会社 化合物半導体素子の製造方法
JP2006216896A (ja) * 2005-02-07 2006-08-17 Canon Inc 太陽電池の製造方法
US10374120B2 (en) 2005-02-18 2019-08-06 Koninklijke Philips N.V. High efficiency solar cells utilizing wafer bonding and layer transfer to integrate non-lattice matched materials
US8089062B2 (en) * 2005-03-23 2012-01-03 Xerox Corporation Wax encapsulated electronic devices
WO2007032546A1 (fr) * 2005-09-16 2007-03-22 Showa Denko K.K. Procede de fabrication d'un dispositif lumineux a semi-conducteur nitrure
US7450295B2 (en) * 2006-03-02 2008-11-11 Qualcomm Mems Technologies, Inc. Methods for producing MEMS with protective coatings using multi-component sacrificial layers
US7956370B2 (en) * 2007-06-12 2011-06-07 Siphoton, Inc. Silicon based solid state lighting
WO2011146015A1 (fr) * 2010-05-18 2011-11-24 Agency For Science, Technology And Research Procédé de formation d'une structure de diode électroluminescente et structure de diode électroluminescente
JP2011253925A (ja) * 2010-06-02 2011-12-15 Toshiba Corp 発光装置の製造方法

Patent Citations (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4816420A (en) * 1980-04-10 1989-03-28 Massachusetts Institute Of Technology Method of producing tandem solar cell devices from sheets of crystalline material
US4661712A (en) * 1985-05-28 1987-04-28 Varian Associates, Inc. Apparatus for scanning a high current ion beam with a constant angle of incidence
US4846931A (en) * 1988-03-29 1989-07-11 Bell Communications Research, Inc. Method for lifting-off epitaxial films
US5336909A (en) * 1991-08-16 1994-08-09 Kabushiki Kaisha Toshiba Bipolar transistor with an improved collector structure
US5458694A (en) * 1992-04-15 1995-10-17 Picogiga Societe Anonyme Multispectral photovoltaic component comprising a stack of cells, and method of manufacture
US5853497A (en) * 1996-12-12 1998-12-29 Hughes Electronics Corporation High efficiency multi-junction solar cells
US20010016366A1 (en) * 1997-01-29 2001-08-23 Sharp Kabushiki Kaisha Method for fabricating semiconductor light emitting element
US6946309B2 (en) * 1997-06-03 2005-09-20 Lumileds Lighting U.S., Llc III-Phosphide and III-Arsenide flip chip light-emitting devices
US6043520A (en) * 1998-04-02 2000-03-28 Mitsubishi Denki Kabushiki Kaisha III-V heterojunction bipolar transistor having a GaAs emitter ballast
US20030047289A1 (en) * 1999-12-13 2003-03-13 Claude Jaussaud Intermediate suction support and its utilisation or producing a thin film structure
US6974521B2 (en) * 2000-10-18 2005-12-13 Katholieke Universiteit Nijmegen Method for separating a film and a substrate
US20030025179A1 (en) * 2001-07-20 2003-02-06 Microlink Devices, Inc. Graded base GaAsSb for high speed GaAs HBT
US20030136956A1 (en) * 2002-01-18 2003-07-24 Nec Compound Semiconductor Devices, Ltd. Heterojunction bipolar transistor and semiconductor integrated circuit device using the same
US20060144435A1 (en) * 2002-05-21 2006-07-06 Wanlass Mark W High-efficiency, monolithic, multi-bandgap, tandem photovoltaic energy converters
US20060162768A1 (en) * 2002-05-21 2006-07-27 Wanlass Mark W Low bandgap, monolithic, multi-bandgap, optoelectronic devices
US20040118451A1 (en) * 2002-05-24 2004-06-24 Wladyslaw Walukiewicz Broad spectrum solar cell
US20040166681A1 (en) * 2002-12-05 2004-08-26 Iles Peter A. High efficiency, monolithic multijunction solar cells containing lattice-mismatched materials and methods of forming same
US7488890B2 (en) * 2003-04-21 2009-02-10 Sharp Kabushiki Kaisha Compound solar battery and manufacturing method thereof
US20040206389A1 (en) * 2003-04-21 2004-10-21 Sharp Kabushiki Kaisha Compound solar battery and manufacturing method thereof
US20050172996A1 (en) * 2004-02-05 2005-08-11 Advent Solar, Inc. Contact fabrication of emitter wrap-through back contact silicon solar cells
US20070032089A1 (en) * 2004-06-04 2007-02-08 The Board Of Trustees Of The University Of Illinois Printable Semiconductor Structures and Related Methods of Making and Assembling
US7687886B2 (en) * 2004-08-19 2010-03-30 Microlink Devices, Inc. High on-state breakdown heterojunction bipolar transistor
US20100237388A1 (en) * 2004-08-19 2010-09-23 Microlink Devices, Inc. High on-state breakdown heterojunction bipolar transistor
US20110147799A1 (en) * 2004-08-19 2011-06-23 Microlink Devices, Inc. High on-state breakdown heterojunction bipolar transistor
US20060054900A1 (en) * 2004-09-09 2006-03-16 Sharp Kabushiki Kaisha Compound semiconductor device epitaxial growth substrate, semiconductor device, and manufacturing method thereof
US20090044860A1 (en) * 2007-07-03 2009-02-19 Microlink Devices, Inc. Methods for fabricating thin film iii-v compound solar cell
US7994419B2 (en) * 2007-07-03 2011-08-09 Microlink Devices, Inc. Methods for fabricating thin film III-V compound solar cell

Cited By (53)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7939428B2 (en) 2000-11-27 2011-05-10 S.O.I.Tec Silicon On Insulator Technologies Methods for making substrates and substrates formed therefrom
US20100047959A1 (en) * 2006-08-07 2010-02-25 Emcore Solar Power, Inc. Epitaxial Lift Off on Film Mounted Inverted Metamorphic Multijunction Solar Cells
US10923617B2 (en) 2007-07-03 2021-02-16 Microlink Devices, Inc. Methods for fabricating thin film III-V compound solar cell
US11901476B2 (en) 2007-07-03 2024-02-13 Microlink Devices, Inc. Methods for fabricating thin film III-V compound solar cell
US20100116327A1 (en) * 2008-11-10 2010-05-13 Emcore Corporation Four junction inverted metamorphic multijunction solar cell
US8236600B2 (en) * 2008-11-10 2012-08-07 Emcore Solar Power, Inc. Joining method for preparing an inverted metamorphic multijunction solar cell
WO2010062991A1 (fr) 2008-11-26 2010-06-03 Microlink Devices, Inc. Pile solaire dotée d'un orifice de surface inférieure permettant de s'engager avec la couche émettrice
US20100203730A1 (en) * 2009-02-09 2010-08-12 Emcore Solar Power, Inc. Epitaxial Lift Off in Inverted Metamorphic Multijunction Solar Cells
US8778199B2 (en) 2009-02-09 2014-07-15 Emoore Solar Power, Inc. Epitaxial lift off in inverted metamorphic multijunction solar cells
US20110048517A1 (en) * 2009-06-09 2011-03-03 International Business Machines Corporation Multijunction Photovoltaic Cell Fabrication
US8633097B2 (en) 2009-06-09 2014-01-21 International Business Machines Corporation Single-junction photovoltaic cell
US20110048516A1 (en) * 2009-06-09 2011-03-03 International Business Machines Corporation Multijunction Photovoltaic Cell Fabrication
US8823127B2 (en) 2009-06-09 2014-09-02 International Business Machines Corporation Multijunction photovoltaic cell fabrication
US20100307591A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Single-Junction Photovoltaic Cell
US20100307572A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Heterojunction III-V Photovoltaic Cell Fabrication
US8802477B2 (en) 2009-06-09 2014-08-12 International Business Machines Corporation Heterojunction III-V photovoltaic cell fabrication
US20100310775A1 (en) * 2009-06-09 2010-12-09 International Business Machines Corporation Spalling for a Semiconductor Substrate
US8703521B2 (en) 2009-06-09 2014-04-22 International Business Machines Corporation Multijunction photovoltaic cell fabrication
WO2011066029A3 (fr) * 2009-09-10 2012-05-31 The Regents Of The University Of Michigan Procédés de préparation de dispositifs photovoltaïques souples à l'aide de décollement épitaxial, et de préservation de l'intégrité de substrats de croissance utilisés dans une croissance épitaxiale
US8378385B2 (en) 2009-09-10 2013-02-19 The Regents Of The University Of Michigan Methods of preparing flexible photovoltaic devices using epitaxial liftoff, and preserving the integrity of growth substrates used in epitaxial growth
US20110186910A1 (en) * 2009-09-10 2011-08-04 The Regents Of The University Of Michigan Methods of preparing flexible photovoltaic devices using epitaxial liftoff, and preserving the integrity of growth substrates used in epitaxial growth
US8927319B2 (en) 2009-09-10 2015-01-06 The Regents Of The University Of Michigan Methods of preparing flexible photovoltaic devices using epitaxial liftoff, and preserving the integrity of growth substrates used in epitaxial growth
US20110155231A1 (en) * 2009-12-31 2011-06-30 Tzer-Perng Chen Multi-junction solar cell
US9559229B2 (en) * 2009-12-31 2017-01-31 Epistar Corporation Multi-junction solar cell
US8659110B2 (en) 2010-02-26 2014-02-25 International Business Machines Corporation Single-junction photovoltaic cell
US8278133B2 (en) 2010-04-20 2012-10-02 Panasonic Corporation Method for joining a film onto a substrate
US20120091474A1 (en) * 2010-10-13 2012-04-19 NuPGA Corporation Novel semiconductor and optoelectronic devices
EP2515349A1 (fr) * 2011-04-18 2012-10-24 Everphoton Energy Corporation Paquet de cellule solaire III-V et son procédé de fabrication
US10686090B2 (en) 2011-05-13 2020-06-16 International Business Machines Corporation Wafer bonded solar cells and fabrication methods
US20120285520A1 (en) * 2011-05-13 2012-11-15 International Business Machines Corporation Wafer bonded solar cells and fabrication methods
US9818901B2 (en) * 2011-05-13 2017-11-14 International Business Machines Corporation Wafer bonded solar cells and fabrication methods
DE102012209891B4 (de) 2011-06-15 2018-12-13 Globalfoundries Inc. Verfahren für eine gesteuerte Entfernung einer Halbleiterelementschicht von einem Grundsubstrat
KR101996607B1 (ko) 2011-07-06 2019-10-01 더 리젠츠 오브 더 유니버시티 오브 미시간 에피택셜 리프트 오프 및 냉간 용접 결합된 반도체 태양 전지를 사용한 일체형 태양열 집열기
KR20140043805A (ko) * 2011-07-06 2014-04-10 더 리젠츠 오브 더 유니버시티 오브 미시간 에피택셜 리프트 오프 및 냉간 용접 결합된 반도체 태양 전지를 사용한 일체형 태양열 집열기
US12132127B2 (en) 2011-07-06 2024-10-29 The Regents Of The University Of Michigan Integrated solar collectors using epitaxial lift off and cold weld bonded semiconductor solar cells
US8497421B2 (en) * 2011-08-26 2013-07-30 Institute Of Nuclear Energy Research Atomic Energy Council, Executive Yuan Lift-off structure for substrate of a photoelectric device and method thereof
TWI585990B (zh) * 2011-08-26 2017-06-01 行政院原子能委員會核能研究所 用於光電元件之基板的剝離結構
US10490688B2 (en) 2011-10-11 2019-11-26 Soitec Multi junctions in a semiconductor device formed by different deposition techniques
US9650148B2 (en) 2012-02-15 2017-05-16 Microlink Devices, Inc. Integration of high-efficiency, lightweight solar sheets onto unmanned aerial vehicle for increased endurance
US10214295B2 (en) 2012-02-15 2019-02-26 Microlink Devices, Inc. High-efficiency, lightweight solar sheets
US20150083202A1 (en) * 2012-03-28 2015-03-26 Soitec Manufacture of multijunction solar cell devices
US20150122313A1 (en) * 2012-03-28 2015-05-07 Soitec Manufacture of multijunction solar cell devices
EP2831929A1 (fr) * 2012-03-28 2015-02-04 Soitec Fabrication de dispositifs de cellule solaire multi-jonctions
US9564335B2 (en) 2012-08-02 2017-02-07 International Business Machines Corporation Method for improving quality of spalled material layers
US9275867B2 (en) 2012-08-02 2016-03-01 International Business Machines Corporation Method for improving quality of spalled material layers
US8916450B2 (en) * 2012-08-02 2014-12-23 International Business Machines Corporation Method for improving quality of spalled material layers
US20140034699A1 (en) * 2012-08-02 2014-02-06 King Abdulaziz City For Science And Technology Method for improving quality of spalled material layers
US10026618B2 (en) 2012-08-02 2018-07-17 International Business Machines Corporation Method for improving quality of spalled material layers
US10680129B1 (en) 2016-10-17 2020-06-09 Stc.Unm Radially stacked solar cells based on 2D atomic crystals and methods for their production
US10141469B1 (en) * 2016-10-17 2018-11-27 Stc.Unm Radially stacked solar cells based on 2D atomic crystals and methods for their production
US10811551B2 (en) 2016-11-22 2020-10-20 Korea Research Institute Of Standards And Science Tandem solar cell including metal disk array
US11398575B2 (en) * 2017-04-07 2022-07-26 Microlink Devices, Inc. Back-contact thin film semiconductor device structures and methods for their production
US10957808B2 (en) 2017-11-28 2021-03-23 Korea Research Institute Of Standards And Science Flexible double-junction solar cell

Also Published As

Publication number Publication date
EP2168172B1 (fr) 2019-05-22
CA2692124A1 (fr) 2009-01-08
US11901476B2 (en) 2024-02-13
JP5576273B2 (ja) 2014-08-20
US7994419B2 (en) 2011-08-09
CN101785115A (zh) 2010-07-21
EP2168172A1 (fr) 2010-03-31
WO2009005824A1 (fr) 2009-01-08
JP2010532576A (ja) 2010-10-07
CN101790794A (zh) 2010-07-28
US10923617B2 (en) 2021-02-16
WO2009005825A8 (fr) 2010-02-11
EP2168172A4 (fr) 2016-05-18
EP2168171A4 (fr) 2016-05-18
CN101785115B (zh) 2013-05-08
KR20100047246A (ko) 2010-05-07
US20210328093A1 (en) 2021-10-21
SG182989A1 (en) 2012-08-30
SG182990A1 (en) 2012-08-30
WO2009005825A1 (fr) 2009-01-08
US20090044860A1 (en) 2009-02-19
US20110318866A1 (en) 2011-12-29
JP5576272B2 (ja) 2014-08-20
CA2692126A1 (fr) 2009-01-08
JP2010532575A (ja) 2010-10-07
EP2168171A1 (fr) 2010-03-31
KR20100049575A (ko) 2010-05-12

Similar Documents

Publication Publication Date Title
US11901476B2 (en) Methods for fabricating thin film III-V compound solar cell
US8927319B2 (en) Methods of preparing flexible photovoltaic devices using epitaxial liftoff, and preserving the integrity of growth substrates used in epitaxial growth
US10186629B2 (en) Thin film lift-off via combination of epitaxial lift-off and spalling
US20150083202A1 (en) Manufacture of multijunction solar cell devices
Tatavarti et al. Lightweight, low cost GaAs solar cells on 4 ″epitaxial liftoff (ELO) wafers
US20150059832A1 (en) Manufacture of multijunction solar cell devices
Pan Epitaxial lift-off of large-area GaAs multi-junction solar cells for high efficiency clean and portable energy power generation
US20150027519A1 (en) Manufacture of multijunction solar cell devices
US8691663B2 (en) Methods of manipulating stressed epistructures

Legal Events

Date Code Title Description
AS Assignment

Owner name: MICROLINK DEVICES, INC., ILLINOIS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PAN, NOREN;HILLIER, GLEN;VU, DUY PHACH;AND OTHERS;REEL/FRAME:023433/0507;SIGNING DATES FROM 20091016 TO 20091022

AS Assignment

Owner name: NASA, DISTRICT OF COLUMBIA

Free format text: CONFIRMATORY LICENSE;ASSIGNOR:MICROLINK DEVICES INC.;REEL/FRAME:024901/0822

Effective date: 20100318

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: U.S. DEPARTMENT OF ENERGY, DISTRICT OF COLUMBIA

Free format text: CONFIRMATORY LICENSE;ASSIGNOR:MICROLINK DEVICES, INC;REEL/FRAME:070118/0473

Effective date: 20241028

点击 这是indexloc提供的php浏览器服务，不要输入任何密码和下载