US20080139761A1

US20080139761A1 - Process for polymerizing 1-butene

Info

Publication number: US20080139761A1
Application number: US12/006,938
Authority: US
Inventors: Luigi Resconi
Original assignee: Basell Polyolefine GmbH
Current assignee: Basell Polyolefine GmbH
Priority date: 2003-05-12
Filing date: 2008-01-07
Publication date: 2008-06-12
Also published as: JP5584639B2; KR101060985B1; US7579423B2; JP4771938B2; US20080132659A1; EP1622948B1; KR20060009330A; US7390862B2; WO2004099269A3; EP1622948A2; US20060235173A1; WO2004099269A2; US20080275254A1; JP2006526042A; JP2011168784A

Abstract

A process for polymerizing 1-butene, optionally with up to 30% by mol of ethylene, propylene or an alpha olefin of formula CH₂═CHT wherein T is a C₃-C₁₀alkyl group, in the presence of a catalyst system obtainable by contacting a metallocene compound of formula (I) Wherein M is an atom of a transition metal; X, is a hydrogen atom, a halogen atoms or a hydrocarbon group; R¹, R², R⁵, R⁶, R⁷, R⁸and R⁹are hydrogen atoms or hydrocarbon groups; with the proviso that at least one of R⁶or R⁷is a C₁-C₂₀alkyl group; R³and R⁴are C₁-C₂₀alkyl groups; and an alumoxane and/or a compound capable of forming an alkyl metallocene cation.

Description

The present invention relates to a process for polymerizing 1-butene by using metallocene compounds and to the isotactic 1-butene polymers obtained thereby.
Isotactic 1-butene polymers are well known in the art. In view of their good properties in terms of pressure resistance, creep resistance, and impact strength they have a lot of uses such as the manufacture of pipes to be used in the metal pipe replacement, easy-open packaging and films.
1-Butene (co)polymers are generally prepared by (co)polymerzing 1-butene in the presence of TiCl₃based catalysts components together with diethylaluminum chloride (DEAC) as cocatalyst. In some cases diethyl aluminum iodide (DEAI) is also used in mixtures with DEAC. The thus obtained polymers, however, generally do not show satisfactory mechanical properties. Furthermore, in view of the low yields obtainable with the TiCl₃based catalysts, the 1-butene polymers prepared with these catalysts have a high content of catalyst residues (generally more than 300 ppm of Ti) which lowers the properties of the polymers making it necessary a deashing step.
1-Butene (co)polymers can also be obtained by polymerizing the monomers in the presence of a stereospecific catalyst comprising (A) a solid component comprising a Ti compound and an electron-donor compound supported on MgCl₂; (B) an alkylaluminum compound and, optionally, (C) an external electron-donor compound. A process of this type is disclosed, for instance, in EP-A-172961 and in WO99/45043. Recently, metallocene compounds have been proposed for producing 1-butene polymers. In Macromolecules 1995, 28, 1739-1749, rac-dimethylsilylbis(4,5,6,7-tetrahydro-1-indenyl)zirconium dichloride and methylaluminoxane have been used for polymerizing 1-butene. The yield of the process is not indicated and the molecular weight of the obtained polymer (Mn) is very low. In Macromol. Rapid Commun. 18, 581-589 (1997), rac- and meso-[dimethylsilylenebis(2,3,5-trimethyl-cyclopentadienyl)]zirconium dichloride have been used for the polymerization of 1-butene. The yields of the process and the molecular weight of the obtained polymers are rather low.
In WO 02/16450, 1-butene polymers endowed with low isotacticity are described. These polymers are obtained by using a specific class of double-bridged metallocene compounds.
In the international application WO 03/042258, 1-butene polymers obtained with metallocene compounds wherein a π ligand is a cyclopentadithiophene moiety are described. It has now been found that, by selecting a specific substitution pattern in the other n moiety of the metallocene compound, the molecular weight of the obtained polymers can be further increased and, at the same time, obtained in high yields.
Thus, according to a first aspect, the present invention provides a process for preparing 1-butene polymers, said process comprising polymerizing 1-butene or copolymerizing 1-butene with ethylene, propylene or an alpha-olefin of formula CH₂═CHT wherein T is a C₃-C₁₀alkyl group, in the presence of a catalyst system obtainable by contacting:

(A) a metallocene compound belonging to the following formula (I):

wherein:
M is an atom of a transition metal selected from those belonging to group 3, 4, or to the lanthanide or actinide groups in the Periodic Table of the Elements; preferably M is zirconium titanium or hafnium;
X, equal to or different from each other, is a hydrogen atom, a halogen atom, a R, OR, OR′O, OSO₂CF₃, OCOR, SR, NR₂or PR₂group wherein R is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and R′ is a C₁-C₂₀-alkylidene, C₆-C₂₀-arylidene, C₇-C₂₀-alkylarylidene, or C₇-C₂₀-arylalkylidene radical; preferably X is a hydrogen atom, a halogen atom, a OR′O or R group; more preferably X is chlorine or a methyl radical;
R¹, R², R⁵, R⁶, R⁷, R⁸and R⁹, equal to or different from each other, are hydrogen atoms, or linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or R⁵and R⁶, and/or R⁸and R⁹can optionally form a saturated or unsaturated, 5 or 6 membered rings, said ring can bear C₁-C₂₀alkyl radicals as substituents; with the proviso that at least one of R⁶or R⁷is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably a C₁-C₁₀-alkyl radical;
preferably R¹, R², are the same and are C₁-C₁₀alkyl radicals optionally containing one or more silicon atoms; more preferably R¹and R²are methyl radicals;
R⁸and R⁹, equal to or different from each other, are preferably C₁-C₁₀alkyl or C₆-C₂₀aryl radicals; more preferably they are methyl radicals;
R⁵is preferably a hydrogen atom or a methyl radical;
R⁶is preferably a hydrogen atom or a methyl, ethyl or isopropyl radical;
R⁷is preferably a linear or branched, saturated or unsaturated C₁-C₂₀-allyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably a C₁-C₁₀-alkyl radical; more preferably R⁷is a methyl or ethyl radical; otherwise when R⁶is different from a hydrogen atom, R⁷is preferably a hydrogen atom
R³and R⁴, equal to or different from each other, are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R³and R⁴equal to or different from each other are C₁-C₁₀-alkyl radicals; more preferably R³is a methyl, or ethyl radical; and R⁴is a methyl, ethyl or isopropyl radical;

(B) an alumoxane or a compound capable of forming an alkyl metallocene cation; and optionally
(C) an organo aluminum compound.

Metallocene compounds of formula (I) have been described, for example, in WO 01/47939.
Preferably the compounds of formula (I) have formula (Ia) or (Ib):

Wherein

M, X, R¹, R², R⁸and R⁹have been described above;
R³and R⁴, equal to or different from each other, are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R³and R⁴equal to or different from each other are C₁-C₁₀-alkyl radicals; more preferably R³is a methyl, or ethyl radical; and R⁴is a methyl, ethyl or isopropyl radical; R⁶and R⁷are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably C₁-C₁₀-alkyl radicals; more preferably R⁷is a methyl or ethyl radical; and R⁶is a methyl, ethyl or isopropyl radical.
Alumoxanes used as component B) can be obtained by reacting water with an organo-aluminium compound of formula H_jAlU_3-jor H_jAl₂U_6-j, where U substituents, same or different, are hydrogen atoms, halogen atoms, C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or or C7-C20-arylalkyl radical, optionally containing silicon or germanium atoms with the proviso that at least one U is different from halogen, and j ranges from 0 to 1, being also a non-integer number. In this reaction the molar ratio of Al/water is preferably comprised between 1:1 and 100:1. The molar ratio between aluminium and the metal of the metallocene generally is comprised between about 10:1 and about 20000:1, and more preferably between about 100:1 and about 5000:1. The alumoxanes used in the catalyst according to the invention are considered to be linear, branched or cyclic compounds containing at least one group of the type:
wherein the substituents U, same or different, are described above.
In particular, alumoxanes of the formula:
can be used in the case of linear compounds, wherein n¹is 0 or an integer from 1 to 40 and the substituents U are defined as above, or alumoxanes of the formula:
can be used in the case of cyclic compounds, wherein n²is an integer from 2 to 40 and the U substituents are defined as above. Examples of alumoxanes suitable for use according to the present invention are methylalumoxane (MAO), tetra-(isobutyl)alumoxane (TIBAO), tetra-(2,4,4-trimethyl-pentyl)alumoxane (TIOAO), tetra-(2,3-dimethylbutyl)alumoxane (TDMBAO) and tetra-(2,3,3-trimethylbutyl)alumoxane (TTMBAO). Particularly interesting cocatalysts are those described in WO 99/21899 and in WO01/21674 in which the alkyl and aryl groups have specific branched patterns. Non-limiting examples of aluminium compounds according to WO 99/21899 and WO01/21674 are:
tris(2,3,3-trimethyl-butyl)aluminium, tris(2,3-dimethyl-hexyl)aluminium, tris(2,3-dimethyl-butyl)aluminium, tris(2,3-dimethyl-pentyl)aluminium, tris(2,3 dimethyl-heptyl)aluminium, tris(2-methyl-3-ethyl-pentyl)aluminium, tris(2-methyl-3-ethyl-hexyl)aluminium, tris(2-methyl-3-ethyl-heptyl)aluminium, tris(2-methyl-3-propyl-hexyl)aluminium, tris(2-ethyl-3-methyl-butyl)aluminium, tris(2-ethyl-3-methyl-pentyl)aluminium, tris(2,3-diethyl-pentyl)aluminium, tris(2-propyl-3-methyl-butyl)aluminium, tris(2-isopropyl-3-methyl-butyl)aluminium, tris(2-isobutyl-3-methyl-pentyl)aluminium, tris(2,3,3-trimethyl-pentyl)aluminium, tris(2,3,3-trimethyl-hexyl)aluminium, tris(2-ethyl-3,3-dimethyl-butyl)aluminium, tris(2-ethyl-3,3-dimethyl-pentyl)aluminium, tris(2-isopropyl-3,3-dimethyl-butyl)aluminium, tris(2-trimethylsilyl-propyl)aluminium, tris(2-methyl-3-phenyl-butyl)aluminium, tris(2-ethyl-3-phenyl-butyl)aluminium, tris(2,3-dimethyl-3-phenyl-butyl)aluminium, tris(2-phenyl-propyl)aluminium, tris[2-(4-fluoro-phenyl)-propyl]aluminium, tris[2-(4-chloro-phenyl)-propyl]aluminium, tris[2-(3-isopropyl-phenyl)-propyl]aluminium, tris(2-phenyl-butyl)aluminium, tris(3-methyl-2-phenyl-butyl)aluminium, tris(2-phenyl-pentyl)aluminium, tris[2-(pentafluorophenyl)-propyl]aluminium, tris[2,2-diphenyl-ethyl]aluminium and tris[2-phenyl-2-methyl-propyl]aluminium, as well as the corresponding compounds wherein one of the hydrocarbyl groups is replaced with a hydrogen atom, and those wherein one or two of the hydrocarbyl groups are replaced with an isobutyl group.
Amongst the above aluminium compounds, trimethylaluminium (TMA), triisobutylaluminum (TIBAL), tris(2,4,4-trimethyl-pentyl)aluminum (TIOA), tris(2,3-dimethylbutyl)aluminium TDMBA) and tris(2,3,3-trimethylbutyl)aluminum (TTMBA) are preferred.
Non-limiting examples of compounds able to form an alkylmetallocene cation are compounds of formula D⁺E⁻ wherein D⁺ is a Brønsted acid, able to donate a proton and to react irreversibly with a substituent X of the metallocene of formula (I) and E⁻ is a compatible anion, which is able to stabilize the active catalytic species originating from the reaction of the two compounds, and which is sufficiently labile to be able to be removed by an olefinic monomer. Preferably, the anion E⁻ comprises of one or more boron atoms. More preferably, the anion E⁻ is an anion of the formula BAr₄ ⁽⁻⁾, wherein the substituents Ar which can be identical or different are aryl radicals such as phenyl, pentafluorophenyl or bis(trifluoromethyl)phenyl. Tetrakis-pentafluorophenyl borate is particularly preferred examples of these compounds are described in WO 91/02012. Moreover, compounds of the formula BAr₃can conveniently be used. Compounds of this type are described, for example, in the published International patent application WO 92/00333. Other examples of compounds able to form an alkylmetallocene cation are compounds of formula BAr₃P wherein P is a substituted or unsubstituted pyrrol radicals. These compounds are described in WO01/62764. Other examples of cocatalyst can be found in EP 775707 and DE 19917985. Compounds containing boron atoms can be conveniently supported according to the description of DE-A-19962814 and DE-A-19962910. All these compounds containing boron atoms can be used in a molar ratio between boron and the metal of the metallocene comprised between about 1:1 and about 10:1; preferably 1:1 and 2.1; more preferably about 1:1.
Non limiting examples of compounds of formula D⁺E⁻ are:

Triethylammoniumtetra(phenyl)borate,
Tributylanunoniumtetra(phenyl)borate,
Trimethylammoniumtetra(tolyl)borate,
Tributylammoniumtetra(tolyl)borate,
Tributylammoniumtetra(pentafluorophenyl)borate,
Tributylammoniumtetra(pentafluorophenyl)aluminate,
Tripropylammoniumtetra(dimethylphenyl)borate,
Tributylammoniumtetra(trifluoromethylphenyl)borate,
Tributylammoniumtetra(4-fluorophenyl)borate,
N,N-Dimethylaniliniumtetra(phenyl)borate,
N,N-Diethylaniliniumtetra(phenyl)borate,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)boratee,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)aluminate,
Di(propyl)ammoniumtetrakis(pentafluorophenyl)borate,
Di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borate,
Triphenylphosphoniumtetrais(phenyl)borate,
Triethylphosphoniumtetrakis(phenyl)borate,
Diphenylphosphoniumtetrakis(phenyl)borate,
Tri(methylphenyl)phosphoniumtetrakis(phenyl)borate,
Tri(dimethylphenyl)phosphoniumtetrakis(phenyl)borate,
Triphenylcarbeniumtetrakis(pentafluorophenyl)borate,
Triphenylcarbeniumtetrais(pentafluorophenyl)aluminate,
Triphenylcarbeniumtetr-akis(phenyl)aluminate,
Ferroceniumtetrakis(pentafluorophenyl)borate,
Ferroceniumtetrakis(pentafluorophenyl)aluminate.
Triphenylcarbeniumtetrais(pentafluorophenyl)borate,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate.

Organic aluminum compounds used as compound C) are those of formula H_jAlU_3-jor H_jAl₂U_6-jdescribed above. The catalysts of the present invention can also be supported on an inert carrier. This is achieved by depositing the metallocene compound A) or the product of the reaction thereof with the component B), or the component B) and then the metallocene compound A) on an inert support such as, for example, silica, alumina, Al—Si, Al—Mg mixed oxides, magnesium halides, styrene/divinylbenzene copolymers, polyethylene or polypropylene. The supportation process is carried out in an inert solvent such as hydrocarbon for example toluene, hexane, pentane or propane and at a temperature ranging from 0° C. to 100° C., preferably the process is carried out at a temperature ranging from 25° C. to 90° C. or the process is carried out at room temperature.
A suitable class of supports which can be used is that constituted by porous organic supports functionalized with groups having active hydrogen atoms. Particularly suitable are those in which the organic support is a partially crosslinked styrene polymer. Supports of this type are described in European application EP-633272. Another class of inert supports particularly suitable for use according to the invention is that of polyolefin porous prepolymers, particularly polyethylene. A further suitable class of inert supports for use according to the invention is that of porous magnesium halides such as those described in International application WO 95/32995.
With the process of the present invention it is possible to obtain 1-butene polymers having high molecular weight, measured in terms of their intrinsic viscosity (I.V.) and in high yields. Thus, according to another aspect, the present invention provides 1-butene homopolymers having the following characteristics:

- isotactic pentads (mmmm)>90, preferably >95;
- intrinsic viscosity (I.V.) measured in tetrahydronaphtalene (THN) at 135° C.>1.2, preferably ≧1.5, more preferably >1.9; even more preferably >2.4;
- melting point (D.S.C.) higher than 100° C.; and
- molecular weight distribution Mw/Mn<4, preferably <3.5.

The 1-butene homopolymers of the present invention do not have 4,1 insertions (regioerrors) detectable with a 400 MHz spectrometer operating at 100.61 MHz.
When 1-butene is copolymerized with ethylene, propylene or alpha olefins of formula CH₂═CHT wherein T is a C₃-C₁₀alkyl group, a copolymer having a content of comonomer derived units of up to 50% by mol can be obtained, preferably up to 20% by mol, more preferably from 0.2% by mol to 15% by mol. Examples of alpha-olefins of formula CH₂═CHT are 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-octene, 4,6-dimethyl-1-heptene, 1-decene, 1-dodecene. Preferred comonomers to be used in the process according to the present invention are ethylene, propylene and 1-hexene.
In particular, the 1-butene ethylene copolymers obtainable by the process of the present invention are endowed with a very low melting point with respect to the ethylene content thus it is possible to lower the melting point of the 1-butene/ethylene polymer by adding small amount of ethylene. furthermore ethylene is used as comonomer in the process of the present invention the resulting copolymer shows a higher molecular weight with respect to the homopolymers and the yield of the process is improved. Therefore a further embodiment of the present invention is a process for preparing copolymer of 1-butene and ethylene, comprising the step of copolymerizing 1-butene and ethylene in the presence of the catalyst system reported above. Preferably the amount of ethylene in the liquid phase ranges from 0.01 to 30% by weight; preferably from 1% to 10% by weight.
Preferably the 1-butene/ethylene copolymers have an ethylene content comprised between 0.2% by mol and 15% by mol; preferably comprised between 1% by mol and 10% by mol; more preferably comprised between 2% by mol and 8% by mol.
Therefore a further object of the present invention is a 1-butene/ethylene copolymer having an ethylene content comprised between 0.2% by mol and 15% by mol; preferably comprised between 1% by mol and 10% by mol; more preferably comprised between 2% by mol and 8% by mol., obtainable by the process of the present invention, having the following characteristics:

- isotactic pentads (mmmm)>90, preferably >95;
- intrinsic viscosity (I.V.) measured in tetrahydronaphtalene (THN) at 135° C.>1.2, preferably ≧1.5, more preferably >1.9; even more preferably >2.4;
  wherein the percent by mol of the ethylene content in the polymer (C₂) and the melting point of the polymer (Tm) meet the following relation:

Tm<−4.4C ₂+92.0.
Preferably the relation is Tm<4.4C₂+90.2; more preferably it is Tm<4.4C₂+89.2.
The polymerization process of the present invention can be carried out in liquid phase, optionally in the presence of an inert hydrocarbon solvent, or in gas phase. Said hydrocarbon solvent can be either aromatic (such as toluene) or aliphatic (such as propane, hexane, heptane, isobutane, cyclohexane and 2,2,4-trimethylpentane). Preferably, the polymerization process of the present invention is carried out by using liquid 1-butene as polymerization medium. The polymerization temperature preferably ranges from 0° C. to 250° C.; preferably comprised between 20° C. and 150° C. and, more particularly between 50° C. and 90° C.; The molecular weight distribution can be varied by using mixtures of different metallocene compounds or by carrying out the polymerization in several stages which differ as to the polymerization temperature and/or the concentrations of the molecular weight regulators and/or the monomers concentration. Moreover by carrying out the polymerization process by using a combination of two different metallocene compounds of formula (I) a polymer endowed with a broad melting is produced. The polymerization yield depends on the purity of the transition metal organometallic catalyst compound (A) in the catalyst, therefore, said compound can be used as such or can be subjected to purification treatments before use.
The polymerization process of the present invention can be carried out in the presence of hydrogen in order to increase the yield. Preferably the concentration of hydrogen in the liquid phase ranges from 0.5 ppm to 20 ppm; more preferably from 1 ppm to 6 ppm. The effect of improving the yield of the process is additive with the effect of ethylene explained above.
A further object of the present invention is a metallocene compound of formula (II):
wherein:
M is an atom of a transition metal selected from those belonging to group 3, 4, or to the lanthanide or actinide groups in the Periodic Table of the Elements; preferably M is zirconium titanium or hafnium; X, equal to or different from each other, is a hydrogen atom, a halogen atom, a R, OR, OR′O, OSO₂CF₃, OCOR, SR, NR₂or PR₂group wherein R is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and R′ is a C₁-C₂₀-alkylidene, C₆-C₂₀-arylidene, C₇-C₂₀-alkylarylidene, or C₇-C₂₀-arylalkylidene radical; preferably X is a hydrogen atom, a halogen atom, a OR′O or R group; more preferably X is chlorine or a methyl radical; R¹, R², R⁵, R⁷, R⁸and R⁹, equal to or different from each other, are hydrogen atoms, or linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or R⁸and R⁹can optionally form a saturated or unsaturated, 5 or 6 membered ring; preferably R¹, R², are the same and are C₁-C₁₀alkyl radicals optionally containing one or more silicon atoms; more preferably R¹and R²are methyl radicals;
R⁸and R⁹, equal to or different from each other, are preferably C₁-C₁₀alkyl or C₆-C₂₀aryl radicals; more preferably they are methyl radicals;
R⁵is preferably a hydrogen atom or a methyl radical;
R⁷is preferably a hydrogen atom;
R³and R⁴, equal to or different from each other, are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R³and R⁴equal to or different from each other are C₁-C₁₀-alkyl radicals; more preferably R³is a methyl, or ethyl radical; and R⁴is a methyl, ethyl or isopropyl radical;
R⁶is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or it can optionally form with R⁵a saturated or unsaturated, 5 or 6 membered ring, said ring can bear C₁-C₂₀alkyl radicals as substituents; preferably R⁶is a C₁-C₁₀alkyl radical; more preferably R⁶is a methyl, ethyl or isopropyl radical;
By using this class of compounds in the process according to the present invention polybutene homo or copolymers endowed with a higher molecular weight measured in terms of their intrinsic viscosity (I.V.) and in high yields are obtained.
A further object of the present invention is a ligand of formula (III):
wherein R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸and R⁹have the meaning described above.
Metallocene compounds of formula (II) can be obtained by reacting the ligand of formula (III) with a compound capable of forming a corresponding dianionic compound thereof and thereafter with a compound of formula Mx₄, wherein M and X have the meaning described above. Example of compound able to form the dianionic compound are alkyl lithium such as methyl lithium or butyl lithium, Grignard reagents or metallic sodium and potassium.
The following examples are for illustrative purpose and do not intend to limit the scope of the invention.

EXAMPLES

Experimental Section

The intrinsic viscosity (I.V.) was measured in tetrahydronaphtalene (THN) at 135° C.
The melting points of the polymers (T_m) were measured by Differential Scanning Calorimetry (D.S.C.) on a Perkin Elmer DSC-7 instrument, according to the standard method. A weighted sample (5-7 mg) obtained from the polymerization was sealed into aluminum pans and heated to 180° C. at 10° C./minute. The sample was kept at 180° C. for 5 minutes to allow a complete melting of all the crystallites, then cooled to 20° C. at 10° C./minute. After standing 2 minutes at 20° C., the sample was heated for the second time to 180° C. at 10° C./min. In this second heating run, the peak temperature was taken as the melting temperature (T_m) and the area of the peak as melting enthalpy (ΔH_f).
Molecular weight parameters and molecular weight distribution for all the samples were measured using a Waters 150C ALC/GPC instrument (Waters, Milford, Mass., USA) equipped with four mixed-gel columns PLgel 20 μm Mixed-A LS (Polymer Laboratories, Church Stretton, United Kingdom). The dimensions of the columns were 300×7.8 mm. The solvent used was TCB and the flow rate was kept at 1.0 mL/min. Solution concentrations were 0.1 g/dL in 1,2,4 trichlorobenzene (TCB). 0.1 g/L of 2,6-di-t-butyl-4-methyl phenol (BHT) was added to prevent degradation and the injection volume was 300 μL. All the measurements were carried out at 135° C. GPC calibration is complex, as no well-characterized narrow molecular weight distribution standard reference materials are available for 1-butene polymers. Thus, a universal calibration curve was obtained using 12 polystyrene standard samples with molecular weights ranging from 580 to 13,200,000. It was assumed that the K values of the Mark-Houwink relationship were: K_PS=1.21×10⁻⁴, dLg and K_PB=1.78×10⁻⁴dL/g for polystyrene and poly-1-butene respectively. The Mark-Houwink exponents a were assumed to be 0.706 for polystyrene and 0.725 for poly-1-butene. Even though, in this approach, the molecular parameters obtained were only an estimate of the hydrodynamic volume of each chain, they allowed a relative comparison to be made.
¹³C-NMR spectra were acquired on a DPX-400 spectrometer operating at 100.61 MHz in the Fourier transform mode at 120° C. The samples were dissolved in 1,1,2,2-tetrachloroethane-d2 at 120° C. with a 8% wt/v concentration. Each spectrum was acquired with a 90° pulse, 15 seconds of delay between pulses and CPD (waltz16) to remove ¹H-¹³C coupling. About 3000 transients were stored in 32K data points using a spectral window of 6000 Hz. The isotacticity of metallocene-made PB is measured by ¹³C NMR, and is defined as the relative intensity of the mmmm pentad peak of the diagnostic methylene of the ethyl branch. This peak at 27.73 ppm was used as internal reference. Pentad assignments are given according to Macromolecules, 1992, 25, 6814-6817. After baseline correction, this region is integrated between 28.60-27.27 ppm (mmmm+mmmr+mmrr) and 26.78-26.48 ppm (mrrm). The phase of the two integrals is then corrected and the first integral splitted at 27.4 ppm to separate the mmrr pentad contribution. The mmmr peak overlaps with the base of the mmmm pentad and cannot be separated. Statistical modelling of pentad distributions was done using a model based on. enantiomorphic site control as a function of the probability parameter b (for the insertion of the preferred enantioface), as described in Chem. Rev. 2000, 100, 1253-1345.
Taking into account the overlap between the mmmm and the mmmr pentads, the following expression were used:
mmmm+mmmr=b ⁵+(1−b)⁵+2[b ⁴(1−b)+b(1−b)⁴]
mmrr=2[b ⁴(1−b)+b(1−b)⁴]
mrrm=b ⁴(1−b)+b(1−b)⁴
Assignments of 4,1 insertion were made according to V. Busico, R. Cipullo, A. Borriello, Macromol. Rapid. Commun. 1995, 16, 269-274.

Preparation of Catalyst Components

Rac dimethylsilyl{(2,4,7-trimethyl-1-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dichloride (A-1); dimethylsilyl{(1-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dichloride (A-2); dimethylsilyl{(2-methyl-1-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dichloride (A-3) were prepared according to WO 01/47939.

Synthesis of dimethylsilyl[1-(2,4,6-trimethyl-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophenyl)]zirconium dichloride (A-4)

a) Synthesis of chloro(2,4,6-trimethyl-indenyl)dimethylsilane

A 2.5 M n-BuLi solution in hexane (37.2 mL, 0.093 mol) was added dropwise at 0° C. under nitrogen atmosphere to a solution of 14.00 g of 2,4,6-trimethyl-indene (prepared according to Eur. Pat. Appl. 693,506) in 100 mL of Et₂O in a 500 mL 3-necked round flask. During the addition a white suspension was formed. The mixture was then allowed to warm up to r.t. and stirred for 30 min, with final formation of a white suspension. Then a solution of Me₂SiCl₂(98%, d=1,064, 11.28 mL, 0.093 mol.) in 30 mL of THF was cooled to 0° C. and slowly added to the lithium salt suspension, also cooled to 0° C. The reaction mixture was allowed to warm up to r. t. and stirred for 2 h with final formation of a light yellow suspension. The solvents were then removed in vacuo and the residue was extracted with 150 mL of toluene to remove the LiCl. The light yellow filtrate was brought to dryness in vacuo to give 21.53 g of a yellow oil, characterized by ¹NMR analysis as the target product, yield 97.5%. This product was used as such in the next step without further purification.

b) Synthesis of 1-(2,4,6-trimethyl-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]dithiophene) dimethylsilane

A 2.5 M n-BuLi solution in hexane (16.74 mL, 41.85 mmol) was added dropwise at 0° C. under stirring to a solution of 8.21 g of 2,5-dimethyl-7H-cyclopenta[1,2-b:4,3-b′]-dithiophene (39.79 mmol) in 150 mL of Et₂O in a 500 mL 3-necked round flask. At the end of the addition, the resulting dark suspension was stirred for 30 min at r. t. A solution of chloro(2,4,6-trimethyl-indenyl)dimethylsilane (10.00 g, 39.87 mmol) in 20 mL of THF was cooled to 0° C. and slowly added to the above suspension, with final formation of a dark suspension. The latter was allowed to warm up to room temperature and stirred for 3 h. Then the reaction mixture was concentrated under reduced pressure to give a dark solid, which was extracted at r. t. with 150 mL of toluene to remove the LiCl. The extract was dried in vacuo to give 17.37 g of a dark colored sticky foam. The ¹NMR analysis showed the presence of the desired ligand together with some impurities. The product was used as such in the next step without further purification.

c) Synthesis of dimethylsilyl[1-(2,4,6-trimethyl-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophenyl)]zirconium dichloride (A-4)

A 2.5 M n-BuLi solution in hexane (33.86 mL, 84.65 mmol) was added dropwise at 0° C. under stirring to a solution of 17.37 g of 1-(2,4,6-trimethyl-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)dimethylsilane (41.29 mmol) in 200 mL of Et₂O in a 500 mL 3-necked round flask. The resulting dark suspension was allowed to warm up to r.t and stirred for 1 h. Then a suspension of 9.55 g of ZrCl₄(40.98 mmol) in 100 mL of toluene was prepared, cooled to 0° C. and slowly added to the lithium salt mixture, previously cooled to 0° C. too. The resulting reaction mixture was stirred at r. t. for 12 h. The solvents were removed in vacuo yielding a residue, which was treated at r. t. with toluene (2×150 mL) and filtered on a G4 frit. The residue was further washed with toluene, while the filtrates were collected and discarded. The residue was dried in vacuo to give 17.24 g of a brick-red powder, which resulted to be the desired complex by NMR analysis, containing about 20% wt. of LiCl (yield 57.8%).

Synthesis of dimethylsilanediyl{1-(2-methyl-4,6-disopropylindenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dichloride (A-5)

a) Synthesis of chloro(2-methyl-4,6-disopropyl-1-indenyl)dimethylsilane

A 2.3 M HexLi solution in hexane (6.00 mL, 13.80 mmol) was added dropwise at 0° C. to a solution of 2.93 g of 2-methyl-4,6-diisopropyl-1-indene (13.67 mmol) in 30 mL of Et₂O. At the end of the addition, the resulting white suspension was allowed to warm up to room temperature and stirred for 1 h. A solution of Me₂SiCl₂(99%, 1.68 mL, d=1.064, 13.68 mmol) in 10 mL of Et₂O was added at 0° C. to the lithium salt solution, previously cooled to 0° C. The reaction mixture was allowed to warm up to room temperature and stirred for 3 h with final formation of a white suspension. The solvents were removed in vacuo and the residue was extracted with 30 mL of toluene to remove the LiCl. The filtrate was brought to dryness in vacuo at 40° C. to give 3.33 g of a thick orange oil. Crude yield=79.4%.
¹H NMR (δ, ppm, CDCl₃): 0.12 (s, 3H, Si—CH₃); 0.45 (s, 3H, Si—CH₃); 1.28-1.36 (m, 12H, CH₃); 2.31 (m, 3H, CH₃); 2.97 (m, 1H, J=7.43 Hz, CH); 3.24 (m, 1H, J=7.43 Hz, CH); 3.58 (s, 1H, CH); 6.77 (m, 1H, Cp-H); 7.01 (bm, 1H, Ar); 7.20 (bm, 1H, Ar).

b) Synthesis of 1-(2-methyl-4,6-disopropylindenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene) dimethylsilane

A 2.3 M HexLi solution in hexane (3.00 mL, 6.90 mmol) was added dropwise at 0° C. to a suspension of 1.41 g of 2,5-dimethyl-7H-cyclopenta[1,2-b:4,3-b′]-dithiophene (6.83 mmol) in 30 mL of Et₂O. The resulting brown solution was stirred at 0° C. for 1 h and then a solution of 2.10 g of chloro(2-methyl-4,6-disopropyl-1-indenyl)dimethylsilane (6.84 mmol) in 20 mL of Et₂O was added at the same temperature. The reaction mixture was then allowed to warm up to room temperature and stirred for 3 h with final formation of a brown suspension. The solvents were evaporated under reduced pressure and the residue was extracted with 30 mL of toluene. The extract was dried in vacuo to give 2.79 g of a sticky dark-brown solid, which was analyzed by ¹H-NMR spectroscopy. The latter showed the presence of the expected ligand, crude yield=68.5%. The product was used as such in the next step without further purification.
¹H NMR (δ, ppm, CD₂Cl₂): −0.34 (s, 3H, Si—CH₃); -0.32 (s, 3H, Si—CH₃); 1.27-1.39 (m, 12H, CH₃); 2.60 (s, 3H, CH₃); 2.62 (s, 3H, CH₃); 2.67 (s, 3H, CH₃); 2.96 (m, 1H, J=7.24 Hz, CH); 3.29 (m, 1H, J=7.24 Hz, CH); 3.87 (s, 1H, CH); 4.04 (s, 1H, CH); 6.82 (bs, 1H, Cp-H); 6.92 (m, 1H, CH); 6.94 (m, 1H, CH); 7.03 (bs, 1H, Ar); 7.23 (bs, 1H, Ar).

c) Synthesis of dimethylsilanediyl{1-(2-methyl-4,6-disopropylindenyl)-7-(2,5 dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dichloride (A-5)

A 2.3 M HexLi solution (5.1 mL, 11.73 mmol) was added dropwise at 0° C. to a solution of 2.79 g of 1-(2-methyl-4,6-disopropylindenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene) dimethylsilane (5.85 mmol) in 30 mL of Et₂O. At the end of the addition, the resulting brown solution was stirred for 1 h at room temperature. Then it was cooled again to 0° C. to add a suspension of 1.36 g of ZrCl₄(5.83 mmol) in 15 mL of toluene, previously cooled to 0° C. The reaction mixture was then allowed to warm up to room temperature and stirred for 16 h with final formation of a light brown suspension. The solvents were removed in vacuo and the crude residue was treated with 25 mL of toluene. The obtained suspension was filtered: the filtrate was eliminated, while the residue was dried to give 2.25 g of an orange powder, which resulted to be the target complex, yield=60.6% with LiCl. 0.9 g of this powder were treated with a mixture of 10 mL of toluene and 2 mL of isobutanol and stirred for 15 min at room temperature. The mixture was then filtered: the filtrate containing LiCl and by-products due to decomposition was discarded, while the residue was concentrated in vacuo yielding 0.5 g of an orange powder free from LiCl. This powder resulted to be the pure complex by ¹H NMR analysis.
¹H NMR (δ, ppm, CD₂Cl₂): 1.18 (s, 3H, Si—CH₃); 1.34 (s, 3H, Si—CH₃); 1.19 (d, 3H, J=6.85 Hz, CH₃); 1.20 (d, 3H, J=6.85 Hz, CH₃); 1.26 (d, 3H, J=6.85 Hz, CH₃); 1.35 (d, 3H, J=6.85 Hz, CH₃); 2.39 (s, 3H, CH₃); 2.42 (d, 3H, J=1.17 Hz, CH₃); 2.61 (d, 3H, J=1.17 Hz, CH₃); 2.82 (m, 1H, J=6.85 Hz, CH); 3.06 (m, 1H, J=6.85 Hz, CH); 6.64 (q, 1H, J=1.17 Hz, CH); 6.78 (q, 1H, J=1.17 Hz, CH); 6.80 (s, 1H, Cp-H); 6.93 (bt, 1H, Ar, H5); 7.32 (bq, 1H, Ar, H7).

Synthesis of rac dimethylsilyl{(2,4,7-trimethyl-1-indenyl)-7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)}zirconium dimethyl (A-6)

The ligand, [3-(2,4,7-trimethylindenyl)][7-(2,5-dimethyl-cyclopenta[1,2-b:4,3-b′]-dithiophene)]dimethyl silane, was prepared as described in WO 01/47939. 30.40 g of this ligand (72.26 mmol) and 170 ml of anhydrous THF were charged under nitrogen in a cylindrical glass reactor equipped with magnetic stirring bar. The brown solution so obtained was cooled and maintained at 0° C., while 58.4 ml of n-BuLi 2.5M in hexane (146 mmol) were added dropwise via dropping funnel. At the end of the addition, the dark brown solution was stirred for 1 hour at room temperature, then cooled to −50° C., and then 48.6 ml of MeLi 3.05 M in diethoxymethane (148.2 mmol) were added to it. In a Schlenk, 16.84 g of ZrCl_1-4(72.26 mmol) were slurried in 170 ml of toluene. Both mixtures were kept at −50° C. and the ZrCl₄slurry was quickly added to the ligand dianion solution. At the end of the addition, the reaction mixture was allowed to reach room temperature and stirred for an additional hour. A yellow-green suspension was obtained. ¹H NMR analysis shows complete conversion to the target complex. All volatiles were removed under reduced pressure, and the obtained free flowing brown powder was suspended in 100 ml of Et₂O. After stirring for a few minutes, the suspension was filtered over a G4 frit. The solid on the frit was then washed twice with Et₂O (until the washing solvent turns from brown to yellow), then dried under vacuum, and finally extracted on the frit with warm toluene (60° C.), until the filtering solution turns from yellow to colorless (about 650 ml of toluene); The extract was dried under reduced pressure to give 28.6 g of yellow powder, which ¹H-NMR showed to be the target complex, free from impurities. The yield based on the ligand was 73.3%.
¹H-NMR: (CD₂Cl₂, r.t.), ppm: −2.09 (s, 3H), −0.79 (s, 3H), 1.01 (s, 3H), 1.04 (s, 3H), 2.38 (s, 3H), 2.39 (s, 3H), 2.43 (d, 3H, J=1.37 Hz), 2.52 (s, 3H), 2.57 (d, 3H, J=1.37 Hz), 6.61 (dq, 1 H, 3=7.04 Hz, J=0.78 Hz), 6.81 (q, 1H, J=1.37 Hz), 6.85 (dq, 1H, J=7.04 Hz, J=0.78 Hz), 6.87 (q, 1H, J=1.37 Hz), 6.91 (s, 1H).

Polymerization Examples 1-5 and Comparative Examples 6-7

The cocatalyst methylalumoxane (MAO) was a commercial product which was used as received (Witco AG, 10% wt/vol toluene solution, 1.7 M in Al). The catalyst mixture was prepared by dissolving the desired amount of the metallocene with the proper amount of the MAO solution, (Al/Zr ratio=500) obtaining a solution which was stirred for 10 min at room temperature before being injected into the autoclave.

Polymerization (General Procedure)

6 mmol of Al(i-Bu)₃(as a 1M solution in hexane) and 1350 g of 1-butene were charged at room temperature in a 4-L jacketed stainless-steel autoclave, equipped with magnetically driven stirrer and a 35-mL stainless-steel vial, connected to a thermostat for temperature control, previously purified by washing with an Al(i-Bu)₃solution in hexanes and dried at 50° C. in a stream of nitrogen. The autoclave was then thermostated at the polymerization temperature, and then the toluene solution containing the catalyst/cocatalyst mixture was injected in the autoclave by means of nitrogen pressure through the stainless-steel vial, and the polymerization carried out at constant temperature for the time indicated in Table 1. Then stirring is interrupted; the pressure into the autoclave is raised to 20 bar-g with nitrogen. The bottom discharge valve is opened and the 1-butene/poly-1-butene mixture is discharged into a heated steel tank containing water at 70° C. The tank heating is switched off and a flow of nitrogen at 0.5 bar-g is fed. After cooling at room temperature, the steel tank is opened and the wet polymer collected. The wet polymer is dried in an oven under reduced pressure at 70° C. The polymerization conditions and the characterization data of the obtained polymers are reported in Table 1.

TABLE 1

				time	Yield	kg/	I.V.		mmmm	4,1	T_m
EX	Met	mg	T_pol	(min)	(g)	(g_cat*h)	(dL/g)	M_w/M_n	%	regioerrors	(Form II)

1	A-1	2	60	60	130	65.0	2.4	3.1	95.8	n.d.	105.5
2	A-1	2	70	60	125	62.5	2.0	3.9	95.3	n.d.	104.4
3	A-1	2	80	60	100	50.0	1.3	3.7	95.2	n.d.	103.9
4	A-4	3	70	60	82.5	27.5	1.7	n.a.	n.a.	n.a.	101
5	A-5	2	70	60	86.6	43.3	1.5	n.a.	n.a.	n.a.	100.2
3*	A-2	4	60	15	80	80.0	0.5	n.a.	85.5	n.d.	78
4*	A-3	3	70	60	109	36.3	1.3	3.1	89.0	n.d.	84

*= comparative
n.d. = not detectable
n.a. = not available

Examples 6-8 Influence of Hydrogen

The procedure of examples 1-5 has been repeated with the metallocene compound A-1 and an Al(MAO)/Zr ratio of 200, with the exception that an amount of H₂reported in table 3 is injected into the autoclave before the injection of the catalyst solution. The results are reported in table 3
TABLE 3

I.V.

T_pol time H₂ H₂ kg_PB/ dL/g, M_v

Ex mg ° C. (min) NmL ppm ⁺ (g_mtcene× h) (THN) (IV_THN)

6 2 70 60 0 0 82.5 2.34 479 800

7 2 70 60 100 2 163 n.a. n.a.

8 2 70 60 200 4 220 1.44 245 600

n.a. not available

⁺ ppm in liquid phase

From these examples result that hydrogen can be used as activating agent in order to increase the final yield.

Examples 9-12 ethylene/1-butene copolymers

The cocatalyst methylalumoxane (MAO) was a commercial product which was used as received (Crompton 10% wt/vol 1.7 M in Al). The catalyst mixture was prepared by dissolving 2 mg of A-1 with the proper amount of the MAO solution, (Al/Zr ratio=200) obtaining a solution which was stirred for 10 min at room temperature before being injected into the autoclave.
A 4.25 litres steel autoclave, equipped with magnetically stirred anchor (usual stirring rate 550 rpm) and with different Flow Record & Control systems (FRC), among which a FRC having maximum flow rate of 9000 gr/hour for 1-butene and two FRC having maximum flow rate of 500 and 30 g/h for ethylene is cleaned with warm nitrogen (1.5 barg N₂, 70° C., 1 hour). After the above mentioned autoclave cleaning, the stirring starts, 1-butene is fed into the reactor (1350 gr at 30° C.) with the amount of ethylene reported in table 4, together with 6 mmol of Al(i-Bu)₃(TIBA) (as a 1 M solution in hexane). Subsequently, the reactor inner temperature is raised from 30° C. to 70° C., the polymerisation temperature; as a consequence the pressure increases. When pressure and temperature are constant, the catalytic solution is fed into the reactor with a nitrogen overpressure and the polymerisation pressure is kept constant feeding only ethylene (amount indicated in table 3). The polymerisation is run for 60 minutes. Then the stirring is interrupted; the pressure into the autoclave is raised to 20 bar-g with nitrogen. The bottom discharge valve is opened and the 1-butene/poly-1-butene mixture is discharged into the steel heated tank containing water at 70° C. The tank heating is switched off and a flux of 0.5 bar-g nitrogen is fed. After 1 hour cooling at room temperature the steel tank is opened and the wet polymer collected. The wet polymer is dried in a oven under nitrogen at 70° C. The polymerization conditions and the characterization data of the obtained polymers are reported in Table 4

TABLE 4

	C₂in liq.		activity	C₂in copol.	R	I.V.
	phase	C₂fed	kg_PB/	mol %	(C₂/C₄)_copo/	dL/g	T_m	mmmm	ΔH
Ex	% wt	g	(g_mtcene× h)	(NMR)	(C₂/C₄)_{liq. phase}	THN	(Form II)	%	J/g

9	0.19	2.6	58	2.28	6.1	2.61	77.8	>90	19.4
10	0.38	4.1	88	2.99	4.0	2.65	75.7	>90	15.7
11	0.64	7.4	122	6.24	5.2	2.56	60.9	>90	0.8
12	0.38	9	191	n.a.	n.a.	n.a.	n.a.	n.a.	n.a.

n.a. not allowable

From table 4 it results that the yield of the process of the present invention can be increased by using ethylene or both ethylene and hydrogen (example 16). In addition the use of ethylene further increases the molecular weight of the polymer.

Claims

1. A process for preparing 1-butene polymers, said process comprising polymerizing 1-butene or copolymerizing 1-butene with ethylene, propylene or an alpha-olefin of formula CH₂═CHT wherein T is a C₃-C₁₀alkyl group, in the presence of a catalyst system obtainable by contacting:

(A) a metallocene compound having the following formula (I)

wherein:

M is an atom of a transition metal selected from those belonging to group 3, 4, or to the lanthanide or actinide groups in the Periodic Table of the Elements;

X, equal to or different from each other, is a hydrogen atom, a halogen atoms or R, OR, OR′O, OSO₂CF₃, OCOR, SR, NR₂or PR₂group, wherein R is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and the R′ is a C₁-C₂₀-alkylidene, C₆-C₂₀-arylidene, C₇-C₂₀-alkylarylidene, or C₇-C₂₀-arylalkylidene radical.

R¹, R², R⁵, R⁶, R⁷, R⁸and R⁹, equal to or different from each other, are hydrogen atoms, or linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or R⁵and R⁶, and/or R⁸and R⁹can optionally form a saturated or unsaturated, 5 or 6 membered rings, said ring can bear C₁-C₂₀alkyl radicals as substituents;

with the proviso that at least one of R⁶or R⁷is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements;

R³and R⁴, equal to or different from each other, are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and

(B) an alumoxane and/or a compound capable of forming an alkyl metallocene cation.

2. The process according to claim 1 wherein in the metallocene of formula (I) R⁷is preferably a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; otherwise when R⁶is different from a hydrogen atom, R⁷is a hydrogen atom.

3. The process according to claims 1 or 2 wherein the catalyst system is obtained by further contacting the components (A) and (13) with:

(C) an organo aluminum compound.

4. The process according to anyone of claims 1-3 wherein in the metallocene of formula (I) X is a hydrogen atom, a halogen atom or a OR′O or R group wherein R is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl, or C₇-C₂₀-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements and R′ is a divalent radical selected from the group consisting of C₁-C₂₀-alkylidene, C₆-C₂₀-arylidene, C₇-C₂₀-alkylarylidene, and C₇-C₂₀-arylalkylidene radicals.

5. The process according to anyone of claims 1 to 4 wherein in the metallocene of formula (I) R¹and R²are the same and are C₁-C₁₀allyl radicals optionally containing one or more silicon atoms.

6. The process according to anyone of claims 1 to 5 wherein in the metallocene of formula (I) R⁸and R⁹, equal to or different from each other, are C₁-C₁₀alkyl or C₆-C₂₀aryl radicals; R⁵is hydrogen atoms or methyl radicals and R⁶is a hydrogen atom or a methyl, ethyl or isopropyl radical.

7. The process according to anyone of claims 1 to 6 wherein in the metallocene of formula (I) R³, R⁴and R⁷, equal to or different from each other, are C₁-C₁₀alkyl radicals.

8. The process according to anyone of claims 1 to 7 wherein the compound of formula (I) has formula (Ia) or (Ib):

Wherein

M, X, R¹, R², R⁸and R⁹have the meaning described in claim 1;

R³and R⁴, equal to or different from each other, are linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements;

R⁶and R⁷are a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements.

9. The process according to claim 8 wherein R³, R⁴, R⁶and R⁷are C₁-C₁₀-alkyl radicals.

10. The process according to anyone of claims 1-9 wherein 1-butene and ethylene are copolymerized in the presence of the catalyst system reported above.

11. The process according to claim 10 wherein the amount of ethylene in the liquid phase ranges from 0.01 to 30% by weight.

12. The process according to anyone of claims 1-12 wherein said process is carried out in the presence of hydrogen.

13. The process according to claim 12 wherein the concentration of hydrogen in the liquid phase ranges from 0.5 ppm to 20 ppm.

14. A 1-butene homopolymer having the following characteristics:

isotactic pentads (mmmm)>90;

intrinsic viscosity (I.V.) measured in tetrahydronaphtalene (THN) at 135° C.>1.2;

melting point (D.S.C.) higher than 100° C.; and

molecular weight distribution Mw/Mn<4;

15. A 1-butene homopolymer having the following characteristics:

isotactic pentads (mmmm)>95;

intrinsic viscosity (I.V.) measured in tetrahydronaphtalene (THN) at 135° C.>1.5;

melting point (D.S.C.) higher than 100° C.; and

molecular weight distribution Mw/Mn<4.

16. A 1-butene/ethylene copolymer having an ethylene content comprised between 0.2% by mol and 15% by mol obtainable by the process of claim 1 having the following characteristics:

isotactic pentads (mmmm)>90

intrinsic viscosity (I.V.) measured in tetrahydronaphtalene (THN) at 135° C.>1.2

wherein ethylene content in the polymer (C₂) (% by mol) and the melting point of the polymer (Tm) meet the following relation:

Tm<−4.4C ₂+92.0.

17. A metallocene compound of formula (II):

wherein:

X, equal to or different from each other, is a hydrogen atom, a halogen atom, a R, OR, OR′O, OSO₂CF₃, OCOR, SR, NR₂or PR₂group wherein R is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl, C₃-C₂₀-cycloalkyl, C₆-C₂₀-aryl, C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and R′ is a C₁-C₂₀-alkylidene, C₆-C₂₀-arylidene, C₇-C₂₀-alkylarylidene, or C₇-C₂₀-arylalkylidene radical;

R¹, R², R⁵, R⁶, R⁷, R⁸and R⁹, equal to or different from each other, are hydrogen atoms, or linear or branched, saturated or unsaturated C₁-C₂₀-alkyl C₃-C₂₀-cycloalkyl C₆-C₂₀-aryl C₇-C₂₀-alkylaryl or C₇-C₂₀-arylalkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or R⁸and R⁹can optionally form a saturated or unsaturated, 5 or 6 membered ring;

R⁶is a linear or branched, saturated or unsaturated C₁-C₂₀-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or it can optionally form with R⁵a saturated or unsaturated, 5 or 6 membered ring, said ring can bear C₁-C₂₀alkyl radicals as substituents.

18. The metallocene compound according to claim 17 wherein:

R¹, R², are the same and are C₁-C₁₀alkyl radicals optionally containing one or more silicon atoms;

R⁸and R⁹, equal to or different from each other, are C₁-C₁₀alkyl or C₆-C₂₀aryl radicals;

R⁵is a hydrogen atom or a methyl radical;

R⁷is a hydrogen atom;

R³and R⁴equal to or different from each other are C₁-C₁₀-alkyl radicals;

R⁶is a C₁-C₁₀-alkyl radical.

19. A ligand of formula (III):

wherein R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸and R⁹have the meaning described in claim 12.